ASTM A1031 A1031M-2010 Standard Specification for Steel Sheet and Strip Heavy-Thickness Coils Alloy Drawing Steel and Structural Steel Hot-Rolled《热轧合金钢、拉制钢和结构钢薄板和带材、特厚卷材用标准规范》.pdf

1、Designation: A1031/A1031M 10Standard Specification forSteel, Sheet and Strip, Heavy-Thickness Coils, Alloy,Drawing Steel and Structural Steel, Hot-Rolled1This standard is issued under the fixed designation A1031/A1031M; the number immediately following the designation indicates theyear of original a

2、doption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers hot-rolled, heavy thicknesscoils beyond th

3、e size limits of Specifications A506 and A507.1.2 The product is available in three designations: AlloySteel, Drawing Steel, and Structural Alloy Steel.1.3 Alloy steel is furnished to chemical composition re-quirements and is intended primarily for general or miscella-neous use where bending and mod

4、erate forming is a require-ment.1.4 Drawing steel is produced principally for applicationsinvolving severe cold plastic deformation such as deep drawnor severely formed parts.1.4.1 Drawing steel may be furnished in several conditions,heat treatments, surface finishes, and edges, as specified herein.

5、1.5 Structural steel is furnished to chemical compositionrequirements and to specific mechanical property requirementswhich may include tension tests, hardness tests, or othercommonly accepted mechanical tests.1.5.1 The formability of structural steel decreases withincreasing yield strength or hardn

6、ess. Therefore, product de-sign in relation to the mechanical properties of the grade usedmust be considered.1.6 This material is available only in coils described asfollows:Product Size Limits, Coils OnlyWidth, in. mm Thickness, in. mmStrip Over 8 to 12, incl 0.230 to 1.000, inclOver 200 to 300 Ove

7、r 6.0 to 25Sheet Over 12 0.230 to 1.000, inclOver 300 from 6.0 through 251.7 Sheet and strip in coils of sizes noted in 1.6 are coveredby this specification only with the following provisions:1.7.1 The material is not to be converted into steel plates forstructural or pressure vessel use unless test

8、ed in completeaccordance with the appropriate sections of SpecificationsA6/A6M (plates provided from coils) or A20/A20M (platesproduced from coils). A plate produced in this manner is nolonger governed by this sheet steel specification and since thismaterial is now plate, the appropriate plate stand

9、ard must nowapply.1.7.2 The dimensional tolerances of Specification A635/A635M are applicable to material produced to this specifica-tion.1.7.3 The material is to be fed directly from coils into ablanking press, drawing or forming operation, tube mill, rollingmill, or sheared or slit into blanks for

10、 subsequent drawing orforming.1.8 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may

11、result in non-conformancewith the standard.1.8.1 Within the text the SI units are shown in brackets.2. Referenced Documents2.1 ASTM Standards:2A6/A6M Specification for General Requirements for RolledStructural Steel Bars, Plates, Shapes, and Sheet PilingA20/A20M Specification for General Requirement

12、s forSteel Plates for Pressure VesselsA370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA505 Specification for Steel, Sheet and Strip, Alloy, Hot-Rolled and Cold-Rolled, General Requirements forA506 Specification for Alloy and Structural Alloy Steel,Sheet and Strip, Hot-Rolled

13、 and Cold-RolledA507 Specification for Drawing Alloy Steel, Sheet andStrip, Hot-Rolled and Cold-RolledA635/A635M Specification for Steel, Sheet and Strip,Heavy-Thickness Coils, Hot-Rolled, Alloy, Carbon, Struc-tural, High-Strength Low-Alloy, and High-Strength Low-Alloy with Improved Formability, Gen

14、eral Requirementsfor1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.Current edition approved May 1, 2010. Published June 2010. Originallyapproved in 2004. L

15、ast previous edition approved in 2009 as A1031/A1031M 09.DOI: 10.1520/A1031_A1031M-10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary

16、 page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.E29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specificat

17、ions3. General Requirements for Delivery3.1 Material furnished under this specification shall con-form to the applicable requirements of Specification A505,current edition, unless otherwise provided herein.4. Ordering Information4.1 Orders for material under this specification shall includethe follo

