SAE AS 5382 3-2004 CABLE FIBER OPTIC SINGLE-MODE 6 125 250 HERMETIC COATED TIGHT BUFFER《包有紧缓冲层的密封单模6 125 250 μm光缆》.pdf

1、AEROSPACE STANDARD CABLE, FIBER OPTIC, SINGLE-MODE, 6/125/250 m, HERMETIC COATED, TIGHT BUFFER AS5382/3ISSUED 2004-06REAFFIRMED 2011-09 THIRD ANGLE PROJECTION CUSTODIAN: SAE AE-8/AE-8D FEDERAL SUPPLY CLASSAS5382/3SHEET 1 OF 3FIGURE 1 - CABLE CONFIGURATION 1. Construction Description:1.1 Optical Fibe

2、r Dimensions and MaterialsCore Diameter: 6 m nom. (0.00024 in) Mode Field Diameter 980 nm: 7 m 1.0 m (0.00028 in 0.00004 in) Core Material: Step Index Silica Glass Cladding Diameter: 125 m 2 m (0.0049 in 0.00008 in) Cladding Material: Silica Glass Core to Cladding Ellipticity: 2% maximum Core to Cla

3、dding Offset: 1 m maximumHermetic Coated: YesCoating Diameter 250 m 15 m (0.0098 in 0.00059 in) Coating Material Acrylate1.2 Cable Dimensions and MaterialsSecondary Buffer Diameter: 0.024 +0.002/-0.005 inches (610 +50/-127 m) Secondary Buffer Material: Wrapped expanded PTFE tape with overall FEP coa

4、ting Strength Member: Braided Aramid Fiber Outer Jacket Diameter: 0.046, +0.002, -0.003 inches (1.2 +0.05/-0.13 mm) Outer Jacket Material: FEPSAE TechnicalStandards Board Rules provide that: “This report is published by SAE toadvance thestate of technical andengineering sciences.The use of thisrepor

5、t is entirely voluntary, andits applicabilityandsuitability forany particularuse, including any patent infringement arising therefrom, is thesole responsibility oftheuser.” SAE reviews each technical report at least every five yearsat which time it may be reaffirmed, revised, orcancelled. SAE invite

6、s yourwritten commentsandsuggestions. Copyright 2011All rights reserved. No part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE

7、. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel: 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE International SAE values your input. To provide feedbackon this Technical Report, please visit http:/www.sae.o

8、rg/technical/standards/AS5382/3AEROSPACE STANDARD CABLE, FIBER OPTIC, SINGLE-MODE, 6/125/250 m, HERMETIC COATED, TIGHT BUFFER AS5382/3 AS5382/3SHEET 2 OF 31.3 Cable PerformanceOperational Mode: Single mode Temperature Rating: -30 to +100 C Storage Temperature: -30 to +100 C Outer Jacket Color: Yello

9、wFinished Cable Weight: 2.0 kg/km maximum 2. Optical Fiber RequirementsMaximum Attenuation: 3.0 dB/km 980 nm Attenuation Uniformity No discontinuities greater than 0.1 dB Radiation Induced Attenuation 11.0 dB/km 980 nm Numerical Aperture: 0.11 nom. Fiber Tensile Proof Test: 200,000 PSI minimum Cut O

10、ff Wavelength 930 nm +30, -40 nm Dynamic Fatigue N100Chromatic Dispersion 80 ps/nm-km 3. Environmental Blocking: No areas of localized adhesion Outgassing TML 1.0% and CVCM 0.1% Vibration 0.05 dB/50 m change in optical transmittance after the test Shock 0.05 dB/50 m change in optical transmittance a

11、fter the test Test Condition M AEROSPACE STANDARD CABLE, FIBER OPTIC, SINGLE-MODE, 6/125/250 m, HERMETIC COATED, TIGHT BUFFER AS5382/3 AS5382/3SHEET 3 OF 34. MechanicalCyclic Flex: 0.1dB change in optical transmittance during the test with 0.05 dB permanent change after test Test temps: -30 C, +25 C

12、, +100 C Cable Tensile Load and 0.1dB change in optical transmittance during the test with Bending: 0.05 dB permanent change after test Maximum tensile load 30 lb Durability of Manufacturers Required unless identification marking is under a clear Identification: jacket Jacket Strippability: Easily R

13、emoved, No damage to Fiber at 10X 5. ThermalThermal Shock: Temperature Range: -30 to +100 C Maximum Cable Diameter Change of 10%0.1dB change in optical transmittance after test Storage Life: Temperature Range: -30 to +100 C No Visual Damage at 10X Magnification 0.1dB change in optical transmittance

14、after test Temperature Cycling: 5 cycles, temperature range: -30 to +100 C Maximum Cable Diameter Change of 10%0.1dB change in optical transmittance during the test with 0.05 dB permanent change after testTemperature Cycling 5 cycles, temperature range: -30 to +100 C With Mandrel: Wrapped 4 times ar

15、ound a 35 mm mandrel Maximum Cable Diameter Change of 10%0.1dB change in optical transmittance during the test with 0.05 dB permanent change after testTemperature Cycling: 5 cycles, temperature range: -30 to +100 C In Vacuum Maximum Cable Diameter Change of 10%0.1dB change in optical transmittance during the test with 0.05 dB permanent change after test