SAE AMS 5694J-2010 Steel Corrosion and Heat-Resistant Welding Wire 27Cr - 21 5Ni (UNS S31080)《27 Cr 21 5Ni耐蚀和耐热钢焊丝》.pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2010 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U

4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5694J AEROSPACE MATERIAL SPECIFICATION AMS5694 REV. J Issued 1948-09 Reaffirmed 2006-04 Re

5、vised 2010-06 Superseding AMS5694H Steel, Corrosion and Heat-Resistant, Welding Wire 27Cr - 21.5Ni (Composition similar to UNS S31080) RATIONALE AMS5694J adds standard wording related to welding wire condition (3.2.1) and results from a Five Year Review and update of this specification. 1. SCOPE 1.1

6、 Form This specification covers a corrosion and heat-resistant steel in the form of welding wire. 1.2 Application This wire has been used typically as filler metal for gas-tungsten-arc or gas-metal-arc welding of corrosion and heat resistant steels and alloys of similar composition, but usage is not

7、 limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is

8、specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA an

9、d Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2248 Chemical Check Analysis Limits, Corrosion and Heat-Resistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS2371 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrou

10、ght Products and Forging Stock AMS2813 Packaging and Marking of Packages of Welding Wire, Standard Method AMS2814 Packaging and Marking of Packages of Welding Wire, Premium Quality AMS2816 Identification, Welding Wire, Tab Marking Method AMS2819 Identification, Welding Wire, Direct Color Code System

11、 ARP1876 Weldability Test for Weld Filler Metal Wire ARP4926 Alloy Verification and Chemical Composition, Inspection of Welding Wire SAE AMS5694J Page 2 of 5 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-

12、9585, www.astm.org. ASTM E 353 Chemical Analysis of Stainless, Heat-Resisting, Maraging, and Other Similar Chromium-Nickel-Iron Alloys 3. TECHNICAL REQUIREMENTS 3.1 Composition Wire shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with AST

13、M E 353, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element min max Carbon Manganese Silicon Phosphorus Sulfur Chromium Nickel Molybdenum Copper - 1.25 0.25 - - 26.00 20.50 - - 0.15 2.50 0.60 0.030 0.025 28.00 22.50 0.75 0.75 3.1.1 Chemi

14、cal analysis of initial ingot, bar, or rod stock before drawing is acceptable, provided the processes used for drawing or rolling, annealing, and cleaning are controlled to ensure continued conformance to composition requirements. 3.1.2 Check Analysis Composition variations shall meet the applicable

15、 requirements of AMS2248. 3.2 Condition Cold worked, bright finish, in a temper and with a surface finish which will provide proper feeding of the wire in machine welding equipment. 3.2.1 Wire shall have a smooth finish that is free from slivers, depressions, scratches, scale, seams, laps, and forei

16、gn matter that would adversely affect welding characteristics, operation of the welding equipment, or properties of the weld metal. 3.3 Fabrication 3.3.1 Wire shall be formed from rod or bar descaled by a process which does not affect the composition of the wire. Surface irregularities inherent with

17、 a forming process that do not tear the wire surfaces are acceptable provided the wire conforms to the tolerances of 3.6. 3.3.2 Butt welding is permissible provided both ends to be joined are alloy verified using a method capable of distinguishing the alloy from all other alloys processed in the fac

18、ility, or the repair is made at the wire processing station. The butt weld shall not interfere with uniform, uninterrupted feeding of the wire in machine welding. 3.3.3 In-process annealing, if required, between cold rolling or drawing operations, shall be performed in vacuum or protective atmospher

19、es to ensure freedom from surface oxidation and absorption of other extraneous elements. SAE AMS5694J Page 3 of 5 3.3.4 Residual elements, drawing compounds, oxides, dirt, oil, dissolved gasses and other foreign materials picked up during wire processing that can adversely affect the welding charact

20、eristics, the operation of the equipment, or the properties of the weld metal, shall be removed by cleaning processes that will neither result in pitting nor cause gas absorption by the wire or deposition of substances harmful to welding operations. 3.4 Properties Wire shall conform to the following

21、 requirements: 3.4.1 Weldability Melted wire shall flow smoothly and evenly during welding and shall produce acceptable welds. ARP1876 may be used to resolve disputes. 3.4.2 Spooled Wire Shall conform to 3.4.2.1 and 3.4.2.2. 3.4.2.1 Cast Wire, wound on standard 12-inch (305-mm) diameter spools, shal

