SAE AMS 4285F-2017 Aluminum Alloy Castings Centrifugal 7 0Si - 0 30Mg (356 0-T6) Solution and Precipitation Heat Treated (UNS A03560).pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2017 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/standards.sae.org/AMS4285F AEROSPACE MATERIAL SPECIFICATION AMS4285 REV. F Issued 1954-05 Reaffirmed 2006-04 Revi

5、sed 2017-04 Superseding AMS4285E Aluminum Alloy Castings, Centrifugal 7.0Si - 0.30Mg (356.0-T6) Solution and Precipitation Heat Treated (Composition similar to UNS A03560) RATIONALE AMS4285F revises Radiographic Acceptance (3.7.1) and results from a Five-Year Review and update of this specification.

6、 1. SCOPE 1.1 Form This specification covers an aluminum alloy in the form of centrifugal castings. 1.2 Application These castings have been used typically for intricate castings with thin walls or sections used at relatively high stresses, but usage is not limited to such applications. 2. APPLICABL

7、E DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has

8、 been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or +1 724-776-4970 (outside USA),

9、 www.sae.org. AMS2175 Casting, Classification and Inspection of AMS2360 Room Temperature Tensile Properties of Castings AMS2694 In-Process Welding of Castings SAE INTERNATIONAL AMS4285 F Page 2 of 8 AMS2771 Heat Treatment of Aluminum Alloy Castings AMS2804 Identification Castings ARP1917 Clarificati

10、on of Terms Used in Aerospace Metals Specifications 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B557 Tension Testing Wrought and Cast Aluminum and Magnesium-Alloy Products ASTM

11、B557M Tension Testing Wrought and Cast Aluminum and Magnesium-Alloy Products (Metric) ASTM B660 Packaging/Packing of Aluminum and Magnesium Products ASTM E10 Brinell Hardness of Metallic Materials ASTM E29 Using Significant Digits in Test Data to Determine Conformance with Specifications ASTM E34 Ch

12、emical Analysis of Aluminum- and Aluminum-Base Alloys ASTM E607 Atomic Emission Spectrometric Analysis of Aluminum Alloys by the Point-to-Plane Technique, Nitrogen Atmosphere ASTM E716 Sampling and Sample Preparation of Aluminum and Aluminum Alloys for Determination of Chemical Composition by Spectr

13、ochemical Analysis ASTM E1251 Analysis of Aluminum and Aluminum Alloys by Atomic Emission Spectrometry ASTM E1417/E1417M Liquid Penetrant Testing ASTM E1742/E1742M Radiographic Examination 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determin

14、ed by wet chemical methods in accordance with ASTM E34, by spectrochemical methods in accordance with ASTM E607, or ASTM E1251, or by other analytical methods acceptable to purchaser (see 3.4.1). Table 1 - Composition Element (3.1.1) Min Max Silicon 6.5 7.5 Iron - 0.6 Copper - 0.25 Manganese - 0.35

15、Magnesium 0.20 0.45 Zinc - 0.35 Titanium - 0.25 Other Elements, each - 0.05 Other Elements, total - 0.15 Aluminum remainder SAE INTERNATIONAL AMS4285 F Page 3 of 8 3.1.1 Test results may be rounded by the “rounding off“ method of ASTM E29. 3.2 Condition Solution and precipitation heat treated. 3.3 C

16、astings Castings shall be produced from metal conforming to 3.1, determined by analysis of a specimen (3.4.1) cast after the last melt addition. 3.4 Cast Test Specimens Chemical analysis specimens and tensile specimens shall be cast as follows: 3.4.1 Chemical Analysis Specimens Shall be cast from ea

17、ch melt after the last melt addition and shall be tested to qualify the melt lot as in 3.1. Spectrochemical sample shall be prepared in accordance with ASTM E716. 3.4.2 Tensile Specimens 3.4.2.1 Unless specimens cut from a casting are specified by purchaser, separately-cast specimens conforming to A

18、STM B557 or ASTM B557M shall be cast from each melt after the last melt addition. Specimens shall be cast in molds representing the mold used for castings. Chills are not permitted on test specimen cavity except on the end face of the specimen when approved in accordance with 4.4.2. Tensile specimen

