AECMA PREN 4195-2005 Aerospace series Paints and varnishes Test method for determination of chromate leaching Edition P 1《航空航天系列.油漆涂料试验方法鉻酸盐过滤.P1版》.pdf

1、ASD STANDARD NORME ASD ASD NORM prEN 4195 Edition P1 November 2005 PUBLISHED BY THE AEROSPACE AND DEFENSE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONGulledelle 94 - B-1200 Brussels - Tel. + 32 2 775 8126 - Fax. + 32 2 763 3565 - www.asd-stan.orgICS: Descriptors: ENGLISH VERSION Aerospace seri

2、es Paints and varnishes Test method for determination of chromate leaching Srie arospatiale Peintures et vernis Test de lixiviation de chromate Luft- und Raumfahrt Anstrichstoffe Chromatauslaugbarkeitstest This “Aerospace Series“ Prestandard has been drawn up under the responsibility of ASD-STAN (Th

3、e Aerospace and Defense Industries Association of Europe - Standardization). It is published for the needs of the European Aerospace Industry. It has been technically approved by the experts of the concerned Domain following member comments. Subsequent to the publication of this Prestandard, the tec

4、hnical content shall not be changed to an extent that interchangeability is affected, physically or functionally, without re-identification of the standard. After examination and review by users and formal agreement of ASD-STAN, it will be submitted as a draft European Standard (prEN) to CEN (Europe

5、an Committee for Standardization) for formal vote and transformation to full European Standard (EN). The CEN national members have then to implement the EN at national level by giving the EN the status of a national standard and by withdrawing any national standards conflicting with the EN. Edition

6、approved for publication 30 November 2005 Comments should be sent within six months after the date of publication to ASD-STAN Non-metallic Material Domain Copyright 2005 by ASD-STAN Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot

7、for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4195:2005 2 Contents Page Foreword2 1 Scope 3 2 Normative references 3 3 Principle3 4 Specimens and test apparatus.3 5 Test procedure.4 6 Analysis of hexavalent chromium4 7 Test report 4 8 Designation 5 Annex A (info

8、rmative) 6 A.1 Diphenylcarbazide solution 6 A.2 Phosphoric-sulphuric acid .6 A.3 Preparation of standard chromium solutions.6 A.4 Calibration for diphenylcarbazide method6 Annex B (informative) Calculation of factor .8 Foreword This standard was reviewed by the Domain Technical Coordinator of ASD-ST

9、ANs Non-metallic Material Domain. After inquiries and votes carried out in accordance with the rules of ASD-STAN defined in ASD-STANs General Process Manual, this standard has received approval for Publication. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS

10、 under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4195:2005 3 1 Scope This standard defines a test procedure for the determination of the leaching rate of hexavalent chromium from the dry paint film of a chromate containing primer for ae

11、rospace use. The rate can be related to requirements either to prescribe the type of primer for an intended use or for the purpose of batch quality consistency. The procedure is applicable to products intended for use in aerospace applications. 2 Normative references The following referenced documen

12、ts are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 3696, Water for analytical laboratory use Specification and test methods. EN

13、2090, Aerospace series Aluminium alloy AL-P2024- T3 Clad sheet and strip 0,3 mm a 6 mm. EN 2334, Aerospace series Chromic-sulphuric acid pickle of aluminium and aluminium alloys. 3 Principle The test involves placing a dry film of chromate primer in distilled water in accordance with ISO 3696 for a

14、period of time at a controlled temperature to allow soluble chromate to leach from the film into solution in the water. The water is collected for the measurement of dissolved hexavalent chromate by a suitable means. Because the rate of leaching can vary considerably over a period of time the collec

15、tion time is divided into a number of periods of different duration appropriate to the rate of leaching over the collection period. Some of the water collected in the collection periods is not used for measurement because normally sufficient data is gained from other collections. Values of chromate

16、leaching can be numerically expressed or for convenience plotted on a graph. 4 Specimens and test apparatus The apparatus shall consist of a stoppered test tube to hold the water and the painted test specimens. The test tube shall be maintained at a constant temperature, as specified, in a suitably

17、controlled chamber. Test specimens shall be of aluminium alloy EN 2090. Test specimens shall be prepared by chrome sulphuric acid pickling in accordance with EN 2334 or other non chromate leaching pretreatment as may be specified in the relevant material specification. They shall then be sprayed wit

18、h primer within four hours to give the paint thickness prescribed in the relevant material specification. When dried and preconditioned as prescribed in the relevant material specification an area of 40 cm2shall be cut from the panel for leaching test immersion. All edges shall be uncoated. Using a

19、test tube for the immersion, it is convenient to cut two panels of dimensions (10 2) cm. This assumes that the panels are coated on one side only and are then placed back to back in the test tube. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license

20、 with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4195:20054 5 Test procedure A test specimen, prepared as above, shall be totally immersed in a stoppered tube containing 50 ml of distilled water maintained at a temperature of (40 2) C. The distilled

21、water shall be renewed after 1, 2, 3, 4, 7, 10, 14, 18, 23, 29 and 36 days. The samples collected at the end of 2, 10 and 36 days only shall be analysed for chromate content as normally this is sufficient to determine the leach rate characteristics of the paint sample under test. However samples fro

22、m other collection periods can also be measured if additional data is required. At the end of the appropriate immersion time, the water in which the painted specimens have been immersed shall be poured into a 100 ml volumetric flask. The specimen and the test container shall be rinsed with a volume

23、of distilled water not exceeding 25 ml and this shall be added to the volumetric flask containing the first solution. Another 50 ml of distilled water shall be added to the original container to proceed with the test for the next immersion period. A suitable method of analysis for chromate determina

