UL 972-2006 UL Standard for Safety Burglary Resisting Glazing Material (Sixth Edition Reprint with Revisions Through and Including December 23 2015)《防盗窗用玻璃材料》.pdf

1、UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL UL 972 Burglary Resisting Glazing MaterialUL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM ULUL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FU

2、RTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL UL Standard for Safety for Burglary Resisting Glazing Material, UL 972 Sixth Edition, Dated November 27, 2006 Summary of Topics This revision to ANSI/UL 972 is being issued to reect the reaffirmation of the ANSI approval of the Standard.

3、No technical changes have been made to the document. The revisions are substantially in accordance with Proposal(s) on this subject dated September 25, 2015. Text that has been changed in any manner or impacted by ULs electronic publishing system is marked with a vertical line in the margin. All rig

4、hts reserved. No part of this publication may be reproduced, stored in a retrieval system, or transmitted in any form by any means, electronic, mechanical photocopying, recording, or otherwise without prior permission of UL. UL provides this Standard as is without warranty of any kind, either expres

5、sed or implied, including but not limited to, the implied warranties of merchantability or tness for any purpose. In no event will UL be liable for any special, incidental, consequential, indirect or similar damages, including loss of prots, lost savings, loss of data, or any other damages arising o

6、ut of the use of or the inability to use this Standard, even if UL or an authorized UL representative has been advised of the possibility of such damage. In no event shall ULs liability for any damage ever exceed the price paid for this Standard, regardless of the form of the claim. Users of the ele

7、ctronic versions of ULs Standards for Safety agree to defend, indemnify, and hold UL harmless from and against any loss, expense, liability, damage, claim, or judgment (including reasonable attorneys fees) resulting from any error or deviation introduced while purchaser is storing an electronic Stan

8、dard on the purchasers computer system. DECEMBER 23, 2015 UL 972 tr1UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL DECEMBER 23, 2015 UL 972 tr2 No Text on This PageUL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUT

9、ION WITHOUT PERMISSION FROM UL NOVEMBER 27, 2006 (Title Page Reprinted: December 23, 2015) 1 UL 972 Standard for Burglary Resisting Glazing Material First Edition June, 1972 Second Edition March, 1978 Third Edition June, 1984 Fourth Edition March, 1995 Fifth Edition December, 2002 Sixth Edition Nove

10、mber 27, 2006 This ANSI/UL Standard for Safety consists of the Sixth Edition including revisions through December 23, 2015. The most recent designation of ANSI/UL 972 as a Reaffirmed American National Standard (ANS) occurred on December 23, 2015. ANSI approval for a standard does not include the Cov

11、er Page, Transmittal Pages, Title Page, or effective date information. Comments or proposals for revisions on any part of the Standard may be submitted to UL at any time. Proposals should be submitted via a Proposal Request in ULs On-Line Collaborative Standards Development System (CSDS) at http:/.

12、ULs Standards for Safety are copyrighted by UL. Neither a printed nor electronic copy of a Standard should be altered in any way. All of ULs Standards and all copyrights, ownerships, and rights regarding those Standards shall remain the sole and exclusive property of UL. COPYRIGHT 2015 UNDERWRITERS

13、LABORATORIES INC. ANSI/UL 972-2006 (R2015)UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL NOVEMBER 27, 2006 BURGLARY RESISTING GLAZING MATERIAL - UL 972 2 No Text on This PageUL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR

14、 DISTRIBUTION WITHOUT PERMISSION FROM UL CONTENTS INTRODUCTION 1 Scope .4 2 Units of Measurement .4 CONSTRUCTION 3 General 4 PERFORMANCE 4 General 4 5 Sample Conditioning 4 5.1 General 4 5.2 Thermal conditioning tests for outdoor use .4 5.3 Thermal conditioning tests for indoor use 4 6 Impact Tests

15、.5 6.1 General 5 6.2 Ball impact test .6 6.3 Outdoor use impact test .6 6.4 Indoor use impact test 6 6.5 High-energy impact test .6 MARKINGS 7 General 6 NOVEMBER 27, 2006 BURGLARY RESISTING GLAZING MATERIAL - UL 972 3UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WIT

16、HOUT PERMISSION FROM UL INTRODUCTION 1 Scope 1.1 These requirements cover clear, translucent, or opaque glazing material intended for indoor and outdoor use principally as a substitute for plate glass show windows or show case panels. 1.2 The material is intended to resist burglarious attacks of the

17、 hit and run type. 1.3 These requirements do not cover the glazing (mounting) methods used for the installation of burglary resisting glazing material. 2 Units of Measurement 2.1 Values stated without parentheses are the requirement. Values in parentheses are explanatory or approximate information.

18、CONSTRUCTION 3 General 3.1 There shall be no defects or visible imperfections in the nished product that may impair its serviceability. PERFORMANCE 4 General 4.1 Representative samples of each construction of glazing material are to be subjected to the following tests. 4.2 Samples of each constructi

19、on, each measuring 24 by 24 inches (610 by 610 mm), are to be used. 5 Sample Conditioning 5.1 General 5.1.1 For the thermal conditioning procedures, all samples are to be conditioned at the specied temperatures for at least 4 hours prior to the applicable impact test. 5.2 Thermal conditioning tests

20、for outdoor use 5.2.1 Three samples of the material are to be conditioned at a temperature of 120F (49C). 5.2.2 Three additional samples are to be conditioned at a temperature of 14F (minus 10C). 5.3 Thermal conditioning tests for indoor use 5.3.1 Three samples of the material are to be conditioned

21、at a temperature of 95F (35C). NOVEMBER 27, 2006 BURGLARY RESISTING GLAZING MATERIAL - UL 972 4UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL 5.3.2 Three additional samples are to be conditioned at a temperature of 55F (13C). 6 Impact Tests

