ACI 440.8M-2013 Specification for Carbon and Glass Fiber-Reinforced Polymer (FRP) Materials Made by Wet Layup for External Strengthening of Concrete and Masonry Structures.pdf

1、ACI 440.8M-13Specification for Carbon and Glass Fiber-Reinforced Polymer (FRP) Materials Made by Wet Layup for External Strengthening of Concrete and Masonry StructuresAn ACI StandardReported by ACI Committee 440(metric)First PrintingMay 2014Specification for Carbon and Glass Fiber-Reinforced Polyme

2、r (FRP) Materials Made by Wet Layup for External Strengthening of Concrete and Masonry StructuresCopyright by the American Concrete Institute, Farmington Hills, MI. All rights reserved. This material may not be reproduced or copied, in whole or part, in any printed, mechanical, electronic, film, or

3、other distribution and storage media, without the written consent of ACI.The technical committees responsible for ACI committee reports and standards strive to avoid ambiguities, omissions, and errors in these documents. In spite of these efforts, the users of ACI documents occasionally find informa

4、tion or requirements that may be subject to more than one interpretation or may be incomplete or incorrect. Users who have suggestions for the improvement of ACI documents are requested to contact ACI via the errata website at www.concrete.org/committees/errata.asp. Proper use of this document inclu

5、des periodically checking for errata for the most up-to-date revisions.ACI committee documents are intended for the use of individuals who are competent to evaluate the significance and limitations of its content and recommendations and who will accept responsibility for the application of the mater

6、ial it contains. Individuals who use this publication in any way assume all risk and accept total responsibility for the ap-plication and use of this information.All information in this publication is provided “as is” without warranty of any kind, either express or implied, includ-ing but not limite

7、d to, the implied warranties of merchantability, fitness for a particular purpose or non-infringement.ACI and its members disclaim liability for damages of any kind, including any special, indirect, incidental, or con-sequential damages, including without limitation, lost revenues or lost profits, w

8、hich may result from the use of this publication.It is the responsibility of the user of this document to establish health and safety practices appropriate to the specific circumstances involved with its use. ACI does not make any representations with regard to health and safety issues and the use o

9、f this document. The user must determine the applicability of all regulatory limitations before applying the document and must comply with all applicable laws and regulations, including but not limited to, United States Occupational Safety and Health Administration (OSHA) health and safety standards

10、.Participation by governmental representatives in the work of the American Concrete Institute and in the develop-ment of Institute standards does not constitute governmental endorsement of ACI or the standards that it develops.Order information: ACI documents are available in print, by download, on

11、CD-ROM, through electronic subscription, or reprint and may be obtained by contacting ACI.Most ACI standards and committee reports are gathered together in the annually revised ACI Manual of Concrete Practice (MCP).American Concrete Institute38800 Country Club DriveFarmington Hills, MI 48331U.S.A.Ph

12、one: 248-848-3700Fax: 248-848-3701www.concrete.orgISBN: 978-0-87031-892-4American Concrete InstituteAdvancing concrete knowledgeThis material specification covers the requirements for carbon and glass fiber-reinforced polymer (FRP) systems made by the wet layup process. These systems are externally

13、bonded to concrete or masonry structures and intended for the structural strengthening of them.Keywords: carbon fiber; fiber-reinforced polymer (FRP); glass fiber; masonry; wet layup.CONTENTS1SCOPE, p. 22DEFINITIONS, p. 23REFERENCED STANDARDS, p. 24CLASSIFICATION, p. 2Carol K. Shield*, Chair William

14、 J. Gold*, SecretaryACI 440.8M-13Specification for Carbon and Glass Fiber-Reinforced Polymer (FRP) Materials Made by Wet Layup for External Strengthening of Concrete and Masonry StructuresAn ACI StandardReported by ACI Committee 440Tarek AlkhrdajiCharles E. Bakis*Lawrence C. BankAbdeldjelil BelarbiB

15、rahim BenmokraneLuke A. BisbyGregg J. Blaszak*Hakim BouadiTimothy E. BradberryGordon L. Brown Jr.Vicki L. BrownJohn P. BuselRaafat El-HachaGarth J. FallisAmir Z. FamNabil F. GraceMark F. GreenZareh B. GregorianDoug D. GremelShawn P. GrossH. R. Trey Hamilton IIIIssam E. HarikKent A. HarriesMark P. He

16、ndersonBohdan N. HoreczkoMichael W. LeeMaria E. Lopez de MurphyIbrahim M. MahfouzAmir MirmiranJohn J. MyersAntonio Nanni*Ayman M. OkeilCarlos E. OspinaRenato ParrettiMax L. PorterAndrea ProtaHayder A. RasheedSami H. RizkallaRajan SenRudolf SeracinoPedro F. SilvaKhaled A. SoudkiSamuel A. Steere IIIJa

