VA 09 91 00-2012 PAINTING.pdf

1、06-01-12 09 91 00 - 1 SECTION 09 91 00 PAINTING MODIFICATION 06-01-12 UPDATE OF STANDARDS Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-06-01-12 09 91 00 - 2 SECTION 09 91 00 PAINTING SPEC WRITER NOTE: Delete between / _/ if not applicable to proje

2、ct. Delete, modify and add to text as required to suit information shown on the drawings and specified in Section 09 06 00, SCHEDULE FOR FINISHES. PART 1-GENERAL 1.1 DESCRIPTION A. Section specifies field painting. B. Section specifies prime coats which may be applied in shop under other sections. C

3、. Painting includes shellacs, stains, varnishes, coatings specified, and striping or markers and identity markings. 1.2 RELATED WORK A. Shop prime painting of steel and ferrous metals: Division 05 - METALS, Division 08 - OPENINGS, Division 10 - SPECIALTIES, Division 11 - EQUIPMENT, Division 12 - FUR

4、NISHINGS, Division 13 SPECIAL CONSTRUCTION, Division 14 CONVEYING EQUIPMENT, Division 21 FIRE SUPPRESSION, Division 22 - PLUMBING, Division 23 HEATING, VENTILATION AND AIR-CONDITIONING, Division 26 - ELECTRICAL, Division 27 - COMMUNICATIONS, and Division 28 ELECTRONIC SAFETY AND SECURITY sections. B

5、. Contractor option: Prefinished flush doors with transparent finishes: Section 08 14 00, WOOD DOORS. C. Type of Finish, Color, and Gloss Level of Finish Coat: Section 09 06 00, SCHEDULE FOR FINISHES. D. Glazed wall surfacing or tile like coatings: Section 09 96 59, HIGH-BUILD GLAZED COATINGS. E. Mu

6、lti-color Textured Wall Finish: Section 09 94 19, MULTICOLOR INTERIOR FINISHING. F. Asphalt and concrete pavement marking: Section 32 17 23, PAVEMENT MARKINGS. 1.3 SUBMITTALS A. Submit in accordance with Section 01 33 23, SHOP DRAWINGS, PRODUCT DATA, AND SAMPLES. B. Manufacturers Literature and Data

7、: Before work is started, or sample panels are prepared, submit manufacturers literature, the current Master Painters Institute (MPI) “Approved Product List“ indicating brand label, product name and product code as of the date of contract award, will be used to determine compliance with the submitta

8、l requirements of this specification. The Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-06-01-12 09 91 00 - 3 Contractor may choose to use subsequent MPI “Approved Product List“, however, only one list may be used for the entire contract and each c

9、oating system is to be from a single manufacturer. All coats on a particular substrate must be from a single manufacturer. No variation from the MPI “Approved Product List“ where applicable is acceptable. C. Sample Panels: 1. After painters materials have been approved and before work is started sub

10、mit sample panels showing each type of finish and color specified. 2. Panels to show color: Composition board, 100 by 250 by 3 mm (4 inch by 10 inch by 1/8 inch). 3. Panel to show transparent finishes: Wood of same species and grain pattern as wood approved for use, 100 by 250 by 3 mm (4 inch by 10

11、inch face by 1/4 inch) thick minimum, and where both flat and edge grain will be exposed, 250 mm (10 inches) long by sufficient size, 50 by 50 mm (2 by 2 inch) minimum or actual wood member to show complete finish. 4. Attach labels to panel stating the following: a. Federal Specification Number or m

12、anufacturers name and product number of paints used. b. Specification code number specified in Section 09 06 00, SCHEDULE FOR FINISHES. c. Product type and color. d. Name of project. 5. Strips showing not less than 50 mm (2 inch) wide strips of undercoats and 100 mm (4 inch) wide strip of finish coa

13、t. D. Sample of identity markers if used. E. Manufacturers Certificates indicating compliance with specified requirements: 1. Manufacturers paint substituted for Federal Specification paints meets or exceeds performance of paint specified. 2. High temperature aluminum paint. 3. Epoxy coating. 4. Int

14、umescent clear coating or fire retardant paint. 5. Plastic floor coating. 1.4 DELIVERY AND STORAGE A. Deliver materials to site in manufacturers sealed container marked to show following: 1. Name of manufacturer. 2. Product type. 3. Batch number. 4. Instructions for use. 5. Safety precautions. Provi

15、ded by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-06-01-12 09 91 00 - 4 B. In addition to manufacturers label, provide a label legibly printed as following: 1. Federal Specification Number, where applicable, and name of material. 2. Surface upon which mater

16、ial is to be applied. 3. If paint or other coating, state coat types; prime, body or finish. C. Maintain space for storage, and handling of painting materials and equipment in a neat and orderly condition to prevent spontaneous combustion from occurring or igniting adjacent items. D. Store materials

17、 at site at least 24 hours before using, at a temperature between 18 and 30 degrees C (65 and 85 degrees F). 1.5 MOCK-UP PANEL SPEC WRITER NOTE: Define spaces and other finishes where sample panel is required. A. Before starting application of water paint mixtures, / cementitious paint / _ /, apply

