SAE AMS-DTL-22499A-2013 Shim Stock Laminated《层压衬垫》.pdf

1、 SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2012 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U

4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMSDTL22499A AEROSPACE MATERIAL SPECIFICATION AMS-DTL-22499 REV. A Issued 1998-09 Reaffirmed

5、2012-02 Revised 2013-03 Superseding AMS-DTL-22499 Shim Stock, Laminated RATIONALE AMS-DTL-22499A revises permitted materials (3.2) to recognize cancelled/superseded specifications, and clarifies available part numbers procurable through the applicable detailed specifications (3.3.5). NOTICE The orig

6、inal issue of this document was taken directly from U.S. Military Specification MIL-DTL-22499D, and contained only minor editorial and format changes required to bring it into conformance with the publishing requirements of SAE technical standards. The initial release of this document was intended t

7、o replace MIL-DTL-22499D. Any part numbers established by the original specification remain unchanged. The original Military Specification was adopted as an SAE standard under the provisions of the SAE Technical Standards Board (TSB) Rules and Regulations (TSB 001) pertaining to accelerated adoption

8、 of government specifications and standards. TSB rules provide for (a) the publication of portions of unrevised government specifications and standards without consensus voting at the SAE Committee level, and (b) the use of the existing government specification or standard format. Under Department o

9、f Defense policies and procedures, any qualifications requirements and associated qualified products lists are mandatory to DOD contracts. Any requirement relating to qualified products lists (QPLs) has not been adopted by SAE and is not part of this technical report. 1. SCOPE 1.1 Scope This specifi

10、cation covers the requirements for surface bonded laminated shim stock. 1.2 Classification Shim stock shall be of the following compositions, types, and classes, as specified in the contract or purchase order (See 6.2): Compositions: Composition 1 - Aluminum alloy. Composition 2 - Brass. Composition

11、 3 - Corrosion resisting steel. SAE AMS-DTL-22499A Page 2 of 11 Composition 4 - Carbon steel. Composition 5 - Titanium alloy. Composition 6 - Polyimide plastic. Types: Type I All laminations. Type II One-half solid stock. Classes: Class 1 .002 inch laminations. Class 2 .003 inch laminations. 2. APPL

12、ICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced documen

13、t has been cancelled and no superseding document has been specified, the last published issue of that document shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA

14、), www.sae.org. AMS4900 Titanium Sheet, Strip, and Plate, Commercially Pure, Annealed, 55 ksi (379 MPa) Yield Strength AMS4901 Titanium Sheet, Strip, and Plate, Commercially Pure, Annealed, 70.0 ksi (485 MPa) AMS4902 Titanium Sheet, Strip, and Plate, Commercially-Pure, Annealed 40.0 ksi (276 MPa) Yi

15、eld Strength AMS4911 Titanium Alloy, Sheet, Strip, and Plate, 6Al - 4V, Annealed AMS4940 Titanium Sheet, Strip, and Plate, Commercially Pure, Annealed, 25.0 ksi (172 MPa) Yield Strength AMS5513 Steel, Corrosion Resistant, Sheet, Strip and Plate AMS5516 Steel, Corrosion Resistant, Sheet, Strip and Pl

16、ate AMS5903 Steel Sheet, Strip, and Plate, Corrosion Resistant AMS5904 Steel Sheet and Strip, Corrosion Resistant AMS5905 Steel Sheet and Strip, Corrosion Resistant AMS5906 Steel Sheet and Strip, Corrosion Resistant AMS5910 Steel Sheet, Strip, and Plate, Corrosion Resistant AMS5911 Steel Sheet and S

17、trip, Corrosion Resistant AMS5912 Steel Sheet and Strip, Corrosion Resistant AMS5913 Steel Sheet and Strip, Corrosion Resistant SAE AMS-DTL-22499A Page 3 of 11 AMS QQ-A-250/5 Aluminum Alloy Alclad 2024, Plate and Sheet AMS QQ-A-250/8 Aluminum Alloy, 5052, Plate and Sheet 2.2 ASTM Publications Availa

18、ble from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B 36 Brass Plate, Sheet, Strip and Rolled Bar ASTM B 121 Leaded Brass Plate, Sheet, Strip and Rolled Bar ASTM B 209 Aluminum and Aluminum-Alloy Sheet and Plate A

19、STM B 601 Temper Designations for Copper and Copper Alloys - Wrought and Cast ASTM D 903 Peel or Stripping Strength of Adhesive Bonds ASTM D 5213 Polymeric Resin Film for Electrical Insulation and Dielectric Applications 2.3 ANSI Publications Available from American National Standards Institute, 25

