ASTM A240 A240M-2009c Standard Specification for Chromium and Chromium-Nickel Stainless Steel Plate Sheet and Strip for Pressure Vessels and for General Applications《通用压力容器的铬和铬-镍不锈.pdf

1、Designation: A240/A240M 09cStandard Specification forChromium and Chromium-Nickel Stainless Steel Plate,Sheet, and Strip for Pressure Vessels and for GeneralApplications1This standard is issued under the fixed designation A240/A240M; the number immediately following the designation indicates the yea

2、rof original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Departme

3、nt of Defense.1. Scope*1.1 This specification2covers chromium, chromium-nickel,and chromium-manganese-nickel stainless steel plate, sheet,and strip for pressure vessels and for general applications.1.2 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard.

4、 The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.3 This specification is expressed in both inch-pound andSI units. However, unless the o

5、rder specifies the applicable“M” specification designation (SI units), the material shall befurnished in inch-pound units.1.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-

6、priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3A370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA480/A480M Specification for General Requirements forFlat-Rolled Stainless an

7、d Heat-Resisting Steel Plate,Sheet, and StripA923 Test Methods for Detecting Detrimental IntermetallicPhase in Duplex Austenitic/Ferritic Stainless SteelsE112 Test Methods for Determining Average Grain SizeE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)2.2 SAE Stan

8、dard:4J 1086 Practice for Numbering Metals and Alloys (UNS)3. General Requirements3.1 The following requirements for orders for materialfurnished under this specification shall conform to the appli-cable requirements of the current edition of SpecificationA480/A480M.3.1.1 Definitions;3.1.2 General r

9、equirements for delivery;3.1.3 Ordering information;3.1.4 Process;3.1.5 Special tests;3.1.6 Heat treatment;3.1.7 Dimensions and permissible variations;3.1.8 Workmanship, finish and appearance;3.1.9 Number of tests/test methods;3.1.10 Specimen preparation;3.1.11 Retreatment;3.1.12 Inspection;3.1.13 R

10、ejection and rehearing;3.1.14 Material test report;3.1.15 Certification; and3.1.16 Packaging, marking, and loading.4. Chemical Composition4.1 The steel shall conform to the requirements as tochemical composition specified in Table 1 and shall conform toapplicable requirements specified in Specificat

11、ion A480/A480M.5. Mechanical Properties5.1 The material shall conform to the mechanical propertiesspecified in Table 2.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.17 on Flat-Rolled

12、 and Wrought Stainless Steel.Current edition approved Nov. 1, 2009. Published December 2009. Originallyapproved in 1940. Last previous edition approved in 2009 as A240/A240M 09b.DOI: 10.1520/A0240_A0240M-09C.2For ASME Boiler and Pressure Vessel Code applications see related Specifi-cation SA-240 in

13、Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.4Available from Society of Automotive

14、 Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 15096-0001, http:/www.sae.org.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.2 When specified by the purchaser

15、, Charpy impact testsshall be performed in accordance with Supplementary Require-ment S1.6. Materials for High-Temperature Service6.1 The austenitic H Types shall conform to an averagegrain size of ASTM No. 7 or coarser as measured by TestMethods E112.6.2 Supplementary Requirement S2 shall be invoke

16、d whennon-H grade austenitic stainless steels are ordered for ASMECode applications for service above 1000F 540C.6.3 Grade S31060, unless otherwise specified in the pur-chase order, shall conform to an average grain size of ASTMNo. 7 or coarser, as measured by Test Methods E112.7. Keywords7.1 chromi

17、um; chromium-nickel stainless steel; chromium-manganese-nickel stainless steel; pressure vesselsA240/A240M 09c2TABLE 1 Chemical Composition Requirements, %AUNSDesignationBTypeCCarbonDManganese Phos-phorusSulfur Silicon Chromium Nickel Molybdenum Nitrogen Copper OtherElementsE,FAustenitic (Chromium-N