19、s shall be processed with each heat treat lot and tested for conformance to 3.6.1. 3.4.2.2 When purchaser specifies specimens cut from a casting or from integrally-cast coupons, such specimens shall be removed after heat treatment, shall conform to ASTM B557 or ASTM B557M, and shall be either 0.500

20、inch (12.70 mm) diameter at the reduced parallel gage section, subsize specimens proportional to the standard, or standard sheet-type specimens, as required by 3.6.1. 3.5 Heat Treatment Shall be in accordance with AMS2771. Unless specimens cut from a casting are specified, one or more sets of separa

21、tely-cast specimens shall, during each stage of heat treatment, be put into a batch-type furnace with each load of castings or into a continuous furnace at intervals of not longer than 3 hours. 3.6 Properties Castings and separately-cast tensile specimens shall conform to the following requirements:

22、 3.6.1 Tensile Properties Shall be as follows, determined in accordance with ASTM B557 or ASTM B557M; conformance to the requirements of 3.6.1.1 shall be used as the basis for acceptance of castings except when purchaser specifies that 3.6.1.2 applies: 3.6.1.1 Separately-Cast Specimens Specimens as

23、in 4.3.2 shall have the properties shown in Table 2. SAE INTERNATIONAL AMS4285 F Page 4 of 8 Table 2 - Minimum tensile properties for separately-cast specimens Property Value Tensile Strength 33.0 ksi (228 MPa) Yield Strength at 0.2% Offset 22.0 ksi (152 MPa) Elongation in 4D 3.0% 3.6.1.2 Specimens

24、Cut from Castings Specimens as in 4.3.4 shall have the properties shown in Table 3. Table 3 - Minimum tensile properties for specimens cut from castings Property Value Tensile Strength 25.0 ksi (172 MPa) Yield Strength at 0.2% Offset 16.0 ksi (110 MPa) Elongation in 4D 1.0% 3.6.1.2.1 When properties

25、 other than those of 3.6.1.2 are required, tensile specimens taken from locations indicated on the drawing, from a casting or castings chosen at random to represent the lot, shall have the properties indicated on the drawing for such specimens. Property requirements may be designated in accordance w

26、ith AMS2360. 3.7 Quality Castings, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the castings. 3.7.1 When acceptance standards are not specified, castings shall meet Grade C of AMS2175 and ra

27、diographic indications of gas holes, sand spots, and inclusions shall be cause for rejection when closer to the edge than twice their maximum dimension. 3.7.2 Methods of inspection and frequency of inspection shall be as agreed upon by purchaser and vendor. A “Casting Class“ of AMS2175 may be select

28、ed to specify the method and frequency of inspection. 3.7.3 Castings shall be produced under radiographic control. This control shall consist of 100% radiographic inspection of castings until process control factors (see 4.4.2) have been established to ensure production of acceptable castings. Unles

29、s otherwise specified by purchaser, continued radiographic inspection of production castings shall be performed at a frequency determined by the vendor to ensure continued maintenance of internal quality. 3.7.4 Radiographic inspection shall be conducted in accordance with ASTM E1742/E1742M, unless o

30、therwise specified by purchaser. 3.7.5 When specified by purchaser, castings shall be fluorescent penetrant inspected using a method specified by purchaser, or, if not specified, a method in accordance with ASTM E1417/E1417M. 3.7.6 Castings shall not be peened, plugged, impregnated, or welded unless

31、 authorized by purchaser. 3.7.6.1 When authorized by purchaser, welding in accordance with AMS2694 or other welding program approved by purchaser may be used. SAE INTERNATIONAL AMS4285 F Page 5 of 8 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of castings shall supply

32、 all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the castings conform to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptan

33、ce Tests Except as specified in 4.2.1.1, composition (3.1), tensile properties of separately-cast specimens (3.6.1.1), and quality (3.7) are acceptance tests and shall be performed to represent each melt or heat treat lot as applicable. 4.2.1.1 Tensile properties of specimens cut from castings shall