20、West 43rd Street, New York, NY 10036-8002, Tel: 212-642-4900, www.ansi.org. ANSI/ASQC Z1.4 Sampling Procedures and Tables for Inspection by Attributes. 2.4 U.S. Government Publications Available from DLA Document Services, Building 4/D, 700 Robbins Avenue, Philadelphia, PA 19111-5094, Tel: (215) 697

21、6396, http:/quicksearch.dla.mil/. QQ-S-698 Steel, Sheet and Strip, Low Carbon MIL-I-24768/13 Insulation, Plastic, Laminated, Thermosetting, Cotton-Fabric-Base. Phenolic-Resin (FBE) MIL-I-24768/15 Insulation, Plastic, Laminated, Thermosetting, Cotton-Fabric-Base. Phenolic-Resin (FBI) 3. REQUIREMENTS

22、 3.1 First article When specified in the contract or purchase order, preproduction samples of shim stock of the composition, type, class, nominal size and lateral dimensions specified (See 1.2 and 3.2) shall be subjected to first article inspection (See 4.3 and 6.3). 3.1.1 Specification sheets The i

23、ndividual item requirements shall be as specified herein and in accordance with the applicable specification sheet. In the event of any conflict between the requirements of this specification and the specification sheets, the latter shall govern. SAE AMS-DTL-22499A Page 4 of 11 3.2 Materials 3.2.1 L

24、aminations and solid stock 3.2.1.1 Composition 1 The laminations shall be manufactured from aluminum 1100, conforming to ASTM B 209, Alloy 1100 (processed to temper H19, with a minimum tensile strength of 24.0 ksi) or from aluminum alloy 5052, conforming to AMS QQ-A-250/8 (processed to temper H19 or

25、 H39, with a minimum tensile strength of 42.0 ksi). 3.2.1.1.1 Solid stock The solid stock shall be manufactured from aluminum alloys conforming to AMS QQ-A-250/5 (alclad 2024) tempers T3, T4, T81 or T861 for use with ASTM B 209, Alloy 1100 laminates; AMS QQ-A-250/8 (5052) tempers H32 or H34 for use

26、with AMS QQ-A-250/8 laminates. 3.2.1.2 Composition 2 The laminations and solid stock shall be manufactured from brass conforming to UNS 26000 of ASTM B 36 or UNS C33500 of ASTM B 121, H01 temper or harder (ASTM B 601). 3.2.1.3 Composition 3 Unless otherwise specified the laminations and solid stock

27、shall be manufactured from corrosion resisting steel conforming to AMS5516, AMS5903, AMS5904, AMS5905, or AMS5906, Type 302, annealed condition or harder. 3.2.1.3.1 Type 304 If Type 302 material cannot be procured to meet all of the requirements of this specification, then Type 304 material may be s

28、ubmitted for Type 302 material, conforming to AMS5513, AMS5910, AMS5911, AMS5912, or AMS5913, annealed condition or harder. 3.2.1.4 Composition 4 The laminations shall be manufactured from carbon steel conforming to QQ-S-698, temper annealed or harder. 3.2.1.5 Composition 5 The lamination shall be m

29、anufactured from titanium alloy conforming to AMS4900, AMS4901, AMS4902 or AMS4940. 3.2.1.5.1 Solid stock The solid stock shall be manufactured from titanium alloy sheet conforming to AMS4911. 3.2.1.6 Composition 6 The lamination shall be manufactured from the polyimide film conforming to ASTM D 521

30、3. 3.2.1.6.1 The solid stock shall be manufactured from phenolic resin cotton fabric base conforming to MIL-I-24768/13 or MIL-I-24768/15 (Type FBE or FBI condition). SAE AMS-DTL-22499A Page 5 of 11 3.2.2 Peel strength Each individual shim lamination for composition 1 through 5 shall have a peel stre

31、ngth no less than 1 pound per linear inch and no more than 5 pounds per linear inch, except at the solid/laminate bond line which may be higher. For composition 6, each individual shim lamination shall have a peel strength no less than 1/2 pound per linear inch and no more than 2 1/2 pounds per line

32、ar inch, except at the solid/laminate bond line which may be higher. 3.3 Construction and dimensions The shim stock shall be fabricated from the materials specified herein. The applicable type, class and nominal size of the shim stock shall be as specified in Table 1, the applicable specification sh

