ASTM A276 A276M-2016 Standard Specification for Stainless Steel Bars and Shapes《不锈钢棒材和型材的标准规格》.pdf

1、Designation: A276/A276M 15A276/A276M 16Standard Specification forStainless Steel Bars and Shapes1This standard is issued under the fixed designation A276/A276M; the number immediately following the designation indicates the yearof original adoption or, in the case of revision, the year of last revis

2、ion. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification covers hot-finished or

3、 cold-finished bars except bars for reforging (Note 1). It includes rounds, squares,and hexagons, and hot-rolled or extruded shapes, such as angles, tees, and channels in the more commonly used types of stainlesssteels. The free-machining types (Note 2) for general corrosion resistance and high-temp

4、erature service are covered in a separatespecification.NOTE 1For bars for reforging, see Specification A314.NOTE 2For free-machining stainless bars designed especially for optimum machinability, see Specification A582/A582M.NOTE 3There are standards covering high nickel, chromium, austenitic corrosi

5、on, and heat-resisting alloy materials. These standards are under thejurisdiction of ASTM Subcommittee B02.07 and may be found in Annual Book of ASTM Standards, Vol. 02.04.1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. Within the text, the SI

6、unitsare shown in brackets. The values stated in each system may not be exact equivalents; therefore, each system shall be usedindependently of the other. Combining values from the two systems may result in non-conformance with the standard. Theinch-pound units shall apply unless the “M” designation

7、 of this specification is specified in the order.2. Referenced Documents2.1 ASTM Standards:2A314 Specification for Stainless Steel Billets and Bars for ForgingA370 Test Methods and Definitions for Mechanical Testing of Steel ProductsA484/A484M Specification for General Requirements for Stainless Ste

8、el Bars, Billets, and ForgingsA582/A582M Specification for Free-Machining Stainless Steel BarsA751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsA1058 Test Methods for Mechanical Testing of Steel ProductsMetricE527 Practice for Numbering Metals and Alloys in the Uni

9、fied Numbering System (UNS)2.2 SAE Document:3SAE J 1086 Recommended Practice for Numbering Metals and Alloys3. Ordering Information3.1 It is the responsibility of the purchaser to specify all requirements that are necessary for material ordered under thisspecification. Such requirements may include

10、but are not limited to the following:3.1.1 Quantity (weight or number of pieces),3.1.2 Name of material: stainless steel,3.1.3 Form (bars, angles, and so forth),3.1.4 Condition (Section 4.1),3.1.5 Finish (Section 8 of Specification A484/A484M),3.1.6 Surface preparation of shapes (Section 8 of Specif

11、ication A484/A484M),3.1.7 Applicable dimensions including size, thickness, width, and length, l.1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.17on Flat-Rolled and Wrought Stainless

12、Steel.Current edition approved Jan. 1, 2015Jan. 1, 2016. Published January 2015January 2016. Originally approved in 1944. Last previous edition approved in 20132015 asA276 13a.A276/A276M 15. DOI: 10.1520/A0276_A0276M-15.10.1520/A0276_A0276M-16.2 For referencedASTM standards, visit theASTM website, w

13、ww.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.3 Available from Society of Automotive Engineers (SAE), 400 Commonwealth Dr., Warrendale, PA 15096-0001, http:/www.sa

14、e.org.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult pri

15、or editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 194

16、28-2959. United States13.1.8 Cross section (round, square, and so forth),3.1.9 Type or UNS designation (Table 1),3.1.10 ASTM designation and date of issue, and3.1.11 Whether bars are to be rolled as bars or cut from strip or plate.3.1.12 Test for magnetic permeability when specified by customer purc

17、hase order when ordering Types 201 and 205.3.1.13 Choice of testing track from the options listed in Test Methods A1058 when material is ordered to an M suffix (SI units)product standard. If the choice of test track is not specified in the order, then the defaultASTM track shall be used as noted in

18、TestMethods A10583.1.14 Supplementary requirements, and3.1.15 Additional requirements.A276/A276M 162TABLE 1 Chemical RequirementsAUNSDesigna-tionBTypeComposition, %Carbon Manganese Phos-phorusSulfur Silicon Chromium Nickel Molyb-denumNitrogen Other ElementsKAustenitic GradesN08020 Alloy 20 0.07 2.00

19、 0.045 0.035 1.00 19.021.0 32.038.0 2.003.00 . . . Cu 3.04.0Nb 8 C min.;1.00 maxN08367 . . . 0.030 2.00 0.040 0.030 1.00 20.022.0 23.525.5 6.07.0 0.180.25 Cu 0.75N08700 . . . 0.04 2.00 0.040 0.030 1.00 19.023.0 24.026.0 4.35.0 . . . Cu 0.50Cb 8 C min0.40 maxN08800 800 0.10 1.50 0.045 0.015 1.00 19.0

