ASTM A213 A213M-2011a Standard Specification for Seamless Ferritic and Austenitic Alloy-Steel Boiler Superheater and Heat-Exchanger Tubes《铁素体和奥氏体无缝合金钢锅炉 过热器和换热管标准规格》.pdf

1、Designation: A213/A213M 11aUsed in USDOE-NE standardsStandard Specification forSeamless Ferritic and Austenitic Alloy-Steel Boiler,Superheater, and Heat-Exchanger Tubes1This standard is issued under the fixed designation A213/A213M; the number immediately following the designation indicates the year

2、of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Departmen

3、t of Defense.1. Scope*1.1 This specification2covers seamless ferritic and auste-nitic steel boiler, superheater, and heat-exchanger tubes, des-ignated Grades T5, TP304, etc. These steels are listed in Tables1 and 2.1.2 Grades containing the letter, H, in their designation,have requirements different

4、 from those of similar grades notcontaining the letter, H. These different requirements providehigher creep-rupture strength than normally achievable insimilar grades without these different requirements.1.3 The tubing sizes and thicknesses usually furnished tothis specification are18 in. 3.2 mm in

5、inside diameter to 5 in.127 mm in outside diameter and 0.015 to 0.500 in. 0.4 to12.7 mm, inclusive, in minimum wall thickness or, if specifiedin the order, average wall thickness. Tubing having otherdiameters may be furnished, provided such tubes comply withall other requirements of this specificati

6、on.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem may not be exact equivalents; therefore, each systemshall be used independently of the other. Combining values

7、from the two systems may result in non-conformance with thestandard. The inch-pound units shall apply unless the “M”designation of this specification is specified in the order.2. Referenced Documents2.1 ASTM Standards:3A262 Practices for Detecting Susceptibility to IntergranularAttack in Austenitic

8、Stainless SteelsA941 Terminology Relating to Steel, Stainless Steel, Re-lated Alloys, and FerroalloysA1016/A1016M Specification for General Requirementsfor Ferritic Alloy Steel, Austenitic Alloy Steel, and Stain-less Steel TubesE112 Test Methods for Determining Average Grain Size2.2 AWS Specificatio

9、ns4A5.5/A5.5M Specification for Low-Alloy Steel Electrodesfor Shielded Metal Arc WeldingA5.23/A5.23M Specification for Low-Alloy Steel Elec-trodes and Fluxes for Submerged Arc WeldingA5.28/A5.28M Specification for Low-Alloy Steel Elec-trodes for Gas Shielded Arc WeldingA5.29/A5.29M Low-Alloy Steel E

10、lectrodes for Flux CoredArc Welding3. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication, refer to Terminology A941.4. Ordering Information4.1 It shall be the responsibility of the purchaser to specifyall requirements that are necessary for products under thisspecificatio

11、n. Such requirements to be considered include, butare not limited to, the following:4.1.1 Quantity (feet, metres, or number of lengths),4.1.2 Name of material (seamless tubes),4.1.3 Grade (Tables 1 and 2),4.1.4 Condition (hot finished or cold finished),4.1.5 Controlled structural characteristics (se

12、e 6.3),4.1.6 Size (outside diameter and minimum wall thickness,unless average wall thickness is specified),4.1.7 Length (specific or random),4.1.8 Hydrostatic Test or Nondestructive Electric Test (see10.1),4.1.9 Specification designation and year of issue,4.1.10 Increased sulfur (for machinability,

13、see Note B, Table1, and 16.3), and1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.10 on Stainless and Alloy Steel Tubular Products.Current edition approved Oct. 1, 2011. Published Nove

14、mber 2011. Originallyapproved in 1939. Last previous edition approved in 2011 as A213/A213M11.DOI: 10.1520/A0213_A0213M-11a.2For ASME Boiler and Pressure Vessel Code applications see related Specifi-cation SA-213 in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.

15、astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Available from American Welding Society (AWS), 550 NW LeJeune Rd.,Miami, FL 33126, http:/www.aws.org.1*A Summary of Chan

16、ges section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.TABLE 1 Chemical Composition Limits, %A, for Low Alloy SteelGradeUNSDesignationComposition, %Carbon Manga-nesePhospho-rusSul-furSilicon Ni

17、ckel Chromium Molybdenum Vana-diumBoron Niobium Nitrogen Aluminum Tungsten OtherElementsT2 K11547 0.100.20 0.300.61 0.025 0.025B0.100.30 . 0.500.81 0.440.65 . . . . . . .T5 K41545 0.15 0.300.60 0.025 0.025 0.50 . 4.006.00 0.450.65 . . . . . . .T5b K51545 0.15 0.300.60 0.025 0.025 1.002.00 . 4.006.00

