1、 Collection of SANS standards in electronic format (PDF) 1. Copyright This standard is available to staff members of companies that have subscribed to the complete collection of SANS standards in accordance with a formal copyright agreement. This document may reside on a CENTRAL FILE SERVER or INTRA
2、NET SYSTEM only. Unless specific permission has been granted, this document MAY NOT be sent or given to staff members from other companies or organizations. Doing so would constitute a VIOLATION of SABS copyright rules. 2. Indemnity The South African Bureau of Standards accepts no liability for any
3、damage whatsoever than may result from the use of this material or the information contain therein, irrespective of the cause and quantum thereof. ISBN 978-0-626-21328-2 SANS 15614-7:2008Edition 1ISO 15614-7:2007Edition 1SOUTH AFRICAN NATIONAL STANDARD Specification and qualification of welding proc
4、edures for metallic materials Welding procedure test Part 7: Overlay welding This national standard is the identical implementation of ISO 15614-7:2007 and is adopted with the permission of the International Organization for Standardization. Published by Standards South Africa 1 dr lategan road groe
5、nkloof private bag x191 pretoria 0001 tel: 012 428 7911 fax: 012 344 1568 international code + 27 12 www.stansa.co.za Standards South Africa SANS 15614-7:2008 Edition 1 ISO 15614-7:2007 Edition 1 Table of changes Change No. Date Scope National foreword This South African standard was approved by Nat
6、ional Committee StanSA TC 5120.08, Welding and allied processes, in accordance with procedures of Standards South Africa, in compliance with annex 3 of the WTO/TBT agreement. This SANS document was published in June 2008. Reference numberISO 15614-7:2007(E)ISO 2007INTERNATIONAL STANDARD ISO15614-7Fi
7、rst edition2007-06-15Specification and qualification of welding procedures for metallic materials Welding procedure test Part 7: Overlay welding Descriptif et qualification dun mode opratoire de soudage pour les matriaux mtalliques preuve de qualification dun mode opratoire de soudage Partie 7: Rech
8、argement par soudage SANS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-7:2007(E) PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or vie
9、wed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in
10、 this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable
11、for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Secretariat at the address given below. COPYRIGHT PROTECTED DOCUMENT ISO 2007 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utiliz
12、ed in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax +
13、41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ii ISO 2007 All rights reservedSANS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-7:2007(E) ISO 2007 All rights reserved iiiContents Page
14、 Foreword iv Introduction v 1 Scope . 1 2 Normative references . 1 3 Terms and definitions. 2 4 Preliminary welding procedure specification (pWPS) 2 4.1 Overlay welding 2 4.2 Hardfacing . 2 4.3 Building-up 3 4.4 Buttering 3 5 Welding procedure test 3 6 Test piece 3 6.1 Shape and dimensions of test p
15、ieces. 3 6.2 Welding of test pieces 5 7 Examination and testing 6 7.1 Extent of testing 6 7.2 Non-destructive testing (NDT). 6 7.3 Location and taking of test specimens 6 7.4 Destructive testing 8 7.5 Acceptance criteria. 10 7.6 Retesting 11 8 Range of qualification 11 8.1 General. 11 8.2 Qualificat
16、ion related to the manufacturer 11 8.3 Qualification related to the material 12 8.4 Qualification related to the filler material/overlay . 13 8.5 Common to welding procedures. 14 8.6 Specific to welding processes 15 9 Welding procedure qualification record (WPQR) 17 Annex A (informative) Welding pro
17、cedure qualification record form (WPQR) 18 Bibliography . 21 SANS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-7:2007(E) iv ISO 2007 All rights reservedForeword ISO (the International Organization for Standardization)
18、 is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be repre
19、sented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are
20、 drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an Internationa
21、l Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 15614-7 was pr
22、epared by the European Committee for Standardization (CEN) Technical Committee CEN/TC 121, Welding, in collaboration with Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee SC 10, Unification of requirements in the field of metal welding, in accordance with the Agreement on te
23、chnical cooperation between ISO and CEN (Vienna Agreement). ISO 15614 consists of the following parts, under the general title Specification and qualification of welding procedures for metallic materials Welding procedure test: Part 1: Arc and gas welding of steels and arc welding of nickel and nick
24、el alloys Part 2: Arc welding of aluminium and its alloys Part 3: Fusion and pressure welding of non-alloyed and low-alloyed cast irons Part 4: Finishing welding of aluminium castings Part 5: Arc welding of titanium, zirconium and their alloys Part 6: Arc and gas welding of copper and its alloys Par
25、t 7: Overlay welding Part 8: Welding of tubes to tube-plate joints Part 10: Hyperbaric dry welding Part 11: Electron and laser beam welding Part 12: Spot, seam and projection welding Part 13: Resistance butt and flash welding Requests for official interpretations of any aspect of this part of ISO 15
26、614 should be directed to the Secretariat of ISO/TC 44/SC 10 via your national standards body. A complete listing of these bodies can be found at www.iso.org. SANS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-7:2007(E
27、) ISO 2007 All rights reserved vIntroduction This part of ISO 15614 is part of a series of standards. Details of this series are given in ISO 15607:2003, Annex A. Previous procedure qualifications to former national standards or specifications should be taken into consideration at the time of the en
28、quiry or contract stage and agreed between the contracting parties. SANS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .SANS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients
