SAE AMS 5902C-2008 Steel Corrosion-Resistant Sheet and Strip 18Cr C 8Ni (SAE 30301) Cold Rolled 3 4 Hard 175 ksi (1207 MPa) Tensile Strength (UNS S30100)《18Cr 8Ni(SAE 30301)冷轧3 4硬度.pdf

1、 SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2014 SAE International All rights reserved. No part of this p

3、ublication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-497

4、0 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS5902C AEROSPACE MATERIAL SPECIFICATION AMS5902 REV. C Issued 1992-01 Revised 2

5、008-12 Reaffirmed 2014-06 Superseding AMS5902B Steel, Corrosion-Resistant, Sheet and Strip 18Cr 8Ni (SAE 30301) Cold Rolled, 3/4 Hard, 175 ksi (1207 MPa) Tensile Strength (Composition similar to UNS S30100) RATIONALE This document has been reaffirmed to comply with the SAE five-year review policy. 1

6、 SCOPE 1.1 Form This specification covers a corrosion-resistant steel in the form of sheet and strip. 1.2 Application These products have been used typically in fabrication of aircraft structural components requiring moderate forming and bending, but usage is not limited to such applications. 1.2.1

7、 Mechanical properties specified herein are obtained by cold working (strain hardening) and not by heat treatment. Therefore, the cold-worked product should not be heated to a temperature which adversely affects the mechanical properties or corrosion resistance before, during, or after fabrication.

8、2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced

9、document has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outs

10、ide USA), www.sae.org. AMS2242 Tolerances, Corrosion and Heat-Resistant Steel, Iron Alloy, Titanium, and Titanium Alloy Sheet, Strip, and Plate AMS2248 Chemical Check Analysis Limits, Corrosion and Heat-Resistant Steels and Alloys, Maraging and Other Highly-Alloyed Steels, and Iron Alloys AMS2371 Qu

11、ality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and Alloys, Wrought Products and Forging Stock (Continued) SAE INTERNATIONAL AMS5902C Page 2 of 5 AMS2807 Identification, Carbon and Low-Alloy Steels, Corrosion and Heat-Resistant Steels and Alloys, Sheet, Strip, Plate, and Ai

12、rcraft Tubing 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM A 370 Mechanical Testing of Steel Products ASTM E 290 Bend Testing of Material for Ductility ASTM E 353 Chemical Analys

13、is of Stainless, Heat-Resisting, Maraging, and Other Similar Chromium-Nickel-Iron Alloys ASTM E 384 Microindentation Hardness of Materials 3. TECHNICAL REQUIREMENTS 3.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM

14、 E 353, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element min max Carbon - 0.15 Manganese - 2.00 Silicon - 1.00 Phosphorus - 0.040Sulfur - 0.030Chromium 16.00 18.00 Nickel 6.00 8.00 Molybdenum - 0.75 Copper - 0.75 3.1.1 Check Analysis C

15、omposition variations shall meet the applicable requirements of AMS2248. 3.2 Condition Solution heat treated, descaled unless solution heat treatment is performed in an atmosphere yielding a bright finish, and cold rolled. 3.3 Properties The product shall conform to the following requirements; tensi

16、le and hardness testing shall be conducted in accordance with ASTM A 370. SAE INTERNATIONAL AMS5902C Page 3 of 5 3.3.1 Tensile Properties Shall be as shown in Table 2 for product over 0.005-inch (0.13-mm) in nominal thickness. TABLE 2 - MINIMUM TENSILE PROPERTIES Property Value Tensile Strength 175

17、ksi (1207 MPa) Yield Strength at 0.2% Offset 135 ksi ( 931 MPa) Elongation in 2 Inches (50.8) or 4D Nominal Thickness Over 0.005 to 0.030 Inch (Over 0.13 to 0.76 mm), incl 10% Over 0.030 inch (Over 0.76 mm) 12% 3.3.2 Hardness Shall be not lower than 37 HRC or equivalent (See 8.2). Product shall not

18、be rejected on the basis of hardness if the tensile properties of 3.3.1 are acceptable, determined on specimens taken from the same sample as that with nonconforming hardness or from another sample with similar nonconforming hardness. 3.3.2.1 Microhardness testing in accordance with ASTM E 384 may b

19、e used for thin gages where superficial hardness testing is impractical. 3.3.3 Bending Product 0.050-inch (1.27-mm) and under in nominal thickness shall be tested in accordance with ASTM E 290 using a specimen prepared nominally 0.75 inch (19.0 mm) in width, with its axis parallel to the direction o

20、f rolling, and shall withstand, without cracking, when bending at room temperature through the angle indicated in Table 3 around a diameter equal to the bend factor times the nominal thickness of the product with axis of bend parallel to the direction of rolling. In case of dispute, results of tests

21、 using the guided bend test of ASTM E 290 shall govern. TABLE 3 - BENDING Nominal Thickness Inch Nominal Thickness Millimeters Angle deg, min Bend Factor Up to 0.050, incl Up to 1.27, incl 180 3 3.4 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and

22、free from foreign materials and from imperfections detrimental to usage of the product. 3.5 Tolerances Shall conform to all applicable requirements of AMS2242. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and s

23、hall be responsible for the performance of all required tests. Purchaser reserves the right to sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements. SAE INTERNATIONAL AMS5902C Page 4 of 5 4.2 Classification of Tests All technic

24、al requirements are acceptance tests and shall be performed on each heat or lot as applicable. 4.3 Sampling and Testing Shall be in accordance with AMS2371. 4.4 Reports The vendor of the product shall furnish with each shipment a report showing the results of tests for composition of each heat and f

25、or tensile, hardness, and bending properties of each lot, and stating that the product conforms to the other technical requirements. This report shall include the purchase order number, heat and lot numbers, AMS5902C, size, and quantity. 4.5 Resampling and Retesting Shall be in accordance with AMS23

26、71. 5. PREPARATION FOR DELIVERY 5.1 Identification Shall be in accordance with AMS2807. 5.2 Packaging The product shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of

27、 the product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall mention this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Product not conforming to this specification, or to modifications authorized

28、 by purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of a document. An (R) symbol to the left of the document t

29、itle indicates a complete revision of the document, including technical revision. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Hardness conversion tables for metals are presented in ASTM E 140. 8.3 Terms used in AMS are clarifie

30、d in ARP1917. 8.4 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary; dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. SAE INTERNATIONAL AMS5

31、902C Page 5 of 5 8.5 Purchase documents should specify not less than the following: AMS5902C Form and size of product desired Quantity of product desired. 8.6 Similar Specifications MIL-S-5059, Type 301, Condition 3/4 Hard, is listed for information only and shall not be construed as an acceptable alternate unless all requirements of this AMS are met. PREPARED BY AMS COMMITTEE “F“