SAE AMS 5822D-2006 Steel Corrosion and Heat-Resistant Welding Wire 11 8Cr - 2 8Ni - 1 6Co - 1 8Mo - 0 32V Vacuum Induction Melted (UNS S41780)《耐腐蚀耐热钢制焊丝11 8Cr 2 8Ni 1 6Co 1 8Mo 0 3.pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2017 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/standards.sae.org/AMS5822D AEROSPACE MATERIAL SPECIFICATION AMS5822 REV. D Issued 1985-10 Revised 2006-01 Reaffir

5、med 2017-12 Superseding AMS5822C Steel, Corrosion and Heat-Resistant, Welding Wire 11.8Cr - 2.8Ni - 1.6Co - 1.8Mo - 0.32V Vacuum Induction Melted (Composition similar to UNS S41780) RATIONALE AMS5822D has been reaffirmed to comply with the SAE Five-Year Review policy. 1. SCOPE: 1.1 Form: This specif

6、ication covers a corrosion and heat-resistant steel in the form of welding wire. 1.2 Application: This wire has been used typically as filler metal for gas-metal-arc or gas-tungsten-arc welding of steels of similar composition requiring joints with good strength and oxidation resistance up to 800 F(

7、427 C), but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS: The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a sp

8、ecific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications: Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 8

9、77-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS 2248 Chemical Check Analysis Limits, Corrosion and Heat-Resistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS 2371 Quality Assurance Sampling and Testing, Corrosion and Heat-Resis

10、tant Steels and Alloys, Wrought Products and Forging Stock AMS 2813 Packaging and Marking of Packaging of Welding Wire, Standard Method AMS 2814 Packaging and Marking of Packaging of Welding Wire, Premium Quality AMS 2816 Identification, Welding Wire, Tab Marking Method AMS 2819 Identification, Weld

11、ing Wire, Direct Color Code System ARP1876 Weldability Test for Weld Filler Metal Wire ARP4926 Alloy Verification and Chemical Analysis Inspection of Welding Wire 2.2 ASTM Publications: Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 61

12、0-832-9585, www.astm.org. ASTM E 353 Chemical Analysis of Stainless, Heat-Resisting, Maraging, and Other Similar Chromium-Nickel-Iron Alloys 3. TECHNICAL REQUIREMENTS: 3.1 Composition: Wire shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance

13、with ASTM E 353, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - Composition Element min max Carbon (3.1.3) Manganese Silicon Phosphorus Sulfur Chromium Nickel Cobalt Molybdenum Vanadium Copper Oxygen (3.1.3) Nitrogen (3.1.3) Hydrogen (3.1.3) 0.10 0.40 -

14、 - - 11.00 2.50 1.30 1.50 0.25 - - - - 0.15 1.30 0.40 0.010 0.008 12.50 3.00 2.00 2.00 0.40 0.75 0.005 ( 50 ppm) 0.040 (400 ppm) 0.001 ( 10 ppm) SAE INTERNATIONAL AMS5822D Page 2 of 6_ 3.1.1 Check Analysis: Composition variations shall meet the applicable requirements of AMS 2248; no variation over

15、maximum is permitted for oxygen, nitrogen, and hydrogen. 3.1.2 Chemical analysis of initial ingot, bar, or rod stock before drawing, other than those analyses required to be done on the finished wire, is acceptable provided the processes used for drawing or rolling, annealing, and cleaning, are cont

16、rolled to ensure continued conformance to chemical composition requirements. 3.1.3 Shall be determined on finished wire. 3.2 Melt Practice: Steel shall be vacuum induction melted; it may be remelted using consumable electrode vacuum process, but remelting is not required. 3.3 Condition: Cold worked,

17、 bright finish, in a temper and with a surface finish which will provide proper feeding of the wire in machine welding equipment. 3.4 Fabrication: 3.4.1 Wire shall be formed from rod or bar descaled by a process which does not affect the composition of the wire. Surface irregularities inherent with

18、a forming process that does not tear the wire surfaces are acceptable provided the wire conforms to the tolerances of 3.7. 3.4.2 Butt welding is permissible provided both ends to be joined are alloy verified using a method capable of distinguishing the alloy from all other alloys processed in the fa

19、cility, or the repair is made at the wire processing station. The butt weld shall not interfere with uniform, uninterrupted feeding of the wire in machine welding equipment. 3.4.3 In-process annealing, if required, between cold rolling or drawing operations, shall be performed in vacuum or protectiv

20、e atmospheres to ensure freedom from surface oxidation and absorption of other extraneous elements. 3.4.4 Residual elements, drawing compounds, oxides, dirt, oil, dissolved gasses and other foreign materials picked up during wire processing that can adversely affect the welding characteristics, the

21、operation of the equipment, or the properties of the weld metal, shall be removed by cleaning processes that will neither result in pitting nor cause gas absorption by the wire or deposition of substances harmful to welding operations. 3.5 Properties: Wire shall conform to the following requirements

22、: 3.5.1 Weldability: Melted wire shall flow smoothly and evenly during welding and shall produce acceptable welds, determined by a procedure acceptable to purchaser. ARP1876 may be used to resolve disputes. SAE INTERNATIONAL AMS5822D Page 3 of 6_ 3.5.2 Spooled Wire: Shall conform to 3.5.2.1 and 3.5.