29、 of the SABS .INTERNATIONAL STANDARD ISO 15614-7:2007(E) ISO 2007 All rights reserved 1Specification and qualification of welding procedures for metallic materials Welding procedure test Part 7: Overlay welding 1 Scope This part of ISO 15614 specifies how a preliminary welding procedure specificatio
30、n for overlay welding is qualified by welding procedure tests. This part of ISO 15614 defines the conditions for carrying out welding procedure tests and the range of qualification for welding procedures for all practical welding operations within the range of variables listed in Clause 8. Additiona
31、l tests may be required by application standards. This part of ISO 15614 applies to all welding processes suitable for overlay welding. This part of ISO 15614 is applicable to all new welding procedures. However, it does not invalidate previous welding procedure tests made to former national standar
32、ds or specifications. Where additional tests are carried out to make the qualification technically equivalent, they are only done on a test piece made in accordance with this part of ISO 15614. This part of ISO 15614 does not apply to overlay welding where cracks are intentionally produced (e.g. spe
33、cial hardfacing applications). 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references the latest edition of the referenced document (including any amendments) appli
34、es. ISO 3452, Non destructive testing Penetrant inspection General principles ISO 5173, Destructive tests on welds in metallic materials Bend tests ISO 6947, Welds Working positions Definitions of angles of slope and rotation ISO 9015-1, Destructive tests on welds in metallic materials Hardness test
35、ing Part 1: Hardness test on arc welded joints ISO 14174, Welding consumables Fluxes for submerged arc welding Classification ISO 14175, Welding consumables Shielding gases for arc welding and cutting ISO/TR 15608, Welding Guidelines for a metallic materials grouping system SANS 15614-7:2008This s t
36、andard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-7:2007(E) 2 ISO 2007 All rights reservedISO 15609-1, Specification and qualification of welding procedures for metallic materials Welding procedure specification Part 1: Arc welding ISO 15609-
37、2, Specification and qualification of welding procedures for metallic materials Welding procedure specification Part 2: Gas welding ISO 15609-3, Specification and qualification of welding procedures for metallic materials Welding procedure specification Part 3: Electron beam welding ISO 15609-4, Spe
38、cification and qualification of welding procedures for metallic materials Welding procedure specification Part 4: Laser beam welding ISO 15613, Specification and qualification of welding procedures for metallic materials Qualification based on pre-production welding test ISO 15614-1, Specification a
39、nd qualification of welding procedures for metallic materials Welding procedure test Part 1: Arc and gas welding of steels and arc welding of nickel and nickel alloys ISO 17637, Non-destructive testing of welds Visual testing of fusion-welded joints ISO 17639, Destructive tests on welds in metallic
40、materials Macroscopic and microscopic examination of welds ISO 17640, Non-destructive testing of welds Ultrasonic testing of welded joints ISO/TR 259011), Welding and related processes Vocabulary 3 Terms and definitions For the purposes of this document, the terms and definitions given in ISO/TR 259
41、01 apply. 4 Preliminary welding procedure specification (pWPS) 4.1 Overlay welding The pWPS shall be in accordance with ISO 15609-1, ISO 15609-3 and ISO 15609-4. It shall specify the tolerances for all the relevant parameters. The welding procedure shall be qualified in accordance with Clauses 5 to
42、8. 4.2 Hardfacing The pWPS shall be in accordance with ISO 15609-1, ISO 15609-2, ISO 15609-3 and ISO 15609-4. It shall specify the tolerances for all the relevant parameters. The welding procedure shall be qualified in accordance with Clauses 5 to 8. 1) To be published (revision of CEN/TR 14599). SA
43、NS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-7:2007(E) ISO 2007 All rights reserved 34.3 Building-up The pWPS shall be in accordance with ISO 15609-1. It shall specify the tolerances for all the relevant parameters
44、. The welding procedure shall be qualified in accordance with ISO 15613 or ISO 15614-1 and Clauses 5 to 8. 4.4 Buttering The pWPS shall be in accordance with ISO 15609-1. It shall specify the tolerances for all the relevant parameters. If buttering is used for welding between dissimilar materials, t
45、he welding procedure shall be qualified in accordance with ISO 15614-1. If buttering is used to produce a metallurgically compatible weld metal between the parent material and overlay welding or hardfacing, the welding procedure shall be qualified in accordance with ISO 15614-1 and Clauses 5 to 8. 5
46、 Welding procedure test A test piece shall be welded using the same welding processes as the ones to be used in production (e.g. strip overlay welding + manual metal arc overlay welding with covered electrode). The welding and testing of test pieces shall be in accordance with Clauses 6 and 7. 6 Tes
47、t piece 6.1 Shape and dimensions of test pieces 6.1.1 General The welding procedure test shall be carried out on standardized test piece(s) in accordance with Figures 1 and 2, and 6.2. Parent material(s) shall be used which represent the material(s) to be welded in production. The dimensions and/or
48、number of test pieces shall be sufficient to allow all required tests to be carried out (see Figures 1 and 2). The thickness and/or diameter of the test pieces shall be selected in accordance with the range of qualification. 6.1.2 Overlay welding and hardfacing A minimum of three beads for the last
49、layer is required. 6.1.3 Buffer layer If a buffer layer is used in production welding, it shall be used in welding the test piece. SANS 15614-7:2008This s tandard may only be used and printed by approved subscription and freemailing clients of the SABS .ISO 15614-7:2007(E) 4 ISO 2007 All rights reservedDimensions in millimetres Key 1 buttering layer, if necessary 2 number of layers in accordance with the pWPS (see 6.1.2) or thickness of overlay deposit