1、SAE-AMS3867/6ADOPTION NOTICESAE-AMS3867/6, “BORON FILAMENT TAPE, EPOXY-RESIN-IMPREGNATED TYPEB8.0-E180 (TYPE BO.203-E82)“, was adopted on 11-FEB-93 for useby the Department of Defense (DoD). Proposed changes by DoDactivities must be submitted to the DoD Adopting Activity:Commander, Defense Supply Ce
2、nter Philadelphia, ATTN: DSCP-ILEA,700 Robbins Avenue, Philadelphia, PA 19111-5096. Copies of thisdocument may be purchased from the Society of AutomotiveEngineers 400 Commonwealth Drive Warrendale, Pennsylvania, UnitedStates, 15096-0001. http:/www.sae.org/_Custodians: Adopting Activity:DLA - ISAir
3、Force - 11DLA - GSReviewer Activities:Air Force - 84, 99FSC 9330DISTRIBUTION STATEMENT A: Approved for public release; distributionis unlimited.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-SAE Techn
4、ical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirelyvoluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the
5、 sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions.Copyright 2001 Society of Automotive Engineers, Inc.All rights reserved. Printed in U.S.A.QUESTIO
6、NS REGARDING THIS DOCUMENT: (724) 772-7161 FAX: (724) 776-0243TO PLACE A DOCUMENT ORDER: (724) 776-4970 FAX: (724) 776-0790SAE WEB ADDRESS: http:/www.sae.org400 Commonwealth Drive, Warrendale, PA 15096-0001AEROSPACE MATERIAL SPECIFICATIONAMS 3867/6AIssued OCT 1984Revised APR 1991Reaffirmed APR 2001S
7、uperseding AMS 3867/6Boron Filament Tape, Epoxy-Resin-ImpregnatedType B8.0-E180(Type B0.203-E82)FOREWORDThis Reaffirm contains format/editorial changes only.1. SCOPE:1.1 Form: This specification covers one type of epoxy-resin-impregnated boron filaments 0.0008 inch (0.203 mm) in diameter in the form
8、 of continuous tape supported on a glass cloth carrier.1.2 Application: Primarily for use in structural composites operating in the range -55 to +82 C (-67 to +180 F).2. APPLICABLE DOCUMENTS: See AMS 3867.3. TECHNICAL REQUIREMENTS: 3.1 Basic Specification: The complete requirements for procuring the
9、 tape described herein shall consist of this document and the latest issue of the basic specification, AMS 3867.3.2 Material: Shall be AMS 3865, high-modulus, 0.0080 inch (0.203 mm) nominal diameter boron filaments impregnated with epoxy resin formulated to meet the requirements specified herein and
10、 supported by an AMS 3824, Style 104, glass cloth carrier.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3867/6A SAE AMS 3867/6A- 2 -3.2.1 Storage Life: Tape shall meet the requirements of this sp
11、ecification when stored in the original unopened containers for a total storage time of 7 months at not higher than -18 C (0 F) and, in addition, 7 days (cumulative) at 25 C 3 (77 F 5).3.2.2 Working Life: Tape shall meet the requirements of this specification when tested after continuous exposure fo
12、r up to 20 days within the relative humidity and temperature limits shown in Figure 1.FIGURE 13.3 Properties of Uncured Impregnated Tape: Shall be as follows; tests shall be performed on the tape after warming to above the dew point prior to sampling and in accordance with test methods listed in the
13、 basic specification:3.3.1 Volatile Content by weight 0.3 - 1.7%3.3.2 Resin Solids by weight 32% 23.3.3 Resin Flow by weight 9 - 18%3.3.4 Gel Time, seconds Preproduction Value 20%3.3.5 TackTape to Interleaf Carrier As agreed uponTape to Tool Shall adhere for not less than30 minutes3.3.6 Dimensions:
14、The thickness of the uncured tape, including scrim, shall be not less than 0.0089 inch (0.226 mm) and the width shall be 6.0 inches (152 mm), unless otherwise ordered. The tape shall contain 102 to 108 filaments for each inch (25.4 mm) width of the tape.Copyright SAE International Provided by IHS un
15、der license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3867/6A SAE AMS 3867/6A- 3 -3.4 Properties of Cured Laminate: Shall be as follows, determined on specimens cut from a test panel prepared and tested in accordance with methods specified in the ba
16、sic specification: 3.4.1 Mechanical Properties: Shall be as specified in Table 1.3.4.1.1 Fiber Volume: Normalized strength and modulus values specified in Table 1 are based on 51% boron filament by volume, determined on the cured laminates for testing. For calculations, use boron filament density of
17、 2.380 Mg/m3.3.4.1.2 Nominal Cured Thickness per Ply: Shall be 0.0092 inch 0.0003 (0.234 mm 0.008).TABLE 1 - Mechanical Properties of Cured LaminatePropertyTest1TemperatureCTest1TemperatureFTime at TestTemperatureAverage Values,minimum2Ultimate StrengthpsiAverage Values,minimum2Ultimate StrengthMPaA
18、verage Values,minimum2Initial Modulus106 psiAverage Values,minimum2Initial ModulusMPaCompression,(0 degree)RT8282RT18018030 minutes200 hours375,000140,000125,000258696586233.031.031.0227,527213,737213,737Flexure(0 degree)RT8282RT18018030 minutes200 hours250,000180,000160,00017241241110327.020.020.01
19、86,158137,895137,895Flexure,(90 degrees)RT8282RT18018030 minutes200 hours11,0008,0007,00075.855.248.32.00.80.813,7905,5165,516Tension,(0 degree)RT8282RT18018030 minutes200 hours200,000150,000140,0001379103496530.026.026.0206,843179,264179,264Tension,(90 degrees)RT8282RT18018030 minutes200 hours7,000
20、3,0002,50048.320.717.23.01.00.720,6846,8954,826Shear,Interlaminar(0 degree)RT8282RT18018030 minutes200 hours14,5007,0004,000100.048.327.6-1 All room temperature values shall be measured at 25 C 3 (77 F 5) and a relative humidity not higher than 65%. Allother tests shall be conducted at the noted tem
21、perature 3 C (5 F).2 Requirements are specified as the average of the number of determinations per test required in AMS 3867. Individualminimums shall be not less than 90% of the value specified for 0-degree orientation specimens and not less than 85%for 90-degree orientation specimens.Copyright SAE
22、 International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3867/6A SAE AMS 3867/6A- 4 -4. QUALITY ASSURANCE PROVISIONS: See AMS 3867.5. PREPARATION FOR DELIVERY: See AMS 3867.6. ACKNOWLEDGMENT: See AMS 3867.7. REJECTIONS: See AMS 3867.8. NOTES: See AMS 3867.PREPARED UNDER THE JURISDICTION OF AMS COMMITTEE “P“Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-