18、ickel) (Chromium-Manganese-Nickel)N08020 . . . 0.07 2.00 0.045 0.035 1.00 19.021.0 32.038.0 2.003.00 . . . 3.04.0 Cb 83C min,1.00 maxN08367 . . . 0.030 2.00 0.040 0.030 1.00 20.022.0 23.525.5 6.07.0 0.180.25 0.75 . . .N08700 . . . 0.04 2.00 0.040 0.030 1.00 19.023.0 24.026.0 4.35.0 . . . 0.50 Cb 83C

19、min0.40 maxN08800 800G0.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . . . . . 0.75 FeH39.5 minAl 0.150.60Ti 0.150.60N08810 800HG0.050.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . . . . . 0.75 FeH39.5 minAl 0.150.60Ti 0.150.60N08811 . . . 0.060.10 1.50 0.040 0.015 1.00 19.023.0 30.035.0 . . . . .

20、. 0.75 FeH39.5 minTiI0.150.60AlI0.150.60N08904 904LG0.020 2.00 0.045 0.035 1.00 19.023.0 23.028.0 4.05.0 0.10 1.02.0 . . .N08926 . . . 0.020 2.00 0.030 0.010 0.50 19.021.0 24.026.0 6.07.0 0.150.25 0.51.5 . . .S20100 201 0.15 5.57.5 0.060 0.030 1.00 16.018.0 3.55.5 . . . 0.25 . . . . . .S20103 . . .

21、0.03 5.57.5 0.045 0.030 0.75 16.018.0 3.55.5 . . . 0.25 . . . . . .S20153 . . . 0.03 6.47.5 0.045 0.015 0.75 16.017.5 4.05.0 . . . 0.100.25 1.00 . . .S20161 . . . 0.15 4.06.0 0.040 0.040 3.04.0 15.018.0 4.06.0 . . . 0.080.20 . . . . . .S20200 202 0.15 7.510.0 0.060 0.030 1.00 17.019.0 4.06.0 . . . 0

22、.25 . . . . . .S20400 . . . 0.030 7.09.0 0.040 0.030 1.00 15.017.0 1.503.00 . . . 0.150.30 . . . . . .S20431 . . . 0.12 5.07.0 0.045 0.030 1.00 17.018.0 2.04.0 . . . 0.100.25 1.53.5 . . .S20432 . . . 0.08 3.05.0 0.045 0.030 1.00 17.018.0 4.06.0 . . . 0.050.20 2.003.00 . . .S20433 . . . 0.08 5.57.5 0

23、.045 0.030 1.00 17.018.0 3.55.5 . . . 0.100.25 1.53.5 . . .S20910 XM-19J0.06 4.06.0 0.040 0.030 0.75 20.523.5 11.513.5 1.503.00 0.200.40 . . . Cb 0.100.30V 0.100.30S21400 XM-31J0.12 14.016.0 0.045 0.030 0.301.00 17.018.5 1.00 . . . 0.35 min . . . . . .S21600 XM-17J0.08 7.59.0 0.045 0.030 0.75 17.522

24、.0 5.07.0 2.003.00 0.250.50 . . . . . .S21603 XM-18J0.03 7.59.0 0.045 0.030 0.75 17.522.0 5.07.0 2.003.00 0.250.50 . . . . . .S21640 . . . 0.08 3.56.5 0.060 0.030 1.00 17.519.5 4.06.5 0.502.00 0.080.30 . . . Cb 0.101.00S21800 . . . 0.10 7.09.0 0.060 0.030 3.54.5 16.018.0 8.09.0 . . . 0.080.18 . . .

25、. . .S24000 XM-29J0.08 11.514.5 0.060 0.030 0.75 17.019.0 2.33.7 . . . 0.200.40 . . . . . .S30100 301 0.15 2.00 0.045 0.030 1.00 16.018.0 6.08.0 . . . 0.10 . . . . . .S30103 301LG0.03 2.00 0.045 0.030 1.00 16.018.0 6.08.0 . . . 0.20 . . . . . .S30153 301LNG0.03 2.00 0.045 0.030 1.00 16.018.0 6.08.0

