SAE AMS 4191J-2009 Aluminum Alloy Welding Wire 6 3Cu - 0 30Mn - 0 18Zr - 0 15Ti - 0 10V (2319) (UNS A92319)《铝合金 6 3Cu 0 3Mn 0 18Zr 0 15Ti 0 10V (2319)焊条》.pdf

1、_SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report isentirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefr

2、om, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions.Copyright 2015 SAE InternationalAll rights reserved. No part of this public

3、ation may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE.TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (outs

4、ide USA)Fax: 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS4191JAEROSPACEMATERIAL SPECIFICATIONAMS4191 REV. JIssued 1962-06Noncurrent 2008-01Revised 2

5、009-11Reaffirmed 2015-10Superseding AMS4191HAluminum Alloy, Welding Wire6.3Cu - 0.30Mn - 0.18Zr - 0.15Ti - 0.10V (2319)(Composition similar to UNS A92319)RATIONALEAMS4191J has been reaffirmed to comply with the SAE five-year review policy.1. SCOPE 1.1 FormThis specification covers an aluminum alloy

6、in the form of welding wire. 1.2 ApplicationThis wire has been used typically as filler metal for gas-metal-arc or gas-tungsten-arc welding of aluminum alloys of similar composition where the joint is capable of being heat treated to a strength level comparable to that of the parent metal, but usage

7、 is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document is

8、sue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside

9、 USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2355 Quality Assurance, Sampling and Testing, Aluminum Alloys and Magnesium Alloy, Wrought Products, Except Forging Stock, and Rolled, Forged, or Flash Welded Rings AMS2813 Packaging and Marking of Packages of Welding Wire, Standard Met

10、hod AMS2814 Packaging and Marking of Packages of Welding Wire, Premium Quality AMS2816 Identification, Welding Wire, Tab Marking Method AMS2819 Identification, Welding Wire, Direct Color Code System ARP1876 Weldability Test for Weld Filler Metal Wire ARP4926 Alloy Verification and Chemical Compositi

11、on Inspection of Welding Wire 3. TECHNICAL REQUIREMENTS 3.1 Wire Composition Shall conform to the percentages by weight shown in Table 1, determined in accordance with AMS2355. TABLE 1 - COMPOSITION Element min maxSilicon - 0.20Iron - 0.30Copper 5.8 6.8Manganese 0.20 0.40Magnesium - 0.02Zinc - 0.10T

12、itanium 0.10 0.20Beryllium - 0.0008 (8 ppm)Vanadium 0.05 0.15Zirconium 0.10 0.25Other Elements, each - 0.05Other Elements, total - 0.15Aluminum Remainder 3.1.1 Chemical analysis of initial ingot, bar, or rod stock before drawing is acceptable provided the processes used for drawing or rolling, annea

13、ling, and cleaning are controlled to ensure continued conformance to composition requirements, and the facility employs procedures to ensure traceability of wire to the originally analyzed source. 3.2 ConditionAs drawn, in a temper and with a surface finish which will provide proper feeding of the w

14、ire in machine-welding equipment.3.3 Fabrication3.3.1 Butt welding is permissible provided both ends to be joined are identified by chemical analysis or the repair is made at the wire processing station. The butt weld shall not interfere with uniform, uninterrupted feeding of the wire in machine wel

15、ding equipment. 3.3.2 Drawing compounds, oxides, dirt, oil, and other foreign materials shall be removed by processes which will neither result in pitting nor cause gas absorption by the wire or deposition of substances harmful to welding operations.3.4 Weldability Melted wire shall flow smoothly an

16、d evenly during welding and shall produce acceptable welds. ARP1876 may be used to resolve disputes. 3.5 QualityWire, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to welding operations, operation of wel

17、ding equipment, or properties of the deposited weld metal.3.6 Sizes and Tolerances Wire shall be supplied in the sizes and to the tolerances shown in 3.6.1 and 3.6.2. SAE INTERNATIONAL AMS4191J Page 2 of 5_3.6.1 DiameterTolerances shall be as shown in Table 2. TABLE 2A - SIZES AND DIAMETER TOLERANCE

