SAE AMS 3906 1B-1992 Glass Non-Woven Fiber Tape and Flat Sheet Epoxy Resin Impregnated for Hand and Machine Layup GL-I-36 - 120 (248)《手工和机器铺叠用环氧树脂浸渍的玻璃非机织纤维带和平板GL-I-36-120(248)》.pdf

1、SAE-AMS3906/1ADOPTION NOTICESAE-AMS3906/1, “GLASS NON-WOVEN FIBER TAPE AND FLAT SHEET EPOXYRESIN IMPREGNATED, FOR HAND AND MACHINE LAYUP, GL-I-36 -120(248)“, was adopted on 30-SEP-89 for use by the Department ofDefense (DoD). Proposed changes by DoD activities must besubmitted to the DoD Adopting Ac

2、tivity: Commander, Naval AirWarfare Center, Aircraft Division, Code 414100B120-3, Highway547, Lakehurst, NJ 08733-5100. Copies of this document may bepurchased from the Society of Automotive Engineers 400Commonwealth Drive Warrendale, Pennsylvania, United States,15096-0001. http:/www.sae.org/_Custod

3、ians: Adopting Activity:Navy - ASArmy - MRNavy - ASAREA CMPSDISTRIBUTION STATEMENT A: Approved for public release; distributionis unlimited.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-The Engineeri

4、ng SocietyFor Advancing MobilityAEROSPACE AMS 3906/1BLand Sea Air and SpaceINTERNATIONALMATERIALIssued JUN 1975400 Commonwealth Drive, Warrendale, PA 15096-0001SPECIFICATIONRevised JUL 1992ReaffirmedOCT 1997Submitted for recognition as an American National Standard Superseding AMS 3906/l AGLASS NON-

5、WOVEN FIBER TAPE AND FLAT SHEETEpoxy Resin Impregnated, For Hand and Machine LayupGL-I-36 - 120 (248)1. SCOPE:1.1 Form:This specification covers one type of epoxy-resin-impregnated, non-woven, glass fiber in the form oftape for hand or machine layup and of flat sheet.1.2 Application:These products h

6、ave been used typically in structural composites requiring moderate strength up to120 C (248 F), but usage is not limited to such applications.1.3 Classification:GL-I-36 - 120 (248), non-woven “E” glass fiber impregnated with epoxy resin for service from-55 to +120 C (-67 to +248 F).2. APPLICABLE DO

7、CUMENTS:See AMS 3906.3. TECHNICAL REQUIREMENTS:3.1 Basic Specification:The complete requirements for procuring the product described herein shall consist of this documentand the latest issue of the basic specification, AMS 3906.SAE Technical Standards Board Rules provide that: This report is publish

8、ed by SAE to advance the state of technical and engineering sciences. The use of this report is entirelyvoluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the sole responsibility of the user.”SAE reviews each technical rep

9、ort at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions,Copyright 1997 Society of Automotive Engineers, IncAll rights reserved. Printed in U.S.A.QUESTIONS REGARDING THIS DOCUMENT: (412) 77297154 FAX: (412) 776-0243TO

10、PLACE A DOCUMENT ORDER: (412) 776-4970 FAX: (412) 776-0790Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/1B SAE AMS 3906/1B3.2 Product:Shall be a non-woven, general purpose, “E” glass fiber m

11、eeting the requirements of MIL-R-60346,Type I, impregnated with epoxy resin formulated to meet the requirements specified herein.3.3 Properties of Uncured Product:Shall be as shown in Table 1, 3.3.6, and 3.3.7. Tests shall be performed on the product as-received,after warming to above the dew point

12、prior to sampling.TABLE 1 - PropertiesParagraph Property Requirement Test Method3.3.1 Volatile Content by2%ASTM D 3530weight, maximum 165C(329F9)15 minutes 13.3.2 Total Nonfiber Content 36% 3by weightASTM D 35293.3.3 Resin Flow by weight17%7ASTM D 3531165C5(329F9)3.3.4 Gel Time 4 minutes 3 ASTM D 35

13、32165 C 5 (329 F 9)3.3.5 Tack Shall adhere for 4.5.2 of AMS 390630 minutes, minimum3.3.6 Total weight per unit area, determined in accordance with 4.5.3 of AMS 3906, shall be as ordered;available levels are shown below.259 grams/square yard 19 (310 g/m2 23)282 grams/square yard 23 (337 g/m2 28)386 g

