SAE AMS 5501E-2002 Steel Corrosion Resistant Sheet Strip and Foil 19Cr - 9 5Ni (304) Cold Rolled 125 ksi (862 MPa) Tensile Strength (UNS S30400)《UNS S30400 抗张强度为125 ksi(862 MPa)的含1.pdf

1、_SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising theref

2、rom, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions.Copyright 2013 SAE InternationalAll rights reserved. No part of this publi

3、cation may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE.TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (out

4、side USA)Fax: 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS5501EAEROSPACE MATERIAL SPECIFICATIONAMS5501 REV. EIssued 1967-11Revised 2002-11Reaffirmed

5、 2013-08Superseding AMS5501DSteel, Corrosion Resistant, Sheet, Strip, and Foil19Cr 9.5Ni (304)Cold Rolled, 125 ksi (862 MPa) Tensile Strength(Composition similar to UNS S30400)RATIONALEAMS5501E has been reaffirmed to comply with the SAE 5-year Review policy.1. SCOPE:1.1 Form:This specification cover

6、s a corrosion-resistant steel in the form of sheet, strip, and foil.1.2 Application:These products have been used typically for parts requiring moderate drawing or forming, but usage is not limited to such applications.2. APPLICABLE DOCUMENTS:The issue of the following documents in effect on the dat

7、e of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the l

8、ast published issue of that document shall apply.2.1 SAE Publications:Available from SAE, 400 Commonwealth Drive, Warrendale, PA 15096-0001 or www.sae.org.AMS 2242 Tolerances, Corrosion and Heat-Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Sheet, Strip, and PlateMAM 2242 Tolerances, Met

9、ric, Corrosion and Heat-Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Sheet, Strip, and PlateAMS 2248 Chemical Check Analysis Limits, Corrosion and Heat-Resistant Steels and Alloys, Maraging and other Highly Alloyed Steels, and Iron AlloysSAE INTERNATIONAL AMS5501E Page 2 of 5 AMS 2371 Q

10、uality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS 2807 Identification, Carbon and Low-Alloy Steels, Corrosion and Heat-Resistant Steels and Alloys, Sheet, Strip, Plate, and Aircraft Tubing AS4194 Sheet and Strip Surface Fini

11、sh Nomenclature 2.2 ASTM Publications: Available from ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959 or www.astm.org. ASTM A 370 Mechanical Testing of Steel Products ASTM A 480/ Flat-Rolled Stainless and Heat-Resisting Steel ASTM A 480M Plate, Sheet, and Strip ASTM E 290 Semi-Guided B

12、end Test for Ductility of Metallic Materials ASTM E 353 Chemical Analysis of Stainless, Heat-Resisting, Maraging, and Other Similar Chromium-Nickel-Iron Alloys 3. TECHNICAL REQUIREMENTS: 3.1 Composition: Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods

13、in accordance with ASTM E 353, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 COMPOSITION Element min max Carbon - 0.08 Manganese - 2.00 Silicon - 1.00 Phosphorus - 0.040 Sulfur - 0.030 Chromium 18.00 20.00 Nickel 8.00 11.00 Molybdenum 0.75 Copper 0.75 3.

14、1.1 Check Analysis: Composition variations shall meet the applicable requirements of AMS 2248. SAE INTERNATIONAL AMS5501E Page 3 of 53.2 Condition:Solution heat treated and temper cold rolled in accordance with ASTM A 480/A 480M, Condition TR and, unless solution heat treatment is performed in an at

15、mosphere yielding a bright finish, descaled, with sheet having a surface appearance comparable to a 2D finish in ASTM A 480/A 480M and AS4194.3.3 Properties:Product shall conform to the following requirements; tensile and bend testing shall be performed in accordance with ASTM A 370.3.3.1 Tensile Pr

16、operties: Product, 0.005 inch (0.13 mm) and over in nominal thickness, shall have the properties shown in Table 2.TABLE 2 - MINIMUM TENSILE PROPERTIESProperty ValueTensile Strength 125 ksi (862 MPa)Yield Strength at 0.2% Offset 75 ksi (517 MPa)Elongation in 2 Inches (50.8 mm) 15%3.3.2 Bending: Produ

17、ct 0.010 inch (0.25 mm) and under in nominal thickness, tested with specimens nominally 0.750 inch (19.06 mm) in width, shall withstand without cracking when examined using at least 20X magnification, bending in accordance with ASTM E 290 through a minimum angle of 180 degrees around a diameter equa

18、l to the nominal thickness of the product, with axis of bending parallel to direction of rolling. In case of dispute, results of tests using the guided bend test shall govern.3.4 Quality:The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign ma

19、terials and from imperfections detrimental to usage of the product.3.5 Tolerances:Product, 0.005 inch (0.13 mm) and over in nominal thickness, shall conform to all applicable requirements of AMS 2242 or MAM 2242.SAE INTERNATIONAL AMS5501E Page 4 of 54. QUALITY ASSURANCE PROVISIONS:4.1 Responsibility

20、 for Inspection:The vendor of the product shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified re

21、quirements.4.2 Classification of Tests:All technical requirements are acceptance tests and shall be performed on each heat or lot as applicable.4.3 Sampling and Testing:Shall be in accordance with AMS 2371.4.4 Reports:The vendor of the product shall furnish with each shipment a report showing the re

22、sults of tests for composition of each heat and for tensile and bending properties of each lot, and stating that the product conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS 5501E, size, and quantity.4.5 Resampling and Retes

23、ting:Shall be in accordance with AMS 2371.5. PREPARATION FOR DELIVERY:5.1 Identification:Shall be in accordance with AMS 2807.5.2 Packaging:Product shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling

24、, packaging, and transportation of the product to ensure carrier acceptance and safe delivery.6. ACKNOWLEDGMENT:A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders.SAE INTERNATIONAL AMS5501E Page 5 of 57. REJECTIONS:Produc

25、t not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection.8. NOTES:8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the prev

26、ious issue of a specification. An (R) symbol to the left of the document title indicates a complete revision of the specification. Change bars and (R) are not used in original publications, nor in specifications that contain editorial changes only.8.2 Terms used in AMS is clarified in ARP1917.8.3 Di

27、mensions and properties in inch/pound units are primary; dimensions and properties in SI units are shown as the approximate equivalents of the primary units and are presented only for information.8.4 Purchase documents should specify not less than the following:AMS 5501EForm and size of product desiredQuantity of product desired.PREPARED UNDER THE JURISDICTION OF AMS COMMITTEE “F”