SAE AMS 5622 H1025-2015 Steel Corrosion-Resistant Bars Wire Forgings Tubing and Rings 16Cr - 4 0Ni - 0 30Cb - 4 0Cu Solution Heat Treated Precipitation Hardened (H1025) Consumable .pdf

1、AEROSPACE MATERIAL SPECIFICATION AMS5622/H1025 Issued 2015-01 Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardened (H1025) Consumable Electrode Remelted (Composition similar to UNS S17400) RATIONALE AMS5622/H1

2、025 is a new specification for purchase of corrosion-resistant steel product in the solution and precipitation heat treated condition. 1. SCOPE 1.1 Form This specification covers a corrosion-resistant steel product in the solution and precipitation heat treated (H1025) condition. 1.1.1 The aged prod

3、uct may be supplied directly by a mill or by a producer other than the mill. The latter would be accomplished by precipitation heat treatment of solution treated material previously certified to AMS5622. The entity assuming responsibility for the aging operation is designated the producer of AMS5622

4、/H1025. 1.1.2 This specification covers product up to 8.0 inches (203 mm) in diameter or least distance between parallel sides, and forging stock of any size (See 8.2). 1.2 Application These products have been used typically for parts requiring corrosion resistance and high strength up to 600 F (316

5、 C) with good ductility and strength in the transverse direction in large section sizes, but usage is not limited to such applications (See 8.1). 1.3 Classification Melting practice classification shall be in accordance with AMS5622. 2. APPLICABLE DOCUMENTS The issue of the following documents in ef

6、fect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been s

7、pecified, the last published issue of that document shall apply. _ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for an

8、y particular use, including any patent infringement arising therefrom, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyri

9、ght 2015 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORD

10、ER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5622/H1025 SA

11、E INTERNATIONAL AMS5622/H1025 Page 2 of 5 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA, www.sae.org. AMS2750 Pyrometry AMS2759/3 Heat Treatment, Precipitation-Hardening

12、 Corrosion-Resistant and Maraging Steel Parts AMS5622 Steel, Corrosion Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb (Nb) - 3.5Cu, Solution Heat Treated, Precipitation Hardenable Consumable Electrode Remelted AMS-H-6875 Heat Treatment of Steel Raw Materials 3. TECHNICAL RE

13、QUIREMENTS 3.1 Composition Shall be in accordance with AMS5622. 3.2 Melting Practice Shall be in accordance with AMS5622. 3.3 Condition Shall be in accordance with AMS5622, and the following: 3.3.1 The product shall be supplied in the precipitation hardened (H1025) heat treat condition. 3.3.2 If str

14、aightening is performed after precipitation hardening heat treatment, product shall be stress relieved by heating to 925 F (496 C) and soaking for at least 1 hour plus one 1 additional for each inch (25 mm) of thickness or fraction thereof greater than 1 inch (25 mm). When load thermocouples are use

15、d, the soaking time shall be at least 1 hour. 3.3.3 Bars shall not be cut from plate (Also see 4.3.3). 3.4 Heat Treatment Shall be in accordance with AMS5622 and the following: 3.4.1 Precipitation Heat Treatment 3.4.1.1 Shall be in accordance with the requirements applicable to either AMS-H-6875 or

16、AMS2759/3 at the vendors option, except acceptance testing and criteria shall be as specified in 3.5.1.3. Precipitation heat treatment furnaces shall have Type B instrumentation. 3.4.1.2 When the product is precipitation heat treated by an entity other than the mill producer of the AMS5622-certified

17、 product, the heat treatment source shall be accredited by a recognized industry agency for stainless steel heat treatment acceptable to the purchaser. 3.5 Properties 3.5.1 All products shall conform to the following requirements: SAE INTERNATIONAL AMS5622/H1025 Page 3 of 5 3.5.1.1 Macrostructure Sh

18、all be in accordance with AMS5622. 3.5.1.2 Microstructure Shall be in accordance with AMS5622. 3.5.1.3 Tensile Properties Shall be in accordance with the following: 3.5.1.3.1 Bars Product, up to 8.0 inches (203 mm) in diameter or least distance between parallel sides, shall be as shown in Table 3. P

19、roperties for larger sizes shall be as agreed upon between purchaser and vendor. Tensile testing shall be performed in accordance with ASTM A370. Table 3A - Tensile properties, inch/pound units Condition Specimen Orientation Tensile Strength ksi Minimum Yield Strength at 0.2% Offset ksi Minimum Elon

