ISO 9618-2016 Aerospace - Nuts hexagonal slotted (castellated) reduced height normal across flats with MJ threads classifications 450 MPa (at ambient temperatur.pdf

1、 ISO 2016 Aerospace Nuts, hexagonal, slotted (castellated), reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature)/120 C, 450 MPa (at ambient temperature)/235 C, 600 MPa (at ambient temperature)/ 425 C, 900 MPa (at ambient temperature)/235 C, 900 MPa

2、(at ambient temperature)/315 C, 900 MPa (at ambient temperature)/ 650 C, 1 100 MPa (at ambient temperature)/235 C, 1 100 MPa (at ambient temperature)/ 730 C and 1 250 MPa (at ambient temperature)/600 C Dimensions Aronautique et espace crous hexagonaux crneaux, hauteur rduite, surplats normaux, filet

3、age MJ, classifications: 450 MPa ( temprature ambiante)/120 C, 450 MPa ( temprature ambiante)/235 C, 600 MPa ( temprature ambiante)/425 C, 900 MPa ( temprature ambiante)/235 C, 900 MPa ( temprature ambiante)/315 C, 900 MPa ( temprature ambiante)/650 C, 1 100 MPa ( temprature ambiante)/235 C, 1 100 M

4、Pa ( temprature ambiante)/730 C et 1 250 MPa ( temprature ambiante)/600 C Dimensions INTERNATIONAL STANDARD ISO 9618 Second edition 2016-02-15 Reference number ISO 9618:2016(E) ISO 9618:2016(E)ii ISO 2016 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2016, Published in Switzerland All rights

5、reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior written permission. Permission can be requested from eithe

6、r ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Ch. de Blandonnet 8 CP 401 CH-1214 Vernier, Geneva, Switzerland Tel. +41 22 749 01 11 Fax +41 22 749 09 47 copyrightiso.org www.iso.org ISO 9618:2016(E)Foreword iv Introduction v 1 Scope . 1 2 Normat

7、ive references 1 3 Configuration and dimensions . 1 ISO 2016 All rights reserved iii Contents Page ISO 9618:2016(E) Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standa

8、rds is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also tak

9、e part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In pa

10、rticular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements o

11、f this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see

12、 www.iso.org/patents). Any trade name used in this document is information given for the convenience of users and does not constitute an endorsement. For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence

13、to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information. The committee responsible for this document is ISO/TC 20, Aircraft and space vehicles, Subcommittee SC 4, Aerospace fastener systems. This second edition cancels and replaces t

14、he first edition (ISO 9618:1996), of which it constitutes a minor revision.iv ISO 2016 All rights reserved ISO 9618:2016(E) Introduction The dimensions specified in this International Standard have been determined to satisfy the requirements of the procurement specification which will be the subject

15、 of a future International Standard. ISO 2016 All rights reserved v Aerospace Nuts, hexagonal, slotted (castellated), reduced height, normal across flats, with MJ threads, classifications: 450 MPa (at ambient temperature)/120 C, 450 MPa (at ambient temperature)/235 C, 600 MPa (at ambient temperature

16、)/425 C, 900 MPa (at ambient temperature)/235 C, 900 MPa (at ambient temperature)/315 C, 900 MPa (at ambient temperature)/650 C, 1 100 MPa (at ambient temperature)/235 C, 1 100 MPa (at ambient temperature)/730 C and 1 250 MPa (at ambient temperature)/600 C Dimensions 1 Scope This International Stand

17、ard specifies the dimensions of hexagon slotted (castellated) nuts, reduced height, normal across flats, with MJ threads, of classifications: 450 MPa/120 C, 450 MPa/235 C, 600 MPa/425 C, 900 MPa/235 C, 900 MPa/315 C, 900 MPa/650 C, 1 100 MPa/235 C, 1 100 MPa/730 C, and 1 250 MPa/600 C. NOTE 1 450 MP

