ASD-STAN PREN 4293-2012 Aerospace series Aluminium alloy AL-P7175- T73511 Extruded bar and section a or D 150 mm (Edition P 2).pdf

1、ASD-STAN STANDARD NORME ASD-STAN ASD-STAN NORM prEN 4293 Edition P 2 May 2012 PUBLISHED BY THE AEROSPACE AND DEFENCE INDUSTRIES ASSOCIATION OF EUROPE - STANDARDIZATIONAvenue de Tervuren, 270 - B-1150 Brussels - Tel. + 32 2 775 8126 - Fax. + 32 2 775 8131 - www.asd-stan.orgICS: Supersedes Edition P 1

2、 of April 1998 Descriptors: ENGLISH VERSION Aerospace series Aluminium alloy AL-P7175- T73511 Extruded bar and section a or D 150 mm Srie arospatiale Alliage daluminium AL-P7175- T73511 Barres et profils fils a ou D 150 mm Luft- und Raumfahrt Aluminiumlegierung AL-P7175- T73511 Stranggeprete Stangen

3、 und Profile a oder D 150 mm This “Aerospace Series“ Prestandard has been drawn up under the responsibility of ASD-STAN (The AeroSpace and Defence Industries Association of Europe - Standardization). It is published for the needs of the European Aerospace Industry. It has been technically approved b

4、y the experts of the concerned Domain following member comments. Subsequent to the publication of this Prestandard, the technical content shall not be changed to an extent that interchangeability is affected, physically or functionally, without re-identification of the standard. After examination an

5、d review by users and formal agreement of ASD-STAN, it will be submitted as a draft European Standard (prEN) to CEN (European Committee for Standardization) for formal vote and transformation to full European Standard (EN). The CEN national members have then to implement the EN at national level by

6、giving the EN the status of a national standard and by withdrawing any national standards conflicting with the EN. Edition approved for publication 01 May 2012 Comments should be sent within six months after the date of publication to ASD-STAN Metallic Material Domain Copyright 2012 by ASD-STAN prEN

7、 4293:2012 (E) 2 Contents Page Foreword 2 Introduction . 3 1 Scope 4 2 Normative references 4 Foreword This standard was reviewed by the Domain Technical Coordinator of ASD-STANs Metallic Material Domain. After inquiries and votes carried out in accordance with the rules of ASD-STAN defined in ASD-S

8、TANs General Process Manual, this standard has received approval for Publication. prEN 4293:2012 (E) 3 Introduction This standard is part of the series of EN metallic material standards for aerospace applications. The general organization of this series is described in EN 4258. This standard has bee

9、n prepared in accordance with EN 4500-2. prEN 4293:2012 (E) 4 1 Scope This standard specifies the requirements relating to: Aluminium alloy AL-P7175- T73511 Extruded bar and section a or D 150 mm for aerospace applications. 2 Normative references The following referenced documents are indispensable

10、for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 4258, Aerospace series Metallic materials General organization of standardization Links between typ

11、es of EN standards and their use EN 4400-3, Aerospace series Aluminium and aluminium alloy wrought products Technical specification Part 3: Bar and section1)EN 4500-2, Aerospace series Metallic materials Rules for drafting and presentation of material standards Part 2: Specific rules for aluminium,

12、aluminium alloys and magnesium alloys 1) 1) Published as ASD-STAN Prestandard at the date of publication of this standard (www.asd-stan.org). prEN 4293:2012 (E) 5 1 Material designation Aluminium alloy AL-P7175- 2 Chemical composition % Element Si Fe Cu Mn Mg Cr Zn Ti Others Al Each Total min. 1,2 2

13、,1 0,18 5,1 Basemax. 0,15 0,20 2,0 0,10 2,9 0,28 6,1 0,10 0,05 0,15 3 Method of melting 4.1 Form Bar and section 4.2 Method of production Extruded 4.3 Limit dimension(s) mm a or D 150 5 Technical specification EN 4400-3 6.1 Delivery condition T73511 Heat treatment 455 C 475 C / WQ 40 C + 1 % control

14、led stretched 3 % + minor straightening + 105 C 125 C / 6 h t 24 h + 172 C 182 C / 6 h t 16 h 6.2 Delivery condition code U 7 Use condition T73511 Heat treatment Delivery condition Characteristics 8.1 Test sample(s) See EN 4400-3. 8.2 Test piece(s) See EN 4400-3. 8.3 Heat treatment Use condition 9 D

15、imensions concerned mm a or D 10 10 a or D 20 20 a or D 50 50 a or D 75 75 a or D 120 120 a or D 150 10 Thickness of cladding on each face % 11 Direction of test piece L L L L L L 12 T Temperature C Ambient Ambient Ambient Ambient Ambient Ambient 13 Proof stress Rp0,2 MPa 400 420 415 410 390 370 14

16、Strength Rm MPa 470 485 485 475 470 450 15 Elongation A % 8 a 8 8 8 7 7 16 Reduction of area Z % 17 Hardness HB 18 Shear strength Rc MPa 19 Bending k 20 Impact strength 21 C Temperature C 22 Time h 23 Stress aMPa 24 Elongation a % 25 Rupture stress R MPa 26 Elongation at rupture A % 27 Notes (see li

17、ne 98) a prEN 4293:2012 (E) 6 32 Electrical conductivity See EN 4400-3. 3 Measurement on the surface of the sample from which tensile specimens are taken. 7 23 MS/m Acceptable 22 MS/m 23 MS/m Acceptable if Rp0,2L Rp0,2 min. L + 85 MPa or if stress corrosion test acceptable 22 MS/m Non acceptable 39

18、Stress corrosion for qualification See EN 4400-3. 3 a or D 25 mm 6 70 % Rp0,2min. L 7 t 20 days 40 Fracture toughness (K1C) for qualification See EN 4400-3. 7Dimensions (mm) T L MPa m 40 a or D 150 25 44 External defects See EN 4400-3. 51 Macrostructure See EN 4400-3. 61 Internal defects See EN 4400

19、-3. 82 Batch uniformity See EN 4400-3. 7 Electrical conductivity or Hardness HB 140 (typical value) 20 per product 30 per batch 95 Marking inspection See EN 4400-3. 96 Dimensional inspection See EN 4400-3. 98 Notes a Or A50mm 7 %. 99 Typical use prEN 4293:2012 (E) 7 100 Product qualification See EN 4400-3. Qualification programme to be agreed between manufacturer and purchaser.