ISO 6363-4-2012 Wrought aluminium and aluminium alloys - Cold-drawn rods bars tubes and wires - Part 4 Drawn rectangular bars and wires - Tolerances on form and.pdf

1、 ISO 2012 Wrought aluminium and aluminium alloys Cold-drawn rods/bars, tubes and wires Part 4: Drawn rectangular bars and wires Tolerances on form and dimensions Aluminium et alliages daluminium corroys Barres, tubes et fils tirs froid Partie 4: Barres rectangulaires et fils tirs Tolrances sur forme

2、 et dimensions INTERNATIONAL STANDARD ISO 6363-4 Second edition 2012-07-15 Reference number ISO 6363-4:2012(E) ISO 6363-4:2012(E) ii ISO 2012 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2012 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or ut

3、ilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fa

4、x + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ISO 6363-4:2012(E) ISO 2012 All rights reserved iii Contents Page Foreword iv 1 Scope 1 2 Normative references . 1 3 T erms and definitions . 1 4 Materials . 1 5 Tolerances on form and dimensions 2 5.1 Tolerances on

5、 width and thickness 2 5.2 Fixed-length tolerances . 3 5.3 Squareness of cut ends . 3 5.4 Corner radii . 3 5.5 Form tolerances . 4 Bibliography . 7 ISO 6363-4:2012(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member

6、bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental

7、and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directive

8、s, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies c

9、asting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 6363-4 was prepared by Technical Committee ISO/TC 79, Light metals and their alloy

10、s, Subcommittee SC 6, Wrought aluminium and aluminium alloys. This second edition cancels and replaces the first edition (ISO 6363-4:1991), which has been technically revised. ISO 6363 consists of the following parts, under the general title Wrought aluminium and aluminium alloys Cold-drawn rods/bar

11、s, tubes and wires: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Drawn round bars and wires Tolerances on form and dimensions (symmetric plus and minus tolerances on diameter) Part 4: Drawn rectangular bars and wires Tolerances on form and dimensions

12、 Part 5: Drawn square and hexagonal bars and wires Tolerances on form and dimensions Part 6: Drawn round tubes Tolerances on form and dimensions iv ISO 2012 All rights reserved INTERNATIONAL STANDARD ISO 6363-4:2012(E) Wrought aluminium and aluminium alloys Cold-drawn rods/ bars, tubes and wires Par

13、t 4: Drawn rectangular bars and wires Tolerances on form and dimensions 1 Scope This part of ISO 6363 specifies the tolerances on form and dimensions of wrought aluminium and aluminium alloy drawn rectangular bars and wires with thicknesses ranging from 2 mm up to and including 60 mm and widths up t

14、o and including 200 mm. For wires, this part of ISO 6363 does not apply to electrical, welding and aeronautical purposes. For drawn bars, 5.1 to 5.4 apply, and only 5.1 applies to drawn wires. 2 Normative references The following referenced documents are indispensable for the application of this doc

15、ument. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 6363-1, Wrought aluminium and aluminium alloys Cold-drawn rods/bars, tubes and wires Part 1: Technical conditions for inspection

16、and delivery 3 T erms and definitio ns For the purposes of this document, the terms and definitions given in ISO 6363-1 apply. 4 Materials For the purposes of this part of ISO 6363, wrought aluminium and aluminium alloys are divided into two groups, which correspond to varying difficulty whenever ma

17、nufacturing the products. The division into group I and group II of the most commonly used general engineering alloys is specified in Table 1. The division into group I and group II of the most commonly used general engineering alloys is specified in Table 1. Grouping of other alloys is subject to a

18、greement between the purchaser and supplier. ISO 2012 All rights reserved 1 ISO 6363-4:2012(E) Table 1 Alloy group Group I 1050, 1050A, 1070, 1100, 1200, 1350 3003, 3102, 3103, 3203 5005, 5005A, 5050, 5051, 5051A 6005, 6005A, 6005C, 6008, 6012, 6014, 6018, 6056, 6060, 6061, 6063, 6063A, 6065, 6081,

19、6082, 6101, 6101A, 6101B, 6110A, 6181, 6261, 6262, 6262A, 6351, 6360, 6463 Group II 2007, 2011, 2011A, 2014, 2014A, 2017, 2017A, 2024, 2030, 2219 5019, 5041, 5049, 5052, 5056, 5083, 5086, 5154, 5154A, 5251, 5454, 5754 7003, 7005, 7020, 7021, 7022, 7049A, 7050, 7075, 7108, 7108A, 7204 NOTE The four-d

20、igit numbers listed in this table are taken from the Registration of International Alloy Designations and Chemical Composition Limits for Wrought Aluminium Alloys (also known as “Teal sheets”) 1 . 5 Tolerances on form and dimensions 5.1 Tolerances on width and thickness The tolerances on width and t

