SAE AMS 5593G-2016 Nickel Alloy Corrosion and Heat Resistant Sheet Strip and Plate 45 5Ni - 25 5Cr - 3 2Co - 3 2Mo - 3 2W - 18 5Fe Solution Heat Treated (UNS N06333).pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2016 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5593G AEROSPACE MATERIAL SPECIFICATION AMS5593 REV. G Issued 1963-07 Reaffirme

5、d 2010-05 Revised 2016-02 Superseding AMS5593F Nickel Alloy, Corrosion and Heat Resistant, Sheet, Strip, and Plate 45.5Ni - 25.5Cr - 3.2Co - 3.2Mo - 3.2W - 18.5Fe Solution Heat Treated (Composition similar to UNS N06333) RATIONALE AMS5593G revises Reports (4.4) and is a Five Year Review and update o

6、f this specification. 1. SCOPE 1.1 Form This specification covers a corrosion and heat resistant nickel alloy in the form of sheet, strip, and plate. 1.2 Application These products have been used typically for parts requiring heat and oxidation resistance up to 2150 F (1177 C), particularly where su

7、ch parts may require welding during fabrication, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subse

8、quent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth D

9、rive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or +1 724-776-4970 (outside USA), www.sae.org. AMS2242 Tolerances, Corrosion and Heat Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Sheet, Strip, and Plate AMS2248 Chemical Check Analysis Limits, Corrosion and Hea

10、t-Resistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS2371 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock SAE INTERNATIONAL AMS5593G Page 2 of 5 AMS2807 Identification, Carbon and Low-Al

11、loy Steels, Corrosion and Heat-Resistant Steels and Alloys, Sheet, Strip, Plate, and Aircraft Tubing AS4194 Sheet and Strip Surface Finish Nomenclature 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585,

12、www.astm.org. ASTM A480/A480M Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and Strip ASTM E3 Preparation of Metallographic Specimens ASTM E8/E8M Tension Testing of Metallic Materials ASTM E18 Rockwell Hardness Hardness of Metallic Materials ASTM E354 Chemical Analysis of High-Tempera

13、ture, Electrical, Magnetic, and Other Similar Iron, Nickel, and Cobalt Alloys 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E354, by spectrochemical methods, or by other analytical met

14、hods acceptable to purchaser: Table 1 - Composition Element min max Carbon Manganese Silicon Phosphorous Sulfur Chromium Nickel Cobalt Molybdenum Tungsten Copper Tin Lead Iron - - 0.75 - - 24.00 44.00 2.50 2.50 2.50 - - - remainder 0.08 2.00 1.50 0.030 0.030 27.00 47.00 4.00 4.00 4.00 0.50 0.025 0.0

15、25 SAE INTERNATIONAL AMS5593G Page 3 of 5 3.1.1 Check Analysis Composition variations shall meet the applicable requirements of AMS2248. 3.2 Condition The product shall be supplied in the following condition: 3.2.1 Sheet and Strip Hot or cold rolled, solution heat treated to meet the requirements of

16、 3.3, and, unless solution heat treatment is performed in an atmosphere yielding a bright finish, descaled having a surface appearance in accordance with ASTM A480/A480M and AS4194 comparable to 3.2.1.1 or 3.2.1.2 as applicable. 3.2.1.1 Sheet No. 2D finish. 3.2.1.2 Strip No. 1 strip finish. 3.2.2 Pl

17、ate Hot rolled, solution heat treated, and descaled. 3.3 Properties The product shall conform to the following requirements: 3.3.1 Tensile Properties Shall be as shown in Table 2, determined in accordance with ASTM E8/E8M. Table 2 - Tensile properties Property Value Tensile Strength, max Elongation

18、in 2 Inches (50.8 mm) or 4D, min 120 ksi (827 MPa) 30% 3.3.2 Hardness Shall be not higher than 95 HRB, or equivalent (see 8.2), determined in accordance with ASTM E18. Product shall not be rejected on the basis of hardness if the tensile properties of 3.3.1 are acceptable, determined on specimens ta

19、ken from the same sample as that with nonconforming hardness or from another sample with similar nonconforming hardness. 3.3.3 Microstructure Shall be free from continuous carbide network, determined by metallographic examination of specimens prepared in accordance with ASTM E3. 3.4 Quality The prod

20、uct, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product. SAE INTERNATIONAL AMS5593G Page 4 of 5 3.5 Tolerances Shall conform to all applicable requirements of AMS2242. 4. QUALITY ASSUR

21、ANCE PROVISIONS 4.1 Responsibility for Inspection The producer of the product shall supply all samples for producers tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure tha

22、t the product conforms to specified requirements. 4.2 Classification of Tests All technical requirements are acceptance tests and shall be performed on each heat or lot as applicable. 4.3 Sampling and Testing Shall be in accordance with AMS2371. 4.4 Reports The producer of the product shall furnish

23、with each shipment a report showing the producers name and the country where the metal was melted (e.g., final melt in the case of metal processed by multiple melting operations) and the results of tests for chemical composition of each heat and for tensile properties and hardness of each lot, and s

24、tating that the product conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5593G, size, and quantity. 4.5 Resampling and Retesting Shall be in accordance with AMS2371. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in

25、accordance with AMS2807. 5.2 Packaging The product shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6.

26、 ACKNOWLEDGMENT A producer shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. SAE INTERNATIONA

27、L AMS5593G Page 5 of 5 8. NOTES 8.1 Revision Indicator A change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document t

28、itle indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Hardness conversion tables for metals are presented in ASTM E140. 8.3 Terms used in AMS are clarifie

29、d in ARP1917. 8.4 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. 8.5 Purchase documents should specify not less than the following: AMS5593G Form and size of product desired Quantity of product desired. PREPARED BY AMS COMMITTEE “F“