SAE AS 3653A-2015 INSERT SCREW THREAD LONG SELF-LOCKING KEY LOCKED SELF-BROACHING KEYS UNS S66286.pdf

1、 AEROSPACE STANDARD INSERT, SCREW THREAD, LONG SELF-LOCKING, KEY LOCKED, SELF-BROACHING KEYS, UNS S66286AS3653Copyright 2015 SAE International All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mec

2、hanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org ISSUED 2014-01REVISE

3、D 2015-02THIRD ANGLE PROJECTION CUSTODIAN: E-25 REV.A FEDERAL SUPPLY CLASS 5325 AS3653 SHEET 1 OF 2 REV. A PROCUREMENT SPECIFICATION: AS5887SAE Technical Standards Board Rules provide that: “This report ispublished by SAE toadvance thestate of technicalandengineering sciences. Theuse ofthisreport is

4、 entirelyvoluntary, andits applicability and suitability forany particularuse,including any patent infringement arising therefrom, isthe soleresponsibilityofthe user.”SAE reviews eachtechnicalreport at least every five years at which time itmay berevised,reaffirmed, stabilized, orcancelled. SAE invi

5、tes yourwrittencomments andsuggestions. SAE values your input. To provide feedbackon this Technical Report, please visit http:/www.sae.org/technical/standards/AS3653A RATIONALE FIGURE 1 UPDATED TO CORRECT REFERENCES TO LOCKING KEYS , DIM L DELETED. THREAD SPEC CORRECTED, CORRECT QPL NUMBER IN NOTE14

6、 AND MASS VALUES RECALCULATED HG(F) /9/C MIN THREAD AGAGE DEPTHLOWER UNTHREADED PORTIONFORMED OUT OF ROUND FORTHREAD LOCKING FEATURE MARK MANUFACTURERS IDENTIFICATION PER AS478-2A-C(K)(.040) /9/LOCKING KEYS /8/(.068) /9/B EXTERNAL THREADMODIFIED MINOR DIA E.006 DA INTERNAL THREADPER AS8879D63AVIEW A

7、ON A LOCKING KEYPER ASME B1.1FIGURE 1 - INSERT TABLE 1 - DIMENSIONS PART NUMBER A INTERNAL THREAD UNJF-3B B EXTERNAL THREAD E EXTERNAL THREAD MODIFIED MINOR DIAMETER F REF G H K REF C MIN GAGE DEPTHAS3653-3 .1900 - 32 .3750-16 UNC-3A .312 - .320 .160 .360 - .390 .255 - .285 .284 .226 AS3653-4 .2500

8、- 28 .4375-14 UNC-3A .375 - .383 .190 .497 - .527 .360 - .390 .344 .324 AS3653-5 .3125 - 24 .5000-13 UNC-3A .432 - .440 .190 .695 - .725 .520 - .550 .407 .475 AS3653-6 .3750 - 24 .5625-12 UNC-3A .495 - .503 .190 .784 - .814 .581 - .611 .469 .536 AS3653-7 .4375 - 20 .6250-11 UNC-3A .551 - .565 .190 .

9、875 - .905 .650 - .680 .532 .593 AS3653-8 .5000 - 20 .6875-12 UN-3A .615 - .625 .190 .983 - 1.013 .723 - .753 .594 .666 PART NUMBER APPROX MASS LB/100 AS3653-3 .59 AS3653-4 .99 AS3653-5 1.75 AS3653-6 2.12 AS3653-7 2.92 AS3653-8 3.49 AEROSPACE STANDARD AS3653 SHEET 2 OF 2 REV. A INSERT, SCREW THREAD,

10、 LONG, SELF-LOCKING, KEY LOCKED, SELF-BROACHING KEYS, UNS S66286 NOTES: 1. MATERIAL: INSERT - STEEL, CORROSION-RESISTANT, TYPE A286 (UNS S66286) IN ACCORDANCE WITH AMS5731, AMS5732, AMS5734, OR AMS5737. LOCKING KEYS: STEEL, CORROSION-RESISTANT, TYPE 420 CRES. CHEMICAL COMPOSITION OF AMS5621. 2. HEAT

11、 TREATMENT: AMS5731, AMS5732, AMS5734 SHALL BE HEAT TREATED TO 140 000 PSI FTU MINIMUM PER AMS2759/3. 3. HARDNESS: INSERTS SHALL HAVE A HARDNESS RANGE OF 31 - 36 HRC KEYS SHALL HAVE A HARDNESS RANGE OF 54 - 57 HRC 4. FINISH: ALL DIMENSIONS APPLY AFTER PLATING. INSERTS: PASSIVATE PER AMS2700 METHOD 1

