SAE AMS 4186D-2012 Aluminum Alloy Bars Rods and Wire Rolled or Cold Finished 5 6Zn - 2 5Mg - 1 6Cu - 0 23Cr (7075-F) As Fabricated or when specified Annealed (7075-O) (UNS A97075)《.pdf

1、_SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising theref

2、rom, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions.Copyright 2012 SAE InternationalAll rights reserved. No part of this publication may b

3、e reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE.TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (outside USA)Fax

4、: 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS4186DAEROSPACEMATERIALSPECIFICATIONAMS4186 REV. DIssued 1974-06Revised 2012-05Superseding AMS4186CAlum

5、inum Alloy Bars, Rods, and Wire, Rolled or Cold Finished5.6Zn - 2.5Mg - 1.6Cu - 0.23Cr (7075-F)As Fabricated, or when specified, Annealed (7075-O)(Composition similar to UNS A97075)RATIONALEAMS4186D adds coverage for O temper (Title, 3.2), and adds tensile properties for annealed product (3.3.2, Tab

6、le 2, 4.2.1) to facilitate future cancellation of AMS-QQ-A-225/9.1. SCOPE1.1 FormThis specification covers an aluminum alloy in the form of bars, rods, and wire in the “as fabricated (F) temper. When specified, product shall be supplied in the annealed (O) condition.1.2 ApplicationThese products hav

7、e been typically used for parts requiring forming and as stock for flash welded rings which are to be subsequently solution and precipitation heat treated, but usage is not limited to such applications. 1.2.1 Certain design and processing procedures may cause these products to become susceptible to

8、stress-corrosion cracking after solution and precipitation heat treatment; ARP823 recommends practices to minimize such conditions.2. APPLICABLE DOCUMENTSThe issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein

9、. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply.SAE AMS4186D Page 2 of 52.1 SAE Publicat

10、ionsAvailable from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org.AMS2355 Quality Assurance, Sampling and Testing, Aluminum Alloys and Magnesium Alloy, Wrought Products (Except Forging Stock),

11、 and Rolled, Forged, or Flash Welded RingsAMS2772 Heat Treatment of Aluminum Alloy Raw MaterialsARP823 Minimizing Stress-Corrosion Cracking in Wrought Heat-Treatable Aluminum Alloy ProductsAS1990 Aluminum Alloy Tempers2.2 ASTM PublicationsAvailable from ASTM International, 100 Barr Harbor Drive, P.O

12、. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org.ASTM B 660 Packaging/Packing of Aluminum and Magnesium ProductsASTM B 666/B 666M Identification Markig of Aluminum and Magnesium Products2.3 ANSI PublicationsAvailable from American National Standards Institute, 25 West 43

13、rd Street, New York, NY 10036-8002, Tel: 212-642-4900, www.ansi.org.ANSI H35.2 Dimensional Tolerances for Aluminum Mill ProductsANSI H35.2 Dimensional Tolerances for Aluminum Mill Products, Metric3. TECHNICAL REQUIREMENTS3.1 CompositionShall conform to the following percentages by weight shown in Ta

14、ble 1, determined in accordance with AMS2355.TABLE 1 - COMPOSITIONElement min maxSiliconIronCopperManganeseMagnesiumChromiumZincTitaniumOther Elements, eachOther Elements, totalAluminum-1.2-2.10.185.1-remainder0.400.502.00.302.90.286.10.200.050.15SAE AMS4186D Page 3 of 53.2 Condition3.2.1 Rolled or

15、cold finished, as ordered, in the as-fabricated condition.3.2.2 When specified, material may be provided annealed in accordance with AMS2772.3.3 PropertiesThe product shall conform to the following requirements, determined in accordance with AMS2355 on the mill produced size:3.3.1 As FabricatedNo re

16、quirements.3.3.2 As Annealed3.3.2.1 Tensile PropertiesShall be as shown in Table 2.TABLE 2 ANNEALED TENSILE PROPERTIESProperty ValueTensile Strength, max 40.0 ksi (276 MPa)Yield Strength at 0.2% Offset, min -Elongation in 2 inches (50.8 mm) or 4D, min 10%3.3.3 Response to Solution and Precipitation

17、Heat TreatmentRods and wire 4 inches (102 mm) and under in nominal diameter; square, hexagonal, and octagonal bar 3-1/2 inches (89 mm) and under in nominal thickness; and rectangular bar 3 inches (76 mm) and under in nominal thickness and 6 inches (152 mm) and under in nominal width or 10 inches (25

18、4 mm) and under in nominal width when nominal thickness is under 3 inches (76 mm) shall have the following properties after solution and precipitation heat treatment in accordance with AMS2772 to the -T62 temper (See AS1990):3.3.3.1 Tensile PropertiesTABLE 3 - MINIMUM TENSILE PROPERTIES IN T62 TEMPE

19、RProperty ValueTensile Strength 77.0 ksi (531 MPa)Yield Strength at 0.2% Offset 66.0 ksi (455 MPa)Elongation in 2 inches (50.8 mm) or 4D 7%3.4 QualityThe product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrim

20、ental to usage of the product.3.5 TolerancesShall conform to all applicable requirements of ANSI H35.2 or ANSI H35.2M.SAE AMS4186D Page 4 of 54. QUALITY ASSURANCE PROVISIONS4.1 Responsibility for InspectionThe vendor of the product shall supply all samples for vendors tests and shall be responsible

21、for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements.4.2 Classification of Tests4.2.1 Acceptance TestsComposition (3.1), tensile properties as annealed

22、(3.3.2.1) (not applicable to F temper), tensile properties after solution and precipitation heat treatment (3.3.3.1) and tolerances (3.5) are classified as acceptance tests and shall, except for composition, be performed on each lot.4.3 Sampling and TestingShall be in accordance with AMS2355.4.4 Rep

23、ortsThe vendor of the product shall furnish with each shipment a report stating that the product conforms to the composition, tolerances and showing the numerical results of tests on each inspection lot to determine conformance to the other technical requirements of this specification. This report s

24、hall include the purchase order number, lot number, AMS4186D,size, and quantity. The report shall also include the identity of the mill and the size of the mill product.4.5 Resampling and RetestingShall be in accordance with AMS2355.5. PREPARATION FOR DELIVERY5.1 IdentificationShall be in accordance

25、 with ASTM B 666/B 666.5.2 PackagingThe product shall be prepared for shipment in accordance with ASTM B 660 and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery.6. ACKNOWLEDGME

26、NTA vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders.7. REJECTIONSProduct not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection.SAE AMS4186D Page 5 of 58. NOTES8.1

27、 A change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, in

28、cluding technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only.8.2 Hardness in the T62 condition should not be lower than 135 or 140 HB/10/500 or equivalent, determined in accordance with ASTM E 10. Hardness has been used

29、to verify that product is properly processed but an out-of-range hardness number” is not always indicative of product with “out of specified tensile strength . Further analysis, including material composition verification, heat treat process parameter review, and/or tensile property measurement may

30、be necessary.8.3 Terms used in AMS are clarified in ARP1917.8.4 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information.8.5 Purchase documents should specify not less than the following:AMS4186DProduct form and size of product desiredQuantity of product desired.PREPARED BY AMS COMMITTEE “D“