SAE AMS 5837G-2006 Nickel Alloy Corrosion and Heat-Resistant Welding Wire 62Ni - 21 5Cr - 9 0Mo - 3 7Cb(Nb) (UNS N06625)《62Ni 21 5Cr 9 0Mo 3 7Cb(Nb) 耐热耐腐蚀镍合金焊纤》.pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2012 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U

4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5837G AEROSPACE MATERIAL SPECIFICATION AMS5837 REV. G Issued 1968-11 Revised 2006-09 Reaff

5、irmed 2012-04 Superseding AMS5837F Nickel Alloy, Corrosion and Heat-Resistant, Welding Wire 62Ni - 21.5Cr - 9.0Mo - 3.7Cb(Nb) (Composition similar to UNS N06625) RATIONALE AMS5837G has been reaffirmed to comply with the SAE five-year review policy. 1. SCOPE 1.1 Form This specification covers a corro

6、sion and heat-resistant nickel alloy in the form of welding wire. 1.2 Application This wire has been used typically as filler metal for gas-tungsten-arc or gas-metal-arc welding of parts fabricated from alloys of similar or dissimilar composition, but usage is not limited to such applications. 2. AP

7、PLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced docum

8、ent has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside U

9、SA), or www.sae.org. AMS 2269 Chemical Check Analysis Limits, Nickel, Nickel Alloys, and Cobalt Alloys AMS 2371 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS 2813 Packaging and Marking of Packages of Welding Wire, Stand

10、ard Method AMS 2814 Packaging and Marking of Packages of Welding Wire, Premium Quality AMS 2816 Identification, Welding Wire, Tab Marking Method AMS 2819 Identification, Welding Wire, Direct Color Code System ARP1876 Weldability Test for Weld Filler Metal Wire ARP4926 Alloy Verification and Chemical

11、 Composition Inspection of Welding Wire SAE AMS5837G Page 2 of 5 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, or www.astm.org. ASTM E 354 Chemical Analysis of High-Temperature, Electrical, Magnetic

12、, and Other Similar Iron, Nickel, and Cobalt Alloys 3. TECHNICAL REQUIREMENTS 3.1 Composition Wire composition shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 354, by spectrochemical methods, or by other analytical methods acc

13、eptable to purchaser. TABLE 1 - COMPOSITION Element min max Carbon Manganese Silicon Phosphorus Sulfur Chromium Molybdenum Columbium (Niobium) Cobalt Titanium Aluminum Iron Nickel - - - - - 20.00 8.00 3.15 - - - - remainder0.10 0.50 0.50 0.0150.01523.00 10.00 4.15 1.00 0.40 0.40 5.00 3.1.1 Chemical

14、analysis of initial ingot, bar, or rod stock before drawing is acceptable, provided the processes used for drawing or rolling, annealing, and cleaning are controlled to ensure continued conformance to composition requirements. 3.1.2 Check Analysis Composition variations shall meet the applicable req

15、uirements of AMS 2269. 3.2 Condition Cold worked, bright finish, in a temper and with a surface finish that will provide proper feeding of the wire in machine welding equipment. 3.3 Fabrication 3.3.1 Wire shall be formed from rod or bar descaled by a process that does not affect the composition of t

16、he wire. Surface irregularities inherent with a forming process that does not tear the wire surfaces are acceptable provided the wire conforms to the tolerances of 3.6. 3.3.2 Butt welding is permissible provided both ends to be joined are alloy verified using a method or methods capable of distingui

17、shing the alloy from all other alloys processed within the facility, or the repair is made at the wire processing station. The butt weld shall not interfere with uniform, uninterrupted feeding of the wire in machine welding equipment. 3.3.3 In-process annealing, if required, between cold rolling or

18、drawing operations shall be performed in a protective atmosphere to ensure freedom from surface oxidation and absorption of other extraneous elements. SAE AMS5837G Page 3 of 5 3.3.4 Residual elements, drawing compounds, oxides, dirt, oil, dissolved gasses, and other foreign materials picked up durin

19、g wire processing that can adversely affect the welding characteristics, the operation of the equipment, or the properties of the weld metal, shall be removed by cleaning processes which will neither result in pitting nor cause gas absorption by the wire or deposition of substances harmful to weldin

20、g operations. 3.4 Properties Wire shall conform to the following requirements: 3.4.1 Weldability Melted wire shall flow smoothly and evenly during welding and shall produce acceptable welds. ARP1876 may be used to resolve disputes. 3.4.2 Spooled Wire Shall conform to 3.4.2.1 and 3.4.2.2. 3.4.2.1 Cas