18、a, 600 MPa, 900 MPa, 1 100 MPa and 1 250 MPa corresponds to the minimum tensile stress which the nut is able to withstand at ambient temperature without breaking or cracking when tested with a bolt of a higher strength class. NOTE 2 120 C, 235 C, 425 C, 315 C, 650 C, 730 C and 600 C corresponds to t

19、he maximum temperature that the nut is able to withstand without permanent alteration to its original characteristics, after ambient temperature has been restored. The maximum temperature is conditioned by the surface treatment. These nuts are intended to be used with split pins in conformity with I

20、SO 1234. This International Standard is applicable for the compilation of aerospace product standards. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition ci

21、ted applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 1234, Split pins ISO 58552, Aerospace MJ threads Part 2: Limit dimensions for bolts and nuts ISO 8788, Aerospace Nuts, metric Tolerances of form and position 3 Configuration and

22、 dimensions See Figure 1 and Table 1. Dimensions and tolerances are expressed in millimetres. They apply after any surface coating(s) but before the application of any lubricant. INTERNATIONAL ST ANDARD ISO 9618:2016(E) ISO 2016 All rights reserved 1 ISO 9618:2016(E) S S R S R S F N G H G s E M L J

23、Key a These values, in micrometres, apply before any surface coating(s) is/are applied. The values do not apply to threads the surface texture of which will be as achieved by the usual manufacturing methods b Applies to height below slots and height of flats (diameter codes 060 to 240). c This dimen

24、sion also applies to the upper chamfer. All forms of entry (chamfer or radius) permissible within these limiting dimensions. d Diameter M may be tangential to, but shall not intrude on the flats. e 6 slots. f Form of contour within limiting dimensions at manufacturers option g (4:1) Form (radius or

25、chamfer) at bottom of slot at manufacturers option. NOTE Tolerances of form and position shall conform to those specified in ISO 8788. Details of form not stated are at the manufacturers discretion. Figure 1 Configurations and dimensions2 ISO 2016 All rights reserved ISO 9618:2016(E)Table 1 Dimensio

26、ns Dimensions in millimetres Diameter code Thread a E F G H J L M N S Maximum split pin diameter b min. h14 0,25 0,25 min - H14 040 MJ4 0,7 4H6H 7,6 7 h12 2,1 4,1 4,2 + 6,4 0,5 1,3 1,0 050 MJ5 0,8 4H6H 8,7 8 2,4 4,8 5,2 7,4 1,7 1,4 060 MJ6 1 4H5H 10,9 10 h13 3,0 5,4 9 6,3 + 9,3 070 MJ7 1 4H5H 12,0 1

27、1 5,8 10 7, 3 10,2 2,1 1,8 080 MJ8 1 4H5H 14,3 13 3,2 6,0 11 8,3 12,2 100 MJ10 1,25 4H5H 18,9 17 4,0 7,6 13 10,3 16,0 0,6 2,6 2,3 120 MJ12 1,25 4H5H 21,1 19 4,8 8,4 16 12,3 18,0 140 MJ14 1,5 4H5H 24,5 22 5,6 10,0 18 14,4 21,0 3,2 2,9 160 MJ16 1,5 4H5H 26,8 24 6,4 10,8 22 16,4 23,0 180 MJ18 1,5 4H5H

28、30,2 27 7, 2 12,4 25 18,4 26,0 4,0 3,7 200 MJ20 1,5 4H5H 33,6 30 8,0 13,2 28 20,4 29,0 220 MJ22 1,5 4H5H 35,8 32 8,8 14,0 30 22,4 30,9 240 MJ24 2 4H5H 40,4 36 9,6 14,8 32 24,5 34,9 aIn accordance with ISO 5855-2. bFor information, in conformity with ISO 1234 for the split pin maximum diameter but not for the split pin maximum diameter/thread diameter combination. ISO 2016 All rights reserved 3 ISO 9618:2016(E) ISO 2016 All rights reserved ICS 49.030.30 Price based on 3 pages