18、S, INCH/POUND UNITS Form Nominal Diameter Inch Tolerance Inch Plus Tolerance Inch MinusCut Lengths 0.047, 0.062, 0.079, 0.094, 0.098, 0.125, 0.156, 0.188, 0.197, 0.250 0.003 0.003 Spools 0.030, 0.035, 0.039, 0.047 0.001 0.002Spools 0.062, 0.079, 0.094, 0.098, 0.125 0.002 0.002TABLE 2B - SIZES AND DI

19、AMETER TOLERANCES, SI UNITS Form Nominal Diameter Millimeters Tolerance Millimeter Plus ToleranceMillimeter Minus Cut Lengths 1.19, 1.57, 2.00, 2.39, 2.50, 3.18, 3.96, 4.78, 5.00, 6.35 0.08 0.08 Spools 0.76, 0.89, 1.00, 1.19 0.025 0.05Spools 1.57, 2.00, 2.39, 2.50, 3.18 0.05 0.053.6.2 LengthCut leng

20、ths shall be furnished in 36-inch (914-mm) lengths unless 27-inch (686-mm) or 18-inch (457-mm) lengths are ordered, and shall not vary more than +0, -0.5 inch (+0, -13 mm) from the length ordered. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of wire shall supply all s

21、amples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the wire conforms to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests

22、Composition (3.1), sizes and tolerances (3.6), and alloy verification (5.2) are acceptance tests and shall be performed on each inspection lot. 4.2.2 Periodic Tests Weldability (3.4) is a periodic test and shall be performed at a frequency selected by the vendor unless frequency of testing is specif

23、ied by purchaser. 4.3 Sampling and Testing Shall be in accordance with AMS2355. 4.4 Reports The vendor of wire shall furnish with each shipment a report stating that the wire conforms to the composition and other technical requirements. This report shall include the purchase order number, inspection

24、 lot number, AMS4191J, nominal size, and quantity. SAE INTERNATIONAL AMS4191J Page 3 of 5_4.5 Resampling and Retesting Shall be in accordance with AMS2355. 5. PREPARATION FOR DELIVERY 5.1 WireWire shall be supplied either on spools in one continuous length for machine welding, or cut in lengths for

25、manual welding as ordered. Wire on each spool or in each package of cut lengths shall be from the same heat of alloy. 5.1.1 Wire furnished on spools shall be closely wound in layers but adjacent turns within a layer need not be necessarily touching, shall be wound so as to avoid producing kinks, wav

26、es, and sharp bends, and shall be free to unwind without restriction caused by overlapping or wedging. 5.2 Alloy Verification Wire on each spool or in each package of cut lengths shall be alloy verified by a method acceptable to purchaser. The alloy verification procedures of ARP4926 are recommended

27、. 5.2.1 An 8-inch (203-mm) length of wire shall be made accessible at one end of each spool for alloy analysis, if required.5.3 Identification Shall be by tab marking in accordance with AMS2816 unless color coding in accordance with AMS2819 or other method is specified by customer. 5.4 Packaging and

28、 Marking Shall be by standard method in accordance with AMS2813 unless premium quality method in accordance with AMS2814 or other method is specified by purchaser. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purc

29、hase orders. 7. REJECTIONS Wire not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial chan

30、ges, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8

31、.2 Terms used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary: dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for in

32、formation. SAE INTERNATIONAL AMS4191J Page 4 of 5_8.4 Purchase documents should specify not less than the following: AMS4191JSize and form (spools or cut lengths) of wire desired Length of cut lengths or weight of spools desired Quantity of wire desired. 8.5 Similar Specifications AWS A5.10, Class R2319 is listed for information only and shall not be construed as an acceptable alternate unless all requirements of this AMS are met. . PREPARED BY AMS COMMITTEE “D” SAE INTERNATIONAL AMS4191J Page 5 of 5_