BS ISO 6361-2-2014 en_7859 Wrought aluminium and aluminium alloys Sheets strips and plates Mechanical properties《锻造铝和铝合金 厚板材 薄板材和带材 机械性能》.pdf

1、BSI Standards Publication BS ISO 6361-2:2014 Wrought aluminium and aluminium alloys Sheets, strips and plates Part 2: Mechanical propertiesBS ISO 6361-2:2014 BRITISH STANDARD National foreword This British Standard is the UK implementation of ISO 6361-2:2014. The UK participation in its preparation

2、was entrusted to Technical Committee NFE/35, Light metals and their alloys. A list of organizations represented on this committee can be obtained on request to its secretary. This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correc

3、t application. The British Standards Institution 2014. Published by BSI Standards Limited 2014 ISBN 978 0 580 84725 7 ICS 77.150.10 Compliance with a British Standard cannot confer immunity from legal obligations. This British Standard was published under the authority of the Standards Policy and St

4、rategy Committee on 30 September 2014. Amendments/corrigenda issued since publication Date T e x t a f f e c t e d ISO 2014 Wrought aluminium and aluminium alloys Sheets, strips and plates Part 2: Mechanical properties Aluminium et alliages daluminium corroys Tles, bandes et tles paisses Partie 2: P

5、roprits mcaniques INTERNATIONAL STANDARD ISO 6361-2 Fourth edition 2014-09-15 Reference number ISO 6361-2:2014(E)BS ISO 6361-2:2014ISO 6361-2:2014(E)ii ISO 2014 All rights reserved COPYRIGHT PROTECTED DOCUMENT ISO 2014 All rights reserved. Unless otherwise specified, no part of this publication may

6、be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below or ISOs member body in the country of the r

7、equester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in SwitzerlandBS ISO 6361-2:2014ISO 6361-2:2014(E) ISO 2014 All rights reserved iii Contents Page Foreword iv 1 Scope . 1 2 Normative refere

8、nces 1 3 T erms and definitions . 1 4 Tensile testing . 1 5 Bend testing . 1 6 Mechanical properties 2 6.1 Tensile test 2 6.2 Bend test . 2 Annex A (normative) Rules for rounding results obtained by inspection and testing 50 Bibliography .51BS ISO 6361-2:2014ISO 6361-2:2014(E) Foreword ISO (the Inte

9、rnational Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has

10、 been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical s

11、tandardization. The procedures used to develop this document and those intended for its further maintenance are described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the different types of ISO documents should be noted. This document was drafted in acc

12、ordance with the editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives). Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Deta

13、ils of any patent rights identified during the development of the document will be in the Introduction and/or on the ISO list of patent declarations received (see www.iso.org/patents). Any trade name used in this document is information given for the convenience of users and does not constitute an e

14、ndorsement. For an explanation on the meaning of ISO specific terms and expressions related to conformity assessment, as well as information about ISOs adherence to the WTO principles in the Technical Barriers to Trade (TBT) see the following URL: Foreword - Supplementary information The committee r

15、esponsible for this document is ISO/TC 79, Light metals and their alloys, Subcommittee SC 6, Wrought aluminium and aluminium alloys. This fourth edition cancels and replaces the third edition (ISO 6361-2:2011), which has been technically revised. ISO 6361 consists of the following parts, under the g

16、eneral title Wrought aluminium and aluminium alloys Sheets, strips and plates: Part 1: Technical conditions for inspection and delivery Part 2: Mechanical properties Part 3: Strips: Tolerances on shape and dimensions Part 4: Sheets and plates: Tolerances on shape and dimensions Part 5: Chemical comp

17、ositioniv ISO 2014 All rights reservedBS ISO 6361-2:2014INTERNATIONAL ST ANDARD ISO 6361-2:2014(E) Wrought aluminium and aluminium alloys Sheets, strips and plates Part 2: Mechanical properties 1 Scope In conjunction with ISO 6361-1, this part of ISO 6361 specifies the mechanical properties of wroug

18、ht aluminium and aluminium alloy sheets, strips, and plates for general engineering applications. It applies to flat-rolled products. The chemical composition of these materials is given in ISO 6361-5. The designations of aluminium and aluminium alloys and the temper designations used in this part o

