SSPC SP 3-2018 Power Tool Cleaning.pdf

1、SSPC-SP 3January 3, 20181SSPC: The Society for Protective CoatingsSURFACE PREPARATION STANDARD NO. 3Power Tool Cleaning1. Scope 1.1 This standard contains the requirements for power tool cleaning to remove loose detrimental foreign matter from steel substrates.1.2 This standard differs from SSPC-SP

2、2 Hand Tool Cleaning, in that SSPC-SP 2 requires use of hand-held tools without supplemental power.1.3 This standard differs from SSPC-SP 15, Commercial Grade Power Tool Cleaning, in that SP 15 uses power tools to remove all visible oil, grease, dirt, rust, coating, metallic oxides, mill scale, corr

3、osion products, and other foreign matter from the surface, with the exception of trace amounts of coating, staining and corrosion in pit bottoms.1.4 Units of Measure: This standard makes use of both the IEEE/ASTM SI 10(1)International System Units (SI) units and U.S. Customary units. The measurement

4、s are not exact equivalents; therefore, each system must be used independently of the other without combining in any way. This standard uses SI units with the U.S. Customary conversions shown in parentheses. 2. Definition2.1 Power tool cleaning is a method of preparing steel surfaces by the use of p

5、ower-assisted hand tools. It does not include the use of laser and heat-induction technologies.2.2 A power tool cleaned surface, when viewed without magnification, shall be free of visible deposits of oil and grease and shall be free of all loose mill scale, loose rust, loose paint, and other loose

6、detrimental foreign matter. It is not intended that adherent mill scale, rust, and paint be removed by this process. Mill scale, rust, and paint are considered adherent if they cannot be removed by lifting with a dull putty knife as described in Section 6.3 (see Notes 8.1 and 8.2). 2.3 DULL PUTTY KN

7、IFE (for use as an inspection tool): A commercially manufactured, straight, flexible metal blade capable of returning to its original shape without permanent distortion after being bent by hand around a 28 to 33-cm (11 to 13-in) diameter mandrel (or pipe or other (1) ASTM International, 100 Barr Har

8、bor Drive, West Conshohocken, PA 19428-2959. For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standards volume information, refer to the standards Document Summary page on the ASTM website. curved surfac

9、e). The blade shall also have the following characteristics: length of approximately 75 to 125 mm (3 to 5 inches); thickness of approximately 760 to 1270 m (30 to 50 mils); and a straight working edge approximately 40 to 75 mm (1.5 to 3 in) in width. The putty knife is acceptable for use if the thic

10、kness at the working edge of the blade is not less than 635 m (25 mils) or 75% of its original thickness, whichever is greater.(2)NOTE: Some commercially manufactured, straight, flexible metal blades are between 500 and 760 m (20 and 30 mils) in thickness. New blade thicknesses between 500 and 760 m

11、 (20 and 30 mils) are permitted, provided the coating being tested is 20 mils or less in thickness, and the thickness of the blade is not worn to less than 20 mils.2.4 Reference photographs of power tool cleaned surfaces found in SSPC-VIS 3 are often used to supplement the written definition. In any

12、 dispute, the written definition set forth in this standard shall take precedence over reference photographs (see Note 8.3).3. Referenced Standards 3.1 The latest issue, revision, or amendment of the referenced standards in effect on the date of publication of this standard shall govern unless other

13、wise specified. Standards marked with an asterisk (*) are not requirements of this standard.3.2 If there is a conflict between the requirements of any of the cited reference standards and this standard, the requirements of this standard shall prevail.3.3 ASTM INTERNATIONAL STANDARDSASTM D4285 Standa

14、rd Test Method for Indicating Oil or Water in Compressed Air 3.4 SSPC STANDARDS AND JOINT STANDARDSSSPC-SP 1 Solvent Cleaning* SSPC-SP 2 Hand Tool Cleaning* SSPC-SP 7/ NACE No. 4Brush-Off Blast Cleaning* SSPC-SP 11 Power Tool Cleaning to Bare Metal* SSPC-SP 15 Commercial Grade Power Tool Cleaning(2)

15、 Exact dimensions of equipment manufactured using S.I. units may vary slightly fro the S.I. values provided. SSPC-SP 3January 3, 20182* SSPC-VIS 3 Guide and Reference Photographs for Steel Surfaces Prepared by Power- and Hand-Tool Cleaning 4. Tools and Methods for Power Tool Cleaning 4.1 POWER TOOLS

