SSPC PS 10 01-1982 Hot-Applied Coal Tar Enamel Painting System《热用煤焦油磁漆涂料系统 编辑修订 2004年11月1日》.pdf

1、5-49SSPC-PS 10.01November 1, 1982Editorial Revisions November 1, 2004SSPC: The Society for Protective CoatingsPAINTING SYSTEM NO. 10.01Hot-Applied Coal Tar Enamel Painting System1. Scope1.1 This specifi cation covers a hot-applied coal tar paint-ing system for underground and underwater steel struct

2、ures, consisting of a primer and two hot-applied coats.1.2 This system is suitable for use on parts or structures exposed in Environmental Zones 2C (fresh water immersion), 3B (chemical, neutral), and 3C (chemical, alkaline). It has good abrasion resistance. It is also suitable for underground use.

3、It must be used with discretion for immersion in corrosive chemi-cals since the coating is dissolved by some organic solvents and attacked by oxidizing solutions.1.3 The coal tar enamel must be topcoated with coal tar emulsion when exposed to sunlight to prevent checking and alligatoring.2. Descript

4、ion2.1 This painting system consists of surface preparation by commercial blast cleaning or pickling, one prime coat, and two fi nish coats of hot-applied coal tar enamel per AWWA C 203, “Standard Specifi cations for Coal-Tar Protective Coatings and Linings for Steel Water PipelinesEnamel and TapeHo

5、t Applied.” A fi nal topcoat of coal tar emulsion is to be applied when exposed to sunlight. The AWWA enamel is recommended for potable water.3. Referenced Standards3.1 The latest issue, revision, or amendment of the refer-enced standards in effect on the date of invitation to bid shall govern, unle

6、ss otherwise specifi ed.3.2 If there is a confl ict between the requirements of any of the cited referenced standards and this specifi cation, the requirements of this specifi cation shall prevail.3.3 SSPC STANDARDS AND JOINT STANDARDS:PA 1 Shop, Field, and Maintenance Painting of SteelPA 2 Measurem

7、ent of Dry Coating Thickness With Magnetic GagesPA Guide 4 Guide to Maintenance Re-painting with Oil Base or Alkyd Painting SystemsPaint 32 Coal Tar Emulsion CoatingSP 5/NACE No. 1 White Metal Blast CleaningSP 6/NACE No. 3 Commercial Blast CleaningSP 8 PicklingSP 10/NACE No. 2 Near-White Blast Clean

8、ing3.4 AMERICAN SOCIETY FOR TESTING AND MATERIALS (ASTM) STANDARDS:D 3925 Standard Practice for Sampling Liquid Paints and Related Pigmented Coatings3.5 AMERICAN WATER WORKS ASSOCIATION (AWWA) SPECIFICATION:C 203 Coal-Tar Protective Coatings and Linings for Steel Water PipelinesEnamel and TapeHot-Ap

9、plied3.6 FEDERAL STANDARDS AND SPECIFICATIONS:MIL-C-15203 Coating Compound, Bituminous, Emulsion Type, Coal Tar Base Canceled. See SSPC-Paint 32.4. Surface Preparation4.1 SSPC-SP 6, “Commercial Blast Cleaning,” or SSPC-SP 8, “Pickling.” If specifi ed in the procurement documents, better degrees of c

10、leaning shall be substituted (SSPC-SP 5, “White Metal Blast Cleaning,” or SSPC-SP 10, “Near- White Blast Cleaning”).5. Paints5.1 PRIMER: Primer complying with specifi cation AWWA C 203, “Standard Specifi cations for Coal-Tar Protective Coatings and Linings for Steel Water PipelinesEnamel and TapeHot

11、Applied.”5.2 SECOND COAT: Second coat complying with specifi ca-tion AWWA C 203, “Standard Specifi cations for Coal Tar Protec-tive Coatings and Linings for Steel Water Pipelines Enamel and TapeHot Applied.”5.3 THIRD COAT: The third coat shall be the same coating as the second coat.5-50SSPC-PS 10.0

12、1November 1, 1982Editorial Revisions November 1, 20045.4 FOURTH COAT (when required): All surfaces that are to be exposed to sunlight shall be given a fourth coat consisting of MIL-C-15203, “Coating Compound, Bituminous, Emulsion Type, Coal-Tar Base.” This coat shall be applied no sooner than two we

13、eks after the third coat is applied. MIL-C-15203 has been canceled; see SSPC-Paint 32.6. Paint Application6.1 PAINT APPLICATION: Follow the requirements of SSPC-PA 1, “Shop, Field, and Maintenance Painting of Steel,” and, where applicable, AWWA C 203, “Standard Specifi cations for Coal-Tar Protectiv

14、e Coatings and Linings for Steel Water PipelinesEnamel and TapeHot-Applied.”6.2 TOUCH-UP PAINTING: In accordance with specifi ca-tion SSPC-PA 1, “Shop, Field, and Maintenance Painting of Steel,” and in particular with the section thereof entitled “Field Painting.”6.3 MAINTENANCE PAINTING: For mainte

15、nance painting procedures, see SSPC-PA Guide 4, “Guide to Maintenance Repainting with Oil Base or Alkyd Painting Systems.”6.4 NUMBER OF COATS: Minimum of three.6.5 DRY FILM THICKNESS OF PAINT SYSTEM: Not less than the following as measured in accordance with SSPC-PA 2, “Measurement of Dry Coating Th

16、ickness with Magnetic Gages”: primer 13 to 50 micrometers (0.5-2.0 mils); second coat 760 micrometers (30 mils); fi nish coat 760 micrometers (30 mils); for the three-coat painting system 1575 micrometers (62 mils); fourth coat (when required) 250 micrometers (10 mils); for the four-coat system 1830

17、 micrometers (72 mils).7. Inspection7.1 All work and materials supplied under this specifi ca-tion are subject to timely inspection by the purchaser or his authorized representative. The contractor shall correct such work or replace such material as is found defective under this specifi cation (See

18、Note 9.1.). In case of dispute, unless otherwise specifi ed, the arbitration or settlement procedure established in the procurement documents shall be followed. If no arbitration or settlement procedure is established, then a procedure mutually agreeable to purchaser, material supplier, and contract

19、or shall be used. 7.2 Samples of paints under this painting system may be requested by the purchaser and shall be supplied upon request along with the manufacturers name and identifi cation for the materials. Samples may be requested at the time the purchase order is placed, or may be taken from uno

20、pened containers at the job site.7.3 Unless otherwise specifi ed, the sampling shall be in accordance with ASTM D 3925.8. Disclaimer8.1 While every precaution is taken to ensure that all information furnished in SSPC standards and specifi cations is as accurate, complete, and useful as possible, SSP

21、C cannot assume responsibility nor incur any obligation resulting from the use of any materials, coatings, or methods specifi ed herein, or of the specifi cation or standard itself.8.2 This specifi cation does not attempt to address problems concerning safety associated with its use. The user of thi

22、s specifi cation, as well as the user of all products or practices described herein, is responsible for instituting appropriate health and safety practices and for insuring compliance with all governmental regulations.9. NotesNotes are not a requirement of this specifi cation. 9.1 The procurement do

23、cuments should establish the responsibility for samples, testing, and any required affi davit certifying full compliance with the specifi cation.9.2 If an electrical inspection is required, use a 7,200 volt holiday detector of an approved type.9.3 Hot enamels are applied at temperatures ranging from 220 to 260C (425 to 500F), and extreme care must be used when melting and handling.