1、ASD STANDARD NORME ASD ASD NORM prEN 4700-003 Edition P 2 July 2009 PUBLISHED BY THE AEROSPACE AND DEFENCE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONAvenue de Tervuren, 270 - B-1150 Brussels - Tel. + 32 2 775 8126 - Fax. + 32 2 775 8131 - www.asd-stan.orgICS: Supersede edition P1 of April 20
2、02 Descriptors: ENGLISH VERSION Aerospace series Steel and heat resisting alloys Wrought products Technical specification Part 003: Tube Srie arospatiale Aciers et alliages rsistant chaud Produits corroys Spcification technique Partie 003 : Tubes Luft- und Raumfahrt Stahl und Hochwarmfesten Legierun
3、gen Umgeformte Erzeugnisse Technische Lieferbedingungen Teil 003: Rohre This “Aerospace Series“ Prestandard has been drawn up under the responsibility of ASD-STAN (The AeroSpace and Defence Industries Association of Europe - Standardization). It is published for the needs of the European Aerospace I
4、ndustry. It has been technically approved by the experts of the concerned Domain following member comments. Subsequent to the publication of this Prestandard, the technical content shall not be changed to an extent that interchangeability is affected, physically or functionally, without re-identific
5、ation of the standard. After examination and review by users and formal agreement of ASD-STAN, it will be submitted as a draft European Standard (prEN) to CEN (European Committee for Standardization) for formal vote and transformation to full European Standard (EN). The CEN national members have the
6、n to implement the EN at national level by giving the EN the status of a national standard and by withdrawing any national standards conflicting with the EN. Edition approved for publication 31 July 2009 Comments should be sent within six months after the date of publication to ASD-STAN Metallic Mat
7、erial Domain Copyright 2009 by ASD-STAN Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4700-003:2009 (E) 2 Contents Page Foreword2 Introduction .3 1 Scope 3 2 Normative references 3 3 Terms and defin
8、itions .5 4 Wording of order5 5 Health and safety .5 6 Technical requirements 5 Foreword This standard was reviewed by the Domain Technical Coordinator of ASD-STANs Metallic Material Domain. After inquiries and votes carried out in accordance with the rules of ASD-STAN defined in ASD-STANs General P
9、rocess Manual, this standard has received approval for Publication. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4700-003:2009 (E) 3 Introduction This standard is part of the series of EN metallic
10、material standards for aerospace applications. The general organization of this series is described in EN 4258. 1 Scope This standard defines the requirements for the ordering, manufacture, testing, inspection and delivery of steel and heat resisting alloy tube. It shall be applied when referred to
11、and in conjunction with the EN material standard unless otherwise specified on the drawing, order or inspection schedule. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undate
12、d references, the latest edition of the referenced document (including any amendments) applies. ISO 3651-1, Determination of resistance to intergranular corrosion of stainless steels Part 1: Austenitic and ferritic-austenitic (duplex) stainless steels Corrosion test in nitric acid medium by measurem
13、ent of loss in mass (Huey test). ISO 3651-2, Determination of resistance to intergranular corrosion of stainless steels Part 2: Ferritic, austenitic and ferritic-austenitic (duplex) stainless steels Corrosion test in media containing sulfuric acid. ISO 3887, Steels Determination of depth of decarbur
14、ization. EN 2002-001, Aerospace series Metallic materials Test methods Part 001: Tensile testing at ambient temperature. EN 2002-002, Aerospace series Metallic materials Test methods Part 002: Tensile testing at elevated temperature. EN 2002-005, Aerospace series Metallic materials Test methods Part
15、 005: Uninterrupted creep and stress-rupture testing. EN 2002-7, Aerospace series Test methods for metallic materials Part 7: Hardness test. 1)EN 2002-8, Aerospace series Test methods for metallic materials Part 8: Micrographic determination of grain size. 1)EN 2002-17, Aerospace series Test methods
16、 for metallic materials Part 17: Integrity test. 1)EN 2002-18, Aerospace series Metallic materials Test methods Part 18: Hydraulic distension test for tube. 1)EN 2002-20, Aerospace series Metallic materials Test methods Part 20: Eddy current testing of circular cross-section tubes. 1)EN 2003-7, Aero
17、space series Steel Test methods Part 7: Macrographic test. 1)1) Published as ASD Prestandard at the date of publication of this standard. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4700-003:2009
