ARMY MIL-P-63196 A (3)-1995 POLYURETHANE ELASTOMER BINDER (FOR USE IN AMMUNITION)《(弹药用)聚胺[甲酸乙]酯弹性体粘合剂》.pdf

1、 _ NIL-P-b3LSbA (3) 9999906 1999826 430 MIL-P-63 196A (AR) AMENDMENT 3 16 March 1995 SUPERSEDING AMENDMENT 2 26 August 1992 MILITARY SPECIFICATION POLYURETHANE ELASTOMER BINDER (For Use in Ammunition) This Amendment forms a part of Military Specification MIL-P- 63196A (AR) dated 27 May 1980 and is a

2、pproved for use by the U.S. Army Armament Research, Development and Engineering Center and is available for use by all Departments and Agencies of the Department of Defense. PAGE 1 1.1 Change “two“ to “three“. Add “Type III: Polyurethane with Talc“. 2.1 Delete: IIMIL-H-48358 (AR) Amendment 2, 8 Apri

3、l 1988 HMX/Resin Explosive Composition LX-14-0 (For use in ammunition)“. PAGE 2 3.1 Delete in its entirety and substitute: “3.1 Phvsical form. The polyurethane elastomer shall be supplied in granular, flake, or pelletized form. Type I shall be dusted with approximately 0.1% of calcium stearate (JAN-

4、C- 362), Type II with approximately 0.1% of commercial talc (MIL- T-50036), and Type III with approximately 0.5% of commercial talc (MIL-T-50036) to facilitate handling. Type III may also contain up to 0.02% Treadlube which is a potassium soap of coconut oil. The certificate of compliance furnished

5、with the shipment shall certify which dusting agent has been used. For Type III orders the concentration of the Treadlube residue shall be provided. I PAGE 3 3.1.2 Viscosity: Delete in its entirety and substitute the following: AMSC N/A 1 of 3 FSC 6810 IBJTI(JN STATEMENT distribution is unlimited. P

6、rovided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,- MIL-P-63196A (3) 9999906 1999827 377 MIL-P-63 19 6 (AR) AMENDMENT 3 “3.1.2 Viscos ity. Solution viscosity of the polyurethane elastomer shall be between 180 and 900 centipoises when tested as described

7、in 4.5.2.“ 3.1.2 Change “180ii to ii225ii. 3.1.3 Phvsical Pronertia: Delete in its entirety. 3.1.7 Add new paragraph: “3.1.7 a. The polyurethane elastomer shall not be older than 90 days from the date of manufacture when shipped.“ PAGE 5 4.5.1.1 Delete in its entirety and substitute: “4.5.1.1 PreDar

8、ation of test so lution. Weigh accurately a 45 f 0.09 gram portion of the sample and transfer this sub- sample into a sealable pint jar (Note: If necessary, cut the sample into pieces approximately 1 cm long). Add 255 i 0.05 grams of methyl ethyl ketone (MEK) to the jar and seal. Dissolve the conten

9、ts of the jar on a roller mixer for a period not to exceed 24 hours. Care should be taken to prevent the loss of the solvent during this procedure. Use this solution for the solubility (4.5.1.2) and viscosity (4.5.2) determinations. II PAGE 6 4.5.2 Change “25 degrees Cl to “23 degrees C“ and add the

10、 following sentence after I . a No. 2 spindle“: calibration of the viscometer shall be verified using 200 and 500 centipoise standards. The viscosity standards shall be prepared in accordance with ASTM D 2162“. “Prior to measuring the samples solution viscosity, the 4.5.3 Correct iioii to Iiofii , “

11、overn“ to “oven“, and IiHqii to IiHgii. 4.5.4 Correct “the“ to “The“. PAGE 8 * 6.5 Change the first sentence from “Materials . B.F. Goodrich Chemical Co.“ to “Materials that have been found satisfactory for use in explosive compositions as a binder: 5702F1, Type II: Estane 5703F1 and Type III: Estan

12、e 5703P manufactured by B.F. Goodrich Chemical Co. Type I: Estane 2 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-63196 (AR) AMENDMENT 3 The margins of this amendment are marked with an asterisk or vertical lines to indicate where change (add

13、itions, modifications, corrections, deletions) from the previous amendment were made. This was done as a convenience only and the Government assumes no liability whatsoever for any inaccuracies in these notations. Bidders and contractors are cautioned to evaluate the requirements of this document based on the entire content irrespective of the marginal notations and relationship to the last previous amendment. Custodian: Army-AR Preparing activity: Army-AR ( Pro ect 6810-AO91 ) 3 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-