34、 be determined when specified by purchaser or when separately-cast specimens are not available. Tensile properties of separately-cast specimens need not be determined when tensile properties of specimens cut from castings are determined. 4.2.2 Periodic Tests Radiographic inspection (3.7.3) following

35、 the establishment of process control (4.4.2) is a periodic test and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.2.3 Preproduction Tests All technical requirements are preproduction tests and shall be performed on the first-articl

36、e shipment of a casting to a purchaser, when a change in materials, and/or processing requires reapproval as in 4.4.2, and when purchaser deems confirmatory testing to be required. 4.3 Sampling and Testing Shall be in accordance with the following: 4.3.1 At least one chemical analysis specimen in ac

37、cordance with 3.4.1 from each melt for conformance to 3.1. 4.3.2 One or more separately-cast tensile specimens in accordance with 3.4.2 from each heat treat lot except when purchaser specifies specimens cut from a casting as in 4.3.4. 4.3.3 One or more preproduction castings in accordance with 4.4.1

38、 of each part number. 4.3.4 One or more castings from each heat treat lot when properties are required from specimens cut from castings. For determining conformance to the requirements of 3.6.1.2, if specimen locations are not shown on the drawing, two specimens from the thickest section and two spe

39、cimens from the thinnest section, shall be cut from a casting or castings from each heat treat lot. SAE INTERNATIONAL AMS4285 F Page 6 of 8 4.4 Approval 4.4.1 Sample castings from new or reworked tooling (i.e., patterns, molds, dies, etc.) and the casting procedure and sample castings, when specifie

40、d, shall be approved by purchaser before castings for production use are supplied, unless such approval be waived by purchaser. 4.4.2 Vendor shall establish, for production of sample castings of each part number, parameters for the process control factors which will produce acceptable castings; thes

41、e shall constitute the approved casting procedure and shall be used for producing production castings. Vendor shall also establish control factors for producing separately cast tensile specimens, but these control factors need not be identical to those used for production of castings. Method for pro

42、duction of separately-cast tensile specimens shall be consistent for all cast material. If necessary to make any change in parameters for the process control factors, vendor shall submit for reapproval a statement of the proposed changes in processing and, when requested, test specimens, sample cast

43、ings, or both. Production castings incorporating the revised operations shall not be shipped prior to receipt of reapproval. 4.4.2.1 Control factors for producing tensile specimens and castings include, but are not limited to, the following. Suppliers procedures shall identify tolerances, ranges, an

44、d/or control limits, as applicable. Control factors for separately-cast tensile specimens must generally represent, but need not be identical to, those factors used for castings: Type of furnace Furnace atmosphere Alloy additions, fluxing, deoxidation, and gas removal procedures Gating and risering

45、practices Mold composition and molding practice Mold setup Mold rotational speed Core composition and fabrication method, when applicable Metal pouring temperature; variation of 50 F (28 C) from the established limit is permissible Solidification and cooling procedures Stabilization/precipitation he

46、at treat cycle Straightening procedure, when applicable Cleaning operations Methods of inspection Radiographic inspection sampling plan, if used 4.4.2.1.1 Any of the above process control factors for which parameters are considered proprietary by the vendor may be assigned a code designation. Each v

47、ariation in such parameters shall be assigned a modified code designation. 4.5 Reports The vendor of castings shall furnish with each shipment a report showing the results of tests for composition of each melt and the results of tests for tensile properties of separately-cast specimens representing

48、each heat treat lot or of specimens cut from a casting from each heat treat lot, and stating that the castings conform to the other technical requirements. This report shall include the purchase order number, melt and heat treat lot numbers, AMS4285F, part number, and quantity. 4.6 Resampling and Re

49、testing If any specimen used in the above tests fails to meet specified requirements, disposition of the castings may be based on the results of testing two additional specimens for each original nonconforming specimen. Failure of any retest specimen to meet the specified requirements shall be cause for rejection of the castings represented. Results of all tests shall be reported. SAE INTERNATIONAL AMS4285 F Page 7 of 8 5. PR