18、 0.450.65 . . . . . . .T5c K41245 0.12 0.300.60 0.025 0.025 0.50 . 4.006.00 0.450.65 . . . . . . Ti4xC0.70T9 K90941 0.15 0.300.60 0.025 0.025 0.251.00 . 8.0010.00 0.901.10 . . . . . . .T11 K11597 0.050.15 0.300.60 0.025 0.025 0.501.00 . 1.001.50 0.440.65 . . . . . . .T12 K11562 0.050.15 0.300.61 0.0

19、25 0.025B0.50 . 0.801.25 0.440.65 . . . . . . .T17 K12047 0.150.25 0.300.61 0.025 0.025 0.150.35 . 0.801.25 . 0.15 . . . . . .T21 K31545 0.050.15 0.300.60 0.025 0.025 0.501.00 . 2.653.35 0.801.06 . . . . . . .T22 K21590 0.050.15 0.300.60 0.025 0.025 0.50 . 1.902.60 0.871.13 . . . . . . .T23 K40712 0

20、040.10 0.100.60 0.030 0.010 0.50 0.40 1.902.60 0.050.30 0.200.30 0.00100.0060.020.08 0.015 0.030 1.451.75 Ti0.0050.060Ti/N $3.5CT24 K30736 0.050.10 0.300.70 0.020 0.010 0.150.45 . 2.202.60 0.901.10 0.200.30 0.00150.007. 0.012 0.02 . Ti0.060.10T36 K21001 0.100.17 0.801.20 0.030 0.025 0.250.50 1.001.

21、30 0.30 0.250.50 0.02 . 0.0150.045 0.02 0.050 . Cu0.500.80T91 K90901 0.070.14 0.300.60 0.020 0.010 0.200.50 0.40 8.09.5 0.851.05 0.180.25 . 0.060.10 0.0300.0700.02 . Ti 0.01Zr 0.01T92 K92460 0.070.13 0.300.60 0.020 0.010 0.50 0.40 8.59.5 0.300.60 0.150.25 0.0010.0060.040.09 0.0300.0700.02 1.52.00 Ti

22、 0.01Zr 0.01T122 K91271 0.070.14 0.70 0.020 0.010 0.50 0.50 10.011.5 0.250.60 0.150.30 0.00050.0050.040.10 0.0400.1000.02 1.502.50 Cu0.301.70Ti 0.01Zr 0.01T911 K91061 0.090.13 0.300.60 0.020 0.010 0.100.50 0.40 8.59.5 0.901.10 0.180.25 0.00030.0060.060.10 0.0400.0900.02 0.901.10 Ti 0.01Zr 0.01AMaxim

23、um, unless range or minimum is indicated. Where ellipses (.) appear in this table, there is no requirement, and analysis for the element need not be determined or reported.BIt is permissible to order T2 and T12 with a sulfur content of 0.045 max. See 16.3.CAlternatively, in lieu of this ratio minimu

24、m, the material shall have a minimum hardness of 275 HV in the hardened condition, defined as after austenitizing and cooling to room temperature but prior to tempering.Hardness testing shall be performed at mid-thickness of the product. Hardness test frequency shall be two samples of product per he

25、at treatment lot and the hardness testing results shall be reported on the materialtest report.A213/A213M11a24.1.11 Special requirements and any supplementary require-ments selected.5. General Requirements5.1 Product furnished to this specification shall conform tothe requirements of Specification A

26、1016/A1016M, includingany supplementary requirements that are indicated in thepurchase order. Failure to comply with the general require-ments of Specification A1016/A1016M constitutes nonconfor-mance with this specification. In case of conflict between therequirements of this specification and Spec

27、ification A1016/A1016M, this specification shall prevail.6. Materials and Manufacture6.1 Manufacture and ConditionTubes shall be made bythe seamless process and shall be either hot finished or coldfinished, as specified. Grade TP347HFG shall be cold finished.6.2 Heat Treatment:6.2.1 Ferritic Alloy a

28、nd Ferritic Stainless SteelsThe fer-ritic alloy and ferritic stainless steels shall be reheated for heattreatment in accordance with the requirements of Table 3. Heattreatment shall be carried out separately and in addition toheating for hot forming.6.2.2 Austenitic Stainless SteelsAll austenitic tu

29、bes shallbe furnished in the heat-treated condition, and shall be heattreated in accordance with the requirements of Table 3.Alternatively, immediately after hot forming, while the tem-perature of the tubes is not less than the minimum solutiontreatment temperature specified in Table 3, tubes may be