33、eet, or as otherwise required. The lateral dimensions shall be as specified in the contract or purchase order for compositions 5 and 6 (See 6.2 and 6.4). Unless otherwise specified, for compositions 1, 2, 3 and 4 the lateral dimensions shall be as specified in the applicable specification sheet, or

34、as otherwise required. The tolerance of the specification width and length shall be 1/8 inch. 3.3.1 Construction details The laminations and solid stock shall be bonded together throughout the whole surface area in a manner which will permit peeling of the laminations for adjustment of the shim thic

35、kness without separation of the remaining laminations and solid parts. The shim stock shall be capable of being cut, using suitable tools, without separation and shall remain intact with normal handling. 3.3.2 Tolerance on nominal size The tolerance on nominal size shall be in accordance with Table

36、2. 3.3.3 Tolerance on lamination thickness The thickness of Class 1 and 2 laminations (See 1.2) shall be within 0.0002 inch and 0.0003 inch, respectively, of the values specified. 3.3.4 Thickness of bond The thickness of the bond shall not exceed 0.0003 inch. 3.3.5 Part numbering identification The

37、existence of an applicable type,class and nominal thickness,as shown in Table 1 is not intended to imply that all products described are available. Only the products described in the applicable detail specification sheets have specific identification part numbers assigned to them. 3.4 Water immersio

38、n The shim stock shall be capable of withstanding total immersion in water at a temperature of 120 F 5 for a period of 3 hours without separation of laminations. 3.5 Workmanship The shim stock shall be uniform in quality, clean, and free of defects detrimental to functional performance of the materi

39、al. SAE AMS-DTL-22499A Page 6 of 11 4. VERIFICATION 4.1 Classification of inspections The inspection of the shim stock shall be classified as: a. First article inspections (See 4.2). b. Quality conformance inspections (See 4.4). 4.2 First article inspection The first article inspection shall consist

40、 of the inspection specified in 4.4 and the additional tests in 4.3. The contractor shall be responsible for the performance of the first article inspection (See 6.3). 4.2.1 First article sample As soon as possible after the award of the contract and prior to production, the contractor shall submit

41、the first article sample. Unless otherwise specified in the contract or purchase order, the first article sample shall consist of two 1 inch by 12 inch strips of shim stock (See 6.3). 4.3 First article testing 4.3.1 Separation of laminations Representative strips of the sample shim stock specified i

42、n 4.2.1 shall be allowed to stand for a minimum period of 8 hours following manufacture or until complete cure, whichever comes first, before being tested for peel strength. The laminations shall peel without separation of the remaining portion. 4.3.1.1 Laminations and bond thickness In the process

43、of performing the test specified in 3.1, the shim stock shall be dimensionally examined to determine compliance with the requirements of 3.3.3 and 3.3.4. 4.3.2 Peel strength Peel strength shall be tested in accordance with ASTM D 903 (see 3.2.3). The number of peels per sample shall be in accordance

44、 with Table 3. 4.3.3 Water immersion Representative strips of the sample shim stock specified in 4.3.1 shall be immersed in water at 120 F 5 for a period of 3 hours. At the end of the test period, the shim stock shall be examined to determine compliance with the requirements of 3.4. 4.4 Quality conf

45、ormance inspection 4.4.1 Lot A lot shall consist of all of the shim stock of the same composition, type, class, nominal size and laterial dimensions, manufactured under essentially the same conditions, and submitted for acceptance at the same time. 4.4.2 Samples Statistical sampling and inspection s

46、hall be in accordance with the general requirements of ANSI/ASQC Z1.4. Lot acceptance criteria shall be based on a single sampling plan with a zero acceptance number. SAE AMS-DTL-22499A Page 7 of 11 4.4.3 Examination The sample shim stock, selected in accordance with 4.4.2, shall be visually and dim

47、ensionally examined to determine compliance with the requirements of this specification. 4.4.4 Inspection of material The material used in the manufacture of the laminated shim stock furnished under this inspection shall have been inspected and accepted in accordance with the respective specificatio

48、ns specified herein. The contractor shall furnish certification that the above requirements have been met. 5. PACKAGING 5.1 Packaging For acquisition purposes, the packaging requirements shall be as specified in the contract or purchase order (See 6.2). When actual packaging of material is to be per

49、formed by DoD personnel, these personnel need to contact the responsible packaging activity to ascertain requisite packaging requirements. Packaging requirements are maintained by the Inventory Control Points packaging activity within the Military Department or Defense Agency, or within the Military Departments System Command. Packaging data retrieval is available from the managing Military Departments or Defense Agencys automated