21、t Wire, wound on standard 12-inch (305-mm) diameter spools, shall have imparted to it a curvature such that a specimen sufficient in length, 4 to 14 feet (1.2 to 4.3 m) to form one loop with a 1-inch (25-mm) overlap, when cut from the spool and laid on a flat surface, shall form a circle 15 to 50 in

22、ches (381 to 1270 mm) in diameter. 3.4.2.2 Helix The specimen on which cast was determined, when laid on a flat surface and measured between adjacent turns, shall show a vertical separation not greater than 1 inch (25 mm). 3.5 Quality Wire, as received by purchaser, shall be uniform in quality and c

23、ondition, sound, and free from foreign materials and from imperfections detrimental to welding operations, operation of welding equipment, or properties of the deposited weld metal. 3.6 Sizes and Tolerances Wire shall be supplied in the sizes and to the tolerances shown in Table 2. 3.6.1 Diameter Sh

24、all be as shown in Table 2. TABLE 2A - SIZES AND DIAMETER TOLERANCES, INCH/POUND UNITS Form Nominal Diameter Inch ToleranceInch plus Tolerance Inch minus Cut Lengths Cut Lengths Spools Spools Spools 0.030, 0.045, 0.062, 0.078 0.094, 0.125, 0.156, 0.188 0.007, 0.010, 0.015, 0.020 0.030, 0.035, 0.045

25、0.062, 0.078, 0.094 0.002 0.003 0.0005 0.001 0.002 0.002 0.003 0.0005 0.002 0.002 SAE AMS5837G Page 4 of 5 TABLE 2B - SIZES AND DIAMETER TOLERANCES, SI UNITS Form Nominal Diameter Millimeters ToleranceMillimeterplus Tolerance Millimeter minus Cut Lengths Cut Lengths Spools Spools Spools 0.76, 1.14,

26、1.57, 1.98 2.39, 3.18, 3.96, 4.78 0.18, 0.25, 0.38, 0.51 0.76, 0.89, 1.14 1.57, 1.98, 2.39 0.05 0.08 0.013 0.025 0.05 0.05 0.08 0.013 0.05 0.05 3.6.2 Length Cut lengths shall be furnished in 18, 27, or 36 inch (457, 686 or 914 mm) lengths, as ordered, and shall not vary more than +0, -0.5 inch (+0,

27、-13 mm) from the length ordered. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of wire shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory

28、testing deemed necessary to ensure that the wire conforms to specified requirements. 4.2 Classification of Tests 4.2.1 Acceptance Tests Composition (3.1), sizes and tolerances (3.6), and alloy verification (5.2) are acceptance tests and shall be performed on each heat or lot as applicable. 4.2.2 Per

29、iodic Tests Weldability (3.4.1), cast (3.4.2.1), and helix (3.4.2.2) are periodic tests and shall be performed at a frequency selected by the vendor unless frequency of testing is specified by purchaser. 4.3 Sampling and Testing Shall be in accordance with AMS 2371. 4.4 Reports The vendor of wire sh

30、all furnish with each shipment a report showing the results of tests for composition of each heat and stating that the wire conforms to the other technical requirements. This report shall include the purchase order number, heat and lot number, AMS 5837G, nominal size, and quantity. 4.5 Resampling an

31、d Retesting Shall be in accordance with AMS 2371. 5. PREPARATION FOR DELIVERY 5.1 Wire shall be supplied either on spools or in one continuous length for machine welding or in cut lengths or manual welding, as ordered. Wire on each spool or in each package of cut lengths shall be from the same heat

32、of alloy. SAE AMS5837G Page 5 of 5 5.2 Alloy Verification 5.2.1 Wire from each spool or package of cut lengths shall be alloy verified by a method acceptable to purchaser and vendor. The alloy verification procedures of ARP4926 are recommended. 5.2.2 An 8-inch (203-mm) length of wire shall be made a

33、ccessible at both ends of each spool for alloy verification. 5.3 Identification Shall be in accordance with AMS 2816 unless AMS 2819 or another method is specified by purchaser. 5.4 Packaging and Marking Shall be by standard method in accordance with AMS 2813 unless premium quality method in accorda

34、nce with AMS 2814 or other method is specified by purchaser. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Wire not conforming to this specification, or to modifications authorized by

35、 purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of a specification. An (R) symbol to the left of the document

36、 title indicates a complete revision of the specification, including technical revision. Change bars and (R) are not used in original publications, nor in specifications that contain editorial changes only. 8.2 Terms used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound u

37、nits and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. 8.4 Purchase documents should specify not less than the following: AMS 5837G Size and form (spools or cut lengths) of wire desired Length of cut lengths or weight of spools desired Quantity of wire desired Method of alloy verification (See 5.2). PREPARED BY AMS COMMITTEE “F”