24、tion has been outlined in Annex A. Whether this or another method is employed for chromate concentration determination, the final volume of chromate containing solution, tube washings and reagents shall be 100 ml. The concentration of hexavalent chromium in the solution shall be measured and calcula

25、ted as milligrams of chromate leached per square decimetre of paint film. 6 Analysis of hexavalent chromium A sample shall be taken from the 100 ml container and analysed for hexavalent chromium content. The result shall be determined as mg Cr per l and expressed as mg CrO4 per dm2of paint film test

26、ed. NOTE For a 40 cm2exposed primer area this involves multiplying the quantity of hexavalent chromium in mg/l by a factor of 0,557 7. Details of the calculation of the factor for this case are given in Annex B. The quantity of CrO4 per dm2shall be converted into CrO4 per dm2per day leaching rate. T

27、his means that the value calculated for the test sample needs to be divided by the number of days over which the paint sample had been in contact with that sample of water since it had been previously renewed. Sample at 2 days duration 1-2 days divide by 1 Sample at 10 days duration 7-10 days divide

28、 by 3 Sample at 36 days duration 29-36 days divide by 7 The results can be numerically expressed or for convenience can be plotted on a semi-logarithmic graph. 7 Test report The test report shall contain at least the following information: Complete identification of the paint used including supplier

29、s code numbers, date of manufacture, batch number, material standard, etc. a) Reference to the test standard; b) The number of specimens tested; Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networki

30、ng permitted without license from IHS-,-,-prEN 4195:2005 5 c) The paint thickness applied; d) Dimensions of specimen tested; e) The overall drying time between application and testing; f) The method of analysis of chromate used for the determination; g) Date of test and traceability to individuals p

31、erforming the test work; h) Any incident which may have affected the results and any deviation from the test method; i) Reference to the material standard; j) The test results. 8 Designation EXAMPLE Description block DETERMINATION OF CHROMATE LEACHING Identity block EN4195 Number of this standard Co

32、pyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4195:20056 Annex A (informative) The following is one of many methods used for determining chromate

33、concentration in a solution. It uses a colormetric determination of diphenylcarbazide complex. A set of standard solutions are prepared with increasing chromium concentrations and are used to construct a suitable calibration curve. The concentration of chromium in the “unknown” solution can then be

34、read off the graph. A.1 Diphenylcarbazide solution 40 g of phthalic anhydride shall be dissolved in 1 l of hot industrial ethyl alcohol The solution shall be cooled and 5 g of diphenylcarbazide added. This shall be stirred with a magnetic stirrer to dissolve. A.2 Phosphoric-sulphuric acid 375 ml of

35、concentrated sulphuric acid (S.G. = 1,84) and 375 ml of concentrated phosphoric acid (S.G. = 1,83) shall be added to 1 l of distilled water. A.3 Preparation of standard chromium solutions 2,828 g of dried “Analar” potassium dichromate shall be accurately weighed, dissolved in about 100 ml of distill

36、ed water and diluted to 1 l in a volumetric flask. This solution shall now contain 1 g/l (or 1 000 g/ml) of chromium. In order to obtain a solution containing 5 g/ml of chromium, 5 ml of the 1 g/l solution shall be pipetted into a 1 l volumetric flask and made up to the mark with distilled water. In

37、 obtain a solution containing 100 g/ml of chromium, 50 ml of the 1 g/l solution shall be pipetted into a 500 ml volumetric flask and made up to the mark with distilled water. NOTE Standard solutions prepared in this way are stable when stored in closed glass containers for a maximum of 12 months. A.

38、4 Calibration for diphenylcarbazide method Using a burette, 2, 5, 10, 15 and 20 ml of 5 g/ml standard solution shall be put into respective volumetric flasks. NOTE This is equivalent to 10, 25, 50, 75 and 100 g of chromium for calibration. 50 ml of distilled water shall be added to another 100 ml vo

39、lumetric flask. This shall be used as a blank. The volume of solution in each flask shall be made up to approximately 50 ml with distilled water. 10 ml of the phosphoric/sulphuric acid solution and 10 ml of diphenylcarbazide shall be added. Copyright Association Europeene des Constructeurs de Materi

40、el Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4195:2005 7 The solutions shall be made up to the mark with distilled water, thoroughly mixed and allowed to stand for 10 minutes. The standards shall be pou

41、red into 1 cm cells, the optical density values shall be measured using the blanks a reference on a suitable spectrophotometer set at a wavelength of 540 nm. A graph of optical density versus chromium content of standards shall be plotted. For test samples the steps outlined in clauses 3 to 5 of thi

42、s section shall be followed and the chromium content equivalent to the measured optical density shall be read from the calibration graph. NOTE A fresh graph must be produced daily or with each batch of samples. Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS

43、 under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4195:2005 8 Annex B (informative) Calculation of factor The result shall be determined as mg Cr per l and expressed as mg CrO4 per dm2of paint film tested. NOTE For a 40 cm2exposed primer

44、 area this involves multiplying the quantity of hexavalent chromium in mg/l by a factor of 0,557 7. Mol wt of CrO4a 115,994 8 Atomic wt of Cr b 51,996 mg Cr per l Y mg Cr per 100 mls Y/10 mg CrO4per 100 mls Y*a/b/10 0,223 084 For 40 cm2Y*a/b/10 0,223 084 For 1 cm2Y*a/b/10/40 0,005 577 For 100 cm2 = 1 dm2Y*a/b/10/40*100 0,557 7 Copyright Association Europeene des Constructeurs de Materiel Aerospatial Provided by IHS under license with AECMANot for ResaleNo reproduction or networking permitted without license from IHS-,-,-