ASTM A109 A109M-2014 Standard Specification for Steel Strip Carbon &40 0 25 Maximum Percent&41 Cold-Rolled《冷轧碳素钢带标准规格(碳最大百分比0 25)》.pdf

1、Designation: A109/A109M 13A109/A109M 14Standard Specification forSteel, Strip, Carbon (0.25 Maximum Percent), Cold-Rolled1This standard is issued under the fixed designation A109/A109M; the number immediately following the designation indicates the yearof original adoption or, in the case of revisio

2、n, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specificati

3、on covers cold-rolled carbon steel strip in cut lengths or coils, furnished to closer tolerances than cold-rolledcarbon steel sheet, with specific temper, with specific edge or specific finish, and in sizes as follows:Width, in. Thickness, in.Over 12 to 231516 0.300 and underOver 12.5 to 600 mm 7.6

4、mm and under1.2 Cold-rolled strip is produced with a maximum specified carbon not exceeding 0.25 percent.1.3 Strip tolerance products may be available in widths wider than 231516 in. 600 mm by agreement between purchaser andsupplier. However, such products are technically classified as cold rolled s

5、heet. The tolerances, finishes, tempers, edges, andavailable widths and thicknesses differentiate cold rolled strip from the product known as cold rolled sheet which is defined bySpecification A568/A568M and from cold rolled high carbon strip which is defined by Specification A682/A682M.1.4 For the

6、purpose of determining conformance with this specification, values shall be rounded to the nearest unit in the righthand place of figures used in expressing the limiting values in accordance with the rounding method of Practice E29.1.5 The SI portions of the tables contained herein list permissible

7、variations in dimensions and mass (see Note 1) in SI (metric)units. The values listed are not exact conversions of the values listed in the inch-pound tables, but instead are rounded orrationalized values. Conformance to SI tolerances is mandatory when the “M” specification is used.NOTE 1The term we

8、ight is used when inch-pound units are the standard. However, under SI the preferred term is mass.1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in eachsystem may not be exact equivalents; therefore, each system shall be used

9、 independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.1.7 This specification is expressed in both inch-pound units and SI units. However, unless the order specifies the applicable “M”specification designation (SI units), the material shall

10、be furnished to inch-pound units.2. Referenced Documents2.1 ASTM Standards:2A370 Test Methods and Definitions for Mechanical Testing of Steel ProductsA568/A568M Specification for Steel, Sheet, Carbon, Structural, and High-Strength, Low-Alloy, Hot-Rolled and Cold-Rolled,General Requirements forA682/A

11、682M Specification for Steel, Strip, High-Carbon, Cold-Rolled, General Requirements For (Withdrawn 2009)3A700 Practices for Packaging, Marking, and Loading Methods for Steel Products for Shipment (Withdrawn 2014)3A751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsA9

12、41 Terminology Relating to Steel, Stainless Steel, Related Alloys, and FerroalloysE8 Test Methods for Tension Testing of Metallic Materials1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee

13、A01.19on Steel Sheet and Strip.Current edition approved Oct. 1, 2013May 1, 2014. Published October 2013May 2014. Originally approved in 1926. Last previous edition approved in 20082013 asA109/A109M 08.A109/A109M 13. DOI: 10.1520/A0109_A0109M-13.10.1520/A0109_A0109M-14.2 For referencedASTM standards,

14、 visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3 The last approved version of this historical standard is referenced on www.astm.org.This d

15、ocument is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions

16、as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. Uni

17、ted States1E29 Practice for Using Significant Digits in Test Data to Determine Conformance with SpecificationsE430 Test Methods for Measurement of Gloss of High-Gloss Surfaces by Abridged Goniophotometry2.2 Military Standard:MIL-STD-129 Marking for Shipment and Storage42.3 Federal Standard:123 Marki

18、ng for Shipments (Civil Agencies)4183 Continuous Identification Marking of Iron and Steel Products43. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 annealingthe process of heating to and holding at a suitable temperature and then cooling at a suitable rate, for suchpurposes as

19、reducing hardness, facilitating cold working, producing a desired microstructure, or obtaining desired mechanical,physical, or other properties.3.1.1.1 box annealinginvolves annealing in a sealed container under conditions that minimize oxidation. The strip is usuallyheated slowly to a temperature b

