1、Comments, suggestions, or questions on this document should be addressed to U.S. Army RDECOM, Tank Automotive Research Development and Engineering Center, ATTN: RDTA-EN/STND/TRANS, MS# 268, 6501 E. 11 Mile Road, Warren, MI 48397-5000 or emailed to DAMI_STANDARDIZATIONconus.army.mil. Since contact in
2、formation can change, you may want to verify the currency of this address information using the ASSIST Online database at http:/assist.daps.dla.mil. AMSC N/A FSC 9150 NOT MEASUREMENT SENSITIVE MIL-PRF-46002D 20 January 2010 SUPERSEDING MIL-PRF-46002C 14 July 2000 PERFORMANCE SPECIFICATION PRESERVATI
3、VE OIL, CONTACT AND VOLATILE CORROSION-INHIBITED This specification is approved for use by all Departments and Agencies of the Department of Defense. 1. SCOPE 1.1 Scope. This specification covers two grades of water-displacing, contact and volatile, corrosion-inhibited preservative oil, known herein
4、after as “oil”, for use in the preservation of material in enclosed systems. 1.2 Classification and part identifying number (PIN). 1.2.1 Grades. The oils are of the following grades, as specified (see 6.2). Grade 1 - light viscosity oil. Grade 2 - medium viscosity oil. 1.2.2 PIN. Oils furnished unde
5、r this performance specification are identified by a PIN consisting of; an “M“ prefix and specification number, a single digit “Dash Number“ which indicates the viscosity grade of the oil. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-46002
6、D 2 M 46002 01 Viscosity Grade (01=Grade 1, 02 = Grade 2) Specification Number Prefix for Military Specification 2. APPLICABLE DOCUMENTS 2.1 General. The documents listed in this section are specified in sections 3 and 4 of this specification. This section does not include documents cited in other s
7、ections of this specification or recommended for additional information or as examples. While every effort has been made to ensure the completeness of this list, document users are cautioned that they must meet all specified requirements in documents cited in sections 3 and 4 of this specification,
8、whether or not they are listed. 2.2 Government documents. 2.2.1 Specifications, standards and handbooks. The following specifications, standards, and handbooks form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those listed cite
9、d in the solicitation or contract (see 6.2). FEDERAL SPECIFICATIONS A-A-51126 - Anodes, Cadmium. A-A-52557 - Fuel Oil, Diesel; for Posts, Camps and Stations. FEDERAL STANDARDS FED-STD-791 - Lubricants, Liquid Fuels, and Related Products; Methods of Testing. DEPARTMENT OF DEFENSE SPECIFICATIONS MIL-P
10、RF-680 - Degreasing Solvent. (Copies of these documents are available online at http:/assist.daps.dla.mil/quicksearch/ or from the Standardization Document Order Desk, 700 Robbins Avenue, Building 4D, Philadelphia, PA 19111-5094) 2.2.2 Other Government documents, drawings, and publications. The foll
11、owing other Government documents, drawings, and publications form a part of this document to the extent Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-46002D 3 specified herein. Unless otherwise specified, the issues of these documents are t
12、hose listed cited in the solicitation or contract (see 6.2). DEPARTMENT OF LABOR (DOL) OSHA 29 CFR 1910.1200 - Hazard Communication Interpretation Regarding Lubricating Oils. (Requests for copies of the Code of Federal Regulations (CFR) Guideline may be obtained from the Superintendent of Documents,
13、 US Government Printing Office, Washington, DC 20402 or www.gpoaccess.gov/cfr/.) NATIONAL TOXICOLOGY PROGRAM Annual Report on Carcinogens. (Requests for copies should be addressed to the Annual Report on Carcinogens, National Toxicology Program, PO Box 12233, Research Triangle Park, NC 27709 or http
14、:/ntp.niehs.hih.gov/.) 2.3 Non-Government publications. The following documents form a part of this document to the extent specified herein. Unless otherwise specified, the issues of these documents are those cited in the solicitation or contract (see 6.2). ASTM INTERNATIONAL ASTM A1008/1008M - Stan
15、dard Specification for Steel, Sheet, Cold-Rolled, Carbon, Structural, High-Strength Low-Alloy, High-Strength Low-Alloy with Improved Formability, Solution Hardened, and Bake Hardenable ASTM B90/90M - Magnesium-Alloy Sheet and Plate (DoD Adopted). ASTM B152/152M - Copper Sheet, Strip, Plate, and Roll
16、ed Bar (DoD Adopted). ASTM B209 - Aluminum and Aluminum-Alloy Sheet and Plate (DoD Adopted). ASTM D91 - Precipitation Number of Lubricating Oils (DoD Adopted). ASTM D92 - Flash and Fire Points by Cleveland Open Cup (DoD Adopted). ASTM D97 - Pour Point of Petroleum Products (DoD Adopted). ASTM D130 -
17、 Detection of Copper Corrosion from Petroleum Products by the Copper Strip Tarnish Test (DoD Adopted). ASTM D445 - Kinematic Viscosity of Transparent and Opaque Liquids (the Calculation of Dynamic Viscosity) (DoD Adopted). Provided by IHSNot for ResaleNo reproduction or networking permitted without