18、wing information, as required, to adequately describethe desired material.4.1.1 ASTM specification number and year of issue,4.1.2 Classification of the material (hot-rolled sheet orhot-rolled strip),4.1.3 Chemical composition (grade),4.1.4 ConditionMaterial in accordance with this specifi-cation is

19、furnished in the hot rolled condition. Pickled (or blastcleaned) must be specified if required. Material ordered aspickled (or blast cleaned) will be oiled unless ordered dry,4.1.5 Heat treatment required, if any,4.1.6 Type of edge must be specified for hot rolled sheetcoils and strip coils, either

20、mill edge or cut edge (sheet), milledge or slit edge (strip),4.1.7 Dimensions (thickness and width of material),NOTE 1Not all producers are capable of meeting all the limitations ofthe thickness tolerance tables in Specification A635/A635M. The pur-chaser should contact the producer regarding possib

21、le limitations prior toplacing an order.TABLE 1 Standard Steels Commonly Produced for Alloy Steel Sheet and StripUNSDesign.SAENo.Chemical Composition Ranges and Limits, % (Heat Analysis)ACMnPSSiBNi Cr Mo V. . . E3310 0.08-0.13 0.45-0.60 0.025 0.025 0.15-0.30 3.25-3.75 1.40-1.75 . . . . . .G40120 401

22、2 0.09-0.14 0.75-1.00 0.025 0.025 0.15-0.30 . . . . . . 0.15-0.25 . . .G41180 4118 0.18-0.23 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.40-0.60 0.08-0.15 . . .G41300 4130 0.280.33 0.400.60 0.025 0.025 0.15-0.30 . . . 0.801.10 0150.25 . . .G41350 4135 0.33-0.38 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.80

23、-1.10 0.15-0.25 . . .G41370 4137 0.35-0.40 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41400 4140 0.380.43 0.751.00 0.025 0.025 0.15-0.30 . . . 0.801.10 0.15-0.25 . . .G41420 4142 0.40-0.45 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41450 4145 0.43-0.48 0.75-

24、1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41470 4147 0.45-0.50 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G41500 4150 0.48-0.53 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.80-1.10 0.15-0.25 . . .G43200 4320 0.17-0.22 0.45-0.65 0.025 0.025 0.15-0.30 1.65-2.00 0.40-0.6

25、0 0.20-0.30 . . .G43400 4340 0.380.43 0.600.80 0.025 0.025 0.15-0.30 1.65-2.00 0.700.90 0.20-0.30 . . .G43406 E4340 0.38-0.43 0.65-0.85 0.025 0.025 0.15-0.30 1.65-2.00 0.70-0.90 0.20-0.30 . . .G45200 4520 0.18-0.23 0.45-0.65 0.025 0.025 0.15-0.30 . . . . . . 0.45-0.60 . . .G46150 4615 0.13-0.18 0.45

26、-0.65 0.025 0.025 0.15-0.30 1.65-2.00 . . . 0.20-0.30 . . .G46200 4620 0.17-0.22 0.45-0.65 0.025 0.025 0.15-0.30 1.65-2.00 . . . 0.20-0.30 . . .G47180 4718 0.16-0.21 0.70-0.90 0.025 0.025 0.15-0.30 0.90-1.20 0.35-0.55 0.30-0.40 . . .G48150 4815 0.13-0.18 0.40-0.60 0.025 0.025 0.15-0.30 3.25-3.75 . .

