ANSI T 1012 OM-2015 Moisture content of fiber glass mats.pdf

1、TAPPI/ANSI T 1012 om-15 OFFICIAL TEST METHOD 1992 WITHDRAWN 2000 REVISED AND REINSTATED 2006 REAFFIRMED 2010 REVISED 2015 2015 TAPPI The information and data contained in this document were prepared by a technical committee of the Association. The committee and the Association assume no liability or

2、 responsibility in connection with the use of such information or data, including but not limited to any liability under patent, copyright, or trade secret laws. The user is responsible for determining that this document is the most recent edition published. Approved by the Standard Specific Interes

3、t Group for this Test Method TAPPI CAUTION: This Test Method may include safety precautions which are believed to be appropriate at the time of publication of the method. The intent of these is to alert the user of the method to safety issues related to such use. The user is responsible for determin

4、ing that the safety precautions are complete and are appropriate to their use of the method, and for ensuring that suitable safety practices have not changed since publication of the method. This method may require the use, disposal, or both, of chemicals which may present serious health hazards to

5、humans. Procedures for the handling of such substances are set forth on Material Safety Data Sheets which must be developed by all manufacturers and importers of potentially hazardous chemicals and maintained by all distributors of potentially hazardous chemicals. Prior to the use of this method, th

6、e user must determine whether any of the chemicals to be used or disposed of are potentially hazardous and, if so, must follow strictly the procedures specified by both the manufacturer, as well as local, state, and federal authorities for safe use and disposal of these chemicals. Moisture content o

7、f fiber glass mats 1. Scope This method covers the determination of the moisture content of fiber glass mat on a dry basis. 2. Applicable document TAPPI T 1007 “Sample Location.” 3. Summary The moisture content of fiber glass mat is determined by placing the test specimen in a suitable oven and meas

8、uring the volatiles lost during heating and cooling, under the conditions specified; the volatiles are assumed to be moisture. 4. Significance The moisture content of fiber glass mat is a physical property which may be of interest in the conversion of the material into a finished product. 5. Apparat

9、us 5.1 Oven, mechanical convection type capable of maintaining a temperature of 220 5F (105 3C). 5.2 Balance, accurate to 0.001 g. 5.3 Paper cutter or sample cutting device of suitable size to cut 6 6 in. (152 152 mm) or same size sample as used to perform basis weight testing procedure. 5.4 Desicca

10、tor with desiccant of sufficient volume to contain the 6 6 in. (152 152 mm) or same size sample as used to perform basis weight testing procedure 5.5 Forceps of sufficient size to retrieve the specimens from the oven. T 1012 om-15 Moisture content of fiber glass mats / 2 6. Test specimen 6.1 Obtain

11、samples in accordance with TAPPI T1007 “Sample Location.” 6.2 Cut five or more 6 6 in. (152 152 mm) or same size sample as used to perform basis weight procedure across the width of the roll. 7. Procedure 7.1 Weigh each of the prepared specimens to the nearest 0.001 g and record this weight as A. 7.

12、2 Place each of the specimens in the convection oven which has been stabilized at 220 5F (105 3C) for 5 1/2 min (or to constant weight). 7.3 Remove specimens from the oven with forceps and place in desiccator (see Note 1) until cooled to room temperature. NOTE 1: Experience has shown that the low ma

13、ss of typical industrial mats facilitates rapid cooling in a normal laboratory environment. Therefore, a desiccator may not be necessary provided that convection current effects are avoided in weighing and that the weighing is done in a sufficiently short time to avoid significant reabsorption of wa

14、ter from the ambient atmosphere. 7.4 Remove each of the specimens and rapidly weigh to the nearest 0.001 g and record this weight as B. 7.5 Calculate the percent of moisture for each of the five specimens to the nearest 0.1% as follows: (A-B) 100 / B 8. Report 8.1 Report the average percent moisture

15、 of the five specimens to the nearest 0.1%. 8.2 The report should include: 8.2.1 The average percentage of moisture. 8.2.2 The number of specimens tested for each determination. 8.2.3 The standard deviation for each specimen set. 9. Precision 9.1 On the basis of studies made in accordance with TAPPI

16、 T 1200 “Interlaboratory Evaluation of Test Methods to Determine TAPPI Repeatability and Reproducibility” test results, each representing an average of 5 determinations from the same sample (commercial 2.00 lb/100ft2 fiberglass mat), are expected to agree within the amounts stated below. The study i

17、ncluded five laboratories. 9.1.1 Average moisture content 1.55 % Repeatability 14 % - 0.21 moisture % Reproducibility 15 % - 0.24 moisture % 9.2 Fiberglass mats are extremely sensitive to environmental conditions (temperature, humidity) and must be allowed to equilibrate before moisture testing. Moi

18、sture content of fiberglass mats tested immediately after manufacturing might differ after shipment to a laboratory. 10. Keywords Fiber glass mats, Moisture content 11. Additional information 11.1 Effective date of issue: April 21, 2015. 11.2 Changes in the 2015 edition were to clarify the sample size and to indicate that the test is to determine the moisture content of fiber glass mat on a dry basis. Your comments and suggestions on this procedure are earnestly requested and should be sent to the TAPPI Standards Department.