30、individually quenched in water or rapidly cooled by othermeans (direct quenched).6.3 If any controlled structural characteristics are required,these shall be so specified in the order as to be a guide as to themost suitable heat treatment.A213/A213M 11a3TABLE 2 Chemical Composition Limits, %A, for A

31、ustenitic and Ferritic Stainless SteelGradeUNSDesignationCompositionCarbonManga-nesePhospho-rusSulfur Silicon Chromium Nickel Molybdenum NitrogenBNiobium TitaniumOtherElementsTP201 S20100 0.15 5.57.5 0.060 0.030 1.00 16.018.0 3.55.5 . 0.25 . . .TP202 S20200 0.15 7.510.0 0.060 0.030 1.00 17.019.0 4.0

32、6.0 . .025 . . .XM-19 S20910 0.06 4.06.0 0.045 0.030 1.00 20.523.5 11.513.5 1.503.00 0.200.40 0.100.30 . V 0.100.30CS21500 0.060.15 5.57.0 0.045 0.030 0.201.00 14.016.0 9.011.0 0.801.20 . 0.751.25 . B 0.0030.009,V 0.150.40CS25700 0.02 2.00 0.025 0.010 6.58.0 8.011.5 22.025.0 0.50 . . . .TP304 S30400

33、 0.08 2.00 0.045 0.030 1.00 18.020.0 8.011.0 . . . . .TP304L S30403 0.035D2.00 0.045 0.030 1.00 18.020.0 8.012.0 . . . . .TP304H S30409 0.040.10 2.00 0.045 0.030 1.00 18.020.0 8.011.0 . . . . .CS30432 0.070.13 1.00 0.040 0.010 0.30 17.019.0 7.510.5 . 0.050.12 0.300.60 . Al 0.0030.030,B 0.0010.010,Cu

34、 2.53.5CS30434 0.070.14 2.00 0.040 0.010 1.00 17.519.5 9.012.0 . . 0.100.40E0.100.25EB 0.0010.004Cu 2.503.50TP304N S30451 0.08 2.00 0.045 0.030 1.00 18.020.0 8.011.0 . 0.100.16 . . .TP304LN S30453 0.035D2.00 0.045 0.030 1.00 18.020.0 8.011.0 . 0.100.16 . . .CS30615 0.0160.24 2.00 0.030 0.030 3.24.0

35、17.019.5 13.516.0 . . . . Al 0.81.5CS30815 0.050.10 0.80 0.040 0.030 1.402.00 20.022.0 10.012.0 . 0.140.20 . . Ce 0.030.08TP309S S30908 0.08 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . .TP309H S30909 0.040.10 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . .TP309LMoN S30925 0.025 2.00 0.040 0.03

36、0 0.70 23.026.0 13.016.0 0.51.2 0.250.40 . . .TP309Cb S30940 0.08 2.00 0.045 0.030 1.00 22.024.0 12.016.0 . . 10xC1.10 . .TP309HCb S30941 0.040.10 2.00 0.045 0.030 1.00 22.024.0 12.016.0 . . 10xC-1.10 . . S30942 0.030.10 2.00 0.040 0.030 1.00 21.023.0 14.516.5 0.100.20 0.500.80 B=0.0010.005CS31002 0

37、02 2.00 0.020 0.015 0.15 24.026.0 19.022.0 0.10 0.10 . . .TP310S S31008 0.08 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . .TP310H S31009 0.040.10 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . . . .TP310MoCbN S31025 0.10 1.50 0.030 0.030 1.00 19.523.0 23.026.0 1.02.0 0.100.25 0.100.40 0.20 B 0.0020

38、010S31035 0.040.10 0.60 0.030 0.015 0.40 21.523.5 23.526.5 . 0.150.30 0.300.60 . W 2.04.0Co 1.02.0Cu 2.03.5B 0.0020.008TP310Cb S31040 0.08 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . 10xC-1.10 . .TP310HCb S31041 0.040.10 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . . 10xC-1.10 . .TP310HCbN S31042 0.04

39、0.10 2.00 0.045 0.030 1.00 24.026.0 19.022.0 . 0.150.35 0.200.60 . .TP310MoLN S31050 0.025 2.00 0.020 0.030 0.40 24.026.0 21.023.0 2.003.00 0.100.16 . . .CS31060 0.050.10 1.00 0.040 0.030 0.50 22.024.0 10.012.5 . 0.180.25 . . Ce + La0.0250.070B 0.0010.010CS31254 0.020 1.00 0.030 0.010 0.80 19.520.5

