SAE AMS 5782G-2013 Steel Corrosion and Heat-Resistant Welding Wire 20 5Cr - 9 0Ni - 0 50Mo - 1 5W - 1 2Cb - 0 20Ti Vacuum Induction Melted (UNS S63197)《20 5Cr 9 0Ni 0 50Mo 1 5W 1 2.pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2013 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U

4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5782G AEROSPACE MATERIAL SPECIFICATION AMS5782 REV. G Issued 1948-11 Reaffirmed 2007-04 Re

5、vised 2013-04 Superseding AMS5782F Steel, Corrosion and Heat-Resistant, Welding Wire 20.5Cr - 9.0Ni - 0.50Mo - 1.5W - 1.2Cb - 0.20Ti Vacuum Induction Melted (Composition similar to UNS S63197) RATIONALE AMS5782G incorporates standard industry requirements for winding (3.5.3.1), cast (3.5.3.2, Table

6、2) and helix (3.5.3.3, Table 2), and is a Five Year Review and update of this specification. 1. SCOPE 1.1 Form This specification covers a corrosion and heat-resistant steel in the form of welding wire. 1.2 Application This wire has been used typically as filler metal for gas-metal-arc or gas-tungst

7、en-arc welding of steels of similar composition requiring joints with strength and corrosion resistance comparable to those of the basis metal, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order form

8、s a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that

9、document shall apply. SAE AMS5782G Page 2 of 7 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2248 Chemical Check Analysis Limits, Corrosion and Heat-Re

10、sistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS2371 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS2813 Packaging and Marking of Packages of Welding Wire, Standard Method AMS2814 P

11、ackaging and Marking of Packages of Welding Wire, Premium Quality AMS2816 Identification, Welding Wire, Tab Marking Method AMS2819 Identification, Welding Wire, Direct Color Code System ARP1876 Weldability Test for Weld Filler Metal Wire ARP4926 Alloy Verification and Chemical Composition Inspection

12、 of Welding Wire 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM E 8/E 8M Tension Testing of Metallic Materials ASTM E 353 Chemical Analysis of Stainless, Heat-Resisting, Maraging,

13、and Other Similar Chromium-Nickel-Iron Alloys 3. TECHNICAL REQUIREMENTS 3.1 Wire Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 353, by spectrochemical methods, or by other analytical methods acceptable to purchas

14、er. TABLE 1 COMPOSITION Element min max Carbon (3.1.1.1) 0.07 0.13 Manganese 1.00 2.00 Silicon 0.30 0.65 Phosphorus - 0.15 Sulfur - 0.10 Chromium 19.00 22.00 Nickel 8.00 9.50 Molybdenum 0.35 0.65 Tungsten 1.25 1.75 Columbium 1.00 1.40 Titanium 0.10 0.30 Tantalum - 0.05 Copper - 0.50 SAE AMS5782G Pag

15、e 3 of 7 3.1.1 Chemical analysis of initial ingot, bar, or rod stock before drawing is acceptable provided processes used for drawing or rolling, annealing, and cleaning are conducted to ensure continued conformance to composition requirements. 3.1.1.1 Carbon shall also be determined periodically on

16、 finished wire (See 4.2.2). 3.1.2 Check Analysis Composition variations shall meet the applicable requirements of AMS2248. 3.2 Melting Practice Steel shall be vacuum induction melted. 3.3 Condition Cold worked, bright finish, in a temper and with a surface finish which will provide proper feeding of

17、 the wire in machine welding equipment. 3.3.1 All wire shall have a smooth finish that is free from slivers, depressions, scratches, scale, seams, laps, and foreign matter that would adversely affect welding characteristics, operation of the welding equipment, or properties of the weld metal. 3.4 Fa

18、brication 3.4.1 In-process annealing between cold rolling or drawing operations shall be performed in vacuum or a protective atmosphere to avoid surface oxidation and absorption of other extraneous materials. 3.4.2 Butt welding is permissible provided both ends to be joined are alloy verified using

19、a method or methods capable of distinguishing the alloy from all other alloys processed within the facility, or the repair is made at the wire processing station. The butt weld shall not interfere with uniform, uninterrupted feeding of the wire in machine welding equipment. 3.4.3 Residual elements,

20、drawing compounds, oxides, dirt, oil, dissolved gases, and other foreign materials picked up during wire processing that can adversely affect the welding characteristics, the operation of the equipment, or properties of the weld metal, shall be removed by a cleaning process that will not result in p

21、itting nor cause gas absorption by the wire nor deposit substances harmful to welding operations. 3.5 Properties Wire shall conform to the following requirements: 3.5.1 Tensile Properties Wire, furnished on spools, shall have tensile strength of 110 to 150 ksi (758 to 1034 MPa), determined in accord

22、ance with ASTM E 8/E 8M. 3.5.2 Weldability Melted wire shall flow smoothly and evenly during welding and shall produce acceptable welds. ARP1876 may be used to resolve disputes. 3.5.3 Spooled Wire Shall conform to 3.5.3.1, 3.5.3. 2 and 3.5.3.3. SAE AMS5782G Page 4 of 7 3.5.3.1 Winding Filler metal i

