SAE AMS 5889C-2010 Nickel Alloy Corrosion and Heat Resistant Sheet and Strip 54Ni - 22Cr - 12 5Co - 9 0Mo - 1 2Al Consumable Electrode or Vacuum Induction Melted Annealed (UNS N066.pdf

1、SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report isentirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising therefr

2、om, is the sole responsibility of the user.”SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions.Copyright 2015 SAE InternationalAll rights reserved. No part of this public

3、ation may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE.TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada)Tel: +1 724-776-4970 (outs

4、ide USA)Fax: 724-776-0790Email: CustomerServicesae.orgSAE WEB ADDRESS: http:/www.sae.orgSAE values your input. To provide feedbackon this Technical Report, please visithttp:/www.sae.org/technical/standards/AMS5889CAEROSPACEMATERIAL SPECIFICATIONAMS5889 REV. CIssued 1990-01Revised 2010-08Reaffirmed 2

5、015-12Superseding AMS5889BNickel Alloy, Corrosion and Heat Resistant, Sheet and Strip54Ni - 22Cr - 12.5Co - 9.0Mo - 1.2AlConsumable Electrode or Vacuum Induction MeltedAnnealed(Composition similar to UNS N06617)RATIONALEAMS5889C has been reaffirmed to comply with the SAE five-year review policy.1. S

6、COPE 1.1 Form This specification covers a corrosion and heat resistant nickel alloy in the form of sheet and strip. 1.2 Application These products have been used typically for parts requiring a combination of high strength and resistance to oxidation, corrosion, and fatigue up to 2200 F (1204 C) and

7、 where such parts may require welding during fabrication, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work t

8、o a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commo

9、nwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2262 Tolerances, Nickel, Nickel Alloy, and Cobalt Alloy Sheet, Strip, and Plate AMS2269 Chemical Check Analysis Limits, Nickel, Nickel Alloys, and Cobalt Alloys AMS2371

10、Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock AMS2807 Identification, Carbon and Low-Alloy Steels, Corrosion and Heat-Resistant Steels and Alloys, Sheet, Strip, Plate, and Aircraft Tubing AS4194 Sheet and Strip Surface Fini

11、sh Nomenclature 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM A 480/A 480M General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet and Strip ASTM E 8/

12、E 8M Tension Testing of Metallic Materials ASTM E 112 Determining Average Grain Size ASTM E 290 Bend Testing of Material for Ductility ASTM E 354 Chemical Analysis of High-Temperature, Electrical, Magnetic, and Other Similar Iron, Nickel, and Cobalt Alloys 3. TECHNICAL REQUIREMENTS 3.1 Composition S

13、hall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 354, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element min max Carbon Manganese Silicon Phosphorus Sulfur Chromium

14、Cobalt Molybdenum Aluminum Titanium Boron Iron Copper Nickel 0.05 - - - - 20.0 10.0 8.0 0.8 - - - - remainder 0.15 0.50 0.50 0.015 0.015 24.0 15.0 10.0 1.5 0.6 0.006 3.0 0.5 3.1.1 Check Analysis Composition variations shall meet the applicable requirements of AMS2269. 3.2 Melting Practice Alloy shal

15、l be multiple melted using consumable electrode practice in the remelt cycle or shall be induction melted under vacuum. If consumable electrode remelting is not performed in vacuum, electrodes which have been produced by vacuum induction melting shall be used for remelting. SAE INTERNATIONAL AMS5889

16、C Page 2 of 5_ 3.3 Condition The product shall be supplied in the following condition: 3.3.1 Sheet and Strip Cold rolled, annealed, and, unless annealing is performed in an atmosphere yielding a bright finish, descaled having a surface appearance comparable to the following commercial corrosion-resi

17、stant steel finishes as described in ASTM A 480/A 480M or AS4194 and the following: 3.3.1.1 Sheet No. 2D finish. 3.3.1.2 Strip No. 1 strip finish. 3.4 Heat Treatment Sheet and strip shall be annealed by heating in the range 2075 to 2175 F (1135 to 1191 C), holding at the selected temperature within

18、25 F (14 C) for a time commensurate with section thickness, and cooling at a rate equivalent to an air cool or faster. 3.5 Properties The product shall conform to the following requirements: 3.5.1 Tensile Properties Shall be as shown in Table 2, determined at room temperature in accordance with ASTM

19、 E 8/E 8M. TABLE 2 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength Yield Strength at 0.2% Offset Elongation in 2 Inches (50.8 mm) 100 ksi (689 MPa) 40.0 ksi (276 MPa) 40% 3.5.2 Bending Product 0.1874 inch (4.760 mm) and under shall be tested in accordance with ASTM E 290 using a sample

20、prepared nominally 0.75 inch (19.0 mm) in width with its axis of bending parallel to the direction of rolling and shall withstand, without cracking, bending at room temperature through an angle of 180 degrees around a diameter equal to the bend factor shown in Table 3 times the nominal thickness of

21、the product. In case of dispute, the results of tests using the guided bend test of ASTM E 290 shall govern. TABLE 3 - BENDING PARAMETERS Nominal Thickness Inch Nominal Thickness Millimeters Bend Factor Up to 0.050, incl Over 0.050 to 0.1874, incl Up to 1.27, incl Over 1.27 to 4.760, incl 1 2 SAE IN

22、TERNATIONAL AMS5889C Page 3 of 5_ 3.5.3 Average Grain Size Shall be not coarser than as shown in Table 4, determined in accordance with ASTM E 112. TABLE 4 - MAXIMUM AVERAGE GRAIN SIZE Nominal Thickness Inch Nominal Thickness Millimeters ASTM Grain Size No. Up to 0.020, incl Over 0.020 to 0.1874, in

23、cl Up to 0.51, incl Over 0.51 to 4.760, incl 4 2 3.6 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product. 3.7 Tolerances Shall conform to all applicable requirement

24、s of AMS2262. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deem

25、ed necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests All technical requirements are acceptance tests and shall be performed on each heat or lot as applicable. 4.3 Sampling and Testing Shall be in accordance with AMS2371. 4.4 Reports The vendor of th

26、e product shall furnish with each shipment a report showing the results of tests for composition of each heat and for tensile properties, bending, and average grain size of each lot, and stating that the product conforms to the other technical requirements. This report shall include the purchase ord

27、er number, heat and lot numbers, AMS5889C, size, and quantity. 4.5 Resampling and Retesting Shall be in accordance with AMS2371. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in accordance with AMS2807. SAE INTERNATIONAL AMS5889C Page 4 of 5_ 5.2 Packaging The product shall be prepared for

28、 shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its

29、 revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Product not conforming to this specification, or to modifications authorized by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (l) located in the left margin is for the convenience of the use

30、r in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of the document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publ

31、ications, nor in documents that contain editorial changes only. 8.2 Terms used in AMS are clarified in ARP1917. 8.3 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. 8.4 Purchase documents should specify not less than the following: AMS5889C Product form and size of product desired Quantity of product desired. PREPARED BY AMS COMMITTEE “F” SAE INTERNATIONAL AMS5889C Page 5 of 5_