ASTM A249 A249M-2016 Standard Specification for Welded Austenitic Steel Boiler Superheater Heat-Exchanger and Condenser Tubes《锅炉 过热器 热交换器和冷凝器用奥氏体钢焊接管的标准规格》.pdf

1、Designation: A249/A249M 16 Used in USDOE-NE StandardsStandard Specification forWelded Austenitic Steel Boiler, Superheater, Heat-Exchanger, and Condenser Tubes1This standard is issued under the fixed designation A249/A249M; the number immediately following the designation indicates the yearof origin

2、al adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of

3、 Defense.1. Scope*1.1 This specification2covers nominal-wall-thicknesswelded tubes and heavily cold worked welded tubes made fromthe austenitic steels listed in Table 1, with various gradesintended for such use as boiler, superheater, heat exchanger, orcondenser tubes.1.2 Grades TP304H, TP309H, TP30

4、9HCb, TP310H,TP310HCb, TP316H, TP321H, TP347H, and TP348H aremodifications of Grades TP304, TP309S, TP309Cb, TP310S,TP310Cb, TP316, TP321, TP347, and TP348, and are intendedfor high-temperature service such as for superheaters andreheaters.1.3 The tubing sizes and thicknesses usually furnished tothi

5、s specification are18 in. 3.2 mm in inside diameter to 12 in.304.8 mm in outside diameter and 0.015 to 0.320 in. 0.4 to8.1 mm, inclusive, in wall thickness. Tubing having otherdimensions may be furnished, provided such tubes complywith all other requirements of this specification.1.4 Mechanical prop

6、erty requirements do not apply totubing smaller than18 in. 3.2 mm in inside diameter or 0.015in. 0.4 mm in thickness.1.5 Optional supplementary requirements are provided and,when one or more of these are desired, each shall be so statedin the order.1.6 The values stated in either inch-pound units or

7、 SI unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem may not be exact equivalents; therefore, each systemshall be used independently of the other. Combining valuesfrom the two systems may result in non-conformance wit

8、h thestandard. The inch-pound units shall apply unless the “M”designation of this specification is specified in the order.1.7 The following safety hazards caveat pertains only to thetest method described in the Supplementary Requirements ofthis specification. This standard does not purport to addres

9、s allof the safety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use. A specific warningstatement is given in Supplementary Requ

10、irement S7, NoteS7.1.2. Referenced Documents2.1 ASTM Standards:3A262 Practices for Detecting Susceptibility to IntergranularAttack in Austenitic Stainless SteelsA480/A480M Specification for General Requirements forFlat-Rolled Stainless and Heat-Resisting Steel Plate,Sheet, and StripA1016/A1016M Spec

11、ification for General Requirements forFerritic Alloy Steel, Austenitic Alloy Steel, and StainlessSteel TubesE112 Test Methods for Determining Average Grain SizeE213 Practice for Ultrasonic Testing of Metal Pipe andTubingE273 Practice for Ultrasonic Testing of the Weld Zone ofWelded Pipe and TubingE5

12、27 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)2.2 ASME Boiler and Pressure Vessel Code:Section VIII42.3 Other Standard:SAE J1086 Practice for Numbering Metals and Alloys(UNS)51This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Stee

13、l and Related Alloys and is the direct responsibility of SubcommitteeA01.10 on Stainless and Alloy Steel Tubular Products.Current edition approved May 1, 2016. Published May 2016. Originallyapproved in 1941. Last previous edition approved in 2015 as A249/A249M 15a.DOI: 10.1520/A0249_A0249M-16.2For A

14、SME Boiler and Pressure Vessel Code applications see related Specifi-cation SA-249 in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the st

15、andards Document Summary page onthe ASTM website.4Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Two Park Ave., New York, NY 10016-5990, http:/www.asme.org.5Available from Society of Automotive Engineers (SAE), 400 CommonwealthDr., Warrendale, PA 1509

16、6-0001, http:/www.sae.org.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1TABLE1ChemicalRequirements,%AGradeComposition,%UNSDesignationBCarbonManganesePhosphorousSulfurS

