1、 AMSC N/A Page 1 of 2 FSC 8455 INCH - POUND MIL-DTL-11484/360 7 August 2013 DETAIL SPECIFICATION SHEET LAPEL BUTTON, OUTSTANDING SERVICE, SENIOR EXECUTIVE SERVICE, U.S. ARMY This specification is approved for use by all Departments and Agencies of the Department of Defense The requirements for acqui

2、ring the product described herein shall consist of this specification sheet and the latest issue of MIL-DTL-11484. MATERIAL: Red Brass 85/15 (UNS Alloy No. C-230) DIMENSIONS: DIAMETER: 3/4 inch (REF) THICKNESS (At rim): 0.065 inch 0.010 inch FINISH: 24K Gold Plated, Matte Finish, Polished Highlights

3、 and shall match The Institute of Heraldry (TIOH) Metal Finish Chip Number 8. EPOXY: Epoxy resin shall be applied to the lapel button as indicated above, and shall match TIOH Hard Enamel Color Chip Numbers listed below. Hard cloisonn enamel may be used in lieu of epoxy. If hard cloisonn enamel is us

4、ed, the required base material shall be Gilding Metal 95/5 (UNS Alloy C-210). TIOH HARD ENAMEL COLOR CHIP NUMBER LOCATION Blue #20 Designation Band BLUE #20 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-DTL-11484/360 Page 2 of 2 ATTACHING DEVIC

5、E: The attaching device shall be a prong with pick and wing type clutch. The prong shall be centered on the reverse side and either fused or hard soldered to the lapel button. ITEM CASE: Lapel buttons to be presented in a case shall be mounted and centered on a polyethylene pad and placed in a rigid

6、 hinged plastic box having a transparent lid and opaque bottom section. The box shall have two plastic hinges and catches and shall be approximately 1-1/8 inches square and 5/8 inch in overall depth. The pad shall be of sufficient depth to restrict movement of the lapel button. NOTES: 1. The term (R

7、EF) refers to measurements taken from the Government furnished hub or die. 2. The manufacturer may deviate from MIL-DTL-11484 by using nickel underplating prior to plating with 24K gold. Custodian: Preparing activity: Army - IH Army - IH (Project No. 8455-2013-180) NOTE: The activities listed above

8、were interested in this document as of the date of this document. Since organizations and responsibilities can change, you should verify the currency of the information above using the ASSIST Online database at https:/assist.dla.mil. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-