20、elow the transformation range, but sometimes above or within it, and is then cooled slowly.3.1.1.2 continuous annealinginvolves heating the strip in continuous strands through a furnace having a controlledatmosphere followed by a controlled cooling.3.1.2 carbon steelthe designation for steel when no

21、 minimum content is specified or required for aluminum, chromium,cobalt, columbium, molybdenum, nickel, titanium, tungsten, vanadium, zirconium or any other element added to obtain a desiredalloying effect; when the specified minimum for copper does not exceed 0.40 % or when the maximum content spec

22、ified for anyof the following elements does not exceed the percentage noted: manganese 1.65, silicon 0.60, or copper 0.60.3.1.2.1 DiscussionIn all carbon steels small quantities of certain residual elements unavoidably retained from raw materials are sometimes foundwhich are not specified or require

23、d, such as copper, nickel, molybdenum, chromium, etc. These elements are considered asincidental and are not normally reported.3.1.3 cold reductionthe process of reducing the thickness of the strip at room temperature. The amount of reduction is greaterthan that used in skin-rolling (see 3.1.7).3.1.

24、4 dead softthe temper of strip produced without definite control of stretcher straining or fluting. It is intended for deepdrawing applications where such surface disturbances are not objectionable.3.1.5 finishthe degree of smoothness or luster of the strip. The production of specific finishes requi

25、res special preparation andcontrol of the roll surfaces employed.3.1.6 normalizingheating to a suitable temperature above the transformation range and then cooling in air to a temperaturesubstantially below the transformation range. In bright normalizing the furnace atmosphere is controlled to preve

26、nt oxidizing ofthe strip surface.3.1.7 skin-rolleda term denoting a relatively light cold rolling operation following annealing. It serves to reduce the tendencyof the steel to flute or stretcher strain during fabrication. It is also used to impart surface finish, or affect hardness or othermechanic

27、al properties, or to improve flatness.3.1.8 temper a designation by number to indicate the hardness as a minimum, as a maximum, or as a range. The tempers areobtained by the selection and control of chemical composition, by amounts of cold reduction, by thermal treatment, and byskin-rolling.3.2 Refe

28、r to Terminology A941 for additional definitions of terms used in this Specification.4. Ordering Information4.1 Orders for material to this specification shall include the following information, as necessary, to describe adequately thedesired product:4.1.1 Quantity,4.1.2 Name of material (cold-rolle

29、d carbon steel strip),4.1.3 Condition (oiled or not oiled),4.1.4 Temper (Section 7),4.1.5 Edge (Section 8),4.1.6 Dimensions (Section 9),4 Available from Standardization Documents Order Desk, DODSSP, Bldg. 4, Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http:/quicksearch.dla.mil/A109/A10

30、9M 1424.1.7 Workmanship, Finish, and Appearance (Section 10),4.1.8 Coil size requirements (15.2),4.1.9 ASTM designation and year of issue,4.1.10 Copper-bearing steel, if required,4.1.11 Application (part identification or description),4.1.12 Cast or heat analysis (request, if required), and4.1.13 Sp

31、ecial requirements, if required.NOTE 2A typical ordering description is as follows: 20 000 lb Cold-Rolled Strip, Oiled, Temper 4, Edge 3, Finish 3, 0.035 by 9 in. by coil, 5000lb max, 16-in. ID ASTM A 109-XX, for Toaster Shells.5. Materials and Manufacture5.1 The steel shall be made by the open-hear

32、th, basic-oxygen, or electric-furnace process.5.2 Cold-rolled carbon steel strip is normally manufactured from continuously cast steel with aluminum used as the deoxidizer.However, some applications are specified as silicon killed. Ingot cast rimmed, capped and semi-killed steels are subject to limi

33、tedavailability.5.3 Cold-rolled carbon steel strip is manufactured from hot-rolled descaled coils by cold reducing to the desired thickness ona single stand mill or on a tandem mill consisting of several single stands in series. Sometimes an anneal is used at someintermediate thickness to facilitate

34、 further cold reduction or to obtain desired temper and mechanical properties in the finished strip.An anneal and skin pass is typically used as the final step for Temper 4 and 5.6. Chemical Composition6.1 Heat Analysis An analysis for each heat of steel shall be made by the manufacturer to determin

35、e the percentage ofelements shown in Table 1. This analysis shall conform to the requirements shown in Table 1. When requested, heat analysis shallbe reported to purchaser or his representative.6.2 Product, Check, or Verification Analysis may be made by the purchaser on the finished material.6.2.1 C