20、23.0 30.035.0 . . . . . . FeI 39.5 min.Cu 0.75Al 0.150.60Ti 0.150.60N08810 800H 0.050.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . . . . . FeI 39.5 min.Cu 0.75Al 0.150.60Ti 0.150.60N08811 . . . 0.060.10 1.50 0.045 0.015 1.00 19.023.0 30.035.0 . . . . . . FeI 39.5 min.Cu 0.75AlJ 0.250.60TiJ 0.250.6

21、0N08904 904L 0.020 2.00 0.045 0.035 1.00 19.023.0 23.028.0 4.05.0 0.10 Cu 1.02.0N08925 . . . 0.020 1.00 0.045 0.030 0.50 19.021.0 24.026.0 6.07.0 0.100.20 Cu 0.801.50N08926 . . . 0.020 2.00 0.030 0.015 0.50 19.021.0 24.026.0 6.07.0 0.150.25 Cu 0.501.50S20100 201 0.15 5.57.5 0.060 0.030 1.00 16.018.0

22、 3.55.5 . . . 0.25 . . .S20161 . . . 0.15 4.06.0 0.045 0.030 3.04.0 15.018.0 4.06.0 . . . 0.080.20 . . .S20162 . . . 0.15 4.08.0 0.040 0.040 2.54.5 16.521.0 6.010.0 0.502.50 0.050.25 . . .S20200 202 0.15 7.510.0 0.060 0.030 1.00 17.019.0 4.06.0 . . . 0.25 . . .S20500 205 0.120.25 14.015.5 0.060 0.03

23、0 1.00 16.518.0 1.01.7 . . . 0.320.40 . . .S20910 XM-19 0.06 4.06.0 0.045 0.030 1.00 20.523.5 11.513.5 1.503.00 0.200.40 Cb 0.100.30,V 0.100.30S21800 . . . 0.10 7.09.0 0.060 0.030 3.54.5 16.018.0 8.09.0 . . . 0.080.18 . . .S21900 XM-10 0.08 8.010.0 0.045 0.030 1.00 19.021.5 5.57.5 . . . 0.150.40 . .

24、 .S21904 XM-11 0.04 8.010.0 0.045 0.030 1.00 19.021.5 5.57.5 . . . 0.150.40 . . .S24000 XM-29 0.08 11.514.5 0.060 0.030 1.00 17.019.0 2.33.7 . . . 0.200.40 . . .S24100 XM-28 0.15 11.014.0 0.045 0.030 1.00 16.519.0 0.502.50 . . . 0.200.45 . . .S28200 . . . 0.15 17.019.0 0.045 0.030 1.00 17.019.0 . .

25、. 0.751.25 0.400.60 Cu 0.751.25S30200 302 0.15 2.00 0.045 0.030 1.00 17.019.0 8.010.0 . . . 0.10 . . .S30215 302B 0.15 2.00 0.045 0.030 2.003.00 17.019.0 8.010.0 . . . 0.10 . . .S30400 304 0.08 2.00 0.045 0.030 1.00 18.020.0 8.011.0 . . . . . . . . .S30403 304LC 0.030 2.00 0.045 0.030 1.00 18.020.0

26、8.012.0 . . . . . . . . .S30451 304N 0.08 2.00 0.045 0.030 1.00 18.020.0 8.011.0 . . . 0.100.16 . . .S30452 XM-21 0.08 2.00 0.045 0.030 1.00 18.020.0 8.010.0 . . . 0.160.30 . . .S30453 304LN 0.030 2.00 0.045 0.030 1.00 18.020.0 8.011.0 . . . 0.100.16 . . .S30454 . . . 0.03 2.00 0.045 0.030 1.00 18.0

27、20.0 8.011.0 . . . 0.160.30 . . .S30500 305 0.12 2.00 0.045 0.030 1.00 17.019.0 11.013.0 . . . . . . . . .S30800 308 0.08 2.00 0.045 0.030 1.00 19.021.0 10.012.0 . . . . . . . . .S30815 . . . 0.050.10 0.80 0.040 0.030 1.402.00 20.022.0 10.012.0 . . . 0.140.20 Ce 0.030.08S30900 309 0.20 2.00 0.045 0.

