SAE AMS 3906 4B-1992 Glass Non-Woven Fiber Tape and Flat Sheet Epoxy Resin Impregnated for Hand and Machine Layup GL-III-26 - 150 (302)《手工和机器铺叠用环氧树脂浸渍的玻璃非机织纤维带和平板GL-III-26-150(302).pdf

1、SAE-AMS3906/4ADOPTION NOTICESAE-AMS3906/4, “GLASS NON-WOVEN FIBER TAPE AND FLAT SHEET EPOXYRESIN IMPREGNATED, FOR HAND AND MACHINE LAYUP GL-III-26 - 150(302)“, was adopted on 30-SEP-89 for use by the Department ofDefense (DoD). Proposed changes by DoD activities must besubmitted to the DoD Adopting

2、Activity: Commander, Naval AirWarfare Center, Aircraft Division, Code 414100B120-3, Highway547, Lakehurst, NJ 08733-5100. Copies of this document may bepurchased from the Society of Automotive Engineers 400Commonwealth Drive Warrendale, Pennsylvania, United States,15096-0001. http:/www.sae.org/_Cust

3、odians: Adopting Activity:Navy - ASArmy - MRNavy - ASAREA CMPSDISTRIBUTION STATEMENT A: Approved for public release; distributionis unlimited.Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-SAE Technic

4、al Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and enginee ring sciences. The use of this report is entirelyvoluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefrom, is the

5、sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invit es your written comments and suggestions.Copyright 1997 Society of Automotive Engineers, Inc.All rights reserved. Printed in U.S.A.QUESTIO

6、NS REGARDING THIS DOCUMENT: (412) 772-7154 FAX: (412) 776-0243TO PLACE A DOCUMENT ORDER: (412) 776-4970 FAX: (412) 776-0790400 Commonwealth Drive, Warrendale, PA 15096-0001AEROS PACE MATERIAL SPECIFIC ATIONSubmitted for recognition as an American National StandardAMS 3906/4BIssued JUN 1975Revised JU

7、L 1992Reaffirmed OCT 1997Superseding AMS 3906/4AGlass Non-Woven Fiber T ape and Flat SheetEpoxy Resin Impregnated, For Hand and Machine LayupGL-III-26 - 150 (302)1. SCOPE:1.1 Form: This specification covers one type of epoxy-resin-impregnated, non-woven, glass fiber in the form of tape for hand or m

8、achine layup and of flat sheet.1.2 Application: These products have been used typically in structural composites requiring high strength up to 150 C (302 F), but usage is not limited to such applications.1.3 Classification: GL-III-26 - 150 (302), non-woven “S” glass fiber impregnated with epoxy resi

9、n for service from -55 to +150 C (-67 to +302 F).2. APPLICABLE DOCUMENTS: See AMS 3906.3. TECHNICAL REQUIREMENTS: 3.1 Basic Specification: The complete requirements for procuring the product described herein shall consist of this document and the latest issue of the basic specification, AMS 3906.Cop

10、yright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/4B SAE AMS 3906/4B- 2 -3.2 Product: Shall be a non-woven, high tensile strength, “S” glass fiber meeting the requirements of MIL-R-60346, Type III,

11、 impregnated with epoxy resin formulated to meet the requirements specified herein.3.3 Properties of Uncured Product: Shall be as shown in Table 1, 3.3.6, and 3.3.7. Tests shall be performed on the product as-received, after warming to above the dew point prior to sampling.3.3.6 Total weight per uni

12、t area, determined in accordance with 4.5.3 of AMS 3906, shall be 336 grams per square yard 21 (402 g/m 2 25).3.3.7 Ply thickness, uncured, determined in accordance with 4.5.4 of AMS 3906, shall be 0.009 inch 0.002 (0.23 mm 0.05).3.4 Properties of Cured Laminate: Shall be as follows, determined on s

13、pecimens cut from a test panel prepared and tested as specified in the basic specification.3.4.1 Mechanical Properties: Shall be as shown in Table 2.TABLE 1 - PropertiesParagraph Property Requirement Test Method3.3.1 Volatile Content byweight, maximum2% ASTM D 3530165 C 5 (329 F 9)15 minutes 13.3.2