18、license from IHS-,-,-MIL-PRF-46002D 4 ASTM D972 - Evaporation Loss of Lubricating Greases and Oils (DoD Adopted). ASTM D1152 - Methanol (Methyl Alcohol). ASTM D1193 - Reagent Water (DoD Adopted). ASTM D1748 - Rust Protection by Metal Preservatives in the Humidity Cabinet (DoD Adopted). (Application
19、for copies should be addressed to ASTM International, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959 or http:/www.astm.org/.) SOCIETY OF AUTOMOTIVE ENGINEERS (SAE) SAE-AMS 4375 - Sheet and Plate, Magnesium Alloy 3.0 Al 1.0 Zn - 0.20 Mn (AZ 31B-0) Annealed and Recrystallized (DoD Adopted) (A
20、pplication for copies should be addressed to Society of Automotive Engineers, Inc., 400 Commonwealth Drive, Warrendale, PA 15096 or http:/www.sae.org/.) 2.4 Order of precedence. In the event of a conflict between the text of this document and the references cited herein, the text of this document ta
21、kes precedence. Nothing in this document, however, supersedes applicable laws and regulations unless a specific exemption has been obtained. 3. REQUIREMENTS 3.1 First article. When specified (see 6.2), a sample shall be subjected to first article inspection in accordance with 4.1. 3.2 Materials. Unl
22、ess otherwise specified herein, the chemical formula of the oil is the prerogative of the contractor as long as all articles submitted to the Government fully meet the operating, interface, support and ownership, and environmental requirements specified. 3.2.1 Recycled, recovered, or environmentally
23、 preferable materials. Recycled, recovered, or environmentally preferable materials should be used to the maximum extent possible provided that the material meets or exceeds the operational and maintenance requirements, and promotes economically advantageous life cycle costs. 3.3 Operating requireme
24、nts. 3.3.1 Kinematic viscosity. The kinematic viscosity of the oil shall be as specified in Table I (see 4.2.2.1). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-46002D 5 TABLE I. Kinematic viscosity. Kinematic viscosity, centistokes (cSt) G
25、rade 1 Grade 2 100 degrees Celsius (C) minimum. - 8.25 Maximum. - 16.60 40C minimum. 11 83.45 Maximum. - 111.20 -40C minimum. - - Maximum. 10,000 - 3.3.2 Corrosion protection. 3.3.2.1 Corrosion protection (humidity cabinet). The oil shall protect metal to the extent that no more than a combined tota
26、l of three corrosion dots, none of which exceed 1 millimeter (mm) in diameter, occur on the panels (see 4.2.2.2.1). 3.3.2.2 Corrosion protection (vapor phase). The oil shall protect metal to the extent that no more than a combined total of three corrosion dots, none of which exceed 1 mm in length, w
27、idth or diameter, occur on the panels (see 4.2.2.2.2). 3.3.2.3 Corrosion protection (vapor phase after evaporation). The oil shall protect metal to the extent that no more than a combined total of three corrosion dots, none of which exceed 1 mm in length, width or diameter, occur on the panels (see
28、4.2.2.2.3). 3.3.3 Acid neutralization. The oil shall protect metal to the extent that no more than a combined total of three corrosion dots, none of which exceed 1 mm in length, width or diameter, occur on the panels (see 4.2.2.3). 3.3.4 Water displacement and water stability. The oil, after storage
29、 in contact with water, shall satisfactorily displace water as evidenced by the absence of rust, mottling, or surface stains on the panels (see 4.2.2.4). 3.4 Interface requirements. 3.4.1 Copper strip corrosion. The oil shall not tarnish the copper strip exceeding the value of 2c on the ASTM D130 Co
30、pper Strip Classification scale (see 4.2.3.1). 3.4.2 Metal protection (immersion). The oil shall not produce corrosion effects as shown by weight gain or loss more than as specified in Table II (see 4.2.3.2). Provided by IHSNot for ResaleNo reproduction or networking permitted without license from I
31、HS-,-,-MIL-PRF-46002D 6 TABLE II. Metal protection requirements. Metal Weight change in milligrams/square centimeter (mg/cm2) Aluminum 0.2 Steel 0.5 Copper 1.0 Magnesium 0.2 Cadmium 0.5 3.4.3 Vapor phase copper protection. The oil shall not tarnish the copper strip exceeding the number 3 rating on t
32、he ASTM D130 Copper Strip Classification scale (see 4.2.3.3). 3.5 Support and ownership requirements. 3.5.1 Precipitation number and hydrocarbon solubility. 3.5.1.1 Solid sediment. The oil shall generate not more than 0.5 milliliters (mL) mean total volume of sediment (see 4.2.4.1.1). 3.5.1.2 Oil se
33、paration. The oil shall not show evidence of stratification or separation of the oil or its additives from the test solution after 24 hours storage at 25 3 degrees Celsius (C) (see 4.2.4.1.2). 3.5.2 Toxicity. The oil shall have no adverse (injurious or damaging) effects on human health when it is us