18、paint as specified to an area, not to exceed 9 m2 (100 ft2), selected by Resident Engineer. B. Finish and texture approved by Resident Engineer will be used as a standard of quality for remainder of work. 1.6 APPLICABLE PUBLICATIONS A. Publications listed below form a part of this specification to t

19、he extent referenced. Publications are referenced in the text by basic designation only. B. American Conference of Governmental Industrial Hygienists (ACGIH): ACGIH TLV-BKLT-2012 Threshold Limit Values (TLV) for Chemical Substances and Physical Agents and Biological Exposure Indices (BEIs) ACGIH TLV

20、-DOC-2012 . Documentation of Threshold Limit Values and Biological Exposure Indices, (Seventh Edition) C. American National Standards Institute (ANSI): A13.1-07 . Scheme for the Identification of Piping Systems D. American Society for Testing and Materials (ASTM): D260-86Boiled Linseed Oil E. Commer

21、cial Item Description (CID): A-A-1555 . Water Paint, Powder (Cementitious, White and Colors) (WPC) (cancelled) A-A-3120 . Paint, For Swimming Pools (RF) (cancelled) F. Federal Specifications (Fed Spec): TT-P-1411A . Paint, Copolymer-Resin, Cementitious (For Waterproofing Concrete and Masonry Walls)

22、(CEP) G. Master Painters Institute (MPI): No. 1-12 . Aluminum Paint (AP) Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-06-01-12 09 91 00 - 5 No. 4-12 . Interior/ Exterior Latex Block Filler No. 5-12 . Exterior Alkyd Wood Primer No. 7-12 . Exterior

23、Oil Wood Primer No. 8-12 . Exterior Alkyd, Flat MPI Gloss Level 1 (EO) No. 9-12 . Exterior Alkyd Enamel MPI Gloss Level 6 (EO) No. 10-12 Exterior Latex, Flat (AE) No. 11-12 Exterior Latex, Semi-Gloss (AE) No. 18-12 Organic Zinc Rich Primer No. 22-12 Aluminum Paint, High Heat (up to 590% - 1100F) (HR

24、) No. 26-12 Cementitious Galvanized Metal Primer No. 27-12 Exterior / Interior Alkyd Floor Enamel, Gloss (FE) No. 31-12 Polyurethane, Moisture Cured, Clear Gloss (PV) No. 36-12 Knot Sealer No. 43-12 Interior Satin Latex, MPI Gloss Level 4 No. 44-12 Interior Low Sheen Latex, MPI Gloss Level 2 No. 45-

25、12 Interior Primer Sealer No. 46-12 Interior Enamel Undercoat No. 47-12 Interior Alkyd, Semi-Gloss, MPI Gloss Level 5 (AK) No. 48-12 Interior Alkyd, Gloss, MPI Gloss Level 6 (AK) No. 49-12 Interior Alkyd, Flat, MPI Gloss Level 1 (AK) No. 50-12 Interior Latex Primer Sealer No. 51-12 Interior Alkyd, E

26、ggshell, MPI Gloss Level 3 No. 52-12 Interior Latex, MPI Gloss Level 3 (LE) No. 53-12 Interior Latex, Flat, MPI Gloss Level 1 (LE) No. 54-12 Interior Latex, Semi-Gloss, MPI Gloss Level 5 (LE) No. 59-12 Interior/Exterior Alkyd Porch mechanical and electrical sections of the specifications for proper

27、surface condition and compatible prime coats to suit finishes specified. For Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-06-01-12 09 91 00 - 10 instance, finish on concrete required to have cementitious coating; type of shop coat on bar joists re

28、quired to be painted; will any parts of mechanical equipment have to be field painted; what kind of primers are specified, if any. 3.2 SURFACE PREPARATION A. Method of surface preparation is optional, provided results of finish painting produce solid even color and texture specified with no overlays

29、. B. General: 1. Remove prefinished items not to be painted such as lighting fixtures, escutcheon plates, hardware, trim, and similar items for reinstallation after paint is dried. 2. Remove items for reinstallation and complete painting of such items and adjacent areas when item or adjacent surface

30、 is not accessible or finish is different. 3. See other sections of specifications for specified surface conditions and prime coat. 4. Clean surfaces for painting with materials and methods compatible with substrate and specified finish. Remove any residue remaining from cleaning agents used. Do not

31、 use solvents, acid, or steam on concrete and masonry. C. Wood: 1. Sand to a smooth even surface and then dust off. 2. Sand surfaces showing raised grain smooth between each coat. 3. Wipe surface with a tack rag prior to applying finish. 4. Surface painted with an opaque finish: a. Coat knots, sap a

32、nd pitch streaks with MPI 36 (Knot Sealer) before applying paint. b. Apply two coats of MPI 36 (Knot Sealer) over large knots. 5. After application of prime or first coat of stain, fill cracks, nail and screw holes, depressions and similar defects with wood filler paste. Sand the surface to make smo