23、2.2. 3.5.2.1 Cast: Wire, wound on standard 12-inch (305-mm) diameter spools, shall have imparted to it a curvature such that a specimen sufficient in length to form one loop with a 1-inch (25-mm) overlap when cut from the spool and laid on a flat surface, shall form a circle 15 to 50 inches (381 to

24、1270 mm) in diameter. 3.5.2.2 Helix: The specimen on which cast was determined, when laid on a flat surface and measured between adjacent turns, shall show a vertical separation not greater than 1-inch (25-mm). 3.6 Quality: Wire, as received by purchaser, shall be uniform in quality and condition, s

25、ound, and free from foreign materials and from imperfections detrimental to welding operations, operation of welding equipment, or properties of the deposited weld metal. 3.7 Sizes and Tolerances: Wire shall be supplied in the following sizes and to the tolerances shown in 3.7.1 and 3.7.2. 3.7.1 Dia

26、meter: Shall be as shown in Table 2. TABLE 2A - Wire Sizes and Tolerances, Inch/Pound Units Form Nominal Diameter Inch Tolerance Inch Plus and Minus Cut Lengths Cut Lengths Spools Spools Spools 0.030, 0.035, 0.045 0.062, 0.094, 0.125, 0.156, 0.187 0.010 0.020, 0.030, 0.035, 0.045 0.062, 0.078, 0.094

27、 0.001 0.002 0.0005 0.001 0.002 TABLE 2B Wire Sizes and Tolerances, SI Units Form Nominal Diameter Millimeters Tolerance Millimeter Plus and Minus Cut Lengths Cut Lengths Spools Spools Spools 0.76, 0.89, 1.14 1.57, 2.39, 3.18, 3.96, 4.75 0.25 0.51, 0.76, 0.89, 1.14 1 57, 1.98, 2.39 0.025 0.05 0.013

28、0.025 0.05 3.7.2 Length: Cut lengths shall be furnished in 18, 27, or 36 inch (457, 686, or 914 mm) lengths, as ordered, and shall not vary more than +0, -0.5 inch (+0, -13 mm) from the length ordered. SAE INTERNATIONAL AMS5822D Page 4 of 6_ 4. QUALITY ASSURANCE PROVISIONS: 4.1 Responsibility for In

29、spection: The vendor of wire shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the wire conforms to specified requirements. 4.2

30、Classification of Tests: 4.2.1 Acceptance Tests: Composition (3.1), sizes and tolerances (3.7), and alloy verification (5.2.1) are acceptance tests and shall be performed on each heat or lot as applicable. 4.2.1.1 Carbon, oxygen, nitrogen, and hydrogen (3.1.3) shall be determined on finished wire fr

31、om each lot. 4.2.2 Periodic Tests: Weldability (3.5.1), cast (3.5.2.1), and helix (3.5.2.2) are periodic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.3 Sampling and Testing: Shall be in accordance with AMS 2371 and as spe

32、cified herein. 4.4 Reports: The vendor of wire shall furnish with each shipment a report showing the results of tests for the full composition of each heat, and for the wire carbon, oxygen, nitrogen and hydrogen analysis of each lot of finished wire, and stating that the wire conforms to the other t

33、echnical requirements. This report shall include the purchase order number, heat and lot numbers, AMS 5822D, nominal size, and quantity. 4.5 Resampling and Retesting: Shall be in accordance with AMS 2371. 5. PREPARATION FOR DELIVERY: 5.1 Wire shall be supplied either on spools in one continuous leng

34、th for machine welding or in cut lengths for manual welding, as ordered. Wire on each spool or in each package of cut lengths shall be from the same heat of steel. 5.2 Alloy Verification: 5.2.1 Wire from each spool or package of cut lengths shall be alloy verified by a method acceptable to purchaser

35、 and vendor. The alloy verification methods of ARP4926 are recommended. SAE INTERNATIONAL AMS5822D Page 5 of 6_ 5.2.2 An 8-inch (203-mm) length of wire shall be made accessible at both ends of each spool for alloy verification. 5.3 Identification: Shall be in accordance with AMS 2816 unless AMS 2819

36、 or another method is specified by purchaser. 5.4 Packaging and Marking: Shall be in accordance with AMS 2813 unless AMS 2814 or another method is specified by purchaser. 6. ACKNOWLEDGMENT: A vendor shall mention this specification number and its revision letter in all quotations and when acknowledg

37、ing purchase orders. 7. REJECTIONS: Wire not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES: 8.1 A change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not edit

38、orial changes, have been made to the previous issue of this specification. An (R) symbol to the left of the document title indicates a complete revision of the specification, including technical revisions. Change bars and (R) are not used in original publications, nor in specifications that contain

39、editorial changes only. 8.2 Terms used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and

40、are presented only for information. 8.4 Purchase documents should specify not less than the following: AMS 5822D Size and form (spools or cut lengths) of wire desired Length of cut lengths or weight of spools desired Quantity of wire desired. 8.5 Key Words: Steel, corrosion-resistant, welding wire, UNS S41780 PREPARED UNDER THE JURISDICTION OF AMS COMMITTEE “F“ SAE INTERNATIONAL AMS5822D Page 6 of 6_