34、ed as intended (see 6.1). Blenders, formulators, and suppliers shall follow the guidelines of OSHA 29 CFR 1910.1200, the American Conference of Governmental Industrial Hygienists (ACGIH) Threshold Limit Values and Biological Indices, and the most current National Toxicology Programs Annual Report on
35、 Carcinogens (see 4.2.4.2). 3.6 Environmental requirements. 3.6.1 Flash point. The minimum flash point of the oil shall be 115.5C for Grade 1 and 120C for Grade 2 (see 4.2.5.1). 3.6.2 Pour point. The maximum pour point of the oil shall be 45.5C for Grade 1 and -23.5C for Grade 2 (see 4.2.5.2). 3.6.3
36、 Evaporation loss. The maximum mass percent evaporation loss of the oil shall be 25 percent (%) for Grade 1 and 5% for Grade 2 (see 4.2.5.3). 3.6.3.1 Viscosity change after evaporation loss. The viscosity change of the oil at 40C after the evaporation loss shall be not more than a 5% decrease or a 2
37、0% increase (see 4.2.5.3.1). 4. VERIFICATION Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-46002D 7 4.1 First article. When specified (see 6.2), a sample shall be subjected to first article inspection in accordance with 4.1.1. 4.1.1 First a
38、rticle inspection. First article inspection shall consist of tests for all of the requirements specified in section 3 and may be performed in any plant or laboratory approved by the qualifying activity or its designated agent (see 6.4). 4.1.2 First article sample. The first article sample shall be 5
39、 gallons of the oil formulation for which first article approval is sought. 4.2 Verification methods. Acceptable verification methods included in this section are visual inspection, and measurement, sample tests, full-scale demonstration tests, simulation, modeling, engineering evaluation, component
40、 properties analysis, and similarity to previously approved or previously qualified designs. 4.2.1 Verification alternatives. The manufacturer may propose alternative test methods, techniques, or equipment, including the application of statistical process control, tool control, or cost effective sam
41、pling procedures to verify performance. See the contract for alternatives that replace verification methods required by this specification (see 6.2). 4.2.2 Operating requirements verifications. 4.2.2.1 Kinematic viscosity. To determine conformance to 3.3.1, the oil shall be tested in accordance with
42、 ASTM D445, and exhibit a kinematic viscosity within the range specified in table I. 4.2.2.2 Corrosion protection. 4.2.2.2.1 Corrosion protection (humidity cabinet). To determine conformance to 3.3.2.1, the oil shall be tested in accordance with ASTM D1748 for a duration of 300 hours, and shall pass
43、. 4.2.2.2.2 Corrosion protection (vapor phase). 4.2.2.2.2.1 Test panels. Prepare three panels measuring 76 x 51 x 3.2 mm of the same material and cleaned in the same manner as specified for the humidity cabinet test (see 4.2.2.2.1). 4.2.2.2.2.2 Polishing test panels. Polish the unnumbered side of th
44、e test panels to a surface finish of 380 130 nanometers using a 240-grit aluminum oxide or silicon carbide abrasive, with either cloth or paper backing. Do not use “wet or dry”, waterproof, or iron oxide abrasive. After abrading, clean the panels immediately, using the following procedure: a. Wipe t
45、he abraded faces of the panels with clean surgical gauze to remove superficial dust. Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-PRF-46002D 8 b. Remove the remaining residue and contamination by holding the panels in a rack at 20 degrees from
46、 the vertical and spraying downward with naphtha. Flush the surfaces progressively downward, spraying first the test surfaces, then the backs of the panels and finally the test surfaces again. c. Heat the panels in boiling naphtha for 5 to 10 minutes. d. Rinse the panels in boiling anhydrous methano
47、l defined by ASTM D1152. e. Inspect the panels carefully under a bright light to determine if any surface residues remain. f. Desiccate the panels at 25 3C and place in use within 2 hours. NOTE: Naphtha, hexane and methanol are flammable and toxic. Do not heat either solvent with an open flame. Avoi
48、d contact with skin and inhalation of vapor. Perform procedures under b, c, and d in an efficient laboratory hood. 4.2.2.2.2.3 Test apparatus. The test apparatus shall consist of a screw top, wide-mouth jar, 100 mm in height and 90 mm in diameter, as illustrated in figure 1. Bend a length of stainle
49、ss steel or Monel (TM) metal into simple framework on which the steel panel can be suspended in a vertical position on one side of the jar. Remove any cardboard seal in the jar lid and replace it with several pieces of filter paper to seal the jar. Use fresh filter papers for each test. The filter paper shall be of high quality and acid-free. 4.2.2.2.2.4