18、(E) 4 EN 2032-1, Aerospace series Metallic materials Part 1: Conventional designation. EN 2032-2, Aerospace series Metallic materials Part 2: Coding of metallurgical condition in delivery condition. EN 2078, Aerospace series Metallic materials Manufacturing schedule, inspection schedule, inspection
19、and test report Definition, general principles, preparation and approval. EN 2950, Aerospace series Test method Wrought heat resisting alloys - Semi-finished products and parts Conditions for macrographic and micrographic examination Atlas of structures and defects. EN 2951, Aerospace series Metalli
20、c materials Test method Micrographic determination of content of non-metallic inclusions. 1)EN 3718, Aerospace series Test method for metallic materials Ultrasonic inspection of tubes. 1)EN 4258, Aerospace series Metallic materials General organization of standardization Links between types of EN st
21、andards and their use. EN 4259, Aerospace series Metallic materials Definition of general terms. 1)EN 4436, Aerospace series Steel Test methods Determination of Delta ferrite content. 1)EN 9100, Aerospace series Quality management systems Requirements (based on ISO 9001:2000) and Quality systems Mod
22、el for quality assurance in design, development, production, installation and servicing (based on ISO 9001:1994). EN 9133, Aerospace series Quality management systems Qualification Procedure for aerospace standard parts. TR 2410, Aerospace series Metallic materials Relationship between dimensional s
23、tandards and material standards. 2)EN 10027-1, Designation systems for steels Part 1: Steel names. EN 10079, Definition of steel products. EN 10233, Metallic Materials Tube Flattering test. EN 10234, Metallic Materials Tube Drift expanding test. AMS 2750, Pyrometry. 3)2) Published as ASD Technical R
24、eport at the date of publication of this standard. 3) Published by: American Society for Testing and Materials (ASTM), 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA, 19428-2959 USA. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking pe
25、rmitted without license from IHS-,-,-prEN 4700-003:2009 (E) 5 3 Terms and definitions For the purposes of this document, the terms and definitions given in EN 4259 apply. For definitions specific to steel, see EN 10079. 3.1 batch for heat treatment using a continuous furnace, a continuous run of les
26、s than or equal to 8 hours may be considered as the same heat treatment charge 4 Wording of order The order shall clearly indicate: quantities to be supplied; dates of delivery; material standard number; delivery condition and metallurgical code of products; dimensions and tolerances or reference to
27、 an appropriate dimensional standard; product designation, when required; forwarding address; nature and type of packing, if required; surface protection, if appropriate; definition and frequency of any special tests and their retest procedures, if required. 5 Health and safety The product in the de
28、livery condition shall fulfil the current health and safety laws of the area of the country where it is to be delivered. A product safety data sheet shall be available. 6 Technical requirements 6.1 General The product shall be manufactured in accordance with the requirements of the relevant material
29、 standard and the applicable requirements of this specification. A manufacturing schedule shall be established and applied in accordance with EN 2078. Product shall satisfy the requirements of the material standard and/or order and shall be free from irregularities prejudicial to the subsequent manu
30、facture or use of this product. Notwithstanding previous acceptance complying with this material standard, any product that is found, at a later stage, to contain such defects shall be rejected. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking p
31、ermitted without license from IHS-,-,-prEN 4700-003:2009 (E) 6 Unless otherwise specified, the requirements in Tables 1 and 2 shall apply in conjunction with those of the relevant material standard. Table 1 relates to lines 1 to 29 (inclusive) of the material standard and Table 2 relates to lines 30
32、 onwards in which the sub-line format is also used. Lines 2 to 98 may also be opened in line 100 if the material standard details specific qualification requirements. If a specific line number is not shown in Tables 1 and 2, the requirement is stated in the material standard and/or order. 6.2 Qualif
33、ication requirements Qualification requirements when invoked by the material standard and/or order are detailed in Tables 1 and 2. Unless otherwise agreed between the manufacturer and purchaser the qualification phase shall be run on the first 3 batches, coming from at least 2 casts. 6.3 Release req
