SAE AMS 4056H-2016 Aluminum Alloy Sheet and Plate 4 4Mg - 0 70Mn - 0 15Cr (5083-0) Annealed (UNS A95083).pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2016 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS4056H AEROSPACE MATERIAL SPECIFICATION AMS4056 REV. H Issued 1960-01 Reaffirme

5、d 2010-10 Revised 2016-02 Superseding AMS4056G Aluminum Alloy, Sheet and Plate 4.4Mg - 0.70Mn - 0.15Cr (5083-O) Annealed (Composition similar to UNS A95083) RATIONALE AMS4056H revises the Title, Properties (3.3.1.1) and Reports (4.4), and is a Five Year Review and update of this specification. 1. SC

6、OPE 1.1 Form This specification covers an aluminum alloy in the form of sheet and plate 0.051 to 8.000 inches (1.30 to 203.20 mm), incl, in thickness (see 8.4). 1.2 Application These products have been used typically for parts requiring moderate forming and where good welding characteristics, modera

7、te strength, and good resistance to corrosion are important, but usage is not limited to such applications. Excessive cold work or prolonged heating in the temperature range 150 to 300 F (66 to 149 C) may cause susceptibility to stress corrosion. 2. APPLICABLE DOCUMENTS: The issue of the following d

8、ocuments in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding docum

9、ent has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or +1 724-776-4970 (outside USA), www.sae.org. AMS2355 Quality Assurance

10、Sampling and Testing, Aluminum Alloys and Magnesium Alloy, Wrought Products, (Except Forging Stock), and Rolled, Forged, or Flash Welded Rings SAE INTERNATIONAL AMS4056H Page 2 of 5 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 1

11、9428-2959, Tel: 610-832-9585, www.astm.org. ASTM B660 Packaging/Packing of Aluminum and Magnesium Products ASTM B666/B666M Identification Marking of Aluminum and Magnesium Products 2.3 ANSI Accredited Publications Copies of these documents are available online at http:/webstore.ansi.org/. ANSI H35.2

12、 Dimensional Tolerances for Aluminum Mill Products ANSI H35.2M Dimensional Tolerances for Aluminum Mill Products (Metric) 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined in accordance with AMS2355. Table 1 - Composition Element min ma

13、x Silicon Iron Copper Manganese Magnesium Chromium Zinc Titanium Other Elements, each Other Elements, total Aluminum - - - 0.40 4.0 0.05 - - - - remainder 0.40 0.40 0.10 1.0 4.9 0.25 0.25 0.15 0.05 0.15 SAE INTERNATIONAL AMS4056H Page 3 of 5 3.2 Condition Annealed with mill finish. 3.3 Properties Th

14、e product shall conform to the following requirements, determined on the mill produced size in accordance with AMS2355: 3.3.1 Tensile Properties Shall be as shown in Table 2. 3.3.1.1 Mechanical property requirements for product outside of the range covered by Table 2 shall be agreed upon between pur

15、chaser and producer. Table 2A - Tensile properties, inch/pound units Nominal Thickness Inches Tensile Strength ksi min Tensile Strength ksi max Yield Strength at 0.2% Offset ksi min Yield Strength at 0.2% Offset ksi max Elongation in 2 inches or 4D %, min 0.051 to 1.500, incl Over 1.500 to 3.000, in

16、cl Over 3.000 to 4.000, incl Over 4.000 to 5.000, incl Over 5.000 to 7.000, incl Over 7.000 to 8.000, incl 40.0 39.0 38.0 38.0 37.0 36.0 51.0 51.0 - - - - 18.0 17.0 16.0 16.0 15.0 14.0 29.0 29.0 - - - - 16 16 16 14 14 12 Table 2B - Tensile properties, SI units Nominal Thickness Millimeters Tensile S

17、trength MPa min Tensile Strength MPa max Yield Strength at 0.2% Offset MPa min Yield Strength at 0.2% Offset MPa max Elongation in 50.8 mm or 4D %, min 1.30 to 38.10, incl Over 38.10 to 76.20, incl Over 76.20 to 101.60, incl Over 101.60 to 127.00, incl Over 127.00 to 177.80, incl Over 177.80 to 203.

18、20, incl 276 269 262 262 255 248 352 345 - - - - 124 117 110 110 103 97 200 200 - - - - 16 16 16 14 14 12 3.4 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product. 3

19、.5 Tolerances Shall conform to all applicable requirements of ANSI H35.2 or ANSI H35.2M. SAE INTERNATIONAL AMS4056H Page 4 of 5 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsible for the perf

20、ormance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to the specified requirements. 4.2 Classification of Tests Composition (3.1), tensile properties (3.3.1), and tolerances (3.5) are accept

21、ance tests and, except for composition, shall be performed on each lot. 4.3 Sampling and Testing Shall be in accordance with AMS2355. 4.4 Reports The vendor of the product shall furnish with each shipment a report stating that the product conforms to the chemical composition and tolerances and showi

22、ng the numerical results of tests on each inspection lot to determine conformance to the other acceptance test requirements. This report shall include the purchase order number, inspection lot number(s), AMS4056H, size, and quantity. The report shall also identify the producer, product form and the

23、mill produced size. 4.4.1 When the product is outside the range covered by Table 2, the report shall contain a statement to that effect. 4.5 Resampling and Retesting Shall be in accordance with AMS2355. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in accordance with ASTM B666/B666M. 5.2 P

24、rotective Treatment Product shall be protected from damage during storage and shipment by a method determined by vendor unless specified by purchaser. Examples of typical protective methods include but are not limited to interleaving with paper or oiling of the surfaces. 5.3 Packaging The product sh

25、all be prepared for shipment in accordance with ASTM B660 and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall mention this specification numbe

26、r and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTION Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. SAE INTERNATIONAL AMS4056H Page 5 of 5 8. NOTES 8.1 Revision Indicator A change ba

27、r (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including tech

28、nical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are show

29、n as the approximate equivalents of the primary units and are presented only for information. 8.3 Terms used in AMS are clarified in ARP1917. 8.4 Purchase documents should specify not less than the following: AMS4056H Form and size of product desired Quantity of product desired Property and acceptan

30、ce requirements from the cognizant engineering organization applicable to sizes outside the range listed in 1.1. 8.5 Similar Specifications AMS-QQ-A-250/6, Temper O, is listed for information only and shall not be construed as an acceptable alternate unless all requirements of this AMS are met. PREPARED BY AMS COMMITTEE “D“