1、I INCH-POUND I MIL-G- 6 3 3 4 3 AMENDMENT 4 (AR) 10 July 1998 SUPERSEDING AMENDMENT 3 4 January 1994 MILITARY SPECIFICATION GRENADE, M74, HEMISPHERES FOR MIL-G-63343 was inactivated after 13 February 1996 for new design. This amendment forms a part of Military Specification MIL-G-63343(AR), dated 11

2、 July 1980, and is approved for use by the U.S. Army Armament Research, Development and Engineering Center, and is available for use by all Departments and Agencies of the Department of Defense. Change item designation from “XM74“ to “M74“ in title and wherever else it appears in this specification.

3、 PAGE 1 2.1 Delete “MIL-1-6866“ and substitute “MIL-STD-6866“. Delete “FSC 1375“ and substitute “FSC 1330“. PAGE 3 3.2.1.1 Microstructure. Delete paragraph in its entirety and substitute the following: “3.2.1.1 Microstructure. The microstructure shall exhibit a uniform distribution of tungsten and b

4、inder material, and matrix depletion (porosity) shall not exceed 0.15% (volume) when viewed at 200 magnifications and tested as specified in 4.5 -3. II AMSC N/A 1 of 3 DISTRIBUTION STATEMENT A. Approved for publie release; distribution 58 unlimited . FSC 1330 Provided by IHSNot for ResaleNo reproduc

5、tion or networking permitted without license from IHS-,-,-MIL-G-63343 (4) 0b 2072542 48T i MIL-G-63343 (AR) AMENDMENT 4 PAGE 7 4.4.2.1 Delete Minors 201 and 202 in their entirety. Minor 209: Delete in its entirety. Minor 211, Add the following: “Straighness incorrect (2 places 0.65%/ 3.2, Gage“. PAG

6、E 10 4.5.3 Microstructure. Delete paragraph in its entirety and substitute the following: “4.5.3 Microstructure. The test shall be performed on a * test blank from a disc using any method satisfactory to the procuring agency. (The measurement techniques outlined in Metals Handbook, 9th Edition, Vol.

7、 9, A.S.M., are approved and recommended.) Only the following will be counted for the purpose of porosity value measurement: a. all areas of binder depletion. b. sub-surface blisters. c. d. porosity caused by inclusions with a dimension greater shrinkage breaks in the binder or gamma phase having a

8、than 10 microns. length greater than 10 microns. If a number of failures exceed the requirments of 4.4.2, the lot shall be rejected. * 4.5.4 Mechanical properties,. Delete paragraph in its entirety and substitute: “4.5.4 Mechanical properties. Tensile test blanks conforming to ASTM E8, Figure 6, sha

9、ll be prepared from completed discs except that dimension C may be .630“, length to be outside diameter of sintered disc and a hole .250“ + .O05 diameter may be drilled in each grip section to aid in test. 2 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IH

10、S-,-,-MIL-G-63343 (AR) AMENDMENT 4 These samples shall be free of scoring when subjected to testing at a strain rate no greater than .10 inch per inch per minute as specified in ASTM E8. If any test specimen fails to meet ultimate tensile strength and elongation requirements, it shall be classified

11、defective. If the number of failures exceeds the requirements of 4.4.2, the lot shall be rejected.“ 4.5.5 Penetrant inspection. First sentence, Delete “MIL-1-6866, Table I“ and substitute “MIL-STD-6866“. 6.3 Submission of inspection equipment for design approval. Delete last sentence in its entirety

12、 and substitute: “Submit designs as required to “Commander, US Army Armament, Research, Development and Engineering Center, ATTN: AMSTA-AR-QAA-B, Picatinny Arsenal, NJ 07806-5000.“ 6.4 Informational tests. Delete paragraph in its entirety. The margins of this amendment are marked with an asterisk or

13、 vertical lines to indicate where changes (additions, modifications, corrections, deletions) from the previous amendment were made. This was done as a convenience only and the Government assumes no liability whatsoever for any inaccuracies in this notations. Bidders and contractors are cautioned to

14、evaluate the requirements of this document based on the entire content irrespective of the marginal notations and relationship to the last previous amendment. Custodian: Army-AR Preparing activity: Amy-AR (Project 1330-0408) 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-