21、hickness shall be in accordance with Tables 2 and 3. The dimensions shall be measured without influence from the corner radii. Table 2 Tolerances on width and thickness for alloy group I Dimensions in millimetres Width ab Thickness a tolerances for thickness ranges a Range Toler- ances 2 a 6 6 10, t

22、he permissible tolerances shall be agreed upon. 2 ISO 2012 All rights reserved ISO 6363-4:2012(E) Table 3 Tolerances on width and thickness for alloy group II Dimensions in millimetres Width ab Thickness a tolerances for thickness ranges a Range Toler- ances 2 a 6 6 10, the permissible tolerances sh

23、all be agreed upon. 5.2 Fixed-length tolerances If fixed-length bars are ordered, their maximum permissible length tolerances shall be in accordance with Table 4. Table 4 Fixed-length tolerances Dimensions in millimetres Width b T olerances on fix ed lengths L 250 250 L 1 000 1 000 L 2 000 2 000 L 5

24、 000 5 000 L b 30 0 1 + 0 2 + 0 3 + 0 5 + By agreement 30 b 50 0 2 + 0 3 + 0 4 + 0 6 + 50 b 120 0 25 + , 0 4 + 0 5 + 0 7 + 120 b 200 0 3 + 0 5 + 0 6 + 0 8 + 5.3 Squareness of cut ends Squareness of cut ends shall be within half of the fixed length tolerance range (Table 4) for both fixed and random

25、lengths. For example, for a fixed-length tolerance of 0 2 +mm, the squareness of cut ends shall be within 1 mm. 5.4 Corner radii The corners of the bars shall be slightly rounded, but the corner radii shall not exceed the values specified in Table 5. ISO 2012 All rights reserved 3 ISO 6363-4:2012(E)

26、 Table 5 Maximum corner radii Dimensions in millimetres Thickness a Maximum corner radii Alloy group I Alloy group II a 10 0,4 0,6 10 a 40 0,8 1,0 40 a 60 1,5 2,0 5.5 Form tolerances 5.5.1 General The maximum form tolerances specified in 5.5.2 to 5.5.4 apply to all tempers, except temper O. Form tol

27、erances are measured by placing the bar on a horizontal plate under its own weight as shown in Figures 1 to 3. 5.5.2 Flatness tolerances The maximum allowable flatness tolerances, e, shall be in accordance with Table 6. The deviation from flatness, e i , shall be measured in accordance with Figure 1

28、. Table 6 Flatness tolerances Dimensions in millimetres Width b Flatness tolerance e b 30 0,2 30 b 50 0,3 50 b 80 0,4 80 b 120 0,6 120 b 200 0,9 Key 1 base plate 2 thickness b width e ideviation from flatness F igure 1 M ea s urem ent of d e viat ion f ro m flatness 4 ISO 2012 All rights reserved IS

29、O 6363-4:2012(E) 5.5.3 Straightness tolerances The maximum allowable straightness tolerance, h, for the total length, l, shall be 2 mm per 1 000 mm of length (see Figure 2). In addition, h 2shall not exceed 0,6 mm for each section of 300 mm length (l 2 ). Dimensions in millimetres Key 1 base plate F

30、igure 2 Measurement of deviation from straightness 5.5.4 Twist tolerance The maximum allowable twist tolerances shall be in accordance with Table 7. The twist, i , shall be measured as shown in Figure 3. For rectangular bars with width less than 10 mm, the twist tolerances shall be agreed between th

31、e supplier and purchaser. Table 7 Twist tolerances Dimensions in millimetres Width b Twist tolerances Per 1 000 mm of length Over the total length L 5 000 5 000 L 10 b 30 1,5 3 By agreement 30 b 50 2 5 50 b 120 3 7 120 b 200 4 10 ISO 2012 All rights reserved 5 ISO 6363-4:2012(E) Key 1 base plate 2 t

32、hickness b width itwist Figure 3 Measurement of twist 5.5.5 Squareness tolerances Squareness tolerances are specified in Table 8. The deviation from square shall be measured as shown in Figure 4. Table 8 Squareness tolerances Dimensions in millimetres Thickness a Maximum deviation from square Z 2 a

33、60 0,005 a Key Z maximum deviation from square Figure 4 Measurement of deviation from square 6 ISO 2012 All rights reserved ISO 6363-4:2012(E) Bibliography 1 Registration of International Alloy Designations and Chemical Composition Limits for Wrought Aluminium Alloys (also known as “Teal sheets”). The Aluminum Association, Arlington, VA. Available at: http:/www.aluminum.org/tealsheets ISO 2012 All rights reserved 7ISO 6363-4:2012(E) ISO 2012 All rights reserved ICS 77.150.10 Price based on 7 pages