28、030 1.00 22.024.0 12.015.0 . . . . . . . . .S30908 309S 0.08 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . . . . .S30940 309Cb 0.08 2.00 0.045 0.030 1.00 22.024.0 12.016.0 . . . . . . Cb 10C-1.10S31000 310 0.25 2.00 0.045 0.030 1.50 24.026.0 19.022.0 . . . . . . . . .S31008 310S 0.08 2.00 0.045

29、0.030 1.50 24.026.0 19.022.0 . . . . . . . . .S31040 310Cb 0.08 2.00 0.045 0.030 1.50 24.026.0 19.022.0 . . . . . . Cb 10C-1.10S31254 . . . 0.020 1.00 0.030 0.010 0.80 19.520.5 17.518.5 6.06.5 0.180.25 Cu 0.501.00S31266 . . . 0.030 2.004.00 0.035 0.020 1.00 23.025.0 21.024.0 5.26.2 0.350.60 Cu 1.002

30、.50W 1.502.50S31400 314 0.25 2.00 0.045 0.030 1.503.00 23.026.0 19.022.0 . . . . . . . . .S31600 316 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 . . . . . .S31603 316LC 0.030 2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 . . . . . .S31635 316Ti 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014

31、.0 2.003.00 0.10 Ti 5(C+N)-0.70S31640 316Cb 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 0.10 Cb 10C-1.10S31651 316N 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 0.100.16 . . .A276/A276M 163TABLE 1 ContinuedUNSDesigna-tionBTypeComposition, %Carbon Manganese Phos-phorusSulfur Silico

32、n Chromium Nickel Molyb-denumNitrogen Other ElementsKS31653S31654316LN. . .0.0300.032.002.000.0450.0450.0300.0301.001.0016.018.016.018.010.013.010.013.02.003.002.003.000.100.160.160.30. . . . .S31700 317 0.08 2.00 0.045 0.030 1.00 18.020.0 11.015.0 3.04.0 0.10 . . .S31725 . . . 0.030 2.00 0.045 0.03

33、0 1.00 18.020.0 13.517.5 4.05.0 0.20 . . .S31726 . . . 0.030 2.00 0.045 0.030 1.00 17.020.0 14.517.5 4.05.0 0.100.20 . . .S31727 . . . 0.030 1.00 0.030 0.030 1.00 17.519.0 14.516.5 3.84.5 0.150.21 Cu 2.84.0S31730 . . . 0.030 2.00 0.040 0.010 1.00 17.019.0 15.016.5 3.04.0 0.045 Cu 4.0-5.0S32053 . . .

34、 0.030 1.00 0.030 0.010 1.00 22.024.0 24.026.0 5.06.0 0.170.22 . . .S32100 321 0.08 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . Ti 5(C+N)-0.70DS32654 . . . 0.020 2.04.0 0.030 0.005 0.50 24.025.0 21.023.0 7.08.0 0.450.55 Cu 0.300.60S34565 . . . 0.030 5.07.0 0.030 0.010 1.00 23.025.0 16.018.0 4

35、.05.0 0.400.60 Cb 0.10S34700 347 0.08 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . Cb 10C1.10S34800 348 0.08 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . Cb 10C1.10,Ta 0.10Co 0.20Austenitic-Ferritic GradesS31100 XM-26 0.06 1.00 0.045 0.030 1.00 25.027.0 6.07.0 . . . . . . Ti 0.25S31803 .

36、 . . 0.030 2.00 0.030 0.020 1.00 21.023.0 4.56.5 2.53.5 0.080.20 . . .S32101 . . . 0.040 4.06.0 0.040 0.030 1.00 21.022.0 1.351.70 0.100.80 0.200.25 Cu 0.100.80S32202 . . . 0.030 2.00 0.040 0.010 1.00 21.524.0 1.002.80 0.45 0.180.26 . . .S32205 . . . 0.030 2.00 0.030 0.020 1.00 22.023.0 4.56.5 3.03.

37、5 0.140.20 . . .S32304 . . . 0.030 2.50 0.040 0.030 1.00 21.524.5 3.05.5 0.050.60 0.050.20 Cu 0.050.60S32506 . . . 0.030 1.00 0.040 0.015 0.90 24.026.0 5.57.2 3.03.5 0.080.20 W 0.050.30S32550 . . . 0.04 1.50 0.040 0.030 1.0 24.027.0 4.56.5 2.93.9 0.100.25 Cu 1.502.50S32750L . . . 0.030 1.20 0.035 0.

38、020 0.80 24.026.0 6.08.0 3.05.0 0.240.32 Cu 0.50S32760E . . . 0.030 1.00 0.030 0.010 1.00 24.026.0 6.08.0 3.04.0 0.200.30 Cu 0.501.00W 0.501.00S82441 . . . 0.030 2.54.0 0.035 0.005 0.070 23.025.0 3.04.5 1.002.00 0.200.30 Cu 0.100.80Ferritic GradesS40500 405 0.08 1.00 0.040 0.030 1.00 11.514.5 0.50 .

