ASTM B153-11(2017) Standard Test Method for Expansion (Pin Test) of Copper and Copper-Alloy Pipe and Tubing.pdf

1、Designation: B153 11 (Reapproved 2017)Standard Test Method forExpansion (Pin Test) of Copper and Copper-Alloy Pipe andTubing1This standard is issued under the fixed designation B153; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision,

2、the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This test method es

3、tablishes the requirements for theexpansion pin test for copper and copper-alloy pipe and tubingwith an inside diameter of 0.125 in. (3.2 mm) and greater or anoutside diameter up to and including 4 in. (102 mm).NOTE 1For tubes of sizes with an inside diameter less than 0.125 in.(3.2 mm), a substitut

4、e test method must be agreed upon between themanufacturer and purchaser.NOTE 2For tubes of sizes greater than 4 in. (102 mm) in outsidediameter, refer to B968/B968M for a test method.1.2 UnitsThe values stated in inch-pound units are to beregarded as standard. The values given in parentheses aremath

5、ematical conversions to SI units that are provided forinformation only and are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and h

6、ealth practices and determine the applica-bility of regulatory limitations prior to use.1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards,

7、 Guides and Recom-mendations issued by the World Trade Organization TechnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2B846 Terminology for Copper and Copper AlloysB968/B968M Test Method for Flattening of Copper andCopper-Alloy Pipe and Tube3. Terminology3.1 For de

8、finitions of terms related to copper and copperalloys, refer to Terminology B846.4. Summary of Test Method4.1 The prepared test specimen is expanded over a conicalpin inserted at a uniform speed or pressure. The expansion ofthe test specimen shall be measured on the outside of the tubediameter and s

9、hall conform to the product specification.5. Significance and Use5.1 When properly performed and interpreted, the expan-sion pin test will provide information with regard to thecapacity of a tube for expansion and to reveal surface defects.The expansion pin test may provide data for research anddeve

10、lopment, engineering design, quality control, and accep-tance or rejections in specifications.5.2 In certain product specifications which establish require-ments for tubes of sizes greater than 4 in. (102 mm), the testdescribed in Test Method B968/B968M may be allowed as asubstitute.6. Apparatus6.1

11、PinThe conical pin shall have an included angle of60, unless provided otherwise in the product specification.The pin shall be made of carbide or tool steel that has beenhardened and ground to the prescribed angle and shall have asmooth, polished surface. The size of the pin at the base shallbe suita

12、ble for the size of tubing being tested.6.2 Testing MachineAny type of testing machine, eitherhydraulically or mechanically operated, that will exert pressureto expand the pipe and tubing on the pin at a uniform rate.7. Sampling and Test Specimen Preparation7.1 The test specimen shall be prescribed

13、in the specifica-tion for the product being tested. In the event that a testspecimen size is not prescribed in the pipe or tubespecification, the specimen shall be of suitable length so that itcan be expanded to the required amount. Both ends shall eitherbe faced square to the longitudinal axis in a

14、 lathe, or suitably1This test method is under the jurisdiction of ASTM Committee B05 on Copperand Copper Alloys and is the direct responsibility of Subcommittee B05.06 onMethods of Test.Current edition approved April 1, 2017. Published April 2017. Originallyapproved in 1941. Last previous edition ap

15、proved in 2011 as B153-11. DOI:10.1520/B0153-11R17.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary

16、 of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in

17、 the Decision on Principles for theDevelopment of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1prepared so as to have a smooth surface free from scratches orburrs, which might interfere with the test.8. Proced

18、ure8.1 The test specimen shall be wiped clean to remove anyloose chips or dirt from the inside surface. The specimen shallbe well lubricated (Note 3) on the inside surface. The pin (6.1)for use in the test, as prescribed in the specifications for theproduct being tested, shall be wiped clean and fre

19、e from dirt,grit, or chips, and coated with lubricant.NOTE 3No. 1 lard oil or any extreme pressure lubricating oil isrecommended as a lubricant.8.2 The test specimen shall be expanded over the pin to theamount prescribed in the specification. During the expansionthe testing machine shall be operated

20、 at a uniform speed orpressure. The longitudinal axes of the test specimen and the pinshall coincide. The expanded tube shall be examined with theunaided eye to determine conformance with the productspecification. Expansion shall be measured on the outsidediameter of the tube.8.2.1 Subject to agreem

21、ent by the manufacturer and thepurchaser, the test specimen may be expanded by hand-hammering or by manually or mechanically pressing the pin,except that in case of dispute another test specimen shall beexpanded as described in 8.2.8.3 In case there is an indication that the specimen was notproperly

22、 prepared or tested, a new specimen from the samesample shall be selected and tested.8.4 During inspection, the expanded section of the testspecimen shall be free of defects, but blemishes of a nature thatdo not interfere with the intended application are acceptable.9. Retests9.1 In case of failure

23、of any specimen a retest shall beallowed in accordance with the requirements of the productspecification.10. Report10.1 When testing is completed by an independent third-party laboratory, the test report shall include the followinginformation. In-house captive laboratories shall only report10.1.1, 1

24、0.1.2 and 10.1.5.10.1.1 The date of the test,10.1.2 Sample identification,10.1.3 Reference to the test method,10.1.4 The number of replicate test pieces used,10.1.5 The test results: Pass or Fail (relative to presence ofdefects) as required above and by the appropriate productspecification, and10.1.

25、6 Any other features of the material noted during theinspection.11. Precision and Bias11.1 No statement is made about either the precision or biasof this test method since the result merely states whether thereis conformance to the acceptance criteria specified in theprocedure and the product specif

26、ication.12. Keywords12.1 copper; copper alloy; expansion; expansion test; pintest; pipe; tubeSUMMARY OF CHANGESCommittee B05 has identified the principal changes to this standard that have been incorporated since the 2005issue as follows:(1) Added references to Test Method B968/B968M. (2) Added a Re

27、port section.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of suc

28、h rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for addit

29、ional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the

30、 ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the

31、aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 11 (2017)2