ASD-STAN PREN 2116-2007 Aerospace series Aluminium alloy 2017A T42 Wire for solid rivets D less than or equal to 10 mm (Edition P 1)《航空航天系列 D≤10mm的铝合金2017A T42制实心铆钉用线材 第1版》.pdf

1、ASD STANDARD NORME ASD ASD NORM prEN 2116 Edition P 1 October 2007 PUBLISHED BY THE AEROSPACE AND DEFENCE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONAvenue de Tervuren, 270 - B-1150 Brussels - Tel. + 32 2 775 8126 - Fax. + 32 2 763 3565 - www.asd-stan.orgICS: Descriptors: ENGLISH VERSION Aero

2、space series Aluminium alloy 2017A T42 Wire for solid rivets D 10 mm Srie arospatiale Alliage daluminium 2017A T42 Fils pour rivets pleins D 10 mm Luft- und Raumfahrt Aluminiumlegierung 2017A T42 Nietdrhte fr Vollniete D 10 mm This “Aerospace Series“ Prestandard has been drawn up under the responsib

3、ility of ASD-STAN (The AeroSpace and Defence Industries Association of Europe - Standardization). It is published for the needs of the European Aerospace Industry. It has been technically approved by the experts of the concerned Domain following member comments. Subsequent to the publication of this

4、 Prestandard, the technical content shall not be changed to an extent that interchangeability is affected, physically or functionally, without re-identification of the standard. After examination and review by users and formal agreement of ASD-STAN, it will be submitted as a draft European Standard

5、(prEN) to CEN (European Committee for Standardization) for formal vote and transformation to full European Standard (EN). The CEN national members have then to implement the EN at national level by giving the EN the status of a national standard and by withdrawing any national standards conflicting

6、with the EN. Edition approved for publication 31 October 2007 Comments should be sent within six months after the date of publication to ASD-STAN Metallic Material Domain Copyright 2007 by ASD-STAN prEN 2116:20072 Foreword This standard was reviewed by the Domain Technical Coordinator of ASD-STANs M

7、etallic Material Domain. After inquiries and votes carried out in accordance with the rules of ASD-STAN defined in ASD-STANs General Process Manual, this standard has received approval for Publication. prEN 2116:2007 3 Introduction This standard is part of the series of EN metallic material standard

8、s for aerospace applications. The general organization of this series is described in EN 4258. This standard has been prepared in accordance with EN 4500-2. 1 Scope This standard specifies the requirements relating to: Aluminium alloy 2017A-T42 Wire for solid rivets D 10 mm for aerospace application

9、s. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 2032-2, Aerospace se

10、ries Metallic materials Part 2: Coding of metallurgical condition in delivery condition. EN 2070-6, Aerospace series Aluminium and aluminium alloy wrought products Technical specification Part 6: Rivet wire. EN 4258, Aerospace series Metallic materials General organization of standardization Links b

11、etween types of EN standards and their use. EN 4500-2, Aerospace series Metallic materials Rules for drafting and presentation of material standards Part 2: Specific rules for aluminium, aluminium alloys and magnesium alloys. 1)ASTM E 112-96, Standard test methods for determining average grain size.

12、 2)1) Published as ASD Prestandard at the date of publication of this standard.2) Published by: American Society for Testing and Materials (ASTM), 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959 USA. prEN 2116:20074 1 Material designation Aluminium alloy 2017A-T42 Others Element

13、 Si Fe Cu Mn Mg Cr Zn Ti + Zr Each Total Al min. 0,20 3,5 0,40 0,40 2 Chemical composition % amax. 0,8 0,7 4,5 1,0 1,0 0,10 0,25 0,25 0,05 0,15 Base 3 Method of melting 4.1 Form Wire 4.2 Method of production Cold drawn 4.3 Limit dimension(s) mm D 10 5 Technical specification EN 2070-6 Delivery condi

14、tion H14 b6.1 Heat treatment 6.2 Delivery condition code F cUse condition T42 7 Heat treatment See line 29. Characteristics 8.1 Test sample(s) See EN 2070-6. 8.2 Test piece(s) See EN 2070-6. 8.3 Heat treatment Delivery condition (see line 6.1) Use condition T42 (see line 29) 9 Dimensions concerned m

15、m D 10 10 Thickness of cladding on each face % 11 Direction of test piece L 12 Temperature C Ambient 13 Proof stress Rp0,2MPa 14 Strength RmMPa 210 Rm 310 400 15 Elongation A % 16 T Reduction of area Z % 17 Hardness 18 Shear strength RcMPa 260 Rc 290 19 Bending k 20 Impact strength 21 Temperature C

16、22 Time h 23 Stress aMPa 24 Elongation a % 25 Rupture stress RMPa 26 C Elongation at rupture A % 27 Notes (see line 98) a, b, cprEN 2116:2007 5 29 Reference heat treatment Delivery condition + (495 5) C 30 min / WQ 40 C + ageing / t 5 d (120 h) Quench delay 10 34 Grain size 1 ASTM E 112-96 2 5 7 G 5

17、 98 Notes a In accordance with Handbook from Aluminium Association International Alloy Designation and Composition Limits and Wrought Aluminium and Wrought Aluminium Alloys. b Instead H14 it is also acceptable to use either H13 or H15. c See EN 2032-2. 99 Typical use prEN 2116:20076 100 Product qualification Qualification programme to be agreed between manufacturer and purchaser.