SAE AMS 3899 1B-1993 Carbon Fiber Tape and Sheet Polysulfone Resin Impregnated C PS 172 (1170) Tensile 16 (110) Modulus 120 (248)《C PS 172(1170)拉力、16(110)模数、120(248)的聚砜树脂浸渍的碳纤维带和薄板.pdf

1、SpaceAEROSPACE3899/1B400 Commonwealth Drive, Warrendale, PA 15096-0001SPECIFICATIONIssued 15 APR 1980Revised 1 OCT 1993Submitted for recognition as an American National StandardSuperseding AMS 3899/1ACARBON FIBER TAPE AND SHEETPolysulfone Resin ImpregnatedC PS 172 (1170) Tensile, 16 (110) Modulus, 1

2、20 (248)1. SCOPE:1.1 Form:This specification covers one type of thermoplastic, polysulfoneresin-impregnated carbon fibers in the form of tape or sheet.1.2 Application:These products have been used typically in structural composites requiringhigh strength up to 120 C (248 F), but usage is not limited

3、 to suchapplications.1.3 Classification:C PS 170 ksi (1170 MPa) tensile strength, 16 Msi (110 GPa) tensile moduluscarbon fiber impregnated with polysulfone resin for service up to 120 C(248 F).2. APPLICABLE DOCUMENTS:See AMS 3899.3. TECHNICAL REQUIREMENTS:3.1 Basic Specification:The complete require

4、ments for producing the product described herein shallconsist of this document and the latest issue of the basic specification,AMS 3899.3.2 Material:The product shall be AMS 3892/1 high-tensile-strength carbon fibersimpregnated with heat-reactive, thermoplastic, polysulfone resin formulatedto meet t

5、he requirements specified herein.SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineeringsciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any pat

6、ent infringementarising therefrom, is the sole responsibility of the user.“SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your writtencomments and suggestions.Copyright 1993 Society of Automotive Engineers, Inc.All r

7、ights reserved. Printed in U.S.A.MATERIALThe Engineering SocietyFor Advancing MobilityLand Sea Air and SpaceINTERNATIONALAMS 3899/1BCopyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3899/1B SAE AMS 3

8、899/1B3.2.1 Storage Life: The product shall meet the requirements of thisspecification when tested at any time up to one year from date of receiptby purchaser, provided it has been stored at room temperature in theoriginal containers.3.3 Properties:The product shall conform to the following requirem

9、ents:3.3.1 Resin Impregnated Fiber Tape and Sheet: Shall be as specified below; testsshall be performed on the as-supplied product and in accordance with testmethods listed in the basic specification, AMS 3899.3.3.1.1 Volatile Content by Weight: Shall be 5% maximum when tested at 260 C 5 (500 F 9) f

10、or 30 minutes 5.3.3.1.2 Total Resin Solids Content by Weight: Shall be 34% 3.3.3.1.3 Resin Flow by Weight: Shall be 4.0% maximum.3.3.2 Molded Laminates: Shall be determined on specimens cut from a test panelprepared as specified in the basic specification and tested in accordancewith test methods sp

11、ecified therein.3.3.2.1 Mechanical Properties: Shall be as specified in Table 1.3.3.2.2 Density: Shall be determined on each test panel used to determinemechanical properties; values shall be reported. Fiber density and resindensity shall also be reported.3.3.2.3 Void Content: Shall be not greater t

12、han 4%.4. QUALITY ASSURANCE PROVISIONS:See AMS 3899.5. PREPARATION FOR DELIVERYSee AMS 3899.6. ACKNOWLEDGMENT:See AMS 3899.7. REJECTIONS:See AMS 3899.8. NOTES:See AMS 3899.- 2 -Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted wit

13、hout license from IHS-,-TABLE 1 - Mechanical Properties of Prepared LaminatesProperty psi MPa psi MPa psi MPaValueValueValueValueValueValueTestTest Test Test Test TestTemperatureTemperature Temperature Temperature Temperature Temperature-55 C 5 -55 C 5 20 to 30 C 20 to 30 C 120 C 5 120 C 5 (-67 F 9)

14、 (-67 F 9) (68 to 86 F)(68 to 86 F) (248 F 9) (248 F 9)Tensile Strength,Longitudinal 190,000 1,310 170,000 1,170 160,000 1,103Transverse 4,50031.0 4,00027.6 3,50024.1Tensile Modulus,Longitudinal 17 x 10 117,211 16 x 10 110,316 15 x 10 103,421Transverse1 x 106,9480.9 x 106,205 0.8 x 105,516 Compressi

15、veStrength,Longitudinal120,00082790,000621 75,000 517Compressive Modulus,Longitudinal17 x10117,211 16 x10110,316 15 x 10103,421FlexuralStrength,Longitudinal200,000 1,379 170,000 1,172 125,000862FlexuralModulus,Longitudinal16 x10110,31615 x10103,421 14 x1096,527Short Beam ShearStrength13,000 89.6 10,

16、000 68.9 6,000 41.4NOTES: A. Average of four determinations per test. No individual value shall be less than 90% of the average valuespecified.B. Test after 30 minutes f 1 exposure at the test temperature.C. Property values are based on a test laminate with a fibervolume of 57% 3. Certain property v

17、alues may beadjusted for other fiber volumes of the test laminate by multiplying the listed requirement by the ratio:laminate.Actual Fiber Volume, %/57. When such adjustment is used, report the actual fiber volume of the test(A)(A)(A)(A)(A)(A)(B)(B)(C)(C)666(C)(C)(C)(C)6666666 6AMS 3899/1B SAE AMS 3899/1B- 3 -(B)(B)(B)(B)6Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-