27、 . 0.20-0.30 . . .G48200 4820 0.18-0.23 0.50-0.70 0.025 0.025 0.15-0.30 3.25-3.75 . . . 0.20-0.30 . . .G50150 5015 0.12-0.17 0.30-0.50 0.025 0.025 0.15-0.30 . . . 0.30-0.50 . . . . . .G50460 5046 0.43-0.50 0.75-1.00 0.025 0.025 0.15-0.30 . . . 0.20-0.35 . . . . . .G51150 5115 0.13-0.18 0.70-0.90 0.0

28、25 0.025 0.15-0.30 . . . 0.70-0.90 . . . . . .G51200 5120 0.170.22 0.700.90 0.025 0.025 0.15-0.30 . . . 0.700.90 . . . . . .G51300 5130 0.28-0.33 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.80-1.10 . . . . . .G5132 5132 0.30-0.35 0.60-0.90 0.025 0.025 0.15-0.30 . . . 0.75-1.00 . . . . . .G51400 5140 0.3

29、80.43 0.700.90 0.025 0.025 0.15-0.30 . . . 0.700.90 . . . . . .G51500 5150 0.480.53 0.700.90 0.025 0.025 0.15-0.30 . . . 0.700.90 . . . . . .G51600 5160 0.550.65 0.751.00 0.025 0.025 0.15-0.30 . . . 0.700.90 . . . . . .G15116 E51100 0.95-1.10 0.25-0.45 0.025 0.025 0.15-0.30 . . . 0.90-1.15 . . . . .

30、 .G15216 E52100 0.95-1.10 0.25-0.45 0.025 0.025 0.15-0.30 . . . 1.30-1.60 . . . . . .G61500 6150 0.48-0.53 0.70-0.90 0.025 0.025 0.15-0.30 . . . 0.80-1.10 . . . 0.15 minG61580 6158 0.550.62 0.701.10 0.025 0.025 0.15-0.30 . . . 0.901.20 . . . 0.100.20G86150 8615 0.130.18 0.700.90 0.025 0.025 0.15-0.3

31、0 0.400.70 0.400.60 0.150.25 . . .G86170 8617 0.15-0.20 0.70-0.90 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86200 8620 0.180.23 0.700.90 0.035 0.035 0.15-0.30 0.40-0.70 0.400.60 0.15.025 . . .G86300 8630 0.28-0.33 0.70-0.90 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86

32、400 8640 0.38-0.43 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86420 8642 0.40-0.45 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86450 8645 0.43-0.48 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86500 8650 0.48-0.53 0.75-1.00 0.02

33、5 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86550 8655 0.50-0.60 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G86600 8660 0.55-0.65 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.15-0.25 . . .G87200 8720 0.18-0.23 0.70-0.90 0.025 0.025 0.15-0.30 0.40-0.70 0.40-

34、0.60 0.20-0.30 . . .G87350 8735 0.33-0.38 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.20-0.30 . . .G87400 8740 0.38-0.43 0.75-1.00 0.025 0.025 0.15-0.30 0.40-0.70 0.40-0.60 0.20-0.30 . . .G92600 9260 0.55-0.65 0.70-1.00 0.025 0.025 1.80-2.20 . . . . . . . . . . . .G92620 9262 0.55-0.65 0.7

35、5-1.00 0.025 0.025 1.80-2.20 . . 0.25-0.40 . . . . . . . . E9310 0.08-0.13 0.45-0.65 0.025 0.025 0.20-0.35 3.30-35.0 1.00-1.40 0.08-0.15 . . .AThe chemical ranges and limits shown are subject to product analysis tolerances. See Specification A505.BOther silicon ranges are available. Consult the prod

36、ucer.A1031/A1031M 1024.1.8 Coil size and weight requirements (must includeinside diameter, ID; outside diameter, OD), and maximumweight,4.1.9 Quantity (weight),4.1.10 Application (part identification and description),4.1.11 Test reports (if required),4.1.12 Cast or heat analysis (if required), and4.

37、1.13 Special requirements (if any).4.1.13.1 When the purchaser requires thickness tolerancesfor38 in. 10 mm minimum edge distance (see SupplementaryRequirement in Specification A635/A635M), this requirementshall be specified in the purchase order or contract.NOTE 2A typical ordering description is a

38、s follows: ASTM A1031:Alloy, hot rolled sheet coils, grade SAE 4118, pickled and oiled, cut edge,0.500 by 40 in. by coil; ID 24 in., OD 72 in. maximum, coil weight 40 000lb maximum; 200 000 lb for roll forming shapes; or, ASTM A1031M:Alloy, hot rolled sheet coils, grade SAE 4118, pickled and oiled,