26、. . . 0.070.20 . . . . . .S30200 302 0.15 2.00 0.045 0.030 0.75 17.019.0 8.010.0 . . . 0.10 . . . . . .S30400 304 0.07 2.00 0.045 0.030 0.75 17.519.5 8.010.5 . . . 0.10 . . . . . .S30403 304L 0.030 2.00 0.045 0.030 0.75 17.519.5 8.012.0 . . . 0.10 . . . . . .S30409 304H 0.040.10 2.00 0.045 0.030 0.7

27、5 18.020.0 8.010.5 . . . . . . . . . . . .S30415 . . . 0.040.06 0.80 0.045 0.030 1.002.00 18.019.0 9.010.0 . . . 0.120.18 . . . Ce 0.030.08S30451 304N 0.08 2.00 0.045 0.030 0.75 18.020.0 8.010.5 . . . 0.100.16 . . . . . .S30452 XM-21J0.08 2.00 0.045 0.030 0.75 18.020.0 8.010.5 . . . 0.160.30 . . . .

28、 . .S30453 304LN 0.030 2.00 0.045 0.030 0.75 18.020.0 8.012.0 . . . 0.100.16 . . . . . .S30500 305 0.12 2.00 0.045 0.030 0.75 17.019.0 10.513.0 . . . . . . . . . . . .S30530 . . . 0.08 2.00 0.045 0.030 0.502.50 17.020.5 8.511.5 0.751.50 . . . 0.753.5 . . .S30600 . . . 0.018 2.00 0.020 0.020 3.74.3 1

29、7.018.5 14.015.5 0.20 . . . 0.50 . . .S30601 . . . 0.015 0.500.80 0.030 0.013 5.05.6 17.018.0 17.018.0 0.20 0.05 0.35 . . .S30615 . . . 0.160.24 2.00 0.030 0.030 3.24.0 17.019.5 13.516.0 . . . . . . . . . Al 0.801.50S30815 . . . 0.050.10 0.80 0.040 0.030 1.402.00 20.022.0 10.012.0 . . . 0.140.20 . .

30、 . Ce 0.030.08S30908 309S 0.08 2.00 0.045 0.030 0.75 22.024.0 12.015.0 . . . . . . . . . . . .S30909 309HG0.040.10 2.00 0.045 0.030 0.75 22.024.0 12.015.0 . . . . . . . . . . . .S30940 309CbG0.08 2.00 0.045 0.030 0.75 22.024.0 12.016.0 . . . . . . . . . Cb 103C min,1.10 maxA240/A240M09c3TABLE 1 Cont

31、inuedUNSDesignationBTypeCCarbonDManganese Phos-phorusSulfur Silicon Chromium Nickel Molybdenum Nitrogen Copper OtherElementsE,FS30941 309HCbG0.040.10 2.00 0.045 0.030 0.75 22.024.0 12.016.0 . . . . . . . . . Cb 103C min,1.10 maxS31008 310S 0.08 2.00 0.045 0.030 1.50 24.026.0 19.022.0 . . . . . . . .

32、 . . . .S31009 310HG0.040.10 2.00 0.045 0.030 0.75 24.026.0 19.022.0 . . . . . . . . . . . .S31040 310CbG0.08 2.00 0.045 0.030 1.50 24.026.0 19.022.0 . . . . . . . . . Cb 103C min,1.10 maxS31041 310HCbG0.040.10 2.00 0.045 0.030 0.75 24.026.0 19.022.0 . . . . . . . . . Cb 103C min,1.10 maxS31050 310

33、MoLNG0.020 2.00 0.030 0.010 0.50 24.026.0 20.523.5 1.602.60 0.090.15 . . . . . .S31060 . . . 0.050.10 1.00 0.040 0.030 0.50 22.024.0 10.012.5 . . . 0.180.25 . . . Ce + La0.0250.070B 0.0010.010S31254 . . . 0.020 1.00 0.030 0.010 0.80 19.520.5 17.518.5 6.06.5 0.180.22 0.501.00 . . .S31266 . . . 0.030