14、Total Nonfiber Contentby weight26% 3 ASTM D 35293.3.3 Resin Flow by weight 9% 6 ASTM D 3531165 C 5 (329 F 9)3.3.4 Gel Time 3 minutes 2 ASTM D 3532165 C 5 (329 F 9)3.3.5 Tack Shall adhere for30 minutes, minimum4.5.2 of AMS 3906Copyright SAE International Provided by IHS under license with SAENot for

15、ResaleNo reproduction or networking permitted without license from IHS-,-AMS 3906/4B SAE AMS 3906/4B- 3 -3.4.2 Density: Shall be determined in accordance with ASTM D 792 on the test laminate used to determine mechanical properties; values for each test laminate shall be reported. Cured resin density

16、 shall also be reported.3.4.3 Void Content: Shall be not greater than 4%, determined in accordance with ASTM D 2734.3.4.4 Fiber Volume: Shall be determined in accordance with 4.5.5 of AMS 3906 on the test laminate used to determine mechanical properties; values for each laminate shall be reported. T

17、he fiber density to be used shall be 2.485 g/cm 3 .4. QUALITY ASSURANCE PROVISIONS: See AMS 3906.5. PREPARATION FOR DELIVERY: See AMS 3906.6. ACKNOWLEDGMENT: See AMS 3906.7. REJECTIONS: See AMS 3906.8. NOTES:See AMS 3906.Copyright SAE International Provided by IHS under license with SAENot for Resal

18、eNo reproduction or networking permitted without license from IHS-,-AMS 3906/4B SAE AMS 3906/4B- 4 -TABLE 2A - Minimum Average Mechanical Properties(A), Inch-Pound UnitsPropertyValue, Testedat -67 F 9ksiValue, Testedat 68 to 86 FksiValue, Testedat 302 F 9ksiTestMethodTensile Strength (B) ASTM D 3039

19、Longitudinal 200 190 125Transverse TBR TBR TBRTensile Modulus (B) ASTM D 3039Longitudinal 8.0 x 10 3 8.0 x 10 3 6.5 x 10 3Transverse TBR TBR TBRCompressive Strength (B) ASTM D 695Longitudinal 95.0 90.0 55.0Transverse NA TBR NACompressive Modulus (B) ASTM D 695Longitudinal TBR 7.8 x 10 3 TBRTransvers

20、e NA TBR NAFlexural Strength (B) ASTM D 790Longitudinal 200 190 90.0Flexural Modulus (B) ASTM D 790Longitudinal 7.8 x 10 3 7.8 x 10 3 6.5 x 10 3Short Beam Shear Strength TBR 7.5 TBR ASTM D 2344Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networki

21、ng permitted without license from IHS-,-AMS 3906/4B SAE AMS 3906/4B- 5 -TABLE 2B - Minimum Average Mechanical Properties(A), SI UnitsPropertyValue, Testedat -55 C 5MPaValue, Testedat 20 to 30 CMPaValue, Testedat 150 C 5MPaTestMethodTensile Strength (B) ASTM D 3039Longitudinal 1379 1310 862Transverse

22、 TBR TBR TBRTensile Modulus (B) ASTM D 3039Longitudinal 55.2 x 10 3 55.2 x 10 3 44.8 x 10 3Transverse TBR TBR TBRCompressive Strength (B) ASTM D 695MLongitudinal 655 621 379Transverse NA TBR NACompressive Modulus (B) ASTM D 695MLongitudinal TBR 53.8 x 10 3 TBRTransverse NA TBR NAFlexural Strength (B

23、) ASTM D 790MLongitudinal 1379 1310 621Flexural Modulus (B) ASTM D 790MLongitudinal 53.8 x 10 3 53.8 x 10 3 44.8 x 10 3Short Beam Shear Strength TBR 52 TBR ASTM D 2344Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without licen

24、se from IHS-,-AMS 3906/4B SAE AMS 3906/4B- 6 -NOTES: (A) Average of three determinations per test. No individual value shall be less than 90%of the average value specified. Test after not less than 30 minutes exposure at the test temperature.(B) Property values are based on a test laminate with a fi

25、ber volume of 65% 3. Certainproperty values may be adjusted for other fiber volumes of the test laminate by multiplyingthe listed requirement by the ratio: Actual Fiber Volume, %/65. When such adjustment is used, report the actual fiber volume of the test laminate.TBR - To be reported.NA - Not applicable.PREPARED UNDER THE JURISDICTION OF AMS COMMITTEE “P”Copyright SAE International Provided by IHS under license with SAENot for ResaleNo reproduction or networking permitted without license from IHS-,-