19、f ISO 6361 are in accordance with ISO 2107. NOTE In certain countries, for purposes of mechanical properties, the thickness limit can be lowered to 0,15 mm by agreement between the purchaser and the supplier, in the case of sheets and strips. 2 Normative references The following documents, in whole

20、or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 6361-1, Wrought aluminium and alumini

21、um alloys Sheets, strips and plates Part 1: Technical conditions for inspection and delivery 3 T erms a nd definiti ons For the purposes of this document, the terms and definitions given in ISO 6361-1 apply. 4 Tensile testing For the selection of the specimens and tensile testing, see ISO 6361-1. 5

22、Bend testing For the selection of the specimens and bend testing, see ISO 6361-1. ISO 2014 All rights reserved 1BS ISO 6361-2:2014ISO 6361-2:2014(E) 6 Mechanical properties 6.1 Tensile test Values for mechanical properties of aluminium and aluminium alloys are given in Tables 1 to 63. For elongation

23、, two different gauge lengths are used. The choice of the gauge length for elongation measurements (A or A 50mm ) is at the discretion of the producer, unless otherwise agreed. NOTE A is the percentage elongation on a gauge length of S . A 50mmis the percentage elongation on a gauge length of 50 mm.

24、 Test results shall be rounded in accordance with the rules given in Annex A. 6.2 Bend test Sheet, strip, and plate shall be capable of being bent cold through an angle of 180, as applicable, around a pin having a radius equal to k times the thickness, t, of the sheet, strip, or plate (for example 0

25、,5t) without cracking. The values of the minimum bend radii for different alloys, tempers, and thicknesses are given in Tables 1 to 63. NOTE The explanations of the numbered notes in Tables 1 to 63 are given after Table 63. Table 1 Aluminium 1050 Temper Tensile test Bend test 2) S p e c i f i e d t

26、h i c k- ness mm Tensile strength MPa 0,2 % proof stress MPa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to H112 4,0 6,5 13,0 25,0 50,0 6,5 13,0 25,0 50,0 75,0 85 80 70 65 65 45 45 35 30 20 10 10 16 22 22 O 0,2 0,5 0,8 1,3 6,5 0,5 0,

27、8 1,3 6,5 50,0 60 60 60 60 60 100 100 100 100 10020 20 20 15 20 25 30 28 0,2 6,0 0t H12 or H22 3) 0,2 0,3 0,5 0,8 1,3 2,9 0,3 0,5 0,8 1,3 2,9 12,0 80 80 80 80 80 80 120 120 120 120 120 12065 65 65 2 3 4 6 8 9 0,2 0,8 0,8 6,0 0t 0,5t H14 or H24 3) 0,2 0,3 0,5 0,8 1,3 2,9 0,3 0,5 0,8 1,3 2,9 12,0 95 9

28、5 95 95 95 95 125 125 125 125 125 12575 75 75 1 2 3 4 5 6 0,2 0,8 0,8 6,0 0,5t 1t2 ISO 2014 All rights reservedBS ISO 6361-2:2014ISO 6361-2:2014(E) Temper Tensile test Bend test 2) S p e c i f i e d t h i c k- ness mm Tensile strength MPa 0,2 % proof stress MPa Elongation 1)min. % S p e c i f ie d t

29、 h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to H16 or H26 3) 0,2 0,5 0,8 1,3 0,5 0,8 1,3 4,0 120 120 120 120 145 145 145 14585 85 1 2 3 4 0,2 4,0 2t H18 0,2 0,5 0,8 1,3 0,5 0,8 1,3 3,0 125 125 125 125 1 2 3 4 Table 2 Aluminium 1050A Temper Tensile test Bend test 2) S p e

30、 c i f i e d t h i c k- ness mm Tensile strength MPa 0,2 % proof stress MPa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to O 0,2 0,5 1,5 3,0 6,0 12,5 0,5 1,5 3,0 6,0 12,5 25,0 65 65 65 65 65 65 95 95 95 95 95 95 20 20 20 20 20 20 20

31、22 26 29 35 3232 H14 0,2 0,5 1,5 3,0 0,5 1,5 3,0 6,0 105 105 105 105 145 145 145 145 85 85 85 85 2 3 4 5 H24 0,2 0,5 1,5 3,0 0,5 1,5 3,0 6,0 105 105 105 105 145 145 145 145 75 75 75 75 3 4 5 8 H18 0,2 0,5 1,5 0,5 1,5 3,0 140 140 140 120 120 120 120 120 120 1 2 2Table 1 (continued) ISO 2014 All right