34、2.04.0 0.035 0.020 1.00 23.025.0 21.024.0 5.26.2 0.350.60 1.002.50 W 1.502.50S31277 . . . 0.020 3.00 0.030 0.010 0.50 20.523.0 26.028.0 6.58.0 0.300.40 0.501.50 . . .S31600 316 0.08 2.00 0.045 0.030 0.75 16.018.0 10.014.0 2.003.00 0.10 . . . . . .S31603 316L 0.030 2.00 0.045 0.030 0.75 16.018.0 10.0

35、14.0 2.003.00 0.10 . . . . . .S31609 316H 0.040.10 2.00 0.045 0.030 0.75 16.018.0 10.014.0 2.003.00 . . . . . . . . .S31635 316TiG0.08 2.00 0.045 0.030 0.75 16.018.0 10.014.0 2.003.00 0.10 . . . Ti 5 3 (C+N)min, 0.70 maxS31640 316CbG0.08 2.00 0.045 0.030 0.75 16.018.0 10.014.0 2.003.00 0.10 . . . Cb

36、 10 3 Cmin, 1.10 maxS31651 316N 0.08 2.00 0.045 0.030 0.75 16.018.0 10.014.0 2.003.00 0.100.16 . . . . . .S31653 316LN 0.030 2.00 0.045 0.030 0.75 16.018.0 10.014.0 2.003.00 0.100.16 . . . . . .S31700 317 0.08 2.00 0.045 0.030 0.75 18.020.0 11.015.0 3.04.0 0.10 . . . . . .S31703 317L 0.030 2.00 0.04

37、5 0.030 0.75 18.020.0 11.015.0 3.04.0 0.10 . . . . . .S31725 317LMG0.030 2.00 0.045 0.030 0.75 18.020.0 13.517.5 4.05.0 0.20 . . . . . .S31726 317LMNG0.030 2.00 0.045 0.030 0.75 17.020.0 13.517.5 4.05.0 0.100.20 . . . . . .S31727 . . . 0.030 1.00 0.030 0.030 1.00 17.519.0 14.516.5 3.84.5 0.150.21 2.

38、84.0 . . .S31753 317LNG0.030 2.00 0.045 0.030 0.75 18.020.0 11.015.0 3.04.0 0.100.22 . . . . . .S32050 . . . 0.030 1.50 0.035 0.020 1.00 22.024.0 20.023.0 6.06.8 0.210.32 0.40 . . .S32053 . . . 0.030 1.00 0.030 0.010 1.00 22.024.0 24.026.0 5.06.0 0.170.22 . . . . . .S32100 321 0.08 2.00 0.045 0.030

39、0.75 17.019.0 9.012.0 . . . 0.10 . . . Ti 5 3 (C+N)min, 0.70 maxS32109 321H 0.040.10 2.00 0.045 0.030 0.75 17.019.0 9.012.0 . . . . . . . . . Ti 4 3 (C+N)min, 0.70 maxS32615 . . . 0.07 2.00 0.045 0.030 4.86.0 16.519.5 19.022.0 0.301.50 . . . 1.502.50 . . .S32654 . . . 0.020 2.04.0 0.030 0.005 0.50 2

40、4.025.0 21.023.0 7.08.0 0.450.55 0.300.60 . . .S33228 . . . 0.040.08 1.00 0.020 0.015 0.30 26.028.0 31.033.0 . . . . . . . . . Ce 0.050.10Cb 0.61.0Al 0.025S33400 334G0.08 1.00 0.030 0.015 1.00 18.020.0 19.021.0 . . . . . . . . . Al 0.150.60Ti 0.150.60S34565 . . . 0.030 5.07.0 0.030 0.010 1.00 23.025

41、.0 16.018.0 4.05.0 0.400.60 . . . Cb 0.10S34700 347 0.08 2.00 0.045 0.030 0.75 17.019.0 9.013.0 . . . . . . . . . Cb 10 3 C min,1.00 maxS34709 347H 0.040.10 2.00 0.045 0.030 0.75 17.019.0 9.013.0 . . . . . . . . . Cb 8 3 C min,1.00 maxS34800 348 0.08 2.00 0.045 0.030 0.75 17.019.0 9.013.0 . . . . .