14、rams/square yard 28 (462 g/m2 33)3.3.7 Ply thickness, uncured, determined in accordance with 4.5.4 of AMS 3906, shall be as ordered;available levels are shown below.0.006 inch 0.002 (0.15 mm 0.05)0.007 inch 0.002 (0.18 mm 0.05)0.011 inch 0.003 (0.28 mm 0.08)Copyright SAE International Provided by IH

15、S under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/1B SAE AMS 3906/1BSee AMS 3906.8. NOTES:See AMS 3906.7. REJECTIONS:See AMS 3906.6. ACKNOWLEDGMENT:See AMS 3906.5. PREPARATION FOR DELIVERY:See AMS 3906.4. QUALITY ASSURANCE PROVISIONS:3.

16、4.4 Fiber Volume: Shall be determined in accordance with 45.5 of AMS 3906 on the test laminateused to determine mechanical properties; values for each laminate shall be reported. The fiberdensity to be used shall be 2.54 g/cm3.3.4.3 Void Content: Shall be not greater than 4%, determined in accordanc

17、e with ASTM D 2734.3.4.2 Density: Shall be determined in accordance with ASTM D 792 on the test laminate used todetermine mechanical properties; values for each test laminate shall be reported. Cured resindensity shall also be reported.3.4.1 Mechanical Properties: Shall be as shown in Table 2.Shall

18、be as follows, determined on specimens cut from a test panel prepared and tested as specifiedin the basic specification:3.4 Properties of Cured Laminate:Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-

19、AMS 3906/1B SAE AMS 3906/1BTABLE 2A - Minimum Average Mechanical Properties(A), Inch-Pound UnitsPropertyValue, Tested Value, Tested Value, Testedat -67 F 9 at 68 to 86 F at 248 F 9ksi ksi ksiTestMethodTensile Strength(B)Longitudinal 125Transverse TBRTensile Modulus(B)LongitudinalTransverse6.0 x103TB

20、RCompressive Strengtht (B)LongitudinalTransverse95.0NACompressive Modulus(B)LongitudinalTransverseTBRNAFlexural Strength(B)LongitudinalFlexural Modulus(B)160Longitudinal5.0 x 103Short Beam Shear Strength TBR115TBR5.8 x 103TBR80.0TBR4.8 x 103TBR1304.8 x 10375.75.0TBR4.0 x 103TBR40.0NATBRNA60.04.0 x 1

21、03TBRASTM D 3039ASTM D 3039ASTM D 695ASTM D 695ASTM D 790ASTM D 790ASTM D 2344-4-Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/1B SAE AMS 3906/1BTABLE 28 - Minimum Average Mechanical Propert

22、ies(A), Sl UnitsPropertyValue, Tested Value, Tested Value, Testedat -55 C 5 at 20 to 30 C at 120 5MPa MPa MPaTestMethodTensile Strengtht(B)LongitudinalTransverseASTM D 3039862TBR793 517TBR TBRTensile Modulus(B)ASTM D 3039LongitudinalTransverse41.4 x 103TBR40 x 10327.6 x 103TBR TBRCompressive Strengt

23、h(B)LongitudinalTransverseASTM D 695M655NA552 276TBR NACompressive Modulus(B)LongitudinalTransverseASTM D 695MTBRNA33.1 x 103TBRTBR NAFlexural Strengtht(B)LongitudinalFlexural Modulus(B)ASTM D 790M1103 896 414ASTM D 790MLongitudinal34.5 x 10333.1 x 10327.6 x 10352 TBRShort Beam Shear Strength TBR AS

24、TM D 2344-5-Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/1B SAE AMS 3906/1BNOTES:(A) Average of three determinations per test. No individual value shall be less than 90%of the average value

25、 specified. Test after not less than 30 minutes exposure at the testtemperature.(8) Property values are based on a test laminate with a fiber volume of 50% 3. Certainproperty values may be adjusted for other fiber volumes of the test laminate by multiplyingthe listed requirement by the ratio: Actual

26、 Fiber Volume, %/50. When such adjustment isused, report the actual fiber volume of the test laminate.TBR - To be reported.NA - Not applicable.PREPARED UNDER THE JURISDICTION OF AMS COMMITTEE “P“-6-Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-