SAE AMS 5715F-2009 Nickel Alloy Corrosion and Heat-Resistant Bars Forgings and Rings 60 5Ni - 23Cr - 14Fe - 1 4Al Annealed (UNS N06601)《60 5Ni 23Cr 14Fe 1 4Al退火的耐腐蚀和耐热镍合金棒材 铸件和环形材》.pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2014 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5715F AEROSPACE MATERIAL SPECIFICATION AMS5715 REV. F Issued 1972-05 Revised 2

5、009-03 Reaffirmed 2014-06 Superseding AMS5715E Nickel Alloy, Corrosion and Heat-Resistant, Bars, Forgings, and Rings 60.5Ni - 23Cr - 14Fe - 1.4Al Annealed (Composition similar to UNS N06601) RATIONALE This document has been reaffirmed to comply with the SAE five-year review policy. 1. SCOPE 1.1 Form

6、 This specification covers a corrosion and heat-resistant nickel alloy in the form of bars, forgings, flash welded rings, and stock for forging or flash welded rings. 1.2 Application These products have been used typically for parts requiring corrosion and oxidation resistance up to 2200 F (1204 C)

7、and where such parts may require welding during fabrication, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent supplied herein. The supplier may work

8、 to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Com

9、monwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2261 Tolerances, Nickel, Nickel Alloy, and Cobalt Alloy Bars, Rods, and Wire AMS2269 Chemical Check Analysis Limits, Nickel, Nickel Alloys, and Cobalt Alloys AMS2371 Q

10、uality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS2374 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steel and Alloy Forgings AMS2806 Identification, Bars, Wire, Mechanical Tubing, and Extrusions, Carbo

11、n and Alloy Steels and Corrosion and Heat-Resistant Steels and Alloys AMS2808 Identification, Forgings AMS7490 Rings, Flash Welded, Corrosion and Heat-Resistant Austenitic Steels, Austenitic-Type Iron, Nickel, or Cobalt Alloys, or Precipitation-Hardenable Alloys SAE INTERNATIONAL AMS5715F Page 2 of

12、5 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM E 8/E 8M Tension Testing of Metallic Materials ASTM E 354 Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Si

13、milar Iron, Nickel, and Cobalt Alloys 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 354, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 -

14、 COMPOSITION Element min max Carbon - 0.10 Manganese 1.00Silicon - 0.50 Sulfur - 0.015 Chromium 21.00 25.00Nickel 58.00 63.00Aluminum 1.00 1.70 Titanium - 0.60Boron 0.006Copper 1.00 Iron remainder 3.1.1 Check Analysis Composition variations shall meet the applicable requirements of AMS2269. 3.2 Cond

15、ition The product shall be supplied in the following condition: 3.2.1 Bars Hot finished and annealed; round bars shall be ground or turned. 3.2.2 Forgings and Flash Welded Rings Annealed. 3.2.2.1 Flash welded rings shall not be supplied unless specified or permitted on purchasers part drawing. When

16、supplied, rings shall be manufactured in accordance with AMS7490. 3.2.3 Stock for Forging or Flash Welded Rings As ordered by the forging or flash welded ring manufacturer. SAE INTERNATIONAL AMS5715F Page 3 of 5 3.3 Properties The product shall conform to the following requirements: 3.3.1 Bars Forgi

17、ngs and Flash Welded Rings Tensile properties of bars, forgings, and flash welded rings 4.00 inches (101.6 mm) and under in least nominal cross section shall be shown in Table 2, determined in accordance with ASTM E 8/E 8M. TABLE 2 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 80 ksi

18、(552 MPa) Yield Strength at 0.2% Offset 30.0 ksi (207 MPa) Elongation in 4D 35% 3.3.2 Forging Stock When a sample of stock is forged to a test coupon and annealed, specimens taken from the heat treated coupon shall conform to the requirements of 3.3.1. If specimens taken from the stock after anneali

19、ng conform to the requirements of 3.3.1, the tests shall be accepted as equivalent to tests of a forged coupon. 3.3.3 Stock for Flash Welded Rings Specimens taken from the stock after annealing shall conform to the requirements of 3.3.1. 3.4 Quality The product, as received by purchaser, shall be un

20、iform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product. 3.4.1 Grain flow of die forgings, except in areas which contain flash-line end grain, shall follow the general contour of the forgings showing no evidence of reentrant g

21、rain flow. 3.5 Tolerances Bars shall conform to all applicable requirements of AMS2261. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser

22、 reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Composition (3.1), tensile properties (3.3), and tolerances (3.5) are acceptance tests and shall be

23、 performed on each heat or lot as applicable. SAE INTERNATIONAL AMS5715F Page 4 of 5 4.2.2 Periodic Tests Tests of forging stock (3.3.2) and of stock for flash welded rings (3.3.3) to demonstrate ability to develop required properties and grain flow of die forgings are periodic tests and shall be pe

24、rformed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.3 Sampling and Testing Shall be as follows: 4.3.1 Bars, Flash Welded Rings, and Stock for Forging or Flash Welded Rings In accordance with AMS2371. 4.3.2 Forgings In accordance with AMS2374. 4.4 Re

25、ports The vendor of the product shall furnish with each shipment a report showing the results of tests for composition of each heat and for tensile properties of each lot, and stating that the product conforms to the other technical requirements. This report shall include the purchase order number,

26、heat and lot numbers, AMS5715F, annealing temperature used, product form, size, and quantity. If forgings are supplied, the size and melt source of stock used to make the forging shall also be included. 4.5 Resampling and Retesting Shall be as follows: 4.5.1 Bars, Flash Welded RIngs, and Stock for F

27、orging or Flash Welded Rings In accordance with AMS2371. 4.5.2 Forgings In accordance with AMS2374. 5. PREPARATION FOR DELIVERY 5.1 Sizes Except when exact lengths or multiples of exact lengths are ordered, straight bars will be acceptable in mill lengths of 6 to 24 feet (1.8 to 7.3 m) but not more

28、than 25% of any shipment shall be supplied in lengths of 6 to 9 feet (1.8 to 2.7 m) except that for bars weighing over 25 pounds per foot (37 kg/m), short lengths down to 2 feet (610 mm) may be supplied. 5.2 Identification Shall be as follows: 5.2.1 Bars In accordance with AMS2806. 5.2.2 Forgings In

29、 accordance with AMS2808. SAE INTERNATIONAL AMS5715F Page 5 of 5 5.2.3 Flash Welded Rings and Stock for Forging or Flash Welded Rings As agreed upon by purchaser and vendor. 5.3 Packaging The product shall be prepared for shipment in accordance with commercial practice and in compliance with applica

30、ble rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. R

31、EJECTIONS Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (I) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been

32、 made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Terms used

33、in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. 8.4 Purchase documents should specify not less than the following: AMS5715F Product form and size or part number of product desired Quantity of product desired. PREPARED BY AMS COMMITTEE “F”