17、y ThomasHoussam A. ToutanjiJ. Gustavo TumialanMilan VatovecDavid WhiteSarah E. WittConsulting membersP. N. BalaguruCraig A. BallingerHarald G. F. BudelmannC. J. BurgoyneElliot P. DouglasRami M. ElhassanDavid M. GaleRussell GentryArie GerritseSrinivasa L. IyerKoichi KishitaniHoward S. KligerKyuichi M

18、aruyamaAntoine E. NaamanHajime OkamuraMark A. PostmaFerdinand S. RostasySurendra P. ShahMohsen ShahawyYasuhisa SonobeMinoru SugitaLuc R. TaerweRalejs TepfersTaketo UomotoPaul Zia_*Contributing authors.Task Group Chair.ACI 440.8M was adopted November 29, 2013 and published May 2014.Copyright 2014, Am

19、erican Concrete Institute.All rights reserved including rights of reproduction and use in any form or by any means, including the making of copies by any photo process, or by electronic or mechanical device, printed, written, or oral, or recording for sound or visual reproduc-tion or for use in any

20、knowledge or retrieval system or device, unless permission in writing is obtained from the copyright proprietors.15MATERIALS AND MANUFACTURE, p. 36PHYSICAL PROPERTIES, p. 37MECHANICAL PROPERTIES, p. 38DURABILITY PROPERTIES, p. 39SAMPLING, FREQUENCY, AND NUMBER OF SPECIMENS, p. 310PRODUCT DATA SHEETS

21、, p. 41SCOPE1.1 This specification describes permitted constituent materials, minimum performance requirements of those constituent materials, and minimum performance require-ments for carbon fiber-reinforced polymer (CFRP) and glass fiber-reinforced polymer (GFRP) laminae made from those constituen

22、t materials using the wet layup process.1.2 This specification only covers the fabric reinforcement and saturating resin that comprise the FRP system. Primers and putty fillers are excluded.1.3 This specification applies to FRP laminae consisting of one ply of continuous, unidirectional fiber reinfo

23、rcement and saturating resin fabricated using the wet layup process. Laminae with fibers in more than one direction that are intended to provide strength in more than one direction are excluded.1.4 Precured FRP systems are not covered by this specification.1.5 Hybrid FRP systems consisting of more t

24、han one type of fiber are excluded.1.6 Only FRP laminae with epoxy resins are covered by this specification.1.7 Values in this specification are stated in SI units. A companion specification in in.-lb units is available.2DEFINITIONS2.1 The following definitions govern in this specifica-tion. For def

25、initions not given below, refer to “ACI Concrete Terminology,” www.concrete.org/Tools/ConcreteTermi-nology.aspx. For definitions used in but not specific to this specification, refer to ASTM C904.fabric reinforcementreinforcing fibers in fabric form.fiber-reinforced polymer laminaa single layer of c

26、omposite material made by combining fabric reinforcement and saturating resin matrix.fiber-reinforced polymer systemthe product fabri-cated using the wet layup method with the FRP system manufacturers fiber reinforcement and saturating resin per the FRP system manufacturers instructions.mean propert

27、ya property value provided by the manu -facturer no greater than the mean of results obtained by a specified test method for at least the specified number of specimens. DiscussionThis value is applicable to FRP chord tensile stiffness, resin properties, and for calculating retention values for durab

28、ility.plya single layer of fiber reinforcement.rovinga parallel bundle of continuous yarns, tows, or fibers with little or no twist.towan untwisted bundle of continuous filaments.ultimate propertya property value provided by the manufacturer no greater than the mean minus three standard deviations o

29、f results obtained by a specified test method for at least the specified number of specimens. DiscussionThis definition is applicable to maximum tensile force.wet layupa manufacturing process where dry fabric fiber reinforcement is impregnated on-site with a saturating resin matrix and then cured in

30、-place.3REFERENCED STANDARDS3.1 ASTM InternationalC581-03(2008)Standard Practice for Determining Chemical Resistance of Thermosetting Resins Used in Glass-Fiber-Reinforced Structures Intended for Liquid ServiceC904-01(2012)Standard Terminology Relating to Chemical-Resistant Nonmetallic MaterialsD638

31、-10Standard Test Method for Tensile Properties of PlasticsD790-10Standard Test Methods for Flexural Properties of Unreinforced and Reinforced Plastics and Electrical Insu-lating MaterialsD1141-98(2013)Standard Practice for the Preparation of Substitute Ocean WaterD2247-11Standard Practice for Testin

32、g Water Resis-tance of Coatings in 100% Relative HumidityD3045-92(2010)Standard Practice for Heat Aging of Plastics Without LoadD3776/D3776M-09a(2013)Standard Test Methods for Mass Per Unit Area (Weight) of FabricD7565/D7565M-10Standard Test Method for Deter -mining Tensile Properties of Fiber Reinf

33、orced Polymer Matrix Composites Used for Strengthening of Civil StructuresE1640-13Standard Test Method for Assignment of the Glass Transition Temperature by Dynamic Mechanical AnalysisG153-13Standard Practice for Operating Enclosed Carbon Arc Light Apparatus for Exposure of Nonmetallic Materials.3.2