34、uirements 6.3.1 Release tests Release testing shall be the responsibility of the manufacturer. The purchaser reserves the right to perform any of the inspections and/or tests required by the material standard and/or order. The test samples shall be representative of the product. When required by the
35、 order, the manufacturer shall inform the purchaser of the planned dates for extraction of samples and release testing in order that these operations may be witnessed. Tables 1 and 2 detail the requirements for each line of the material standard. Unless otherwise specifically requested by the purcha
36、ser, a particular inspection and/or test for release shall be carried out if corresponding acceptance criteria and/or values are stated in the applicable material standard, but see also in 6.3.5. 6.3.2 Retests If any requirement is not met, retests shall be carried out under the following conditions
37、 unless otherwise stated in the material standard or order. If the test procedure or test piece preparation is faulty, testing shall be re-applied at the original frequency after rectification of the original cause of failure, on a test sample located near the first one. For tube with hardness resul
38、ts below the minimum or above the maximum value, the softest or hardest tube, as appropriate, shall be submitted to a tensile test. If the results comply with the specified tensile requirements, all tube shall be accepted. When failure cannot be attributed to faulty testing, or test piece preparatio
39、n, further test samples shall be selected at twice the original frequency from the product, one of which shall be that on which the original results were obtained unless already withdrawn by the manufacturer after suitable identification of the cause of failure. If all retest results are satisfactor
40、y, the batch shall be accepted. If one or more tests are unsatisfactory, the batch shall be: rejected, or 100 % retested and the conforming products accepted, or partially or fully re-heat treated if heat treatment can rectify the cause of the failure and tested as a completely new batch except for
41、chemical composition and cleanness inspection. The reheat treatment shall be stated on the release test certificate. For cleanness inspection, if the material fails the requirement the product may be cut back before retesting. For deformation under pressure, test samples from 25 % of the tubes in th
42、e batch shall be tested. All samples shall meet the requirements. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitted without license from IHS-,-,-prEN 4700-003:2009 (E) 7 6.3.3 Rejection Any failure to meet the requirements of the materi
43、al standard shall be cause for rejection. 6.3.4 Special tests Special tests may be required by the purchaser. In such cases, the nature of the test, method, frequency and technical requirements shall be specified on the order or inspection schedule and shall be mutually agreed by the manufacturer an
44、d purchaser. 6.3.5 Capability clause Where the capability clause is invoked and where sufficient statistical evidence exists, the test need not be carried out (unless specifically requested by the purchaser). However, this in no way reduces the obligations of the manufacturer to fulfil the requireme
45、nts. If subsequent testing indicates that the product does not comply with the requirements, the batch shall be rejected. If sufficient statistical evidence does not exist, the test shall be carried out at a frequency agreed between the manufacturer and purchaser. 6.3.6 Statistical process control R
46、eduction in the extent of release testing, other than that defined in 6.3.5 above, may be negotiated with the purchaser on the basis of appropriate statistical process control and/or statistical data. 6.3.7 Inspection and test report The manufacturer shall furnish, with each delivery, a report confo
47、rming to the requirements of EN 2078 stating the following: manufacturers name and address and, if appropriate, identification of the plant; order number; material standard number; method of melting; delivery condition and metallurgical code of the product; quantity and dimensions; manufacturing and
48、 inspection schedule reference; cast and batch number; all heat treatment, including re-heat treatment and, where appropriate, straightening and stress relieving parameters, applied to the batch; test samples heat treatment; results of the tests and retests if any. 6.4 Traceability Each product shall be traceable to the cast, production batch and/or heat treatment batch at all stages of manufacture, testing and delivery. Copyright ASD-STAN Provided by IHS under license with AECMA Not for ResaleNo reproduction or networking permitt