33、oth and finish flush with adjacent surface. 6. Before applying finish coat, reapply wood filler paste if required, and sand surface to remove surface blemishes. Finish flush with adjacent surfaces. 7. Fill open grained wood such as oak, walnut, ash and mahogany with MPI 91 (Wood Filler Paste), color

34、ed to match wood color. a. Thin filler in accordance with manufacturers instructions for application. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-06-01-12 09 91 00 - 11 b. Remove excess filler, wipe as clean as possible, dry, and sand as specifie

35、d. D. Ferrous Metals: 1. Remove oil, grease, soil, drawing and cutting compounds, flux and other detrimental foreign matter in accordance with SSPC-SP 1 (Solvent Cleaning). 2. Remove loose mill scale, rust, and paint, by hand or power tool cleaning, as defined in SSPC-SP 2 (Hand Tool Cleaning) and S

36、SPC-SP 3 (Power Tool Cleaning). Exception: where high temperature aluminum paint is used, prepare surface in accordance with paint manufacturers instructions. 3. Fill dents, holes and similar voids and depressions in flat exposed surfaces of hollow steel doors and frames, access panels, roll-up stee

37、l doors and similar items specified to have semi-gloss or gloss finish with TT-F-322D (Filler, Two-Component Type, For Dents, Small Holes and Blow-Holes). Finish flush with adjacent surfaces. a. This includes flat head countersunk screws used for permanent anchors. b. Do not fill screws of item inte

38、nded for removal such as glazing beads. 4. Spot prime abraded and damaged areas in shop prime coat which expose bare metal with same type of paint used for prime coat. Feather edge of spot prime to produce smooth finish coat. 5. Spot prime abraded and damaged areas which expose bare metal of factory

39、 finished items with paint as recommended by manufacturer of item. E. / Zinc-Coated (Galvanized) Metal, / Aluminum, / Copper and Copper Alloys / Surfaces Specified Painted: 1. Clean surfaces to remove grease, oil and other deterrents to paint adhesion in accordance with SSPC-SP 1 (Solvent Cleaning).

40、 2. Spot coat abraded and damaged areas of zinc-coating which expose base metal on hot-dip zinc-coated items with MPI 18 (Organic Zinc Rich Coating). Prime or spot prime with MPI 134 (Waterborne Galvanized Primer) or MPI 135 (Non- Cementitious Galvanized Primer) depending on finish coat compatibilit

41、y. F. Masonry, Concrete, Cement Board, Cement Plaster and Stucco: 1. Clean and remove dust, dirt, oil, grease efflorescence, form release agents, laitance, and other deterrents to paint adhesion. 2. Use emulsion type cleaning agents to remove oil, grease, paint and similar products. Use of solvents,

42、 acid, or steam is not permitted. 3. Remove loose mortar in masonry work. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-06-01-12 09 91 00 - 12 4. Replace mortar and fill open joints, holes, cracks and depressions with new mortar specified in Sectio

43、n 04 05 13, MASONRY MORTARING / Section 04 05 16, MASONRY GROUTING/. Do not fill weep holes. Finish to match adjacent surfaces. 5. Neutralize Concrete floors to be painted by washing with a solution of 1.4 Kg (3 pounds) of zinc sulfate crystals to 3.8 L (1 gallon) of water, allow to dry three days a

44、nd brush thoroughly free of crystals. 6. Repair broken and spalled concrete edges with concrete patching compound to match adjacent surfaces as specified in CONCRETE Sections. Remove projections to level of adjacent surface by grinding or similar methods. G. Gypsum Plaster and Gypsum Board: 1. Remov

45、e efflorescence, loose and chalking plaster or finishing materials. 2. Remove dust, dirt, and other deterrents to paint adhesion. 3. Fill holes, cracks, and other depressions with CID-A-A-1272A Plaster, Gypsum (Spackling Compound) finished flush with adjacent surface, with texture to match texture o

46、f adjacent surface. Patch holes over 25 mm (1-inch) in diameter as specified in Section for plaster or gypsum board. 3.3 PAINT PREPARATION A. Thoroughly mix painting materials to ensure uniformity of color, complete dispersion of pigment and uniform composition. B. Do not thin unless necessary for a

47、pplication and when finish paint is used for body and prime coats. Use materials and quantities for thinning as specified in manufacturers printed instructions. C. Remove paint skins, then strain paint through commercial paint strainer to remove lumps and other particles. D. Mix two component and tw

48、o part paint and those requiring additives in such a manner as to uniformly blend as specified in manufacturers printed instructions unless specified otherwise. E. For tinting required to produce exact shades specified, use color pigment recommended by the paint manufacturer. 3.4 APPLICATION A. Star

49、t of surface preparation or painting will be construed as acceptance of the surface as satisfactory for the application of materials. B. Unless otherwise specified, apply paint in three coats; prime, body, and finish. When two coats applied to prime coat are the same, first coat applied over primer is body coat and second coat is finish coat. C. Apply e