34、 International Code CouncilEvaluation Service (ICC-ES)AC125Acceptance Criteria for Concrete and Reinforced and Unreinforced Masonry Strengthening Using Exter-nally Bonded Fiber-Reinforced Polymer (FRP) Composite Systems4CLASSIFICATION4.1 Fiber-reinforced polymer systems shall be classified according

35、 to their fiber reinforcement composition with the first letter of the acronym designating fiber type as follows:a) CFRPCarbon fiber-reinforced polymer systems;b) GFRPGlass fiber-reinforced polymer systemsAmerican Concrete Institute Copyrighted Materialwww.concrete.org2 SPECIFICATION FOR CFRP AND GF

36、RP MATERIALS MADE BY WET LAYUP (ACI 440.8M-13)5MATERIALS AND MANUFACTURE5.1 Fiber reinforcement5.1.1 Fiber reinforcement shall be arranged in a usable form as either continuous glass fiber rovings or carbon fiber tows of a single size and areal weight.5.1.2 Rovings or tows shall be assembled by the

37、fabric manufacturer into fabric reinforcement such that the rovings or tows are aligned in a single direction along the fabric length. Fiber of any material running at an angle to the rovings or tows is permitted to hold the fabric together.5.2 Resin5.2.1 Only epoxy resins shall be used for the satu

38、rating resin.5.2.2 Resins shall not be diluted with organic solvents such as thinner.6PHYSICAL PROPERTIES6.1 Glass transition temperature6.1.1 Glass transition temperature of the FRP lamina shall be determined from specimens at a frequency defined in 9.1.6.1.2 The glass transition temperature of the

39、 FRP lamina shall not be less than 60C. The glass transition tempera-ture shall be measured according to the dynamic mechanical analysis (DMA) method in ASTM E1640 on a coupon cut from panels produced in accordance with ASTM D7565/D7565M. Manufacturer shall report any pretreatments used.6.2 Areal we

40、ight6.2.1 Areal weight of dry fabric shall be determined from specimens at a frequency defined in 9.1.6.2.2 The areal weight of dry fabric shall be determined by measuring the mass per unit area according to ASTM D3776/D3776M Option C and reported in g/m2.7MECHANICAL PROPERTIES7.1 Mechanical propert

41、ies of saturating resins7.1.1 Mechanical properties of the saturating resins shall be determined from specimens at a frequency defined in 9.2.7.1.2 Saturating resin shall conform to the requirements for mechanical properties shown in Table 7.1.2.7.2 Mechanical properties of FRP laminaMechanical prop

42、erties of the FRP lamina shall be determined in accor-dance with ASTM D7565/D7565M on specimens taken from test panels. All properties shall be reported on a per ply basis.7.2.1 Ultimate tensile force per unit widthThe ulti-mate tensile force per unit width shall be determined at a frequency defined

43、 in 9.3. The ultimate tensile force per unit width shall be divided by the areal weight of the dry fabric as determined in 6.2 and conform to the requirements shown in Table 7.2.1.7.2.2 Chord tensile stiffness per unit widthThe mean chord tensile stiffness per unit width shall be determined at a fre

44、quency defined in 9.3. The chord tensile stiffness per unit width shall be divided by the areal weight of the dry fabric as determined in 6.2, and conform to the requirements shown in Table 7.2.1.7.2.3 Ultimate rupture strainThe ultimate rupture strain shall be calculated as the ultimate tensile for

45、ce per unit width divided by the mean chord tensile stiffness per unit width.8DURABILITY PROPERTIES8.1 FRP laminaThe FRP lamina shall conform to the retained tensile force per unit width requirements shown in Table 8.1 for the given environmental exposure conditions. The mean tensile force per unit

46、width shall be determined in accordance with ASTM D7565/D7565M. Mean values of test results for the unexposed and exposed specimens, tested at a frequency defined in 9.4, shall be used to calculate percent retention of tensile strength.9SAMPLING, FREQUENCY, AND NUMBER OF SPECIMENS9.1 Physical proper

47、ties9.1.1 For determining areal weight, at least five specimens shall be tested from five fabric samples.9.1.2 For determining glass transition temperature, at least five specimens shall be tested from five FRP single- or double-ply lamina panels made in accordance with ASTM D7565/D7565M. At least o

48、ne specimen for each test shall be taken from each of the five panels.9.1.3 Tests for physical properties shall be performed at least once every three years for each product and when the constituent materials are modified.9.2 Mechanical properties of saturating resins9.2.1 Each mechanical property s

49、hall be determined as the mean value of test results from at least five specimens.9.2.2 Tests shall be performed at least once for each resin product and when the constituent materials are modified.9.3 Mechanical properties of FRP lamina9.3.1 For the determination of tensile stiffness and ulti-mate force, at least 20 specimens shall be tested from four FRP single- or double-ply lamina panels made in accordance with ASTM D7565/D7565M. At least five specimens shall be taken from each of the four panels. Ten