12、 OR 2. SILVER PLATED PER AMS2411 ON THE INTERNAL THREADS ONLY WITH OPTIONAL COVERAGE ON COUNTERSINK. ON INSERTS WITH THREAD A OF .2500 OR LARGER THE PLATING THICKNESS SHALL BE .0002 TO .0006. INSERTS WITH THREAD A OF .1900 SHALL SHOW COMPLETE PLATING COVERAGE ON THE THREAD, PLATING THICKNESS NOT AN

13、ACCEPTANCE REQUIREMENT. LOCKING KEYS: PASSIVATE PER AMS2700 METHOD 1 OR 2. 5. FLUORESCENT PENETRANT INSPECTION PER ASTM E1417/1417M TYPE I, SENSITIVITY LEVEL 2, PRIOR TO PLATING. 6. SURFACE TEXTURE: SYMBOLS PER ASME Y14.36M. REQUIREMENTS PER ASME B46.1. UNLESS OTHERWISE SPECIFIED, SURFACES TO BE 125

14、 MICROINCHES Ra. INTERNAL SCREW THREADS TO BE 63 MICROINCHES Ra. 7. DIMENSIONING AND TOLERANCING: ANSI Y14.5M-1982. (ASME PUBLICATION) /8/ INSERTS WITH INTERNAL THREAD SIZES .1900 AND .2500 SHALL BE SUPPLIED WITH TWO LOCKING KEYS SPACED 180 DEGREES APART. INSERTS WITH INTERNAL THREAD SIZE .3125 AND

15、GREATER SHALL BE SUPPLIED WITH FOUR LOCKING KEYS SPACED 90 DEGREES APART. /9/ DIMENSION APPLIES TO LOCKING KEYS, SLOT CONFIGURATION PER MANUFACTURERS OPTION, KEYS TO BE RETAINED IN SLOT UNTIL USE/INSTALLATION. 10. INSERTS SHALL BE FREE OF BURRS AND SLIVERS. 11. UNLESS OTHERWISE SPECIFIED, BREAK SHAR

16、P EDGES .015 MAXIMUM. 12. INSERTS TO BE INSTALLED IN ACCORDANCE WITH AS4724. 13. UNLESS OTHERWISE SPECIFIED, FILLETS R .015 MAXIMUM 14. PROCUREMENT SPECIFICATION: AS5887. 15. PRODUCT SUPPLIED TO THIS SPECIFICATION SHALL BE MANUFACTURED BY AN ACCREDITED MANUFACTURER AS LISTED IN THE PERFORMANCE REVIE

17、W INSTITUTE (PRI) QUALIFIED PRODUCTS LIST PRI-QPL-AS3653 FOR THIS STANDARD. THIS PART STANDARD MAY BE RELEASED PRIOR TO A MANUFACTURER BEING APPROVED AND LISTED ON PRI-QPL-AS3653. IT IS THE USERS RESPONSIBILITY TO ENSURE AN APPROVED MANUFACTURER IS LISTED PRIOR TO SPECIFYING ANY OF THESE PARTS FOR U

18、SAGE. 16. UNDEFINED FEATURES ARE AT MANUFACTURERS DISCRETION. 17. DESIGNED FOR USE IN MATERIALS WITH A MINIMUM ULTIMATE SHEAR STRENGTH OF 27 000 PSI. 18. A CHANGE BAR (l) LOCATED IN THE LEFT MARGIN IS FOR THE CONVENIENCE OF THE USER IN LOCATING AREAS WHERE TECHNICAL REVISIONS, NOT EDITORIAL CHANGES,

19、 HAVE BEEN MADE TO THE PREVIOUS ISSUE OF THIS DOCUMENT. AN (R) SYMBOL TO THE LEFT OF THE DOCUMENT TITLE INDICATES A COMPLETE REVISION OF THE DOCUMENT, INCLUDING TECHNICAL REVISIONS. CHANGE BARS AND (R) ARE NOT USED IN ORIGINAL PUBLICATIONS, NOR IN DOCUMENTS THAT CONTAIN EDITORIAL CHANGES ONLY. AS AND AMS ARE SAE INTERNATIONAL PUBLICATIONS. ASME IS AN AMERICAN SOCIETY OF MECHANICAL ENGINEERS PUBLICATION. ASTM IS AN ASTM INTERNATIONAL PUBLICATION.