17、iliconChromiumNickelMolybdenumNitrogenCCopperOtherTP201S201000.155.507.50.0600.0301.0016.018.03.55.5.0.25.TP201LNS201530.036.47.50.0450.0150.7516.017.54.05.0.0.100.251.00.TP202S202000.157.510.00.0600.0301.0017.019.04.06.0.0.25.TPXM-19S209100.064.06.00.0450.0301.0020.523.511.513.51.503.000.200.40.NbG

18、0.100.30V0.100.30TPXM-29S240000.0811.514.50.0600.0301.0017.019.02.33.7.0.200.40.TP304S304000.082.000.0450.0301.0018.020.08.011.0.TP304LDS304030.0302.000.0450.0301.0018.020.08.012.0.TP304HS304090.040.102.000.0450.0301.0018.020.08.011.0.S304150.040.060.800.0450.0301.002.0018.019.09.010.0.120.18.Ce0.03

19、0.08TP304NS304510.082.000.0450.0301.0018.020.08.011.0.0.100.16.TP304LNDS304530.0302.000.0450.0301.0018.020.08.011.0.0.100.16.TP305S305000.122.000.0450.0301.0017.019.011.013.0.S306150.160.242.000.0300.0303.24.017.019.513.516.0.S308150.050.100.800.0400.0301.402.0020.022.010.012.0.0.140.20.Ce0.030.08TP

20、309SS309080.082.000.0450.0301.0022.024.012.015.0.TP309HS309090.040.102.000.0450.0301.0022.024.012.015.0.GradeComposition,%UNSDesignationBCarbonManganesePhosphorousSulfurSiliconChromiumNickelMolybdenumNitrogenCCopperOther.S306010.0150.500.800.0300.0135.05.617.018.017.018.00.200.050.35.TP309CbS309400.

21、082.000.0450.0301.0022.024.012.016.0.Nb10xC-1.10TP309HCbS309410.040.102.000.0450.0301.0022.024.012.016.0.Nb10xC-1.10TP310SS310080.082.000.0450.0301.0024.026.019.022.0.TP310HS310090.040.102.000.0450.0301.0024.026.019.022.0.TP310CbS310400.082.000.0450.0301.0024.026.018.022.0.Nb10xC-1.10TP310HCbS310410

22、.040.102.000.0450.0301.0024.026.019.022.0.Nb10xC-1.10.S310500.0302.000.0300.0150.4024.026.021.023.02.003.000.100.16.S312540.0201.000.0300.0100.8019.520.517.518.56.06.50.180.250.501.00.S312660.0302.004.000.0350.0201.0023.025.021.024.05.26.20.350.601.002.50W1.502.50.S312770.0203.000.0300.0100.5020.523

23、.026.028.06.58.00.300.400.501.50.TP316S316000.082.000.0450.0301.0016.018.010.014.02.003.00.TP316LDS316030.0302.000.0450.0301.0016.018.010.014.02.003.00.TP316HS316090.040.102.000.0450.0301.0016.018.010.014.02.003.00.TP316NS316510.082.000.0450.0301.0016.018.010.013.02.003.000.100.16.TP316LNDS316530.03

24、02.000.0450.0301.0016.018.010.013.02.003.000.100.16.S316550.0302.000.0450.0151.0019.521.58.09.50.501.500.140.251.00.TP317S317000.082.000.0450.0301.0018.020.011.015.03.04.0.TP317LS317030.0302.000.0450.0301.0018.020.011.015.03.04.0.GradeComposition,%UNSDesignationBCarbonManganesePhosphorousSulfurSilic

25、onChromiumNickelMolybdenumNitrogenCCopperOther.S317250.0302.000.0450.0301.0018.020.013.517.54.05.00.20.S317260.0302.000.0450.0301.0017.020.014.517.54.05.00.100.20.S317270.0301.000.0300.0301.0017.519.014.516.53.84.50.150.212.84.0.S320500.0301.500.0350.0201.0022.024.020.023.06.06.80.210.320.40.A249/A2