22、 6.1 General 6.1.1 Where thermal conditioning procedures are specied, samples are to be tested immediately upon removal from the thermal conditioning chamber. The samples of the glazing material are to be mounted horizontally in a frame so as to provide uniform clamping on all four edges of the mate

23、rial and an unsupported area of 22 by 22 inches (560 by 560 mm). See 6.1.2. 6.1.2 The frame is to be constructed of 2-inch (51-mm) steel angles, at least 1/4 inch (6.4 mm) thick, welded at all four corners to form a rigid square. The square is to be supported by steel members, at least 8 inches (205

24、 mm) high, at each of the four corners. The entire assembly is to be mounted on a solid wood platform formed of 3/4-inch (19.1-mm) plywood. The four clamping members are to be of the same angle steel as used in the frame. 6.1.3 The part of the frame and clamping members that come in contact with the

25、 test sample are to be lined with hardwood stripping. The wood, in turn, is to be covered with rubber or felt stripping approximately 1/8 inch (3.2 mm) thick. At least two clamps are to be used on each of the four sides to secure the test sample between the frame and the clamping members. 6.1.4 The

26、impacts are to be conducted using a 3-1/4 inch (83 mm) diameter smooth hardened-steel ball weighing 5 lbs (2.3 kg). 6.1.5 During the Ball impact test, Section 6.2; Outdoor use impact test, Section 6.3; and the Indoor use impact test, Section 6.4, the steel ball is to be released so as to strike each

27、 sample successively at ve different locations within a 5-inch (127-mm) diameter circle, the center of which is to be located at the approximate center of the sample. 6.1.6 Except for retrieving the steel ball, or resecuring the clamps, the test sample is not to be disturbed until the specied number

28、 of impacts have been conducted. 6.1.7 During the Ball impact test, Section 6.2; Outdoor use impact test, Section 6.3; and the Indoor use impact test, Section 6.4, if the steel ball falls outside of the 5-inch (127-mm) diameter circle or if the test sample is damaged in handling, the results are to

29、be considered inconclusive and the test(s) is to be repeated using a reserve sample. 6.1.8 The steel ball shall not penetrate the glazing material: a) On any one of the ve impacts on three samples tested as specied in Sections 6.2, 6.3, and 6.4, or b) On any of the single impacts on the three sample

30、s tested during the High-energy impact test, Section 6.5. Penetration is considered to occur if the ball passes completely through the glazing material. NOVEMBER 27, 2006 BURGLARY RESISTING GLAZING MATERIAL - UL 972 5UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WIT

31、HOUT PERMISSION FROM UL 6.1.9 If one of the three samples tested in 6.1.8(a) should fail, three additional samples shall be tested. If the three additional samples pass, the results are acceptable. If one of the three additional samples should fail, results are not acceptable. 6.1.10 If two of the t

32、hree samples tested in 6.1.8(a) should fail, the results are not acceptable. 6.2 Ball impact test 6.2.1 The glazing material shall withstand ve 50-foot-pound (68-J) impacts, as produced by dropping the steel ball specied in 6.1.4 through a vertical distance of 10 feet (3 m). 6.2.2 The test is to be

33、conducted on three samples of the glazing material maintained at room temperature, 70 80F (21 27C). 6.3 Outdoor use impact test 6.3.1 After thermal conditioning as specied in 5.2.1 and 5.2.2, each of the samples shall withstand ve 40-foot-pound (54-J) impacts, as produced by dropping the steel ball

34、described in 6.1.4 through a vertical distance of 8 feet (2.4 m) as described in 6.1.5. 6.4 Indoor use impact test 6.4.1 After thermal conditioning as specied in 5.3.1 and 5.3.2, each of the samples shall withstand ve 50-foot-pound (68-J) impacts, as produced by dropping the steel ball described in

35、6.1.4 through a vertical distance of 10 feet (3 m) as described in 6.1.5. 6.5 High-energy impact test 6.5.1 The glazing material shall withstand one 200-foot-pound (270-J) impact, as produced by dropping the steel ball described in 6.1.4 through a vertical distance of 40 feet (12.1 m). 6.5.2 The tes

36、t is to be conducted on three samples of the glazing material maintained at room temperature, 70 80F (21 27C). MARKINGS 7 General 7.1 The nished glazing material panel shall be plainly marked with the manufacturers or private labelers identication or a distinctive catalog number or the equivalent by

37、 which the product may be readily identied. 7.2 The marking may be located on the protective covering or package of the glazing material panel(s) as shipped from the factory. 7.3 If a manufacturer produces glazing material at more than one factory, each nished glazing material panel shall have a dis

38、tinctive marking to identify it as the product of a particular factory. NOVEMBER 27, 2006 BURGLARY RESISTING GLAZING MATERIAL - UL 972 6UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL 7.4 Burglary resisting glazing material intended for indo

39、or use only, shall be marked to indicate that condition of use. 7.4 effective November 27, 2008 7.5 Burglary resisting glazing material shall be marked with the date of manufacture. The date marking shall include the week, month, or quarter, and the year, any of which may be abbreviated or in an est

40、ablished or otherwise traceable code. A date code marking shall not repeat in less than 20 years. 7.5 effective November 27, 2008 NOVEMBER 27, 2006 BURGLARY RESISTING GLAZING MATERIAL - UL 972 7UL COPYRIGHTED MATERIAL NOT AUTHORIZED FOR FURTHER REPRODUCTION OR DISTRIBUTION WITHOUT PERMISSION FROM UL NOVEMBER 27, 2006 BURGLARY RESISTING GLAZING MATERIAL - UL 972 8 No Text on This Page