SAE AMS 3894 10A-1989 Carbon Fiber Tape and Sheet Epoxy Resin Impregnated G 210 000 (1448) Tensile 20 000 000 (138) Modulus 175 (347)《G210000(1448)拉力、20000000(138)模数、175(347)的环氧树脂浸.pdf

1、 AEROSPACE MATERIAL SPECIFICATION Carbon Fiber Tape and Sheet Epoxy Resin Impregnated G 210,000 (1448) Tensile, 20,000,000 (138) Modulus, 175 (347) SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use o

2、f this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or

3、 cancelled. SAE invites your written comments and suggestions. Copyright 2005 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise,

4、 without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA) Fax: 724-776-0790 Email: custsvcsae.org SAE WEB ADDRESS: http:/www.sae.org AMS 3894/10AIssued APR 1983 Revised JAN 1989 Reaffirmed JUN 2005 Superseding A

5、MS 3894/10 1. SCOPE:1.1 Form: This specification covers one type of epoxy-resin-impregnated carbonfibers in the form of tape and sheet.1.2 Application: Primarily for use in structural composites requiring hightensile strength up to 175C (347F).1.3 Classification: G 210,000 psi (1448 MPa) tensile str

6、ength, 20,000,000 psi(138 GPa) tensile modulus carbon fiber impregnated with epoxy resin forservice up to 175C (347F).2. APPLICABLE DOCUMENTS: See AMS 3894.3.TECHNICAL REQUIREMENTS:3.1 Basic Specification: The complete requirements for procuring the productdescribed herein shall consist of this docu

7、ment and the latest issue of thebasic specification, AMS 3894.3.2 Material: The product shall be AMS 3892/1 high tensile strength carbonfibers impregnated with epoxy resin formulated to meet the requirementsspecified herein.3.2.1 Storage Life: The product shall meet the requirements of thisspecifica

8、tion when tested at any time up to six months from date ofreceipt by purchaser provided it has been stored in the original unopenedcontainers at not higher than -18C (0F).3.2.2 Working Life: The product shall meet the requirements of thisspecification when tested after continuous exposure for up to

9、20 dayswithin the relative humidity and temperature limits shown in Fig. 1.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE - 2 - AMS 3894/10A AMS 3894/10A1.5Preproduction Value 10%Shall adhere fo

10、r not lessthan 30 minutes3.4.1Mechanical Properties: Shall be as specified in Table I.3.4Properties of Cured Laminates: Shall be as follows, determined on specimenscut from a test panel prepared as specified in the basic specification andtested in accordance with test methods specified therein:3.3.5

11、 Tack3.3.4 Gel Time, minimum3.3.3 Resin Flow, % by weight 10 - 303.3.2 Resin Solids Content, % by weight Preproduction Value 3Test temperature: 120C 5(248F 9)Test time: 15 - 60 minutes3.3.1 Volatile Content, % of resinweight, maximum3.3 Properties of Uncured Impregnated Product: Shall be as specifie

12、d in 3.3.1through 3.3.5. Tests shall be performed on the product after warming toabove the dew point prior to sampling and in accordance with test methodslisted in the basic specification.Figure 1TemperatureCopyright SAE International Provided by IHS under license with SAENot for ResaleNo reproducti

13、on or networking permitted without license from IHS-,-,-SAE - 3 - AMS 3894/10A AMS 3894/10A3.4.2 Density: Shall be determined on the test laminate used to determinemechanical properties; values for each test laminate shall be reported.Fiber density and cured resin density shall also be reported.3.4.

14、3Void Content: Shall be not greater than 1%.4. QUALITY ASSURANCE PROVISIONS: See AMS 3894.5. PREPARATION FOR DELIVERY: Shall be in accordance with AMS 3894 and thefollowing:5.1 Exterior package marking shall indicate storage temperature of “-18C (0F),maximum“.6. ACKNOWLEDGMENT: See AMS 3894.7. REJEC

15、TIONS: See AMS 3894.8. NOTES: See AMS 3894.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-SAE - 4 - AMS 3894/10A AMS 3894/10AValue (1)Test Temperature (3)TABLE IMECHANICAL PROPERTIES OF CURED LAMINA

16、TES-55C 5- 30C(-67F 9)(68psiMPa20- 86F)psiMPaProperty (2)Tensile Strength, minimumLongitudinal TransverseTBR (4) TBRTBR210,0001,448TBR7,00048175C 5(347F 9)psiMPa178,0001,2274,6003218,000,000124,106TBRTBRTBRTBRTBRNA (5)13.0TBRTBRTBRTBRTBRTBR155,0001,06916,500,000113,7647,80053.8137,895TBR20,000,000TB

17、RTBRTBR TBRTensile Modulus, minimumLongitudinal TransverseCompressive Strength, minimumLongitudinal TransverseCompressive Modulus, minimumLongitudinal TransverseFlexural Strength, minimumLongitudinalFlexural Modulus, minimumLongitudinalInterlaminar Shear Strength, minimumTBRTBRNANANANA240,0001,655TB

18、RTBRTBRTBRNANATBRTBRTBRTBR204,000NA1,8901,407117,21110317,000,00015,000NOTES:1.Average of 4 determinations for each property except interlaminar shear strength. No individual value shall beless than 90% of the average value specified.2.Property values are based on a test laminate with a fiber volume

19、 of 60% 3. Certain property values may beadjusted for other fiber volumes of the test laminate by multiplying the listed requirement by the ratio: Actual Fiber Volume, %/60. When such adjustment is used, report the actual fiber volume of the test laminate.3.Test after not less than 30 minutes exposure at the test temperature.4.TBR - To be reported in preproduction test report.5.NA - Not applicable.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-,-