26、49M 162TABLE1Continued.S320530.0301.000.0300.0101.0022.024.024.026.05.06.00.170.22.TP321S321000.082.000.0450.0301.0017.019.09.012.0.0.10.Ti5(C+N)-0.70TP321HS321090.040.102.000.0450.0301.0017.019.09.012.0.0.10.Ti5(C+N)-0.70.S326150.072.000.0450.0304.806.0016.519.519.022.00.301.50.1.502.50.S326540.020

27、2.04.00.0300.0050.5024.025.021.023.07.08.00.450.550.300.60.S332280.040.081.000.0200.0150.3026.028.031.0333.0.Nb0.601.00Ce0.050.10Al0.025.S345650.0305.07.00.0300.0101.0023.025.016.018.04.05.00.400.60.Nb0.10TP347S347000.082.000.0450.0301.0017.019.09.012.0.Nb10xC-1.10TP347HS347090.040.102.000.0450.0301

28、.0017.019.09.012.0.Nb8xC-1.10TP348S348000.082.000.0450.0301.0017.019.09.012.0.(Nb+Ta)10xC-1.10Ta0.10Co0.20TP348HS348090.040.102.000.0450.0301.0017.019.09.012.0.(Nb+Ta)8xC-1.10Ta0.10Co0.20.S350450.060.101.500.0450.0151.0025.029.032.037.0.0.75Al0.150.60Ti0.150.60TPXM-15S381000.082.000.0300.0301.502.50

29、17.019.017.518.5.S388150.0302.000.0400.0205.56.513.015.015.017.00.751.50.0.751.50Al0.30maxAlloy20N080200.0702.000.0450.0351.0019.021.032.038.02.003.00.3.004.00Nb8Cmin.to1.00max.N083670.0302.000.0400.0301.0020.022.023.525.56.07.00.180.250.75.800N088000.101.500.0450.0151.0019.023.030.035.0.0.75Al0.150

30、.60Ti0.150.60FeE39.5min800HN088100.050.101.500.0450.0151.0019.023.030.035.0.0.75Al0.150.60Ti0.150.60FeE39.5minA249/A249M 163TABLE1Continued.N088110.050.101.500.0450.0151.0019.023.030.035.0.0.75Al0.250.60FTi0.250.60FFeE39.5min.N089260.0202.000.0300.0100.5019.021.024.026.06.07.00.150.250.501.50.N08904

31、0.0202.000.0400.0301.0019.023.023.028.04.05.00.101.002.00.AMaximum,unlessotherwiseindicated.BNewdesignationestablishedinaccordancewithPracticeE527andSAEJ1086.CThemethodofanalysisfornitrogenshallbeamatterofagreementbetweenthepurchaserandmanufacturer.DForsmalldiameterorthinwalls,orboth,wheremanydrawin

32、gpassesarerequired,acarbonmaximumof0.040%isnecessaryinGradesTP304LandTP316L.Smalloutsidediametertubesaredefinedasthoselessthan0.500in.12.7mminoutsidediameterandlightwallarethoselessthan0.049in.1.2mminminimumwallthickness.EIronshallbedeterminedarithmeticallybydifferenceof100minusthesumoftheotherspeci

33、fiedelements.F(Al+Ti)=0.85to1.20.GThetermNiobium(Nb)andColumbium(Cb)arealternatenamesforthesameelement.A249/A249M 1643. Ordering Information3.1 It is the responsibility of the purchaser to specify allrequirements that are necessary for material ordered under thisspecification. Such requirements may

34、include, but are notlimited to, the following:3.1.1 Quantity (feet, metres, or number of lengths),3.1.2 Name of material welded tubes (WLD) or heavily coldworked tubes (HCW),3.1.3 Grade (Table 1),3.1.4 Size (outside diameter and nominal wall thickness),3.1.5 Length (specific or random),3.1.6 Optiona

35、l requirements (13.6),3.1.7 Test report required (see Certification Section ofSpecification A1016/A1016M),3.1.8 Specification designation, and3.1.9 Special requirements and any supplementary require-ments selected.4. General Requirements4.1 Material furnished under this specification shall con-form