36、apped or rimmed steels are not technologically suited to product analysis due to the nonuniform character of theirchemical composition and therefore, the tolerances in Table 2 do not apply. Product analysis is appropriate on these types of steelonly when misapplication is apparent or for copper when

37、 copper steel is specified.6.2.2 For steels other than rimmed or capped, when product analysis is made by the purchaser, the chemical analysis shall notvary from the limits specified by more than the amounts in Table 2. The several determinations of any element shall not vary bothabove and below the

38、 specified range.6.3 For referee purposes, if required, Test Methods, Practices, and Terminology A751 shall be used.6.4 For applications where cold-rolled strip is to be welded, care must be exercised in selection of chemical composition, as wellas mechanical properties, for compatibility with the w

39、elding process and its effect on altering the properties.7. Temper and Bend Test Requirement7.1 Cold-rolled carbon strip specified to temper numbers shall conform to the Rockwell hardness requirements shown in Table3.7.1.1 When a temper number is not specified, Rockwell hardness requirements are est

40、ablished by agreement.7.2 It is recommended that hardness values be specified in the same scale as that which will be used in testing the strip.7.3 Bend tests shall be conducted at room temperature and test specimens shall be capable of being bent to the requirementsshown in Table 4.7.4 All mechanic

41、al tests are to be conducted in accordance with Test Methods and Definitions A370.8. Edge8.1 The desired edge number shall be specified as follows:8.1.1 Number 1 Edge is a prepared edge of a specified contour (round or square), which is produced when a very accurate widthis required or when an edge

42、condition suitable for electroplating is required, or both.8.1.2 Number 2 Edge is a natural mill edge carried through the cold rolling from the hot-rolled strip without additionalprocessing of the edge.8.1.3 Number 3 Edge is an approximately square edge, produced by slitting, on which the burr is no

43、t eliminated. Normal coilingor piling does not necessarily provide a definite positioning of the slitting burr.8.1.4 Number 4 Edge is a rounded edge produced by edge rolling either the natural edge of hot-rolled strip or slit-edge strip.This edge is produced when the width tolerance and edge conditi

44、on are not as exacting as for No. 1 edge.8.1.5 Number 5 Edge is an approximately square edge produced from slit-edge material on which the burr is eliminated usuallyby rolling or filing.A109/A109M 1438.1.6 Number 6 Edge is a square edge produced by edge rolling the natural edge of hot-rolled strip o

45、r slit-edge strip. This edgeis produced when the width tolerance and edge condition are not as exacting as for No. 1 edge.8.1.7 Skived Edges are custom shaped edges produced by mechanical edge shaving with special tooling.TABLE 1 Heat Analysis AComposition Wt %Element Temper No.1, 2, 3 Temper No.4,

46、5Carbon, max 0.25 0.15Manganese, max 0.90 0.60Phosphorous, max 0.025 0.025Sulfur, max 0.025 0.025SiliconA . . . . . .AluminumA,B . . . . . .Copper, when copper steel isspecified, min0.20 0.20Copper, maxC 0.20 0.20CopperC 0.20 0.20Nickel, maxC 0.20 0.20Nickel, maxD 0.20 0.20Chromium, maxC, D 0.15 0.1

47、5Chromium, maxD, E 0.15 0.15Molybdenum, maxC 0.06 0.06Molybdenum, maxD 0.06 0.06VanadiumE . . . . . .VanadiumF . . . . . .ColumbiumE . . . . . .ColumbiumF . . . . . .TitaniumE . . . . . .TitaniumF . . . . . .A Where an ellipsis (. . .) appears in this table, there is no requirement, but theanalysis

48、shall be reported unless otherwise specified in this specification.B The analysis shall be reported. When killed steel is specified and aluminum is thedeoxidizing element, the minimum is 0.02, and the analysis shall be reported.C When copper steel is specified, the copper limit specified is a minimu

49、mrequirement. When copper steel is not specified, the copper limit is a maximumrequirement.D The sum of copper, nickel, chromium, and molybdenum shall not exceed 0.50 %on heat analysis. When one or more of these elements is specified, the sum doesnot apply; in which case, only the individual limits on the remaining elements willapply.E Chromium is permitted, at the producers option, to 0.25 % maximum when thecarbon is less than or equal to 0.05 %. In such case, the limit on the sum of the fourelements in Footnote CD does not apply.F Reporting shall be req