32、s reserved 3BS ISO 6361-2:2014ISO 6361-2:2014(E) Table 3 Aluminium 1070, 1080, and 1085 Temper Tensile test Bend test 2) S p e c i f i e d t h i c k- ness mm Tensile strength MPa 0,2 % proof stress MPa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50

33、mm A over up to H112 4,0 6,5 13,0 25,0 50,0 6,5 13,0 25,0 50,0 75,0 75 70 60 55 55 35 35 25 20 15 13 15 20 25 25 O 0,2 0,3 0,5 0,8 1,3 13,0 0,3 0,5 0,8 1,3 13,0 50,0 55 55 55 55 55 55 95 95 95 95 95 9515 15 15 15 20 25 30 35 30 0,2 6,0 0t H12 or H22 3) 0,2 0,3 0,5 0,8 1,3 2,9 0,3 0,5 0,8 1,3 2,9 12,

34、0 70 70 70 70 70 70 110 110 110 110 110 11055 55 55 2 3 4 6 8 9 0,2 6,0 0t H14 or H24 3) 0,2 0,3 0,5 0,8 1,3 2,9 0,3 0,5 0,8 1,3 2,9 12,0 85 85 85 85 85 85 120 120 120 120 120 12065 65 65 1 2 3 4 5 6 0,2 0,8 0,8 6,0 0,5t 1t H16 or H26 3) 0,2 0,5 0,8 1,3 0,5 0,8 1,3 4,0 100 100 100 100 135 135 135 13

35、575 75 1 2 3 4 0,2 0,8 0,8 6,0 1t 1,5t H18 0,2 0,5 0,8 1,3 0,5 0,8 1,3 3,0 120 120 120 120 1 2 3 44 ISO 2014 All rights reservedBS ISO 6361-2:2014ISO 6361-2:2014(E) Table 4 Aluminium 1070A Temper Tensile test Bend test 2) S p e c i f i e d t h i c k- ness mm Tensile strength MPa 0,2 % proof stress M

36、Pa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to O/H111 0,2 0,5 1,5 3,0 6,0 12,5 0,5 1,5 3,0 6,0 12,5 25,0 60 60 60 60 60 60 90 90 90 90 90 90 15 15 15 15 15 15 23 25 29 32 3532 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 0t 0t 0t 0,5t

37、 0,5t H112 6,0 12,5 12,5 25,0 70 70 20 20 20 H12 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 80 80 80 80 80 120 120 120 120 120 55 55 55 55 55 5 6 7 9 12 0,2 0,5 1,5 0,5 1,5 3,0 0,5t 0,5t 0,5t H14 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 100 100 100 100 100 140 140 140 140 140 70 70 70 70 70 4 4 5 6 7

38、0,2 0,5 1,5 0,5 1,5 3,0 0,5t 0,5t 1t H16 0,2 0,5 1,5 0,5 1,5 4,0 110 110 110 150 150 150 90 90 90 2 2 3 0,2 0,5 1,5 0,5 1,5 4,0 1t 1t 1t H18 0,2 0,5 1,5 0,5 1,5 3,0 125 125 125 105 105 105 2 2 2 H22 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 80 80 80 80 80 120 120 120 120 120 50 50 50 50 50 7 8 10 12

39、15 0,2 0,5 1,5 0,5 1,5 3,0 0,5t 0,5t 0,5t H24 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 100 100 100 100 100 140 140 140 140 140 60 60 60 60 60 5 6 7 9 11 0,2 0,5 1,5 0,5 1,5 3,0 0,5t 0,5t 1t H26 0,2 0,5 1,5 0,5 1,5 4,0 110 110 110 150 150 150 80 80 80 3 3 4 ISO 2014 All rights reserved 5BS ISO 6361-2

40、:2014ISO 6361-2:2014(E) Table 5 Aluminium 1080A Temper Tensile test Bend test 2) S p e c i f i e d t h i c k- ness mm Tensile strength MPa 0,2 % proof stress MPa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to O/H111 0,2 0,5 1,5 3,0 6