36、to the applicable requirements of the current edition ofSpecification A1016/A1016M, unless otherwise providedherein.5. Manufacture5.1 The welded (WLD) tubes shall be made from flat-rolledsteel by an automatic welding process with no addition of fillermetal.5.1.1 Subsequent to welding and prior to fi

37、nal heattreatment, the tubes shall be cold worked either in both weldand base metal or in weld metal only. The method of coldworking may be specified by the purchaser. When cold drawn,the purchaser may specify the minimum amount of reduction incross-sectional area or wall thickness, or both.5.1.2 He

38、avily cold worked (HCW) tubes shall be made byapplying cold working of not less than 35 % reduction in bothwall and weld to a welded tube prior to the final anneal. Nofiller metal shall be used in the making of the weld. Prior tocold working, the weld shall be 100 % radiographically in-spected in ac

39、cordance with the requirements of ASME Boilerand Pressure Vessel Code, Section VIII, Division 1, latestrevision, Paragraph UW 51.6. Heat Treatment6.1 All material shall be furnished in the heat-treatedcondition in accordance with the requirements of Table 2.6.2 A solution annealing temperature above

40、 1950 F 1065C may impair the resistance to intergranular corrosion aftersubsequent exposure to sensitizing conditions in TP309HCb,TP310HCb, TP321, TP321H, TP347, TP347H, TP348, andTP348H. When specified by the purchaser, a lower temperaturestabilization or re-solution anneal shall be used subsequent

41、 tothe initial high temperature solution anneal (see SupplementaryRequirement S4).6.3 N08020 shall be supplied in the stabilization treatmentcondition.7. Chemical Composition7.1 The heat analysis shall conform to the requirements asto chemical composition given in Table 1.8. Product Analysis8.1 An a

42、nalysis of either one length of flat-rolled stock orone tube shall be made for each heat. The chemical composi-tion thus determined shall conform to the requirements given inSection 7.8.2 A product analysis tolerance of Table A1.1 in Specifi-cation A480/A480M shall apply. The product analysis toler-

43、ance is not applicable to the carbon content for material with aspecified maximum carbon of 0.04 % or less.8.3 If the original test for product analysis fails, retests oftwo additional lengths of flat-rolled stock or tubes shall bemade. Both retests for the elements in question shall meet therequire

44、ments of the specification; otherwise all remainingmaterial in the heat or lot (See 13.9.1) shall be rejected or, atthe option of the producer, each length of flat-rolled stock ortube may be individually tested for acceptance. Lengths offlat-rolled stock or tubes that do not meet the requirements of

45、the specification shall be rejected.9. Tensile Requirements9.1 The material shall conform to the tensile propertiesprescribed in Table 3.10. Hardness Requirements10.1 The tubes shall have a Rockwell hardness number notexceeding the values specified in Table 3.11. Reverse-Bend Test Requirement11.1 A

46、section 4 in. 100 mm minimum in length shall besplit longitudinally 90 on each side of the weld. The sampleshall then be opened and bent around a mandrel with amaximum thickness of four times the wall thickness, with themandrel parallel to the weld and against the original outsidesurface of the tube

47、. The weld shall be at the point of maximumbend. There shall be no evidence of cracks, or of overlapsresulting from the reduction in thickness of the weld areas bycold working. When the geometry or size of the tubing make itdifficult to test the sample as a single piece, the sample may besectioned i

48、nto smaller pieces provided a minimum of 4 in. ofweld is subjected to reverse bending.NOTE 1The reverse bend test is not applicable when the specified wallis 10 % or more of the specified outside diameter, or the wall thickness is0.134 in. 3.4 mm or greater, or the outside diameter size is less than0.375 in. 9.5 mm. Under these conditions the reverse flattening test ofSpecification A1016/A1016M shall apply.12. Grain Size Requirement12.1 The grain size of Grades TP309H, TP309HCb,TP310H and TP310HCb, as determined in accordance withTest Me