16、: Any hand-held motorized tool on which the media described in Sections 4.1.1 and 4.1.2 are capable of being mounted in accordance with manufacturers instructions and which will produce a steel surface meeting the requirements of Sections 2.1 and 2.2 is acceptable (see Notes 8.4, 8.5 and 8.6). Secti

17、ons 4.1.1 and 4.1.2 describe the two main categories of power tools. It is possible for power tools to alter an existing surface profile. 4.1.1 Grinding Tools: Grinding tools use media containing bonded abrasive grains to cut through corroded surfaces and include, but are not limited to, discs or wh

18、eels as described in Note 8.7.1. 4.1.2 Impact Tools: Impact tools use media that repeatedly collide with the target surface and include, but are not limited to, various rotary and reciprocating devices as described in Note 8.7.2. 4.2. The use of several different power tools meeting the requirements

19、 of Section 4.1 is sometimes necessary to achieve power tool cleaned surface meeting the requirements of Sections 2.1 and 2.2 (see Note 8.4 and subsections).5. Procedures Prior to Power Tool Cleaning 5.1 Prior to power tool cleaning, visible deposits of oil, grease, or other materials that interfere

20、 with coating adhesion shall be removed in accordance with SSPC-SP 1 or other methods as specified. 5.2 Surface imperfections such as slivers and laminations, sharp edges, weld spatter, or burning slag shall be removed from the surface to the extent specified by the procurement documents project spe

21、cifications (see Notes 8.8 and 8.9). 5.3 When air-driven tools are used, cleanliness of the compressed air shall be verified in accordance with the procedure described in ASTM D4285.6. Procedures Following Power Tool Cleaning and Immediately Prior to Coating6.1 Visible deposits of oil, grease, or ot

22、her materials that interfere with coating adhesion shall be removed in accordance with SSPC-SP 1 or as specified. 6.2 Dust and loose residues shall be removed from power tool cleaned surfaces by brushing; blowing off with clean, dry air per Section 5.3; vacuum cleaning; or other methods.6.3 When usi

23、ng a dull flexible putty knife to test paint, mill scale, or rust remaining on the surface after cleaning, the straight working edge of the blade shall be held flat against the surface at a maximum of 45 degrees to the surface and pushed with light to moderate pressure so that the end of the blade r

24、emains in flat contact with the surface. The corners of the blade shall not be used to dig at the residues. A putty knife shall not be used as an inspection tool if the working edge of the blade is nicked or gouged, or if dry paint or other material is present along the working edge that would preve

25、nt the blade from making intimate contact with the surface.6.4 After power tool cleaning, any remaining surface imperfections (e.g., laminations, sharp edges, weld spatter, burning slag, scabs, slivers) shall be removed to the extent required by the procurement documents (project specification) (see

26、 Note 8.9).6.5 Immediately prior to coating application, the entire surface to be coated shall comply with the requirements of Section 2.2 (see Note 8.10).7. Disclaimer7.1 While every precaution is taken to ensure that all information furnished in SSPC standards and specifications is as accurate, co

27、mplete, and as useful as possible, SSPC cannot assume responsibility nor incur any obligation resulting from the use of any materials, coatings, or methods specified herein, or of the specification or standard itself.7.2 This standard does not attempt to address problems concerning safety associated

28、 with its use. The user of this standard, as well as the user of all products or practices described herein, is responsible for instituting appropriate health and safety practices and for ensuring compliance with all applicable governmental regulations.8. NotesNotes are not requirements of this stan

29、dard.8.1 FUNCTION: The type of power tool surface preparation described in this standard removes loosely adherent foreign matter. This standard is suitable where removal of loosely adherent foreign matter is required, but where the effort to remove all tightly adherent rust, mill scale, old coatings

30、, and other tightly adherent foreign matter is not necessary. The surfaces prepared according to this standard should not be compared to surfaces cleaned by brush-off abrasive blast cleaning. Although this method produces surfaces that resemble SSPC-SP 7 (brush-off blast cleaned surfaces), they are

31、not necessarily equivalent SSPC-SP 3January 3, 20183to those surfaces produced by abrasive blast cleaning. The contracting parties should agree on the appropriateness of the finished surface to accept the specified coating system. Selection of power tools and cleaning media should be based on (1) th

32、e condition of the surface prior to surface preparation; (2) the extent of cleaning that is required.The SSPC Surface Preparation Commentary (SSPC-SP COM) provides additional information on subjects related to power tool cleaning. The recommendations contained in SSPC-SP COM are believed to represen

33、t good practice, but are not to be considered requirements of this standard.8.2 STRATIFIED RUST, PACK RUST AND RUST SCALE: As noted in Section 4.3.1 of SSPC-COM, Surface Preparation Commentary for Steel and Concrete Substrates, stratified rust, pack rust or rust scale can adhere so tightly to the ba