20、gation in 2 Inches or 4D % Minimum Reduction of Area % H1025 Longitudinal Transverse 155 185 155 185 145 145 12 7 45 27 Table 3B - Tensile properties, SI units Condition Specimen Orientation Tensile Strength MPa Minimum Yield Strength at 0.2% Offset MPa Minimum Elongation in 50.8 mm or 4D % Minimum

21、Reduction of Area % H1025 Longitudinal Transverse 1069 1276 1069 1276 1000 1000 12 7 45 27 3.5.1.3.1.1 Bars tested in the transverse direction need not be tested in the longitudinal direction. 3.5.1.3.1.2 Mechanical property requirements for product outside the range covered by 1.1.2 shall be agreed

22、 upon between purchaser and producer. 3.5.1.3.2 All other product forms The property requirements of 3.5.1.3.1 shall apply. Test plans shall be as agreed upon between vendor and purchaser. 3.5.1.3.3 When the ultimate tensile strength exceeds 185 ksi, one additional aging cycle may be performed. The

23、set temperature for the additional aging may be up to 25 F (11 C) higher. The soaking time shall be not more than the original precipitation heat treatment cycle. 3.5.1.3.4 When the tensile properties as specified in Table 3 are not met, it is permissible to again perform solution heat treatment in

24、accordance with AMS5622 and precipitation heat treatment to the requirements specified in 3.4, and retest. 3.5.1.4 Hardness Not Applicable SAE INTERNATIONAL AMS5622/H1025 Page 4 of 5 3.6 Quality Shall be in accordance with AMS5622. 3.7 Tolerances Shall be in accordance with AMS5622. 4. QUALITY ASSUR

25、ANCE PROVISIONS 4.1 Responsibility for Inspection The vendor shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product confo

26、rms to specified requirements. Applicable acceptance test data generated for prior certification to AMS5622 need not be repeated for certification to AMS5622/H1025. 4.2 Classification of Tests Shall be in accordance with AMS5622 and the following: 4.2.1 Acceptance Tests 4.2.1.1 Tensile properties (3

27、.5.1.3) and tolerances (3.6) are acceptance tests and shall be performed on each lot. 4.2.2 Sampling and Testing Shall be in accordance with AMS5622. 4.2.2.1 Resampling and Retesting Shall be in accordance with AMS5622. 4.3 Reports 4.3.1 Material Provided by a Producing Mill The vendor of product sh

28、all furnish with each shipment a report showing the vendors name and country where the metal was melted (e.g., final melt in the case of metal processed by multiple melting operations) and the results of tests for composition and macrostructure rating of each heat and for tensile properties of each

29、lot, and stating that the product conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5622/H1025, type of melting practice used, details of the precipitation heat treatment used (including, if straightened, the subsequent stress

30、 relief cycle), size, and quantity. If the product size being shipped is different from the nominal metallurgically worked cross-sectional size, details of how the shipped size was extracted from the larger product shall be reported. 4.3.2 Product from Other than a Producing Mill using Material Prev

31、iously Certified to AMS5622 The vendor of product shall furnish with each shipment the original mill certification of the AMS5622 product and the H1025 heat treatment process certification and test report, including traceability to accreditation of the precipitation heat treat facility (See 3.4.1.2)

32、. 4.3.3 When the product size is outside the range covered by 1.1.2, the report shall contain a statement to that effect (Also see 3.3.3). 5. PREPARATION FOR DELIVERY Shall be in accordance with AMS5622. SAE INTERNATIONAL AMS5622/H1025 Page 5 of 5 6. ACKNOWLEDGMENT Shall be in accordance with AMS562

33、2. 7. REJECTIONS Shall be in accordance with AMS5622. 8. NOTES Shall be in accordance with AMS5622 and the following: 8.1 A change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous

34、issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 When planning a manufacturing ope

35、ration, users of this product should consider the surface condition that may be on the as-received product. 8.3 Procurement documents should specify not less than the following: AMS5622/H1025 Size of product desired Property and acceptance requirements from the cognizant engineering organization applicable to sizes outside the range listed in 1.1.2 Quantity of product desired. PREPARED BY AMS COMMITTEE “F”