ASTM A1010 A1010M-2013 Standard Specification for Higher-Strength Martensitic Stainless Steel Plate Sheet and Strip《高强度马氏体不锈钢板材、片材和带材标准规格》.pdf

1、Designation: A1010/A1010M 01 (Reapproved 2009)A1010/A1010M 13Standard Specification forHigher-Strength Martensitic Stainless Steel Plate, Sheet, andStrip1This standard is issued under the fixed designation A1010/A1010M; the number immediately following the designation indicates theyear of original a

2、doption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope Scope*1.1 This specification covers martensitic stainless steels for var

3、ious structural, architectural, pressure vessel, and heat-resistingapplications. The mechanical properties of these steels are customarily, but not necessarily, developed by a suitable heat treatmentgenerally referred to as tempering.1.2 Steel products under this specification are available in two g

4、rades:Grade Yield Strength, min, ksi MPa40 275 40 27550 350 50 35050 345 50 3451.3 The maximum thickness of plates is limited only by the capacity of the composition to meet the specified mechanicalproperty requirements; however, current practice normally limits the maximum thickness of plates furni

5、shed under thisspecification to 12 in. 2550 mm.1.4 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from

6、thetwo systems may result in non-conformance with the standard.2. Referenced Documents2.1 ASTM Standards:2A480/A480M Specification for General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and StripA673/A673M Specification for Sampling Procedure for Impact Testing of

7、Structural SteelE527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)2.2 Other Document:SAE J1086 Recommended Practice for Numbering Metals and Alloys33. General Requirements3.1 The following requirements for orders for material furnished under this specification shall

8、conform to the applicablerequirements of the current edition of Specification A480/A480M.3.1.1 Terminology,3.1.2 Ordering Information,3.1.3 Process,3.1.4 Heat Analysis,3.1.5 Product Analysis,3.1.6 Finish for Sheet,3.1.7 Finish for Strip,3.1.8 Finish for Plates,3.1.9 Test Specimens,1 This specificati

9、on is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.17on Flat-Rolled and Wrought Stainless Steel.Current edition approved May 1, 2009Oct. 1, 2013. Published June 2009October 2013. Originally approved in 20

10、00. Last previous edition approved in 20012009 asA1010/A1010M 01.A1010/A1010M 01 (2009). DOI: 10.1520/A1010_A1010M-01R09.10.1520/A1010_A1010M-13.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsv

11、olume information, refer to the standards Document Summary page on the ASTM website.3 Available from Society of Automotive Engineers (SAE), 400 Commonwealth Dr., Warrendale, PA 15096-0001, http:/www.sae.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM sta

12、ndard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by AS

13、TM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States13.1.10 Number of Tests,3.1.11 Test Methods,3.1.12 Retests and Retreatment,3.

14、1.13 Dimensions and Permissible Variations,3.1.14 Workmanship,3.1.15 Packaging, Marking, and Loading,3.1.16 Inspection,3.1.17 Rejection and Rehearing, and3.1.18 Material Test Report and Certification.4. Chemical Composition4.1 The steel shall conform to the requirements as to chemical composition sp

15、ecified in Table 1, and shall conform to applicablerequirements specified in the current edition of Specification A480/A480M.5. Heat Treatment5.1 The material shall be heat-treated by tempering to meet the requirements of this specification. The tempering temperatureshall not exceed 1400F 760C. Prio

16、r to tempering, the steel shall be in the as-rolled, normalized or quenched condition.6. Mechanical Properties6.1 The material shall conform to the mechanical properties specified in Table 2.7. Keywords7.1 architectural steel; martensitic; plate; stainless steel; steel; structural steel; temperedTAB

17、LE 1 Chemical Composition Requirements, %AUNSDesignationBType Carbon Manganese Phosphorus Sulfur Silicon Chromium Nickel Molybdenum Nitrogen OtherElementsS41003 . . . 0.030 1.50 0.040 0.030 1.00 10.5-12.5 1.50 . . . 0.030 . . .S41003 . . . 0.030 1.50 0.040 0.010 1.00 10.5-12.5 1.50 . . . 0.030 . . .

18、A Maximum, unless range or minimum is indicated.B Designation established in accordance with Practice E527 and SAE J 1086.A1010/A1010M 132SUPPLEMENTARY REQUIREMENTSSupplementary requirements shall not apply unless specified on the purchase order. Requirementsother than those shown in this section ma

19、y be specified subject to agreement between the supplier andthe purchaser. The following supplementary requirements are suitable for use with this specification.S1. Charpy V-Notch Impact TestS1.1 Charpy V-notch impact tests shall be conducted in accordance with Specification A673/A673M.S1.2 The freq

20、uency of testing, the test temperature to be used, and the absorbed energy requirements shall be as specified onthe order.S2. Ultrasonic ExaminationS2.1 The material shall be ultrasonically examined in accordance with the requirements specified on the order.SUMMARY OF CHANGESCommittee A01 has identi

21、fied the location of selected changes to this standard since the last issue(A1010/A1010M 01R09) that may impact the use of this standard. (Approved Oct. 1, 2013.)(1) Revised all references to 350 Mpa to 345 Mpa.(2) Revised paragraph 1.3, changed normal maximum thickness from 1 in. 25 mm to 2 in. 50

22、mm.(3) Changed sulfur in Table 1 to 0 .010.(4) Deleted hardness from the mechanical properties Table 2.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that d

23、etermination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved

24、 or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel t

25、hat your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprint

26、s (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM

27、website (www.astm.org/COPYRIGHT/).TABLE 2 Mechanical Test RequirementsGrade YieldStrength,min, ksiMPaTensileStrength,min, ksiMPaElongation in2 in. 50 mm,min, %BrinellHardness,maxCold Blend40 40 275 66 455 18 223 not required50 50 350 70 485 18 223 not requiredTABLE 2 Mechanical Test RequirementsGrade YieldStrength,min, ksiMPaTensileStrength,min, ksiMPaElongation in2 in. 50 mm,min, %Cold Blend40 40 275 66 455 18 not required50 50 345 70 485 18 not requiredA1010/A1010M 133