ISO 8533 AMD 1-2012 Plastics piping systems for pressure and non-pressure drainage and sewerage - Glass-reinforced thermosetting plastics (GRP) systems based on.pdf

1、 ISO 2012 Glass-reinforced thermosetting plastics (GRP) pipes and fittings Test methods to prove the design of cemented or wrapped joints AMENDMENT 1 Tubes et raccords en plastiques thermodurcissables renforcs de verre (PRV) Mthodes dessai pour confirmer la conception des assemblages scells ou enrob

2、s AMENDEMENT 1 INTERNATIONAL STANDARD ISO 8533 First edition 2003-12-01 Reference number ISO 8533:2003/Amd.1:2012(E) AMENDMENT 1 2012-03-01 ISO 8533:2003/Amd.1:2012(E) ii ISO 2012 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2012 All rights reserved. Unless otherwise specified, no part of th

3、is publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-12

4、11 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in Switzerland ISO 8533:2003/Amd.1:2012(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The wor

5、k of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governme

6、ntal, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The m

7、ain task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. A

8、ttention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Amendment 1 to ISO 8533:2003 was prepared by Technical Committee ISO/TC 138, Plastics pipes, fittings

9、and valves for the transport of fluids, Subcommittee SC 6, Reinforced plastics pipes and fittings for all applications. ISO 2012 All rights reserved iii Glass-reinforced thermosetting plastics (GRP) pipes and fittings Test methods to prove the design of cemented or wrapped joints AMENDMENT 1 Title C

10、orrect the title to the following: Plastics piping systems for pressure and non-pressure drainage and sewerage Glass-reinforced thermosetting plastics (GRP) systems based on unsaturated polyester (UP) resin Test methods to prove the design of cemented or wrapped joints Page 1, Scope Replace the firs

11、t sentence with the following: This International Standard specifies methods of test for cemented or wrapped joints intended to be used in plastics piping systems for pressure and non-pressure drainage and sewerage made of glass-reinforced thermosetting plastics (GRP) based on unsaturated polyester

12、(UP) resin. Page 6, 7.4.7 Replace the subclause with the following: Steadily increase the hydrostatic pressure to 2,0 times the nominal pressure of the joint, expressed in bars, and maintain within 2 % for not less than 24 h. Page 6, 7.5.1 Replace the subclause with the following: Steadily increase

13、the hydrostatic pressure to 2,0 times the nominal pressure of the joint, expressed in bars, and maintain within 2 % for not less than 24 h (see Table 1). Page 7, 7.5.7 Replace the subclause with the following: Either increase the pressure to 2,5 times the nominal pressure of the joint, expressed in

14、bars, and maintain that pressure within 2 % for 100 h (see Table 1) or increase the pressure to 3 times the nominal pressure of the joint, expressed in bars, and maintain that pressure within 2 % for 6 min. During either of these times the joint shall not fracture. Leakage of the joint does not cons

15、titute a failure. Page 8, Table 1 Replace Table 1 with the following, in which some of the table headings have been updated and the test pressure for the resistance to bending and internal pressure and resistance to internal pressure have changed from 1,5 times PN to 2,0 times PN: ISO 8533:2003/Amd.

16、1:2012(E) ISO 2012 All rights reserved 1 ISO 8533:2003/Amd.1:2012(E) Table 1 Summary of test requirements Property to be tested Test to be performed Test pressure Duration Subclause number External pressure differential Negative pressure -0,8 bar (-0,08 MPa) 1 h 7.2 and Figure 1 Initial leakage Init

17、ial pressure 1,5 PN 15 min 7.3 and Figure 1 Resistance to bending and internal pressure Preliminary pressure 1,5 PN 15 min 7.4.1 to 7.4.6 and Figure 2 Maintained pressure 2,0 PN 24 h 7.4.7 to 7.4.11 and Figure 2 Resistance to internal pressure Maintained pressure 2,0 PN 24 h 7.5.1 to 7.5.3 and Figur

18、e 1 Positive cyclic pressure atmospheric to 1,5 PN and back to atmospheric 10 cycles of 1,5 to 3,0 min each 7.5.4 to 7.5.6 and Figure 1 or Figure 2 Maintained pressure 2,5 PN or 3,0 PN 100 h 6 min 7.5.7 to 7.5.9 and Figure 1 NOTE 1 Nominal pressure (PN) is an alphanumeric designation of pressure rel

19、ated to the resistance of a component of a piping system to internal pressure. For the purposes of this table, PN is expressed in bars. NOTE 2 A test sequence different from that given in this table may be used. 2 ISO 2012 All rights reservedISO 8533:2003/Amd.1:2012(E) ISO 2012 All rights reserved ICS 23.040.20; 23.040.45 Price based on 2 pages