41、,0 0,5 1,5 3,0 6,0 12,5 60 60 60 60 60 90 90 90 90 90 15 15 15 15 15 26 28 31 35 35 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 0t 0t 0t 0,5t 0,5t H112 6,0 12,5 12,5 25,0 70 70 20 20 H12 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 80 80 80 80 80 120 120 120 120 120 55 55 55 55 55 5 6 7 9 12 0,2 0,5 1,5 0,

42、5 1,5 3,0 0,5t 0,5t 0,5t H14 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 100 100 100 100 100 140 140 140 140 140 70 70 70 70 70 4 4 5 6 7 0,2 0,5 1,5 0,5 1,5 3,0 0,5t 0,5t 1t H16 0,2 0,5 1,5 0,5 1,5 4,0 110 110 110 150 150 150 90 90 90 2 2 3 0,2 0,5 1,5 0,5 1,5 4,0 1t 1t 1t H18 0,2 0,5 1,5 0,5 1,5 3,0

43、125 125 125 105 105 105 2 2 2 H22 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 80 80 80 80 80 120 120 120 120 120 50 50 50 50 50 8 9 11 13 15 0,2 0,5 1,5 0,5 1,5 3,0 0,5t 0,5t 0,5t H24 0,2 0,5 1,5 3,0 6,0 0,5 1,5 3,0 6,0 12,5 100 100 100 100 100 140 140 140 140 140 60 60 60 60 60 5 6 7 9 11 0,2 0,5 1,5

44、0,5 1,5 3,0 0,5t 0,5t 1t H26 0,2 0,5 1,5 0,5 1,5 4,0 110 110 110 150 150 150 80 80 80 3 3 46 ISO 2014 All rights reservedBS ISO 6361-2:2014ISO 6361-2:2014(E) Table 6 Aluminium 1100, 1100A, 1200, and 1230A Temper Tensile test Bend test 2) S p e c i f i e d t h i c k- ness mm Tensile strength MPa 0,2

45、% proof stress MPa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to H112 4,0 6,5 13,0 50,0 6,5 13,0 50,0 75,0 95 90 85 80 50 50 35 25 9 9 14 20 O 0,2 0,5 0,8 1,3 6,5 0,5 0,8 1,3 6,5 75,0 75 75 75 75 75 105 105 105 105 105 25 25 25 25 2

46、5 17 22 22 30 2825 0,2 6,0 0t H12 or H22 3) 0,2 0,3 0,5 0,8 1,3 2,9 0,3 0,5 0,8 1,3 2,9 12,0 95 95 95 95 95 95 125 125 125 125 125 125 75 75 75 75 75 75 2 3 4 6 8 9 0,2 6,0 0,5t H14 or H24 3) 0,2 0,3 0,5 0,8 1,3 2,9 0,3 0,5 0,8 1,3 2,9 12,0 120 120 120 120 120 120 145 145 145 145 145 145 95 95 95 95

47、 95 95 1 2 3 4 5 6 0,2 6,0 1t H16 or H26 3) 0,2 0,5 0,8 1,3 0,5 0,8 1,3 4,0 135 135 135 135 165 165 165 165 115 115 115 115 1 2 3 4 0,2 4,0 2t H18 0,2 0,5 0,8 1,3 0,5 0,8 1,3 3,0 150 150 150 150 130 130 130 130 1 2 3 4 Table 7 Alloy 2014 Temper Tensile test Bend test 2) S p e c i f i e d t h i c k-

48、ness mm Tensile strength MPa 0,2 % proof stress MPa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to O 4) 0,4 0,5 13,0 0,5 13,0 25,0 220 220 220 140 140 140 16 16 109 0,4 1,6 2,9 1,6 2,9 6,0 0,5t 1t 1,5t ISO 2014 All rights reserved 7B

49、S ISO 6361-2:2014ISO 6361-2:2014(E) Temper Tensile test Bend test 2) S p e c i f i e d t h i c k- ness mm Tensile strength MPa 0,2 % proof stress MPa Elongation 1)min. % S p e c i f ie d t h ic k ne s s mm Radius over up to min. max. min. max. A 50mm A over up to T3 0,4 0,5 6,0 6,3 0,5 6,0 6,3 12,0 395 395 395 395 245 245 240 235 14 14 14 13 0,4 0,5 1,6 2,9 0,5 1,6 2,9 6,0 1,5t 2,5t 3t 3,5t T4 0,4 0,5 6,0 6,3 0,5 6,0 6,3 12,0 395 395 400 400 240