39、 . . . . . Al 0.100.30S40976 . . . 0.030 1.00 0.040 0.030 1.00 10.511.7 0.751.00 . . . 0.040 Cb 10(C+N)-0.80S42900 429 0.12 1.00 0.040 0.030 1.00 14.016.0 . . . . . . . . . . . .S43000 430 0.12 1.00 0.040 0.030 1.00 16.018.0 . . . . . . . . . . . .S44400 444 0.025 1.00 0.040 0.030 1.00 17.519.5 1.00

40、 1.752.50 0.035 Ti+Cb 0.20+4 (C+N)-0.80S44600 446 0.20 1.50 0.040 0.030 1.00 23.027.0 0.75 . . . 0.25 . . .S44627 XM-27F 0.010G 0.40 0.020 0.020 0.40 25.027.5 0.50 0.751.50 0.015G Cu 0.20Cb 0.050.20S44700 . . . 0.010 0.30 0.025 0.020 0.20 28.030.0 0.15 3.54.2 0.020 C+N 0.025Cu 0.15S44800 . . . 0.010

41、 0.30 0.025 0.020 0.20 28.030.0 2.002.50 3.54.2 0.020 C+N 0.025Cu 0.15Martensitic GradesS40300 403 0.15 1.00 0.040 0.030 0.50 11.513.0 . . . . . . . . . . . .S41000 410 0.080.15 1.00 0.040 0.030 1.00 11.513.5 . . . . . . . . . . . .S41040 XM-30 0.18 1.00 0.040 0.030 1.00 11.013.0 . . . . . . . . . C

42、b 0.050.30S41400 414 0.15 1.00 0.040 0.030 1.00 11.513.5 1.252.50 . . . . . . . . .S41425 . . . 0.05 0.501.00 0.020 0.005 0.50 12.015.0 4.07.0 1.502.00 0.060.12 Cu 0.30S41500 H 0.05 0.501.00 0.030 0.030 0.60 11.514.0 3.55.5 0.501.00 . . . . . .S42000 420 0.15 min 1.00 0.040 0.030 1.00 12.014.0 . . .

43、 . . . . . . . . .S42010 . . . 0.150.30 1.00 0.040 0.030 1.00 13.515.0 0.350.85 0.400.85 . . . . . .S43100 431 0.20 1.00 0.040 0.030 1.00 15.017.0 1.252.50 . . . . . . . . .S44002 440A 0.600.75 1.00 0.040 0.030 1.00 16.018.0 . . . 0.75 . . . . . .S44003 440B 0.750.95 1.00 0.040 0.030 1.00 16.018.0 .

44、 . . 0.75 . . . . . .S44004 440C 0.951.20 1.00 0.040 0.030 1.00 16.018.0 . . . 0.75 . . . . . .A Maximum, unless range or minimum is indicated. Where elipsesellipses (. . .) appear in this table, there is no requirement and the element need not be determined orreported.B Designations established in

45、accordance with Practice E527 and SAE J 1086.C For some applications, the substitution ofType 304LforType 304, orType 316LforType 316 may be undesirable because of design, fabrication, or service requirements.In such cases, the purchaser should so indicate on the order.D Nitrogen content is to be re

46、ported for this grade.E % Cr + 3.3 % Mo + 16 % N $ 40.F Nickel plus copper shall be 0.50 % max.G Product analysis tolerance over the maximum limit for carbon and nitrogen shall be 0.002 %.H Wrought version of CA 6NM.I Iron shall be determined arithmetically by difference of 100 minus the sum of spec

47、ified elements.A276/A276M 164NOTE 4Atypical ordering description is as follows: 5000 lb 2270 kg Stainless Steel Bars,Annealed and Centerless Ground, 112 in. 40 mm Round,10 to 12 ft 3 to 3.7 m in length, Type 304, ASTM Specification A276/A276M dated _. End use: machined valve parts.4. Manufacture4.1

48、Condition:4.1.1 Bars shall be furnished in one of the following conditions listed in the Mechanical Requirements table:4.1.1.1 Condition AAnnealed.4.1.1.2 Condition HHardened and tempered at a relatively low temperature.4.1.1.3 Condition THardened and tempered at a relatively high temperature.4.1.1.4 Condition S Strain HardenedRelatively light cold work.4.1.1.5 Condition BRelatively severe cold work.4.1.1.6 Condition SAStabilized annealed.5. Chemical Composition5.1 The steel shall conform to the requirements for chemica