39、cut edge,10 mm by 900 mm by coil; ID 600 mm, OD 1800 mm, maximum, coilweight 18 000 kg maximum; 90 000 kg for roll forming shapes.5. Manufacture5.1 Heat Treatment:5.1.1 As-rolled,5.1.2 Annealed,5.1.2.1 Spheroidized annealed,(1) Drawing SteelUnless otherwise specified on theorder, drawing steel will

40、be furnished with a spheroidizedannealed heat treatment.(2) If the material is to be heat treated by other than theproducer, the order shall so state. The material may be orderedin the as-rolled condition, in such cases.5.1.2.2 Normalized, or5.1.2.3 Normalized-and-tempered.6. Chemical Requirements6.

41、1 The heat analysis of the steel shall conform to therequirements for the grade specified on the order.6.2 Standard Alloy Steel grades listed in Table 1 are thosecommonly produced for alloy steel sheet and strip.6.3 Nonstandard Alloy Steel grades may be specified usingthe ranges and limits shown in

42、Table 2.6.4 Structural Alloy SteelThe grade shall be specified asoutlined in 6.2 or 6.3. However, since different mechanicalproperties may be expected for each of the many chemicalcompositions and conditions (heat treatment) that may bespecified, consideration must be given to these factors inselect

43、ing the chemical composition to be specified.7. Metallurgical Structure7.1 Microstructure:7.1.1 Drawing SteelA minimum of 75 % of the carbidemicrostructure shall be of the globular type for material with anordered thickness of less than or equal to 0.400 in. 10 mm.For material with an ordered thickn

44、ess greater than 0.400 in.10 mm, the percent minimum globular carbide microstructureguarantee shall be by agreement between the purchaser and theproducer.7.1.2 Number of TestsThe number of tests shall be inaccordance with the producers standard quality control pro-cedures.8. Mechanical Requirements8

45、.1 Alloy SteelMechanical tests are not applicable toregular quality alloy steel sheet and strip.8.2 Test specimen preparation and mechanical testing shallbe in accordance with Test Methods and Definitions A370.8.3 Drawing Steel and Structural Alloy Steel:8.3.1 Tension and Hardness Tests:8.3.1.1 Tens

46、ile, Hardness PropertiesWhen tension and/orhardness tests are specified on the order, the test results shallconform to the requirements specified on the order. Yieldstrength, tensile strength, elongation and hardness require-ments may be specified. The properties will vary depending onthe chemical c

47、omposition, condition, and heat treatment. Pro-ducers are frequently consulted as to grade, resultant mechani-cal properties, recommended heat treatment, and other infor-mation needed to establish the property parameters to meet enduse requirements. Rockwell hardness requirements may bespecified, pr

48、oviding the requirements are compatible with theTABLE 2 Heat (Cast) Analysis Ranges for Other than StandardSteel Alloy Sheet and StripElementWhen Maximum ofSpecified Element is, %Range orLimit, %Carbon To 0.55 incl 0.05Over 0.55 to 0.70 incl 0.08Over 0.70 to 0.80 incl 0.10Over 0.80 to 0.95 incl 0.12

49、Over 0.95 to 1.35 incl 0.13Manganese To 0.60 incl 0.20Over 0.60 to 0.90 incl 0.20Over 0.90 to 1.05 incl 0.25Over 1.05 to 1.90 incl 0.30Over 1.90 to 2.10 incl 0.40Phosphorus . 0.025 maxSulfur . 0.025 maxSilicon To 0.15 incl 0.08Over 0.15 to 0.20 incl 0.10Over 0.20 to 0.40 incl 0.15Over 0.40 to 0.60 incl 0.20Over 0.60 to 1.00 incl 0.30Over 1.00 to 2.20 incl 0.40Copper To 0.60 incl 0.20Over 0.60 to 1.50 incl 0.30Over 1.50 to 2.00 incl 0.35Nickel To 0.50 incl 0.20Over 0.50 to 1.50 incl 0.30Over 1.50 to 2.00 incl 0.35Over 2