42、. . . . (Cb + Ta) 103Cmin, 1.00 maxTa 0.10Co 0.20S34809 348H 0.040.10 2.00 0.045 0.030 0.75 17.019.0 9.013.0 . . . . . . . . . (Cb + Ta) 83Cmin, 1.00 maxTa 0.10Co 0.20A240/A240M09c4TABLE 1 ContinuedUNSDesignationBTypeCCarbonDManganese Phos-phorusSulfur Silicon Chromium Nickel Molybdenum Nitrogen Cop

43、per OtherElementsE,FS35045 . . . 0.060.10 1.50 0.045 0.015 1.00 25.029.0 32.037.0 . . . . . . 0.75 Al 0.150.60Ti 0.150.60S35115 865 0.030 1.00 0.045 0.015 0.501.50 23.025.0 19.022.0 1.502.50 0.200.30 . . . . . .S35125 . . . 0.10 1.001.50 0.045 0.015 0.50 20.023.0 31.035.0 2.003.00 . . . . . . Cb 0.2

44、50.60S35135 . . . 0.08 1.00 0.045 0.015 0.601.00 20.025.0 30.038.0 4.04.8 . . . 0.75 Ti 0.401.00S35140 . . . 0.10 1.03.0 0.045 0.030 0.75 20.022.0 25.027.0 1.002.00 0.080.20 . . . Cb 0.250.75S35315 . . . 0.040.08 2.00 0.040 0.030 1.202.00 24.026.0 34.036.0 . . . 0.120.18 . . . Ce 0.030.10S38100 XM-1

45、5J0.08 2.00 0.030 0.030 1.502.50 17.019.0 17.518.5 . . . . . . . . . . . .S38815 . . . 0.030 2.00 0.040 0.020 5.56.5 13.015.0 13.017.0 0.751.50 . . . 0.751.50 Al 0.30Duplex (Austenitic-Ferritic)S31200 . . . 0.030 2.00 0.045 0.030 1.00 24.026.0 5.56.5 1.202.00 0.140.20 . . . . . .S31260 . . . 0.03 1.

46、00 0.030 0.030 0.75 24.026.0 5.57.5 2.53.5 0.100.30 0.200.80 W 0.100.50S31803 . . . 0.030 2.00 0.030 0.020 1.00 21.023.0 4.56.5 2.53.5 0.080.20 . . . . . .S32001 . . . 0.030 4.06.0 0.040 0.030 1.00 19.521.5 1.003.00 0.60 0.050.17 1.00 . . .S32003 . . . 0.030 2.00 0.030 0.020 1.00 19.522.5 3.04.0 1.5

47、02.00 0.140.20 . . . . . .S32101 . . . 0.040 4.06.0 0.040 0.030 1.00 21.022.0 1.351.70 0.100.80 0.200.25 0.100.80 . . .S32202 . . . 0.030 2.00 0.040 0.010 1.00 21.524.0 1.002.80 0.45 0.180.26 . . . . . .S32205 2205G0.030 2.00 0.030 0.020 1.00 22.023.0 4.56.5 3.03.5 0.140.20 . . . . . .S32304 2304G0.

48、030 2.50 0.040 0.030 1.00 21.524.5 3.05.5 0.050.60 0.050.20 0.050.60S32506 . . . 0.030 1.00 0.040 0.015 0.90 24.026.0 5.57.2 3.03.5 0.080.20 . . . W 0.050.30S32520 . . . 0.030 1.50 0.035 0.020 0.80 24.026.0 5.58.0 3.04.0 0.200.35 0.502.00 . . .S32550 255G0.04 1.50 0.040 0.030 1.00 24.027.0 4.56.5 2.93.9 0.100.25 1.502.50 . . .S32750 2507G0.030 1.20 0.035 0.020 0.80 24.026.0 6.08.0 3.05.0 0.240.32 0.50 . . .S32760K. . . 0.030 1.00 0.030 0.010 1.00 24.026.0 6.08.0 3.04.0 0.2