34、se metal that a power wire brush will not remove it. Even though it is considered “tightly adherent” because it cannot be lifted with a dull flexible putty knife, it provides a very poor surface to paint over. Specifiers should consider providing additional instructions in the project specification

35、regarding the acceptable methods for, and the acceptable level of, removal of these types of rust.8.3 VISUAL GUIDES AND COMPARATORS: Note that the use of visual guides or comparators in conjunction with this standard is required only when they are specified in the procurement documents (project spec

36、ification) covering the work. It is recommended, however, that the use of visual guides or comparators be made mandatory in the procurement documents. SSPC-VIS 3 provides a suitable comparative visual guide for SSPC-SP 2, SSPC-SP 3, SSPC-SP 11, and SSPC-SP 15. However, visual comparators for blast-c

37、leaned steel (e.g., SSPC-VIS 1) are not suitable for assessing power tool cleaned surfaces. Because power tool cleaning is time- and labor-intensive, it is advisable to prepare a test area of 1 x 1 m (3 x 3 ft) for large areas or 30 x 30 cm (12 x 12 in) for spot cleaning to an acceptable level agree

38、d upon by the contracting parties. A 30 x 30 cm (12 x 12 in) steel test plate can also be power tool cleaned to an acceptable level and photographed or retained to serve as a project standard. 8.4 SELECTION OF TOOLS AND MEDIA 8.4.1 Selection of Tools: Power tools should be selected on the basis of t

39、he size and speed rating of the media. These requirements may differ from one type of medium to another and should be taken into consideration if more than one type of medium will be used in the surface preparation process. Power tools should be selected that will produce enough power to perform the

40、 cleaning operation efficiently. Operator fatigue should be considered in the selection of power tools.8.4.2 Selection of Media: When power tool cleaning rusted surfaces, it is important to avoid embedding rust into the substrate. These factors may require employing more than one type of medium in o

41、rder to obtain the desired end result. Power wire brushes or sanding discs when used alone may remove or degrade an existing profile to an unacceptable level. After removal of excessive corrosion, a structural inspection may be warranted to ascertain if the metal thickness remains in compliance with

42、 the governing requirements, including applicable codes (e.g. ASME codes for pressure vessels). 8.5 CAUTION: Improper use of power tools can result in damage to the surface being cleaned. Excessive pressure or an overly long dwell time on a surface being cleaned using impact tools can result in form

43、ation of burrs and gouges. Rotary or grinding tools that remain over a specific location too long can bend the peaks of an existing profile and damage the anchor pattern. In extreme cases, burnishing of the surface may result. Improper use of tools with embedded abrasive media, including, but not li

44、mited to discs, wheels, pads, and flappers, may result in partial melting and smearing of the matrix on the surface. A review of the manufacturers literature or a discussion with the technical representative about the tool, its use and the intended substrate should be undertaken if in doubt or if th

45、e operator has little or no experience with the tool.8.6 CLEANING LIMITED ACCESS AREAS: SSPC defines a “limited access area” as a location in which the configuration of a structure or surface or the characteristics of a tool restrict the use or performance of that tool at that location. Alternative

46、methods should be considered for limited access areas. 8.7 SUITABLE TOOLS AND MEDIA: The tools/media in the text of this standard are intended solely to guide the user to typical types of equipment and media that are available to meet the specification. The tools/media cited in this document do not

47、include all of the tools, devices, or products available, nor does their mention constitute an endorsement by SSPC. The presence of hazardous material in the coatings, cleaning media, or in the work area itself, can place restrictions on the methods of cleaning permitted.8.7.1 Grinding tools/media:

48、Any rotary or reciprocating tool that uses bonded abrasives as the cutting media for generating surfaces described in Section 2. These include, but are not limited to, wire brushes, reciprocating sanders, orbital sanders, or any grinding device, whether right angle or straight shaft, that utilizes a

49、brasive cloths, discs, wheels, or flaps. 8.7.2 Impact tools/media: Any rotary or reciprocating tool that uses repetitious impact for generating surfaces described in Section 2. This includes, but is not limited to: rotary flap, cutter bundle, needle gun, bristle impact, and hammer flail assemblies.SSPC-SP 3January 3, 201848.8 MAINTENANCE AND REPAIR PAINTING: When this standard is used in maintenance painting, specific instructions should be given on the extent of surface to be power tool cleaned, including any additional requirements for retaining old paint, removing unsound paint, f