23、n coils and on spools shall be wound so that kinks, waves, sharp bends, overlapping, or wedging are not encountered, leaving the filler metal free to unwind without restriction. The outside end of the electrode (the end where welding is to begin) shall be identified so it can be located readily and

24、shall be fastened to avoid unwinding. The winding shall be level winding. 3.5.3.2 Cast Wire, wound on standard diameter spools as shown in Table 2 shall have imparted to it a curvature such that a specimen sufficient in length to form one loop with a 1-inch (25-mm) overlap, when cut from the spool a

25、nd laid on a flat surface, shall form a circle (cast) within the limits shown in Table 2. 3.5.3.3 Helix The specimen on which cast was determined, when laid on a flat surface and measured between adjacent turns, shall show a vertical separation not greater than shown in Table 2. TABLE 2A-CAST AND HE

26、LIX REQUIREMENTS INCH-POUND UNITS Spool Diameter Cast-Diameter Inches Helix Inches inches min max max 4 2.5 15 0.5 8 8 50 1 12 15 50 1 TABLE 2B-CAST AND HELIX REQUIREMENTS SI UNITS Spool Diameter Cast Millimeters Helix Millimeters Millimeters min max max 100 65 380 13 200 200 1300 25 300 380 1300 25

27、 3.6 Quality Wire, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to welding operations, operation of welding equipment, or properties of the deposited weld metal. 3.7 Sizes and Tolerances Wire shall be s

28、upplied in the sizes and to the tolerances shown in 3.7.1 and 3.7.2. 3.7.1 Diameter Shall be as shown in Table 3. SAE AMS5782G Page 5 of 7 TABLE 3A - SIZES AND DIAMETER TOLERANCES, INCH/POUND UNITS Form Nominal Diameter Inch Tolerance Inch Plus and Minus Cut Lengths 0.030, 0.035, 0.045 0.001 Cut Len

29、gths 0.062, 0.078, 0.094, 0.125, 0.156, 0.187 0.002 Spools 0.007, 0.010, 0.015 0.0005 Spools 0.020, 0.030, 0.035, 0.045 0.001 Spools 0.062, 0.078, 0.094 0.002 TABLE 3B - SIZES AND DIAMETER TOLERANCES, SL UNITS Form Nominal Diameter Millimeter Tolerance Millimeter Plus and Minus Cut Lengths 0.76, 0.8

30、9, 1.14 0.025 Cut Lengths 1.57, 1.98, 2.39, 3.18, 3.96, 4.75 0.05 Spools 0.18, 0.25, 0.38 0.013 Spools 0.51, 0.76, 0.89, 1.14 0.025 Spools 1.57, 1.98, 2.39 0.05 3.7.2 Length Cut lengths shall be furnished in 18, 27, or 36-inch (457, 686, or 914-mm) lengths, as ordered and shall not vary more than +0

31、, -0.5 inch (-13 mm) from the length ordered. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of wire shall supply all samples for vendors test and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any c

32、onfirmatory testing deemed necessary to ensure that the wire conforms to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Composition (3.1.1), tensile properties (3.5.1), sizes and tolerances (3.7), and alloy verification (5.2) are acceptance tests and shall be performed on

33、 each heat or lot as applicable. 4.2.2 Periodic Tests Determination of carbon on finished wire (3.1.1.1), weldability (3.5.2), cast (3.5.3.2), and helix (3.5.3.3) are periodic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.

34、3 Sampling and Testing Shall be in accordance with AMS2371 and as specified herein. SAE AMS5782G Page 6 of 7 4.4 Reports The vendor of wire shall furnish with each shipment a report showing the results of tests for composition of each heat and tensile properties of each lot, and stating that the wir

35、e conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5782G, nominal size, and quantity. 4.5 Resampling and Retesting Shall be in accordance with AMS2371. 5. PREPARATION FOR DELIVERY 5.1 Wire shall be supplied either on spools i

36、n one continuous length for machine welding or in cut lengths for manual welding, as ordered. Wire on each spool or in each package of cut lengths shall be from the same heat of steel. 5.2 Alloy Verification Wire on each spool or in each package of cut lengths shall be alloy verified by a method acc

37、eptable to purchaser. The alloy verification procedures of ARP4926 are recommended. 5.2.1 An 8-inch (203-mm) length of wire shall be made accessible at both ends of each spool for alloy verification. 5.3 Identification Shall be in accordance with AMS2816 unless AMS2819 or another method is specified

38、 by purchaser. 5.4 Packaging and Marking Shall be in accordance with AMS2813 unless AMS2814 or another method is specified by purchaser. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS

39、Wire not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the

40、previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Terms used in AMS are clarified in ARP1917. 8.3 Dimensi

41、ons in inch/pound units are primary; dimensions in SI units are shown as the approximate equivalents of the primary units and are presented only for information. SAE AMS5782G Page 7 of 7 8.4 Purchase documents should specify not less than the following: AMS5782G Size and form (spools or cut lengths) of wire desired Length of cut lengths or weight of spools desired Quantity of wire desired. PREPARED BY AMS COMMITTEE “F“