SAE AMS-DTL-23053 13A-2012 Insulation Sleeving Electrical Heat Shrinkable Fluoroelastomer Flexible《柔性含氟聚合物热收缩电气绝缘套管》.pdf

1、_ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringement arising there

2、from, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be reaffirmed, revised, or cancelled. SAE invites your written comments and suggestions. Copyright 2012 SAE International All rights reserved. No part of this publication m

3、ay be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside U

4、SA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMSDTL23053/13A AEROSPACE MATERIAL SPECIFICATION AMS-DTL-23053/13 REV. A Issued 1999-07 Revis

5、ed 2012-08 Superseding AMS-DTL-23053/13 Insulation Sleeving, Electrical, Heat Shrinkable, Fluoroelastomer, Flexible FSC 5970 RATIONALE Revise to include comments received by the government and industry, update references, align specification with SAE guidelines, and review specification for known te

6、chnical problems. The requirements for acquiring the sleeving described herein shall consist of this specification sheet and the issue of the following specification listed in that issue of the Department of Defense Index of Specifications and Standards (DODISS) specified in the solicitation: MIL-DT

7、L-23053. REQUIREMENTS Polymer type: The base elastomer used in formulating this sleeving shall be fluoroelastomer. Continuous operating temperature range: -40 F (-40 C) to +392 F (+200 C). Color: The heat shrinkable sleeving shall be furnished in the color specified by the acquisition activity (See

8、6.2); however, black shall be considered standard. Colors shall conform to the requirements of Class II of MIL-STD-104. (See 1.2.1 and 3.4.2.1) Longitudinal change: 20 percent. SAE AMS-DTL-23053/13A Page 2 of 4 Military part number: The Military part number shall consist of the basic number of this

9、specification sheet and dash numbers as follows: M23053/13 - X XX - X Example: Black, 0.500 inch (12.7 mm) as supplied ID sleeving shall be identified as M23053/13-004-0. TABLE I. CONSTRUCTION DETAILS, INCHES (MM). 1/ Military part number 1/ As supplied ID minimum After unrestricted shrinkage ID max

10、imum Wall Thickness 2/ M23053/13-001-* 0.187(4.75) 0.094(2.38) 0.035 0.007(0.889 0.178) M23053/13-002-* 0.250(6.35) 0.125(318) 0.035 0.007(0.889 0.178) M23053/13-003-* 0.375(9.53) 0.187(4.75) 0.035 0.007(0.889 0.178) M23053/13-004-* 0.500(12.70) 0.250(6.35) 0.035 0.007(0.889 0.178) M23053/13-005-* 0

11、.625(15.88) 0.312(7.92) 0.042 0.008(1.067 0.203) M23053/13-006-* 0.750(19.05) 0.375(9.53) 0.042 0.008(1.067 0.203) M23053/13-007-* 0.875(22.23) 0.437(11.10) 0.049 0.011(1.245 0.279) M23053/13-008-* 1.000(25.40) 0.500(12.70) 0.049 0.011(1.245 0.279) M23053/13-009-* 1.250(31.75) 0.625(15.88) 0.055 0.0

12、15(1.397 0.381) M23053/13-010-* 1.500(38.10) 0.750(1905) 0.055 0.015(1.397 0.381) M23053/13-011-* 2.000(56.80) 1.000(25.40) 0.065 0.017(1.651 0.432) M23053/13-012-* 0.125(3.18) 0.063(1.60) 0.030 0.007(0.762 0.178) 1/ Diameter limits for object to be enclosed shall be as specified in technical data.

13、2/ Wall thickness values are less when shrinkage is restricted. 3/ The asterisk in the part number shall be replaced by color code designations (See 1.2.1). Black is the standard color. Unrestricted shrinkage: Test method 4.6.5; 392 F 9 (200 C 5) for 10 minutes maximum. Color code designator (See 1.

14、2.1) Size identifier (See Table 1) Class (Where no classes are specified in the specification sheet, the numeric “0” is used) Specification sheet SAE AMS-DTL-23053/13A Page 3 of 4 TABLE 2 - PHYSICAL PROPERTIES Characteristic Requirement Test procedure and condition As supplied: ID, minimum Table 1 4

15、.6.3.1.1 Cold impact No cracking 4.6.7.2 -40 F 1 (-40 C 2) Heat shock No cracks, flowing or dripping 4.6.8 572 F 9 (300 C 5) Restricted shrinkage No cracks 4.6.6 392 F 4 (200 C 2) Voltage withstand Pass 4.6.6.3 After unrestricted shrinkage: ID, maximum Table 1 4.6.3.1.2 Wall thickness Table 1 4.6.3.

16、2 Tensile strength, psi (MPa), minimum 1200(8.2) 4.6.13, ASTM D 412 Ultimate elongation, percent 250 4.6.13, ASTM D 412 Tensile stress at 200 percent elongation, psi (MPa), maximum 2000(13.8) 4.6.2 ASTM D 412 Dielectric strength, volts/mil, (Kv/mm), minimum 200(7.9) 4.6.2 ASTM D 2671 Volume resistiv

17、ity, Ohm-cm, minimum 1094.6.2 ASTM D 876 Corrosion No corrosion or pitting 4.6.10.1 and 4.6.10.2 347 F 4 (175 C 2) for 16 hours. Heat resistance, properties after: 4.6.9 482 F 5.4 (250 C 3) for 168 hours Tensile strength, psi (MPa), minimum 1200(8.2) Ultimate elongation, percent, minimum 200 Water a

18、bsorption, percent, maximum 0.5 4.6.2 ASTM D 570, 24 hrs at 73 F (23 C) SAE AMS-DTL-23053/13A Page 4 of 4 TABLE 2 - PHYSICAL PROPERTIES (CONT.) Characteristic Requirement Test procedure and condition Fluid resistance, properties after: 4.6 .11 Tensile strength, psi (MPa), minimum 1200 (8.2) Ultimate

19、 elongation, percent, minimum 250 Flammability Self-extinguishing within 15 seconds 4.6.14 Procedure A ASTM D 2671 Fungus resistance properties after: Tensile Strength, psi (MPa), minimum Ultimate elongation, percent, minimum Dielectric strength, volts/mil (Kv/mm), minimum No growth or 1200 (8.2) 25

20、0 200 (7.9) 4.6.2 ASTM G 21 4.6.17 Storage life: The supplier shall certify storage at 65 to 95 F (18 to 35 C) for a period of 2 years. Conformance to 3.5. See 3.5.2 for storage life extension. Intended use: Heat shrinkable, flexible, fluoroelastomer sleeving is used in high temperature applications

21、 or where exposure to high temperature solvents is expected. NOTES A change bar (l) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of this document. An (R) symbol to the left of th

22、e document title indicates a complete revision of the document, including technical revisions. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. Dimensions and properties in inch/pound units and the Fahrenheit temperatures are primary: dimensions and properties in SI units and the Celsius temperatures are shown as the approximate equivalents of the primary units and are presented only for information. PREPARED BY AE-8D WIRE AND CABLE COMMITTEE