22、l have imparted to it a curvature such that a specimen sufficient in length to form one loop with a 1-inch (25-mm) overlap, when cut from the spool and laid on a flat surface, shall form a circle 15 to 50 inches (381 to 1270 mm) in diameter. 3.4.2.2 Helix The specimen on which cast was determined, w

23、hen laid on a flat surface and measured between adjacent turns, shall show a vertical separation not greater than 1-inch (25-mm). 3.5 Quality Wire, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to weldin

24、g characteristics, operation of welding equipment, or properties of the deposited weld metal. 3.6 Sizes and Tolerances Wire shall be supplied in the sizes and to the tolerances shown in 3.6.1 and 3.6.2. 3.6.1 Diameter Shall be as shown in Table 2. TABLE 2A - SIZES AND DIAMETER TOLERANCES, INCH/POUND

25、 UNITS Form Nominal Diameter Inch Tolerance Inch Plus Tolerance Inch Minus Cut Lengths Cut Lengths Spools Spools Spools 0.030, 0.035, 0.045 0.062, 0.078, 0.094, 0.125, 0.156, 0.187 0.007, 0.010, 0.015 0.020, 0.030, 0.035, 0.045 0.062, 0.078, 0.094 0.001 0.002 0.0005 0.001 0.002 0.001 0.002 0.0005 0.

26、001 0.002 SAE AMS5694J Page 4 of 5 TABLE 2B - SIZES AND DIAMETER TOLERANCES, SI UNITS Form Nominal Diameter Millimeters Tolerance Millimeter Plus Tolerance Millimeter Minus Cut Lengths Cut Lengths Spools Spools Spools 0.76, 0.89, 1.14 1.57, 1.98, 2.39, 3.18, 3.96, 4.75 0.18, 0.25, 0.38 0.51, 0.76, 0

27、.89, 1.14 1.57, 1.98, 2.39 0.025 0.05 0.013 0.025 0.05 0.025 0.05 0.013 0.025 0.05 3.6.2 Length Cut lengths shall be furnished in 18, 27, or 36 inch (457, 686, or 914 mm) lengths, as ordered, and shall not vary more than +0, -0.5 inch (-13 mm) from the length ordered. 4. QUALITY ASSURANCE PROVISIONS

28、 4.1 Responsibility for Inspection The vendor of wire shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the wire conforms to spe

29、cified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Composition (3.1), sizes and tolerances (3.6), and alloy verification (5.2) are acceptance tests and shall be performed on each heat or lot as applicable. 4.2.2 Periodic Tests Weldability (3.4.1), cast (3.4.2.1), and helix (3.4.

30、2.2) are periodic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.3 Sampling and Testing In accordance with AMS2371. 4.4 Reports The vendor of wire shall furnish with each shipment a report showing the results of tests for c

31、hemical composition of each heat, and stating that the wire conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5694J, nominal size, and quantity. 4.5 Resampling and Retesting In accordance with AMS2371. 5. PREPARATION FOR DELIV

32、ERY 5.1 Wire shall be supplied either on spools in one continuous length for machine welding or in cut lengths for manual welding, as ordered. Wire on each spool or in each package of cut lengths shall be from the same heat of steel. SAE AMS5694J Page 5 of 5 5.2 Alloy Verification 5.2.1 Wire from ea

33、ch spool or package of cut lengths shall be alloy verified by a method acceptable to purchaser and vendor. The alloy verification methods of ARP4926 are recommended. 5.2.2 An 8-inch (203-mm) length of wire shall be made accessible at both ends of each spool for alloy verification. 5.3 Identification

34、 Shall be in accordance with AMS2816 unless AMS2819 or another method is specified by purchaser. 5.4 Packaging and Marking Shalll be in accordance with AMS2813 unless AMS2814 or another method is specified by purchaser. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revis

35、ion letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Wire not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (l) located in the left margin is for the convenience of the user in loca

36、ting areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications,

37、 nor in documents that contain editorial changes only. 8.2 Terms used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equiva

38、lents of the primary units and are presented only for information. 8.4 Purchase documents should specify not less than the following: AMS5694J Size and form (spools or cut lengths) of wire desired Length of cut lengths or weight of spools desired Quantity of wire desired. PREPARED BY AMS COMMITTEE “F“