40、17.518.5 6.06.5 0.180.22 . . Cu 0.501.00CS31272 0.080.12 1.502.00 0.030 0.015 0.300.70 14.016.0 14.016.0 1.001.40 . . 0.300.60 B 0.0040.008CS31277 0.020 3.00 0.030 0.010 0.50 20.523.0 26.028.0 6.58.0 0.300.40 . . Cu 0.501.50TP316 S31600 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 . . . .A2

41、13/A213M11a4TABLE 2 ContinuedGradeUNSDesignationCompositionCarbonManga-nesePhospho-rusSulfur Silicon Chromium Nickel Molybdenum NitrogenBNiobium TitaniumOtherElementsTP316L S31603 0.035D2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 . . . .TP316H S31609 0.040.10 2.00 0.045 0.030 1.00 16.018.0 11.0

42、14.0 2.003.00 . . . .TP316Ti S31635 0.08 2.00 0.045 0.030 0.75 16.018.0 10.014.0 2.003.00 0.10 . 5X(C+N)0.70.TP316N S31651 0.08 2.00 0.045 0.030 1.00 16.018.0 10.013.0 2.003.00 0.100.16 . . .TP316LN S31653 0.035D2.00 0.045 0.030 1.00 16.018.0 10.013.0 2.003.00 0.100.16 . . .TP317 S31700 0.08 2.00 0.

43、045 0.030 1.00 18.020.0 11.015.0 3.04.0 . . . .TP317L S31703 0.035 2.00 0.045 0.030 1.00 18.020.0 11.015.0 3.04.0 . . . .TP317LM S31725 0.03 2.00 0.045 0.030 1.00 18.020.0 13.517.5 4.05.0 0.20 . . Cu 0.75TP317LMN S31726 0.03 2.00 0.045 0.030 1.00 17.020.0 13.517.5 4.05.0 0.100.20 . . Cu 0.75CS32050

44、0.030 1.50 0.035 0.020 1.00 22.024.0 20.023.0 6.06.8 0.210.32 . . Cu 0.40TP321 S32100 0.08 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . 5(C + N)0.70.TP321H S32109 0.040.10 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . 4(C + N)0.70.CS32615 0.07 2.00 0.045 0.030 4.86.0 16.519.5 19.022.0 0.301.50 . . .

45、Cu 1.502.50CS33228 0.040.08 1.00 0.020 0.015 0.30 26.028.0 31.033.0 . . 0.601.00 . Ce 0.050.10,Al 0.025CS34565 0.030 5.07.0 0.030 0.010 1.00 23.025.0 16.018.0 4.05.0 0.400.60 0.10 . .TP347 S34700 0.08 2.00 0.045 0.030 1.00 17.020.0 9.013.0 . . 10xC1.10 . .TP347W S34705 0.05 2.00 0.040 0.030 1.00 17.

46、020.0 8.0011.0 . 0.100.25 0.250.50 . V 0.200.50W 1.502.60TP347H S34709 0.040.10 2.00 0.045 0.030 1.00 17.019.0 9.013.0 . . 8xC1.10 . .TP347HFG S34710 0.060.10 2.00 0.045 0.030 1.00 17.019.0 9.013.0 . . 8xC1.10 . .TP347LN S34751 0.0050.020 2.00 0.045 0.030 1.00 17.019.0 9.013.0 . 0.060.10 0.200.50F.

47、TP348 S34800 0.08 2.00 0.045 0.030 1.00 17.019.0 9.013.0 . .G. Co 0.20, Ta0.10TP348H S34809 0.040.10 2.00 0.045 0.030 1.00 17.019.0 9.013.0 . .H. Co 0.20, Ta0.10. S35045 0.060.10 1.50 0.045 0.015 1.00 25.029.0 32.037.0 . . . 0.150.60 Al 0.150.60Cu 0.75XM-15 S38100 0.08 2.00 0.030 0.030 1.502.50 17.

48、019.0 17.518.5 . . . . . S38815 0.030 2.00 0.040 0.020 5.56.5 13.015.0 15.017.0 0.751.50 . . . Cu 0.751.50Al 0.30800 N08800 0.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . Cu 0.75Al 0.150.60Ti 0.150.60FeI39.5 minA213/A213M11a5TABLE 2 ContinuedGradeUNSDesignationCompositionCarbonManga-nesePhospho-rusSulfur Silicon Chromium Nickel Molybdenum NitrogenBNiobium TitaniumOtherElements800H N08810 0.050.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . Cu 0.75Al 0.150.60Ti 0.150.60FeI39.5 min. N08811 0.060.10 1.50 0.045